CN102765200A - 连续纤维编织拉挤管的浸胶方法 - Google Patents
连续纤维编织拉挤管的浸胶方法 Download PDFInfo
- Publication number
- CN102765200A CN102765200A CN2012102604350A CN201210260435A CN102765200A CN 102765200 A CN102765200 A CN 102765200A CN 2012102604350 A CN2012102604350 A CN 2012102604350A CN 201210260435 A CN201210260435 A CN 201210260435A CN 102765200 A CN102765200 A CN 102765200A
- Authority
- CN
- China
- Prior art keywords
- resin
- fiber
- fibrage
- woven layer
- vacuum
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明创造涉及化工技术领域，具体地说是一种纤维编织增强树脂管的浸胶方法，其特征在于该浸胶方法利用抽真空的原理，将运动中的纤维编织层 浸泡在一个密封的树脂胶筒中，并进行抽真空处理，使树脂迅速穿透纤维编织层，达到浸透胶的目的，真空箱(1)采用二个半圆筒组合而成，二半之间用密封胶垫(11)密封，编织纤维层(7)用环形软橡胶棒(6)密封，树脂通过进料口(3)进入真空箱(1)内，将纤维编织层(7)浸泡在树脂中，树脂透过纤维层(7)到模具(8)的槽内，形成几道内胶环(9)；关闭进料口(3)，启动真空设备(5)，跟随纤维层(7)进来的空气在负压作用下，迅速上升破裂，使树脂迅速渗透到纤维层(7)内，达到快速完成浸透纤维，本发明创造同现有技术相比，采用真空负压完成纤维浸胶的工艺，产品结合牢固，强度高，表面光洁度高。
Description
[技术领域]
本发明创造涉及化工技术领域，主要是编织纤维的浸胶方法，具体地说是一种纤维编织增强树脂管的浸胶方法。
[背景技术]
众所周知，纤维编织增强的热固性树脂管道生产时，无法对单根纤维预浸胶，只能在编织好后进行浸胶，由于编织好的纤维比较紧密，常规的浸胶方法难以在短时间奏效，现有的缠绕和挤拉工艺中，纤维浸胶工艺可以让纤维单丝预浸胶，然后进炉固化，但编织好的纤维管却不能进行单丝预浸胶，这就要求有一种浸胶方法能在短时间内（大约2-3分钟）将编织好的纤维整体浸胶，到目前为止在世界上还没有人对运动中的编织纤维有好的浸胶处理方法。
[发明内容]
本发明为了解决上述问题，根据编织纤维的特性，采用抽真空的原理，将一个组合真空箱 与运动中的编织纤维、模具通过一个软质密封环组成一个密封系统，在真空负压下，快速使编织纤维层浸胶透彻。
为实现上述目的，设计一种连续纤维编织拉挤管浸胶方法，包括纤维层和材料其特征在于：该浸胶方法利用抽真空的原理，将运动中的纤维编织层 浸泡在一个密封的树脂胶筒中，并进行抽真空处理，使树脂迅速穿透纤维编织层，达到浸透胶的目的，真空箱(1)采用两个半圆筒组合而成，两个半圆筒之间用密封胶垫(11)密封，编织纤维层(7)用环形软橡胶棒(6)密封，树脂通过进料口(3)进入真空箱(1)内，将纤维编织层(7)浸泡在树脂中，树脂透过纤维层(7)到模具(8)的槽内，形成几道内胶环(9)；关闭进料口(3)，启动真空设备(5)，跟随纤维层(7)进来的空气在负压作用下，迅速上升破裂，使树脂迅速渗透到纤维层(7)内，达到快速完成浸透纤维。
所用的浸胶树脂是环氧树脂或聚酯树脂或酚醛树脂，也可以是各种改性高性能热固性树脂。高性能热固性树脂：脲醛树脂、三聚氰胺-甲醛树脂、不饱和树脂、聚氨酯、聚酰亚胺等增强树脂，包括替代玻璃的热固性树脂。
本发明创造同现有技术相比采用真空负压完成纤维浸胶工艺，使产品结合牢固，强度高，表面光洁度高。
[附图说明]
图1是本发明创造的结构示意图。
图2是图1的侧视图。
参见图1和图2，1，为真空箱，2为阀门，3为进料口，4为真空口，5为真空泵，6为密封环， 7为编织纤维层，8为模具，9为内胶环，10为放料口，11为胶垫，12螺栓。
[具体实施方式]
以下结合图1浸胶系统示意图，对本发明创造做进一步操作说明，采用真空技术对本专业的人是非常清楚的。
1、参照图1，在各种产品模具（8）表面编织好纤维层（7）；
2、将真空箱（1）两个半圆筒用螺栓（12）锁紧 ，并加上密封条（11）和环向密封环（6），形成密封系统；
3、打开阀门（2），让树脂通过进料口（3）进入真空箱（1）内；
4、当树脂料达到一定量时，关闭阀门（2），启动真空泵（5），开始抽真空。
5、启动主机，纤维层（7）开始运动，出来的纤维层已浸胶好，进入下一步工序；
6、当树脂消耗到一定程度，打开阀门（2），补充树脂。
Claims (3)
1.一种连续纤维编织拉挤管浸胶方法，包括纤维层和树脂材料，其特征在于：
该浸胶方法利用抽真空的原理，将运动中的纤维编织层 浸泡在一个密封的树脂胶筒中，并进行抽真空处理，使树脂迅速穿透纤维编织层，达到浸透胶的目的，真空箱(1)采用两个半圆筒组合而成，两个半圆筒之间用密封胶垫(11)密封，编织纤维层(7)用环形软橡胶棒(6)密封，树脂通过进料口(3)进入真空箱(1)内，将纤维编织层(7)浸泡在树脂中，树脂透过纤维层(7)到模具(8)的槽内，形成几道内胶环(9)；关闭进料口(3)，启动真空设备(5)，跟随纤维层(7)进来的空气在负压作用下，迅速上升破裂，使树脂迅速渗透到纤维层(7)内，达到快速完成浸透纤维。
2.如权利要求1所述的一种连续纤维编织拉挤管浸胶方法，其特征在于该方法实施例操作步骤如下：
A.在模具(8)表面编织好纤维层(7)；
B.将真空箱(1)两个半圆筒用螺栓(12)锁紧 ，并加上密封条(11)和环向密封环(6)，形成密封系统；
C.打开阀门(2)，让树脂通过进料口(3)进入真空箱1内；
D.当树脂料达到一定量时，关闭阀门(2)，启动真空泵(5)，开始抽真空；
E.启动主机，纤维层(7)开始运动，出来的纤维层已浸胶好，进入下一步工序；
F.当树脂消耗到一定程度，打开阀门(2)，补充树脂。
3.如权利要求1所述的一种连续纤维编织拉挤管浸胶方法，其特征在于：
所用的浸胶树脂是环氧树脂或聚酯树脂或酚醛树脂，也可以是各种改性高性能热固性树脂。