CN102765115A - Process bamboo rhizome, as well as processing method and use thereof - Google Patents
Process bamboo rhizome, as well as processing method and use thereof Download PDFInfo
- Publication number
- CN102765115A CN102765115A CN2012102034978A CN201210203497A CN102765115A CN 102765115 A CN102765115 A CN 102765115A CN 2012102034978 A CN2012102034978 A CN 2012102034978A CN 201210203497 A CN201210203497 A CN 201210203497A CN 102765115 A CN102765115 A CN 102765115A
- Authority
- CN
- China
- Prior art keywords
- bamboo
- bamboo whip
- whip
- processing method
- rhizomes
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention relates to the field of bamboo ware processing and preparation, in particular to a bamboo rhizome processing method and use of a bamboo rhizome. The bamboo rhizome processing method sequentially comprises the following steps: collecting: shearing bamboo rhizomes, which grow outside the soil, have uniform internodes and are 1.0-2.0 cm in diameter, from November each year to the following February, and then trimming root hairs on the nodes of the bamboo rhizomes; bundling the collected bamboo rhizomes and drying the collected bamboo rhizomes in shade; unbundling the bamboo rhizomes dried in shade and orderly arranging the bamboo rhizomes to naturally drying the bamboo rhizomes in the sun until the color of the bamboo rhizomes changes from green to earthy yellow, wherein the bamboo rhizomes is prevented from getting wet in the rain and becoming mildewed; then polishing, preparing a cooking agent from a softening agent or a mildew-retarding agent, water and oxydol in the weight ratio of 1:1000:(50-150), putting the polished bamboo rhizomes into the cooking agent, heating to 90-100 DEG C and preserving the heat for 40-45 min; and finally drying the bamboo rhizomes under the blazing sun for quite a long time. The process bamboo rhizome prepared by the method has the advantages of aesthetic appearance, good toughness and long service life, and can be used for manufacturing handles of handbags, buttons, handicraft articles and the like.
Description
Technical field
The present invention relates to a kind of bamboo product processing and preparing field, relate in particular to a kind of bamboo whip processing method and purposes.
Background technology
The bamboo form is graceful, noble character and sterling integrity, and culture is deep.The bamboo whip is strong but pliable in texture, Jie Mi and swelling, and the root point of arranging equably on the flagellum, profile is peculiar simple and unsophisticated natural.On the bamboo whip joint is arranged, takes root on the joint, through can the preparing various kinds handicraft after the above-mentioned processing, be worth very high, yet natural bamboo whip quality is uneven, fragility is big, easily broken yielding, service life short, has to be further processed.
CN201709598 (2011-1-19) discloses a kind of " bamboo whip frame mandarin fan ", is to constitute fan frame and fan handle with a bamboo whip bending one, and the fan handle that solves bamboo frame mandarin fan is prone to from fanning the problem that frame comes off.And the present invention is the preparing raw material method of bamboo whip handicraft processing, belongs to its preceding road processing technology, and its range of application is applicable to the processing of various bamboo whip handicrafts.
Summary of the invention
One of the object of the invention provides the processing method of the technology of a kind of good looking appearance, good toughness, long service life with the bamboo whip.
First technical purpose of the present invention is achieved through following technical scheme: a kind of technology comprises step successively with the processing method of bamboo whip:
(1) gather: in the February in November to the second in every year year, shear be grown in the outer internode of earth uniformly, diameter is at the bamboo whip of 1.0-2.0cm, prunes the coring on the bamboo flagellum then;
(2) pile dries in the shade: the bamboo after will gathering is whipped and bundle is placed on temperature is to place 60-90 days in 10～20 ℃, the indoor environment of aeration-drying;
(3) natural drying: the bamboo whip after will drying in the shade is taken marshalling apart, lets the sun dry naturally, treats that the color of bamboo whip changes khaki into by green, can not drench with rain to produce to go mouldy, and bamboo whip moisture content is in 15%;
(4) polishing;
(5) drug treating: with the spirit of softening agent or entomophthora, water and hydrogen peroxide solution by weight 1:1000: (50-150) be mixed with cooking liquor, the bamboo whip after will polishing then drops in the said cooking liquor, is heated to 90-100 ℃ and keep 40-45min;
(6) drying of being exposed to the sun: the bamboo whip after the drug treating is exposed to the sun under the sun 3-5 solar day, transfers milky to the surface, moisture content goes to baking room in 15%, and oven dry is 4-5 hour in 80-85 ℃ of degree environment, makes it moisture content and reaches 9-11%;
(7) filing classification.
Bamboo whip of the present invention is the subterranean stem of bamboo plant cross growth in soil.Time that grasp is gathered and quality in conjunction with follow-up drying in the shade and natural drying, obtain toughness bamboo whip preferably; Through polishing, obtain flagellum size to fit and mellow and full bamboo whip then; Pass through drug treating again, further strengthen its toughness and mildew resistance; Obtain the profile and the color of required bamboo whip then through the drying of being exposed to the sun, thereby the processing through each step of the present invention, the technology that obtains good looking appearance, good toughness, long service life is used the bamboo whip.
As preferably, said step (4) polishing is that the bamboo whip behind the natural drying is put into showering polishing machine polishing 35-50min is mellow and full to flagellum.
As preferably, the bamboo that said bamboo whip is taken from is one or more in red shell bamboo, Ph. bambusoides, mottled bamboo or the golden mao bamboon.
As preferably, when said step (1) is pruned the coring on the bamboo flagellum, keep coring length 3-4mm.
As preferably, said step (1) bamboo whip length is 40-55cm.
As preferably, earlier the coring on the khaki bamboo flagellum is pruned with reservation coring length 0.9-1.2mm before said step (4) polishing, and the length saw of bamboo whip is 40-52cm.
As preferably, the boiling medicine of said step (5) is the mixed liquor of softening agent, water and the hydrogen peroxide solution of weight ratio 1:1000:100.
As preferably, the softening agent of said step (5) is alkyl acyl quaternary ammonium salt, pyridine quaternary ammonium salt type or imidazole type softening agent.
As preferably, the bamboo whip after said step (5) will be polished drops in the said cooking liquor, is heated to 90-190 ℃ and keep 40-45min.
As preferably; Said step (7) filing classification specifically is that dried bamboo whip is accurately filed with diameter; With 2mm is a level time, and the bamboo whip tentatively is divided into 1.0-1.2mm, 1.2-1.4mm, 1.4-1.6mm, 1.6-1.8mm, five levels of 1.8-2.0mm time by thickness.
More preferably, in each level is inferior, divide credit rating again:
⑴. first quality: 1.. bamboo whip two thickness differs and is no more than 0.1cm; 2.. the quantity of control joint; 3.. the distance of whole bamboo whip ring and ring is even; 4.. broken skin and spot can not be arranged; 5.. bamboo shoot bud lines can not twist; 6.. the hole at two can not surpass 0.4cm; 7.. the age will be about 2 years; 8.. the whip body will be justified;
⑵. secondary quality: 1.. bamboo whip two thickness differs and is no more than 0.1cm, 2.. and the distance of whole bamboo whip ring and ring is even; 3.. broken skin and obvious spot can not be arranged; 4.. bamboo shoot bud lines can not twist; 5.. the hole at two can not surpass 0.5cm; 6.. the age will be about 2 years; 7.. the bamboo body will be justified;
⑶. three grades of quality: 1.. bamboo whip two thickness differs and is no more than 0.2cm; 2.. too big broken skin and spot can not be arranged; 3.. the age will be more than 1 year.
As preferably, said method comprises that also step (8) deposits dispensing, and said step (8) uses the silica-gel desiccant sealing of 2-5mm to preserve when depositing.
Two of the object of the invention provides a kind of technology that makes according to said method and uses the bamboo whip.
As preferably, said technology uses the length of bamboo whip to be 40-52cm, and bamboo whip two thickness differs and is no more than 0.2cm, and bamboo whip water content is 9～11%.
Three of the object of the invention provides the purposes of a kind of technology that makes according to said method with the bamboo whip.
A kind of technology that makes according to said method is used the bamboo whip, and what be characterized in being used to making case and bag carries hand and button, handicraft etc.
Through above-mentioned processed, bamboo whip good looking appearance of the present invention, high, the long service life of toughness have good practicality; Have waterproof, anticorrosive, good weatherability, do not damaged by worms, performance such as nonhazardous, no paint, especially can be used for making the hand of carrying of case and bag, replace traditional chemical industry or leather to carry hand; Each ring is supporting with finger; The special efficacy that massage is promptly arranged has fashion effect attractive in appearance again, meets the new industry requirement of environmental protection of country.
The specific embodiment
Embodiment one
Shear in November winter at the year end that the internode be grown in earth outside is uniform, diameter is at the bamboo whip of 1.0-2.0cm, bamboo whip length is 40-45cm when gathering, the bamboo that the bamboo whip is taken from is red shell bamboo, prunes the coring on the bamboo flagellum then; Keep coring length 3-4mm.Bamboo after gathering whipped bundle to be placed on aeration-drying, temperature be to place in 10～20 ℃ the indoor environment to dry in the shade in 60-70 days; Bamboo whip after will drying in the shade is taken marshalling apart, lets the sun dry naturally, treats that the color of bamboo whip changes khaki into by green, can not drench with rain to produce to go mouldy, and moisture content is 12-15%; Coring on the khaki bamboo flagellum is pruned with reservation coring length 0.9-1.2mm, and the length saw of bamboo whip is 40-52cm, then with the polishing of the bamboo whip behind natural drying 35-50min; Alkyl acyl quaternary ammonium salt softening agent, water and hydrogen peroxide solution are mixed with cooking liquor by weight 1:1000:120, and bamboo whip after will polishing then drops in the cooking liquor, is heated to 90 ℃ and keep 45-50min; With the bamboo whip after the drug treating summer 3～5 solar day to the surfaces of being exposed to the sun under the sun transfer milky, moisture content in 15%, go to baking room, oven dry is 4 hours in 80-85 ℃ of degree environment, makes it moisture content and reaches 9-11%;
File classification then and deposit dispensing:
Specifically being that the bamboo whip after being exposed to the sun is accurately filed with diameter, is a level time with 2mm, and the bamboo whip tentatively is divided into 1.0-1.2mm, 1.2-1.4mm, 1.4-1.6mm, 1.6-1.8mm, five levels of 1.8-2.0mm time by thickness; In each level is inferior, divide credit rating then again:
⑴. first quality: 1.. bamboo whip two thickness differs and is no more than 0.1cm; 2.. the quantity of control joint; 3.. the distance of whole bamboo whip ring and ring is even; 4.. broken skin and spot can not be arranged; 5.. bamboo shoot bud lines can not twist; 6.. the hole at two can not surpass 0.4cm; 7.. the age will be about 2 years; 8.. the whip body will be justified;
⑵. secondary quality: 1.. bamboo whip two thickness differs and is no more than 0.1cm, 2.. and the distance of whole bamboo whip ring and ring is even; 3.. broken skin and obvious spot can not be arranged; 4.. bamboo shoot bud lines can not twist; 5.. the hole at two can not surpass 0.5cm; 6.. the age will be about 2 years; 7.. the bamboo body will be justified;
⑶. three grades of quality: 1.. bamboo whip two thickness differs and is no more than 0.2cm; 2.. too big broken skin and spot can not be arranged; 3.. the age will be more than 1 year.
The bamboo whip that to file again after the classification is put into the warehouse, stacks neatly, must dryly ventilate; Perhaps use polybag, in add silica-gel desiccant drier sealing and preserve; According to the Different products needs, select the bamboo whip raw material dispensing of different brackets and diameter.
The technology that detection this method makes compares with unprocessed original bamboo whip of directly gathering, the performance parameter of PVC dermatine with the performance parameter of bamboo whip simultaneously, and the result sees table 1.
The temperature tolerance evaluation criterion: one-level, can be low temperature resistant-60 ℃, high temperature resistant 150 ℃;
Secondary, low temperature resistant-40 ℃, high temperature resistant 110 ℃;
Three grades, low temperature resistant-30 ℃, high temperature resistant 100 ℃;
Level Four, can be used for 50 ℃ by low temperature resistant-5 ℃.
Embodiment two
In December winter at the year end, shear be grown in the outer internode of earth uniformly, diameter is at the bamboo whip of 1.0-2.0cm, bamboo whip length is 45-50cm when gathering.The bamboo that the bamboo whip is taken from is a Ph. bambusoides, prunes the coring on the bamboo flagellum then; Keep coring length 3-4mm.Bamboo after gathering whipped bundle to be placed on aeration-drying, temperature be to place 70-80 days in 10～20 ℃ the indoor environment; Bamboo whip after will drying in the shade is taken marshalling apart, lets the sun dry naturally, treats that the color of bamboo whip changes khaki into by green, can not drench with rain to produce to go mouldy, and moisture content is 9-12%; Coring on the khaki bamboo flagellum is pruned with reservation coring length 0.9-1.2mm, and the length saw of bamboo whip is 40-52cm, then with the polishing of the bamboo whip behind natural drying 50min; Water and hydrogen peroxide solution are mixed with cooking liquor by weight 100:10, and bamboo whip after will polishing then drops in the cooking liquor, is heated to 95 ℃ and keep 35-40min; Bamboo whip after the drug treating is exposed to the sun 3-5 solar day to transferring milky, moisture content in 15% to the surface under the sun, goes to baking room, oven dry is 4.5 hours in 80-85 ℃ of degree environment, makes it moisture content and reaches 9-11%; Then with embodiment one filing classification with deposit.
Embodiment three
In January winter at the beginning of the year, shear be grown in the outer internode of earth uniformly, diameter is at the bamboo whip of 1.0-2.0cm, bamboo whip length is 50-55cm when gathering.The bamboo that the bamboo whip is taken from is golden mao bamboon, prunes the coring on the bamboo flagellum then; Keep coring length 3-4mm.Bamboo after gathering whipped bundle to be placed on temperature be to place 80-90 days in 10～20 ℃ the indoor environment; Bamboo whip after will drying in the shade is taken marshalling apart, lets the sun dry naturally, treats that the color of bamboo whip changes khaki into by green, can not drench with rain to produce to go mouldy, and moisture content is 8-11%; Coring on the khaki bamboo flagellum is pruned with reservation coring length 1.0-1.1mm, and the length saw of bamboo whip is 48-50cm, the bamboo whip behind the natural drying is put into showering polishing machine polishing 40-45min; Imidazole type softening agent, water and hydrogen peroxide solution are mixed with cooking liquor by weight 1:1000:100, and bamboo whip after will polishing then drops in the cooking liquor, is heated to 95-100 ℃ and keep 40-45min; Bamboo whip after the drug treating is exposed to the sun 3-5 solar day to moisture content in 15% under the sun, goes to baking room, oven dry is 5 hours in 80-85 ℃ of degree environment, makes it moisture content and reaches 9-11%; Then with embodiment one filing classification with deposit.
The comparative example one
With embodiment one, different is without drying in the shade but directly natural drying, polishing back drug treating are exposed to the sun again.
The comparative example two
With embodiment two, different is without drug treating.
The comparative example three
With embodiment three, different is polishing 10-15min drops into then and is heated to 80 ℃ and keep 50min in the hydrogen peroxide solution, is exposed to the sun, files and deposit.
The comparative example four
With embodiment three, different is, and the 1 day water content to the bamboo whip of being exposed to the sun is 15%.
[0034]
The performance parameter of each embodiment product of table 1 and original bamboo whip, PVC dermatine relatively
The performance parameter of each comparative example's product of table 2 and original bamboo whip, PVC dermatine relatively
This specific embodiment only is to explanation of the present invention; It is not a limitation of the present invention; Those skilled in the art can make the modification that does not have creative contribution to present embodiment as required after reading this specification, but as long as in claim scope of the present invention, all receive the protection of Patent Law.
Claims (10)
1. a technology is characterized in that: comprise step successively with the processing method of bamboo whip:
(1) gather: in the February in November to the second in every year year, shear be grown in the outer internode of earth uniformly, diameter is at the bamboo whip of 1.0-2.0cm, prunes the coring on the bamboo flagellum then;
(2) pile dries in the shade: after the bamboo after will gathering is whipped bundle, in aeration-drying, temperature are 10～20 ℃ indoor environment, placed 60-90 days;
(3) natural drying: the bamboo whip after will drying in the shade is taken marshalling apart, is positioned under the sun and dries naturally, treats that the color of bamboo whip changes khaki into by green, can not drench with rain to produce to go mouldy, and moisture content is below 15%;
(4) polishing;
(5) drug treating: with the spirit of softening agent or entomophthora, water and hydrogen peroxide solution by weight 1:1000: (50-150) be mixed with cooking liquor, the bamboo whip after will polishing then drops in the said cooking liquor, is heated to 90-100 ℃ and keep 30-55min;
(6) drying of being exposed to the sun: the bamboo whip after the drug treating is exposed to the sun 3-5 solar day to moisture content in 15% under the sun, oven dry 4-5 hour to moisture content reaches 9-11% in 80-85 ℃ of environment then;
(7) filing classification.
2. a kind of technology according to claim 1 is characterized in that with the processing method of bamboo whip: the bamboo that said bamboo whip is taken from is one or more in red shell bamboo, Ph. bambusoides, mottled bamboo or the golden mao bamboon, and said step (1) bamboo whip length is at 40-55cm.
3. a kind of technology according to claim 2 is characterized in that with the processing method of bamboo whip: said step (4) is that the bamboo whip behind the natural drying is put into showering polishing machine polishing 30-50min.
4. a kind of technology according to claim 3 is characterized in that with the processing method of bamboo whip: earlier the coring on the khaki bamboo flagellum is pruned with reservation coring length 0.9-1.2mm before said step (4) polishing, and the length saw of bamboo whip is 40-52cm.
5. a kind of technology according to claim 4 is characterized in that with the processing method of bamboo whip: the boiling medicine of said step (5) is the mixed liquor of softening agent, water and the hydrogen peroxide solution of weight ratio 1:1000:100.
6. a kind of technology according to claim 5 is characterized in that with the processing method of bamboo whip: the softening agent of said step (5) is alkyl acyl quaternary ammonium salt, pyridine quaternary ammonium salt type or imidazole type softening agent.
7. a kind of technology according to claim 6 is characterized in that with the processing method of bamboo whip: the bamboo whip after said step (5) will be polished drops in the said cooking liquor, is heated to 90-100 ℃ and keep 40-45min.
8. a kind of technology according to claim 7 is with the processing method of bamboo whip; It is characterized in that: said step (7) filing classification specifically is that the bamboo whip after being exposed to the sun is accurately filed with diameter; With 2mm is a level time, and the bamboo whip tentatively is divided into 1.0-1.2mm, 1.2-1.4mm, 1.4-1.6mm, 1.6-1.8mm, five levels of 1.8-2.0mm time by thickness.
9. a kind of technology according to claim 7 is characterized in that with the processing method of bamboo whip: comprise that also step (8) deposits dispensing, said step (8) uses the silica-gel desiccant sealing of 2-5mm to preserve when depositing.
10. use the bamboo whip according to each described a kind of technology of claim 1-8 with the technology that the processing method of bamboo whip is prepared from, what it is characterized in that being used to making case and bag carries hand and button.