CN102757756A - 一种双组份透明环氧树脂光纤粘合胶 - Google Patents
一种双组份透明环氧树脂光纤粘合胶 Download PDFInfo
- Publication number
- CN102757756A CN102757756A CN2012102761313A CN201210276131A CN102757756A CN 102757756 A CN102757756 A CN 102757756A CN 2012102761313 A CN2012102761313 A CN 2012102761313A CN 201210276131 A CN201210276131 A CN 201210276131A CN 102757756 A CN102757756 A CN 102757756A
- Authority
- CN
- China
- Prior art keywords
- epoxy resin
- optical fiber
- component
- fiber adhesive
- adhesive glue
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及一种双组份透明环氧树脂光纤粘合胶。该光纤粘合胶由主剂A与固化剂B两组分构成,经A、B组分按1∶(0.01-0.02)混合后用于施工,其中A组分由94.5%~96%脂环族环氧树脂、3%~5%增韧剂和0.3%~1.0%消泡剂,B组分为阳离子型固化剂。本发明提供一种透明、粘度小、粘结力强、不易开裂、耐高温高蚀且耐低温的光纤粘合胶,广泛用于光纤光缆连接器、光学元器件及光通讯,且制备工艺简单,生产成本较低,适合工业化大规模生产。
Description
技术领域
本发明涉及一种光纤粘合胶,具体涉及一种环氧树脂光纤粘合胶,其粘合质量高,可用于光纤光缆和连接器之间的固定。
背景技术
光纤通信是现代信息传输的重要方式之一,它具有容量大、中继距离长、保密性好、不受电磁干扰和节省铜材等优点。光纤粘合剂是用于光纤光缆与连接器之间粘接固定的一种粘合剂,由于其特殊的使用范围,因此对其要求较高,需满足以下几点:⑴较强的粘结力和持久性,粘合后不会因外界影响而出现脱胶移动现象;⑵高透光性,使用后不会产生光传导折射作用,不会造成传输损失;⑶稳定性高,耐高温高蚀且耐低温,具有良好的抵抗性。
在实际应用中常见的有:AB胶、热凝固环氧树脂胶、紫外线凝固粘合剂、预注入热溶胶和厌氧胶等。近年来,厌氧胶因其凝固速度快且不需要固化炉而得到比较广泛的应用,但其在使用时,必须使用离子催化剂处理才能够凝固,若粘合剂未接触到离子催化剂,则将不会凝固,导致光纤无法被固定而产生活塞效应。AB胶由主剂和固化剂两部分组成,其主剂多采用环氧树脂,具有成本低廉、透明性好,力学和热学性能优良以及加工工艺成熟等优点。芳香族环氧树脂含有可吸收紫外线的苯环,吸收紫外线后会氧化变黄,而脂环族环氧树脂由于环氧基直接连接在脂环上,能形成紧密的刚性分子结构,固化后交联密度增大,使得固化后的材料具有较高的热变形温度,分子结构中因不含苯环,表现出良好的耐UV性能和低吸湿性。为了增强环氧树脂的韧性,在主剂中加入适当的有机硅增韧剂即能很好的降低其脆性。另一方面,阳离子固化剂引发的光聚合具有不受氧阻聚、体积收缩小、厚膜等优点,既确保光纤光缆与连接器形成可靠的粘合,又能起到填补器件空隙防止高负荷受压等作用。
发明内容
本发明的目的是提供一种透明、粘度小、粘结力强、耐高温高蚀且耐低温的光纤粘合胶,对光纤、金属、玻璃、陶瓷和多数塑胶具有良好的附着力,可广泛用于光纤光缆连接器、光学元器件及光通讯。
本发明的内容是一种双组份透明环氧树脂光纤粘合胶,该粘合胶由主剂A与固化剂B两组分构成,经A、B组分按质量比1:(0.01-0.02)混合后用于施工,其特征在于,A组分制备方法为:将质量百分比为94.5%~96%脂环族环氧树脂、3%~5%增韧剂和0.3%~1.0%消泡剂按比例称量好,在70-80℃条件下搅拌3-4h至混合均匀。
按上述方案的一种双组份透明环氧树脂光纤粘合胶,其特征在于所述的脂环族环氧树脂为70%~75%3,4-环氧环已基甲基-3,4-环氧环已基碳酸酯与25%~30%聚[(2-环氧乙烷基)-1,2-环己二醇] 2-乙基-2-(羟甲基)-1,3-丙二醇醚。
按上述方案的一种双组份透明环氧树脂光纤粘合胶,其特征在于所述的增韧剂为有机硅增韧剂。
按上述方案的一种双组份透明环氧树脂光纤粘合胶,其特征在于所述的固化剂为鎓盐类阳离子光引发剂。
一种双组份透明环氧树脂光纤粘合胶,该光纤粘合胶具有如下特点:(1)外观为透明液体,无离析、颗粒及凝胶,透光性好,使用后不会产生光传导折射作用,避免造成传输损失;(2)A、B两组分按一定比例混合后,在紫外光照射下即可快速固化,且固化后具有较强的粘结力和持久性;(3)冲击强度>12.8 KJ/m2、抗弯强度>14J、玻璃化温度>423K;(4)冷热冲击:-70℃(30min)→100℃(30min)循环200-300次,无变化;(5)过两次回流焊(峰值温度:260-265℃,时间10-30s),粘合胶无脱落及黄变现象;(6)85℃、85%相对湿度、红墨水100℃浸煮1h或常温浸泡30天,均无渗透,耐高温高湿性能优异。
具体实施方式
下面通过实施例进一步介绍本发明,但是实施例不会构成对本发明的限制。
实施例1
(1)组分A:称取7.06Kg 3,4-环氧环已基甲基-3,4-环氧环已基碳酸酯、2.5 Kg聚[(2-环氧乙烷基)-1,2-环己二醇] 2-乙基-2-(羟甲基)-1,3-丙二醇醚、0.4 Kg有机硅增韧剂与 0.04 Kg消泡剂,在70℃条件下搅拌4h至混合均匀;
(2)组分B:0.1 Kg烷基碘鎓盐;
(3)将上述A、B两组分混匀后用于施工。
实施例2
(1)组分A:称取7.06Kg 3,4-环氧环已基甲基-3,4-环氧环已基碳酸酯、2.5 Kg聚[(2-环氧乙烷基)-1,2-环己二醇] 2-乙基-2-(羟甲基)-1,3-丙二醇醚、0.4 Kg有机硅增韧剂与 0.04 Kg消泡剂,在80℃条件下搅拌3.5h至混合均匀;
(2)组分B:0.2 Kg烷基碘鎓盐;
(3)将上述A、B两组分混匀后用于施工。
Claims (3)
1.一种双组份透明环氧树脂光纤粘合胶,其特征在于:该粘合胶由主剂A与固化剂B两组分构成,经A、B两组分按质量比1:(0.01-0.02)混合后用于施工,其特征在于,A组分制备方法为:将质量百分比为94.5%~96%脂环族环氧树脂、3%~5%有机硅增韧剂、和0.3%~1.0%消泡剂按比例称量好,在70-80℃条件下搅拌3-4h至混合均匀。
2.如权利要求1所述的一种双组份透明环氧树脂光纤粘合胶,其特征在于所述的脂环族环氧树脂为70%~75%3,4-环氧环已基甲基-3,4-环氧环已基碳酸酯与25%~30%聚[(2-环氧乙烷基)-1,2-环己二醇] 2-乙基-2-(羟甲基)-1,3-丙二醇醚。
3.如权利要求1所述的一种双组份透明环氧树脂光纤粘合胶,其特征在于所述的固化剂为鎓盐类阳离子光引发剂。