CN102757193B - 一种混凝土用复合掺合料 - Google Patents

一种混凝土用复合掺合料 Download PDF

Info

Publication number
CN102757193B
CN102757193B CN2012102406928A CN201210240692A CN102757193B CN 102757193 B CN102757193 B CN 102757193B CN 2012102406928 A CN2012102406928 A CN 2012102406928A CN 201210240692 A CN201210240692 A CN 201210240692A CN 102757193 B CN102757193 B CN 102757193B
Authority
CN
China
Prior art keywords
concrete
less
parts
sodium
surface area
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
CN2012102406928A
Other languages
English (en)
Other versions
CN102757193A (zh
Inventor
钱炳
黄泰东
罗小庆
雷欣
刘顺波
胡潮胡
杨杨
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
CHENGDU JIAXIN TECHNOLOGY CO LTD
Original Assignee
CHENGDU JIAXIN TECHNOLOGY CO LTD
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by CHENGDU JIAXIN TECHNOLOGY CO LTD filed Critical CHENGDU JIAXIN TECHNOLOGY CO LTD
Priority to CN2012102406928A priority Critical patent/CN102757193B/zh
Publication of CN102757193A publication Critical patent/CN102757193A/zh
Application granted granted Critical
Publication of CN102757193B publication Critical patent/CN102757193B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种混凝土用复合掺合料，由粉煤灰、硅灰、粒化高炉矿渣粉、元明粉、羟丙基甲基纤维素、UEA膨胀剂、聚羧酸减水剂、柠檬酸、硼酸、葡萄糖酸钠、磷酸钠、酒石酸钠、碳酸钙、碳酸锂、甲酸钙、乙酸钙、纤维素醚制备而成。本发明在实际应用中提高了混凝土强度，混凝土和易性好、泌水少，同时也降低水泥用量，降低单位体积用水量，有效改善其工作性能，使水化热降低。

Description

一种混凝土用复合掺合料
技术领域
本发明涉及混凝土技术领域，具体涉及一种混凝土用复合掺合料。
背景技术
混凝土用复合掺合料主要用于大幅度提高普通硅酸盐水泥的早期及中长期强度，具有需水量小、早期活性指数高、强度发展状况良好等特点。可广泛应用于以普通硅酸盐水泥为基础材料的各种混凝土构件、灌浆材料、修补材料等领域。目前国内外都积极展开了混凝土复合掺合料的研发，但仍然存在以下几个技术难点：1.需水量较高，造成施工困难且无法保证施工后的强度要求；2.无法取得很高的早期强度并保证后期强度持续增加，甚至出现后期强度倒缩的现象；3.氯离子含量超标；烧失量超标；4.密度太小，导致装卸困难且一次性运输量大大减少。
发明内容
鉴于上述不足之处，本发明的目的在于提供一种降低水泥用量，降低单位体积用水量，提高混凝土强度，混凝土和易性好、泌水少的混凝土用复合掺合料。
为了达到上述目的，本发明采用了以下技术方案：一种混凝土用复合掺合料，按重量份配比计由以下组分组成：
粉煤灰  7份
硅灰   45份
粒化高炉矿渣粉    42份
元明粉   6份
羟丙基甲基纤维素 0.5份
UEA膨胀剂  0.5份
聚羧酸减水剂  0.3份
柠檬酸  0.02份
硼酸  0.02份
葡萄糖酸钠  0.02份
磷酸钠  0.02份
酒石酸钠  0.02份
碳酸钙  0.02份
碳酸锂  0.02份
甲酸钙  0.02份
乙酸钙  0.02份
纤维素醚  0.03份。
最优的，上述粉煤灰为一级粉煤灰，比表面积≥1m2/g,28d抗压强度比≥65%。
最优的，上述硅灰中的二氧化硅含量不小于85%，含水率小于3%，烧失量小于6%，火山灰活性指数大于85%，比表面积≥20m2/g。
最优的，上述粒化高炉矿渣粉为S95级，比表面积≥0.36m2/g,28d活性指数大于等于70%。   
本发明的有益效果在于：1.通过对掺合料组成原料的筛选，有效控制了氯离子含量、烧失量和密度。2.通过减水剂的筛选，提高了浆体流动度，降低需水比，有效保证施工和易性和防止收缩开裂。3.通过调节合适的配比，大幅度提高普通硅酸盐水泥的早期强度并保证后期强度的稳定增长。
具体实施方式
称取：比表面积≥1m2/g,28d抗压强度比≥65%的一级粉煤灰70kg，硅灰450kg（其中硅灰中的二氧化硅含量不小于85%，含水率小于3%，烧失量小于6%，火山灰活性指数大于85%，比表面积≥20m2/g），比表面积≥0.36m2/g,28d活性指数大于等于70%的S95级粒化高炉矿渣粉420kg，元明粉60kg，羟丙基甲基纤维素 5kg，UEA膨胀剂5kg，聚羧酸减水剂3kg，柠檬酸0.2kg，硼酸0.2kg，葡萄糖酸钠0.2kg，磷酸钠0.2kg，酒石酸钠0.2kg，碳酸钙0.2kg，碳酸锂0.2kg，甲酸钙0.2kg，乙酸钙0.2kg，纤维素醚0.3kg。然后再经过机械搅拌混匀制成本发明产品混凝土用复合掺合料。
表1 本发明产品各项性能指标检测结果表。
Figure 612632DEST_PATH_IMAGE001
表2本发明产品的应用效果对照表。
Figure 392370DEST_PATH_IMAGE002
注：所用水泥为52.5普通硅酸盐水泥。
本发明产品在实际应用中提高了混凝土强度，混凝土和易性好、泌水少，同时也降低水泥用量，降低单位体积用水量，有效改善其工作性能，使水化热降低。

Claims (1)

1.一种混凝土用复合掺合料，其特征在于该混凝土用复合掺合料按重量份配比计由以下组分组成：
粉煤灰  7份
硅灰   45份
粒化高炉矿渣粉    42份
元明粉   6份
羟丙基甲基纤维素 0.5份
UEA膨胀剂  0.5份
聚羧酸减水剂  0.3份
柠檬酸  0.02份
硼酸  0.02份
葡萄糖酸钠  0.02份
磷酸钠  0.02份
酒石酸钠  0.02份
碳酸钙  0.02份
碳酸锂  0.02份
甲酸钙  0.02份
乙酸钙  0.02份
纤维素醚  0.03份；
所述粉煤灰为一级粉煤灰，比表面积≥1m2/g,28d抗压强度比≥65%；
所述硅灰中的二氧化硅含量不小于85%，含水率小于3%，烧失量小于6%，火山灰活性指数大于85%，比表面积不小于20 m2/g；
所述粒化高炉矿渣粉为S95级，比表面积≥0.36m2/g,28d活性指数大于等于70%。
CN2012102406928A 2012-07-12 2012-07-12 一种混凝土用复合掺合料 Expired - Fee Related CN102757193B (zh)