CN102746566A - 一种变频器专用辐照交联电力电缆料及其制备方法 - Google Patents

一种变频器专用辐照交联电力电缆料及其制备方法 Download PDF

Info

Publication number
CN102746566A
CN102746566A CN2012101923024A CN201210192302A CN102746566A CN 102746566 A CN102746566 A CN 102746566A CN 2012101923024 A CN2012101923024 A CN 2012101923024A CN 201210192302 A CN201210192302 A CN 201210192302A CN 102746566 A CN102746566 A CN 102746566A
Authority
CN
China
Prior art keywords
parts
power cable
cable material
antioxidant
special
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN2012101923024A
Other languages
English (en)
Other versions
CN102746566B (zh
Inventor
沈志海
沈志荣
邹强
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Anhui Huahai Special Cable Group Co Ltd
Original Assignee
Anhui Huahai Special Cable Group Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Anhui Huahai Special Cable Group Co Ltd filed Critical Anhui Huahai Special Cable Group Co Ltd
Priority to CN201210192302.4A priority Critical patent/CN102746566B/zh
Publication of CN102746566A publication Critical patent/CN102746566A/zh
Application granted granted Critical
Publication of CN102746566B publication Critical patent/CN102746566B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种变频器专用辐照交联电力电缆料及其制备方法，其组成原料的重量份为：聚烯烃弹性体POE8450/美国杜邦60-80、氢氧化铝80-100、高密度聚乙烯树脂30-40、氯化聚乙烯40-60、硼酸锌15-30、半补强炭黑2-3、硅灰石粉40-60、氧化锌4-6、防老剂3-6、硅烷偶联剂KH550 3-5、硬酯酸钙4-6、抗氧剂1010 4-5、硬酯酸单甘油酯3-5、氯化石蜡3-4。本发明采用多种配方混合，值得的电缆料具有良好的阻燃性能、机械性能大大幅提高，较好的力学性能等优点。

Description

一种变频器专用辐照交联电力电缆料及其制备方法
技术领域
本发明涉及一种电缆料及其制备方法，具体涉及一种变频器专用辐照交联电力电缆料及其制备方法。
背景技术
随着经济的迅速发展，电线电缆在各个行业、领域中都得到广泛的应用，随着电气火灾事故的频繁发生，电线电缆的阻燃问题逐渐引起世界各国的重视；电缆燃烧时释放出大量烟雾和有毒的、腐蚀性的气体是火灾中危险因素，在火灾中妨碍了人们的安全撤离和灭火工作，使生命财产遭到严重损失，变频器的电缆也随之加强需求，提供变频器专用辐照交联电力电缆料及其制备方法。
发明内容
为了缓解现有技术的不足和缺陷，本发明的目的在于提供一种变频器专用辐照交联电力电缆料及其制备方法。
本发明采用如下技术方案：
变频器专用辐照交联电力电缆料，其组成原料的重量份为：
聚烯烃弹性体POE 8450/美国杜邦 60-80、氢氧化铝80-100、高密度聚乙烯树脂30-40、氯化聚乙烯40-60、硼酸锌15-30、半补强炭黑2-3、硅灰石粉40-60、氧化锌4-6、防老剂3-6、硅烷偶联剂KH550  3-5、硬酯酸钙4-6、抗氧剂1010  4-5、硬酯酸单甘油酯3-5、氯化石蜡3-4。
变频器专用辐照交联电力电缆料，其组成原料的重量份为：
聚烯烃弹性体POE 8450/美国杜邦 70、氢氧化铝90、高密度聚乙烯树脂35、氯化聚乙烯50、硼酸锌22、半补强炭黑2.5、硅灰石粉50、氧化锌5、防老剂5、硅烷偶联剂KH550  4、硬酯酸钙5、抗氧剂1010  4.5、硬酯酸单甘油酯4、氯化石蜡3.5。
变频器专用辐照交联电力电缆料，所述的防老剂为防老剂OD、防老剂ODA、防老剂TPPD、防老剂NBC或防老剂MB。
变频器专用辐照交联电力电缆料的制备方法，包括以下步骤：按组成原料的重量份称取各原料，混合均匀，然后在160-180℃下混炼20-30分钟，接着进行高能辐射，在功率与能量分别为9-11KW、9-11Mev电子束下辐照交联，辐照剂量为180-230Gy，挤出造料。
本发明的优点：
本发明采用多种配方混合，值得的电缆料具有良好的阻燃性能、机械性能大大幅提高，较好的力学性能等优点。
具体实施方式
实施例1：变频器专用辐照交联电力电缆料，其组成原料的重量份为：
聚烯烃弹性体POE 8450/美国杜邦 60、氢氧化铝80、高密度聚乙烯树脂30、氯化聚乙烯40、硼酸锌15、半补强炭黑2、硅灰石粉40、氧化锌4、防老剂OD 3、硅烷偶联剂KH550  3、硬酯酸钙4、抗氧剂1010  4、硬酯酸单甘油酯3、氯化石蜡3。
变频器专用辐照交联电力电缆料的制备方法，包括以下步骤：按组成原料的重量份称取各原料，混合均匀，然后在160-180℃下混炼20-30分钟，接着进行高能辐射，在功率与能量分别为9-11KW、9-11Mev电子束下辐照交联，辐照剂量为180-230Gy，挤出造料。
实施例2：变频器专用辐照交联电力电缆料，其组成原料的重量份为：
聚烯烃弹性体POE 8450/美国杜邦 70、氢氧化铝90、高密度聚乙烯树脂35、氯化聚乙烯50、硼酸锌22、半补强炭黑2.5、硅灰石粉50、氧化锌5、防老剂ODA  5、硅烷偶联剂KH550  4、硬酯酸钙5、抗氧剂1010  4.5、硬酯酸单甘油酯4、氯化石蜡3.5。
变频器专用辐照交联电力电缆料的制备方法，如同实施例1。
实施例3：变频器专用辐照交联电力电缆料，其组成原料的重量份为：
聚烯烃弹性体POE 8450/美国杜邦 80、氢氧化铝100、高密度聚乙烯树脂40、氯化聚乙烯60、硼酸锌30、半补强炭黑3、硅灰石粉60、氧化锌6、防老剂NBC  6、硅烷偶联剂KH550  5、硬酯酸钙6、抗氧剂1010  5、硬酯酸单甘油酯5、氯化石蜡4。
变频器专用辐照交联电力电缆料的制备方法，如同实施例1。
通过本发明制备的电缆料的性能检测数据：
拉伸强度为16.5-19.3Mpa，断裂伸出率为230-450%，氧指数35-37.3%，烟密度为67-73，体积电阻率8.4×1014欧姆.厘米，能通过136℃×168小时的热老化试验。

Claims (4)

1.一种变频器专用辐照交联电力电缆料，其特征在于其组成原料的重量份为：
聚烯烃弹性体POE 8450/美国杜邦 60-80、氢氧化铝80-100、高密度聚乙烯树脂30-40、氯化聚乙烯40-60、硼酸锌15-30、半补强炭黑2-3、硅灰石粉40-60、氧化锌4-6、防老剂3-6、硅烷偶联剂KH550  3-5、硬酯酸钙4-6、抗氧剂1010  4-5、硬酯酸单甘油酯3-5、氯化石蜡3-4。
2.根据权利要求1所述的变频器专用辐照交联电力电缆料，其特征在于其组成原料的重量份为：
聚烯烃弹性体POE 8450/美国杜邦 70、氢氧化铝90、高密度聚乙烯树脂35、氯化聚乙烯50、硼酸锌22、半补强炭黑2.5、硅灰石粉50、氧化锌5、防老剂5、硅烷偶联剂KH550  4、硬酯酸钙5、抗氧剂1010  4.5、硬酯酸单甘油酯4、氯化石蜡3.5。
3.根据权利要求1所述的变频器专用辐照交联电力电缆料，其特征在于：所述的防老剂为防老剂OD、防老剂ODA、防老剂TPPD、防老剂NBC或防老剂MB。
4.一种如权利要求1所述的变频器专用辐照交联电力电缆料的制备方法，其特征在于包括以下步骤：按组成原料的重量份称取各原料，混合均匀，然后在160-180℃下混炼20-30分钟，接着进行高能辐射，在功率与能量分别为9-11KW、9-11Mev电子束下辐照交联，辐照剂量为180-230Gy，挤出造料。
CN201210192302.4A 2012-06-12 2012-06-12 一种变频器专用辐照交联电力电缆料及其制备方法 Expired - Fee Related CN102746566B (zh)