CN102746541A - 一种改性氯丁橡胶耐火电缆料及其制备方法 - Google Patents

一种改性氯丁橡胶耐火电缆料及其制备方法 Download PDF

Info

Publication number
CN102746541A
CN102746541A CN2012101968896A CN201210196889A CN102746541A CN 102746541 A CN102746541 A CN 102746541A CN 2012101968896 A CN2012101968896 A CN 2012101968896A CN 201210196889 A CN201210196889 A CN 201210196889A CN 102746541 A CN102746541 A CN 102746541A
Authority
CN
China
Prior art keywords
parts
chloroprene rubber
maleic anhydride
modified chloroprene
cable material
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN2012101968896A
Other languages
English (en)
Other versions
CN102746541B (zh
Inventor
魏善恒
李小康
陶天宝
陈国林
王敏
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
SUZHOU YIPUDUN NEW MATERIAL TECHNOLOGY Co.,Ltd.
Original Assignee
Anhui Huatong Cable Group Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Anhui Huatong Cable Group Co Ltd filed Critical Anhui Huatong Cable Group Co Ltd
Priority to CN201210196889.6A priority Critical patent/CN102746541B/zh
Publication of CN102746541A publication Critical patent/CN102746541A/zh
Application granted granted Critical
Publication of CN102746541B publication Critical patent/CN102746541B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种改性氯丁橡胶耐火电缆料及其制备方法，其组成原料的重量份为：氯丁橡胶60-70、马来酸酐接枝乙烯-醋酸乙酯共聚物70-80、马来酸酐接枝聚烯烃弹性体20-30、甲基乙烯基硅橡胶40-60、沉淀法白炭黑1-4、漂白活性硅酸钙2-6、异氰酸酯3-7、促进剂C-15E86 3-6、防老剂ODA 3-6、过氧化二异丙苯DCP 2-5、复合铅盐稳定剂2-5、抗氧剂DSTP 3-6、硬酯酸单甘油酯1-3、二辛酯4-5、三氧化锑50-70和硼酸锌1-4。本发明制备方法简单，电性能优异，具有柔软、耐磨、不吸水优点，通过国家A级耐火试验。

Description

一种改性氯丁橡胶耐火电缆料及其制备方法
技术领域
本发明涉及一种改性氯丁橡胶耐火电缆料及其制备方法，属于电缆料技术领域。
背景技术
随着经济的迅速发展，电线电缆在各个行业、领域中都得到广泛的应用。随着电气火灾事故的频繁发生，电线电缆的阻燃问题逐渐引起世界各国的重视。电缆燃烧时释放出大量烟雾和有毒的、腐蚀性的气体是火灾中危险因素，在火灾中妨碍了人们的安全撤离和灭火工作，使生命财产遭到严重损失。同时随着通讯事业、汽车工业和计算机工业的发展，特别是航空导线、汽车用线、高温仪表电缆、石油钻井平台电缆等许多场合，越来越需要使用改性氯丁橡胶耐火电缆料。
发明内容
本发明的目的是提供一种改性氯丁橡胶耐火电缆料及其制备方法，本发明制备方法简单，电性能优异，具有柔软、耐磨、不吸水优点，通过国家A级耐火试验。
为实现上述目的本发明的采用如下技术方案：
改性氯丁橡胶耐火电缆料，其组成原料的重量份为：氯丁橡胶60-70、马来酸酐接枝乙烯-醋酸乙酯共聚物70-80、马来酸酐接枝聚烯烃弹性体20-30、甲基乙烯基硅橡胶  40-60、沉淀法白炭黑1-4、漂白活性硅酸钙  2-6、异氰酸酯  3-7、促进剂C-15E86  3-6、防老剂ODA   3-6、过氧化二异丙苯DCP  2-5、复合铅盐稳定剂  2-5、抗氧剂DSTP  3-6、硬酯酸单甘油酯  1-3、二辛酯4-5、三氧化锑50-70和硼酸锌  1-4。
改性氯丁橡胶耐火电缆料，其组成原料的重量份为：氯丁橡胶65、马来酸酐接枝乙烯-醋酸乙酯共聚物75、马来酸酐接枝聚烯烃弹性体25、甲基乙烯基硅橡胶  50、沉淀法白炭黑2.5、漂白活性硅酸钙  4、异氰酸酯  5、促进剂C-15E86  4、防老剂ODA   5、过氧化二异丙苯DCP  4、复合铅盐稳定剂  3.5、抗氧剂DSTP 4、硬酯酸单甘油酯 2、二辛酯4.5、三氧化锑60和硼酸锌  3。
改性氯丁橡胶耐火电缆料的制备方法，包括以下步骤：按组成原料的重量份称取各原料，然后在温度在100-120℃下混炼25-35分钟得到成品。
本发明的有益效果：
本发明制备方法简单，电性能优异，具有柔软、耐磨、不吸水优点，通过国家A级耐火试验。
具体实施方式
实施例1：改性氯丁橡胶耐火电缆料，其组成原料的重量份为：氯丁橡胶65、马来酸酐接枝乙烯-醋酸乙酯共聚物75、马来酸酐接枝聚烯烃弹性体25、甲基乙烯基硅橡胶  50、沉淀法白炭黑2.5、漂白活性硅酸钙  4、异氰酸酯  5、促进剂C-15E86  4、防老剂ODA   5、过氧化二异丙苯DCP  4、复合铅盐稳定剂  3.5、抗氧剂DSTP 4、硬酯酸单甘油酯 2、二辛酯4.5、三氧化锑60和硼酸锌  3。
改性氯丁橡胶耐火电缆料的制备方法，包括以下步骤：按组成原料的重量份称取各原料，然后在温度在100-120℃下混炼25-35分钟得到成品。
    通过本发明的实施例1制得的电缆料性能数据：
拉伸强度为15.3-18Mpa，断裂伸出率为680-750%，老化后拉伸强度保持率（120℃，96h） 83%，老化后断裂伸出保持率（120℃，96h）77%，冲击脆化温度-35℃--53℃。单根垂直燃烧试验，续燃时间为6秒，烧焦端距上夹具下缘距离为250毫米；成束燃烧试验，炭化长度为0.9米。

Claims (3)

1.一种改性氯丁橡胶耐火电缆料，其特征在于其组成原料的重量份为：氯丁橡胶60-70、马来酸酐接枝乙烯-醋酸乙酯共聚物70-80、马来酸酐接枝聚烯烃弹性体20-30、甲基乙烯基硅橡胶  40-60、沉淀法白炭黑1-4、漂白活性硅酸钙  100-120、异氰酸酯  3-7、促进剂C-15E86  3-6、防老剂ODA   3-6、过氧化二异丙苯DCP  2-5、复合铅盐稳定剂  2-5、抗氧剂DSTP  3-6、硬酯酸单甘油酯  1-3、二辛酯4-5、三氧化锑50-70和硼酸锌  1-4。
2.根据权利要求1所述的改性氯丁橡胶耐火电缆料，其特征在于其组成原料的重量份为：氯丁橡胶65、马来酸酐接枝乙烯-醋酸乙酯共聚物75、马来酸酐接枝聚烯烃弹性体25、甲基乙烯基硅橡胶  50、沉淀法白炭黑2.5、漂白活性硅酸钙  4、异氰酸酯  5、促进剂C-15E86  4、防老剂ODA   5、过氧化二异丙苯DCP  4、复合铅盐稳定剂  3.5、抗氧剂DSTP 4、硬酯酸单甘油酯 2、二辛酯4.5、三氧化锑60和硼酸锌  3。
3.一种如权利要求1所述的改性氯丁橡胶耐火电缆料的制备方法，其特征在于包括以下步骤：按组成原料的重量份称取各原料，然后在温度在100-120℃下混炼25-35分钟得到成品。
CN201210196889.6A 2012-06-15 2012-06-15 一种改性氯丁橡胶耐火电缆料及其制备方法 Active CN102746541B (zh)