CN102733574A - 变色面砖及其制造方法 - Google Patents
变色面砖及其制造方法 Download PDFInfo
- Publication number
- CN102733574A CN102733574A CN2012102251715A CN201210225171A CN102733574A CN 102733574 A CN102733574 A CN 102733574A CN 2012102251715 A CN2012102251715 A CN 2012102251715A CN 201210225171 A CN201210225171 A CN 201210225171A CN 102733574 A CN102733574 A CN 102733574A
- Authority
- CN
- China
- Prior art keywords
- face brick
- light
- fragment
- semiproduct
- variable color
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及建筑装饰材料,特别涉及是面砖。变色面砖的制造方法包括步骤:A,压出砖坯、待干燥后窑炉高温烧成表面粗糙而不平整的半成品面砖;B,在半成品面砖的一面均匀喷涂一层粘结胶剂,并趁未干之前向半成品面砖喷涂有粘结胶剂的一面撒落反光碎片;C,待半成品面砖上的粘结胶剂干燥后,向半成品面砖粘结有反光碎片的一面涂抹透光树脂料,并刮平透光树脂层;D,烘干固化半成品面砖上的透光树脂料,即制得变色面砖成品。通过上述方法制得的变色面砖,包括:一个面砖本体,面砖本体至少具有一个粗糙而不平整表面;多个反光碎片,粘结于面砖本体的一个粗糙而不平整表面上;一层透光树脂层,覆盖于面砖本体的粗糙而不平整表面上的反光碎片上。
Description
技术领域
本发明涉及建筑装饰材料,特别涉及是面砖。
背景技术
面砖是贴设在建筑物的表面(如外墙、内墙、地面等),用于保护建筑物且具有美观的装饰效果,是一种最为广泛应用的建筑装饰材料。为了使面砖具有颜色变化的效果,中国专利号95102188.5提出的变色陶瓷装饰砖是在陶瓷装饰砖坯的表面上制造出断面为“V”形的沟槽,在“V”形槽的两个面施以不同颜色和釉料,则不同视角将产生变色的效果,但是该方案的不足也是很明显的,即砖瓷表面的是不平整,不仅制造工艺复杂且也容易堆积灰尘,在一些场合应用受限。
针对变色面砖表面不平整的问题,另一中国专利号200810070618.X提出一种含有偏光颜料的变色涂料喷涂在釉面砖上而实现的方案。这种变色面砖是通过应用在汽车、塑料制品、家具等领域的偏光颜料来实现,本质上是利用偏光颜料(又名变色龙颜料、光变颜料、OVP)通过对光线的吸收与反射而形成随视角异色的动态变色效果。这种变色面砖虽然解决了面砖表面不平整的问题,但是偏光颜料材料较贵,因而制造成本较高。并且,现有的偏光颜料在使用一段时间后易发生老化变质而失去变色效果,尤其是将这种变色面砖用在建筑外墙上,经常在太阳下暴晒,该老化现象更为明显。
发明内容
因此,申请人经过大量试验尝试,成功实现了一种能够经久耐用且制造成本低廉的一种表面平整的变色面砖。
本发明的技术方案是:
一种变色面砖的制造方法,包括步骤:
A,压出砖坯、待干燥后窑炉高温烧成表面粗糙而不平整的半成品面砖;
B,在半成品面砖的一面均匀喷涂一层粘结胶剂,并趁粘结胶剂未干之前向半成品面砖喷涂有粘结胶剂的一面撒落反光碎片;
C,待半成品面砖上的粘结胶剂干燥后,向半成品面砖粘结有反光碎片的一面涂抹透光树脂料,并刮平透光树脂层;
D,烘干固化半成品面砖上的透光树脂料,即制得变色面砖成品。
进一步的,所述的反光碎片由铝箔经过上色,不同颜色的铝箔经过碎化并随机混合而制得,碎化后的每个铝箔碎片的面积不大于0.8mm2。
进一步的,所述的透光树脂层是通过刮刀刮平的。
一种变色面砖,包括:
-一个面砖本体,面砖本体至少具有一个粗糙而不平整表面;
-多个反光碎片,粘结于面砖本体的一个粗糙而不平整表面上;
-一层透光树脂层,覆盖于面砖本体的粗糙而不平整表面上的反光碎片上,其外表面为平整面。
进一步的,所述的反光碎片为不同颜色的铝箔碎片,且铝箔碎片的面积不大于0.8mm2。
本发明采用如上的技术方案,具有的技术优点是:a.采用的材料成本低,制造工艺较为简单,因此制造成本较为低廉,易于广泛推广。b.制得的面砖表面平整,不易堆积灰尘,因此适合广泛应用。c.变色效果更佳绚丽,且经久耐用而不老化。
具体实施方式
现结合具体实施方式对本发明进一步说明。
变色面砖的制造方法,包括步骤:
A)压出砖坯、待干燥后窑炉高温烧成表面粗糙而不平整的半成品面砖。制备半成品面砖的工艺与现有技术无区别,可以采用高岭土、页岩、石灰岩等多种材料来源,由于窑炉高温烧制的过程中会有气泡产生溢出,因此刚烧制出来的半成品面砖的表面一般均是粗糙而不平整的。优选的,为了加大半成品面砖表面粗糙度,还可以在烧制面砖的材料内加入一定量的起泡剂。
B)在半成品面砖的一面均匀喷涂一层粘结胶剂,并趁粘结胶剂未干之前向半成品面砖喷涂有粘结胶剂的一面撒落反光碎片。所述的反光碎片由铝箔(也可以是其他金属箔片)经过上色,不同颜色的铝箔经过碎化并随机混合而制得,碎化后的每个铝箔碎片的面积不大于0.8mm2。铝箔的上色一般选用色泽鲜艳且性质稳定而不易老化的化学染色剂,而从成本的角度和效果上考虑一般不适用矿物染料或生物染色剂。铝箔的碎化可以借助机器或人工先剪裁成较小箔片,然后再放入破碎机继续碎化,优选的碎化的程度是每个铝箔碎片的面积不大于0.8mm2。
C)待半成品面砖上的粘结胶剂干燥后,向半成品面砖粘结有反光碎片的一面涂抹透光树脂料,并刮平透光树脂层。优选的,所述的透光树脂层是通过刮刀刮平的。
D)烘干固化半成品面砖上的透光树脂料,即制得变色面砖成品。优选的,透光树脂料采用耐候性好且透光率高的树脂材料。
通过上述的制造方法制得的变色面砖,包括:
-一个面砖本体,面砖本体至少具有一个粗糙而不平整表面;
-多个反光碎片,粘结于面砖本体的一个粗糙而不平整表面上;
-一层透光树脂层,覆盖于面砖本体的粗糙而不平整表面上的反光碎片上,其外表面为平整面。
优选的,所述的反光碎片为不同颜色的铝箔碎片,且铝箔碎片的面积不大于0.8mm2。
本发明的变色面砖是利用烧制半成品面砖而自然形成的表面粗糙而不平整的面为基础,然后在这层表面粗糙不平整的表面上粘结了多种颜色的反光碎片,就相当于在面砖的一面是形成了无数个不同颜色的不同角度的反射面。而人眼在不同位置观察到的面砖就会由其中的一些角度范围内的多个反光碎片反射出不同颜色的光线的混合颜色,这样就可以获得十分绚丽的变色效果。为了保证面砖的变色面能够平整光滑,且也对反光碎片进行抗老化保护,在面砖的变色面上还涂抹并固化透光树脂料。
尽管结合优选实施方案具体展示和介绍了本发明,但所属领域的技术人员应该明白,在不脱离所附权利要求书所限定的本发明的精神和范围内,在形式上和细节上可以对本发明做出各种变化,均为本发明的保护范围。
Claims (5)
1.一种变色面砖的制造方法,包括步骤:
A,压出砖坯、待干燥后窑炉高温烧成表面粗糙而不平整的半成品面砖;
B,在半成品面砖的一面均匀喷涂一层粘结胶剂,并趁粘结胶剂未干之前向半成品面砖喷涂有粘结胶剂的一面撒落反光碎片;
C,待半成品面砖上的粘结胶剂干燥后,向半成品面砖粘结有反光碎片的一面涂抹透光树脂料,并刮平透光树脂层;
D,烘干固化半成品面砖上的透光树脂料,即制得变色面砖成品。
2.根据权利要求1所述的变色面砖的制造方法,其特征在于:所述的反光碎片由铝箔经过上色,不同颜色的铝箔经过碎化并随机混合而制得,碎化后的每个铝箔碎片的面积不大于0.8mm2。
3.根据权利要求1所述的变色面砖的制造方法,其特征在于:所述的透光树脂层是通过刮刀刮平的。
4.一种变色面砖,包括:
-一个面砖本体,面砖本体至少具有一个粗糙而不平整表面;
-多个反光碎片,粘结于面砖本体的一个粗糙而不平整表面上;
-一层透光树脂层,覆盖于面砖本体的粗糙而不平整表面上的反光碎片上,其外表面为平整面。
5.根据权利要求1所述的变色面砖,其特征在于:所述的反光碎片为不同颜色的铝箔碎片,且铝箔碎片的面积不大于0.8mm2。