CN102731871B - 耐160度的高温橡胶 - Google Patents

耐160度的高温橡胶 Download PDF

Info

Publication number
CN102731871B
CN102731871B CN 201210213560 CN201210213560A CN102731871B CN 102731871 B CN102731871 B CN 102731871B CN 201210213560 CN201210213560 CN 201210213560 CN 201210213560 A CN201210213560 A CN 201210213560A CN 102731871 B CN102731871 B CN 102731871B
Authority
CN
China
Prior art keywords
rubber
temperature
resistant rubber
dibenzoate
sulfydryl
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN 201210213560
Other languages
English (en)
Other versions
CN102731871A (zh
Inventor
钱佑武
钱必树
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Wuhu City Hongda Rubber Plastic Valve Manufacture Co Ltd
Original Assignee
Wuhu City Hongda Rubber Plastic Valve Manufacture Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Wuhu City Hongda Rubber Plastic Valve Manufacture Co Ltd filed Critical Wuhu City Hongda Rubber Plastic Valve Manufacture Co Ltd
Priority to CN 201210213560 priority Critical patent/CN102731871B/zh
Publication of CN102731871A publication Critical patent/CN102731871A/zh
Application granted granted Critical
Publication of CN102731871B publication Critical patent/CN102731871B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了耐160度的高温橡胶，所述的橡胶含有以下物质：丁腈橡胶、氧化锌、硬脂酸、碳黑N330、碳黑N660、石蜡油、石蜡、硫黄、2-脱氧-2,2二氟-戊呋喃糖-1-酮-3,5-二苯甲酸酯 、1-(2-二甲基氨基乙基)-1H-5-巯基-四氮唑、2-氯甲基-3-甲基-4-（2,2,2-三氟乙氧基）吡啶盐酸盐、防老剂、促进剂，本发明与现有技术相比，通过在配方中加入2-脱氧-2,2二氟-戊呋喃糖-1-酮-3,5-二苯甲酸酯、1-(2-二甲基氨基乙基)-1H-5-巯基-四氮唑、4,5,6,7-四氢噻吩[3,2-C]吡啶盐酸盐，使丁腈橡胶的耐热温度提高到了160-170℃。

Description

耐160度的高温橡胶
技术领域
本发明涉及橡胶，特别涉及用于管道衬套的耐160度的高温橡胶。
背景技术
丁腈橡胶具有良好的耐水、耐油性，常用于管道的衬套，但其使用的温度范围为-40到120℃，不能适用于160℃以上液体的运输。
发明内容
本发明所要解决的技术问题是提供一种适用于温度为160℃液体运输的耐高温橡胶。
本发明解决技术问题的技术方案为：耐160度的高温橡胶，含有以下物质及重量份：
Figure BDA0000180829151
Figure BDA0000180829152
所述的丁腈橡胶的型号为3365E。
所述的防老剂为：2,2,4-三甲基-1,2-二氢喹啉聚合物，防老剂RD。
所述的促进剂为:4-4'-二硫化二吗啉（DTDM）
本发明的制备方法与现有的橡胶的制备方法相同。
本发明与现有技术相比，通过在配方中加入2-脱氧-2,2二氟-戊呋喃糖-1-酮-3,5-二苯甲酸酯、1-(2-二甲基氨基乙基)-1H-5-巯基-四氮唑、4,5,6,7-四氢噻吩[3,2-C]吡啶盐酸盐，使丁腈橡胶的耐热温度提高到了160-170℃。
具体实施方式：
下面结合实施例对本发明作详细的说明。
所述的石蜡油由山东省武城县一帆橡化有限公司生产。
石蜡由衡水宇祥橡胶化工生产。
实施例1：
耐高温橡胶，含有以下物质及重量份：
Figure BDA0000180829153
Figure BDA0000180829154
实施例2：
耐高温橡胶，含有以下物质及重量份：
实施例3
耐高温橡胶，含有以下物质及重量份：
Figure BDA0000180829156
将实施例1、2、3所制的管道衬套，用于运输160-170℃的液体（如食用油），连续使用1年，管道没有泄漏。

Claims (4)

1.耐160度的高温橡胶，其特征在于：含有以下物质及重量份：
Figure FDA0000180829141
2.根据权利要求1所述的耐160度的高温橡胶，其特征在于：所述的丁腈橡胶的型号为3365E。
3.根据权利要求1所述的耐160度的高温橡胶，其特征在于：所述的防老剂为2,2,4-三甲基-1,2-二氢喹啉聚合物。
4.根据权利要求1所述的耐160度的高温橡胶，其特征在于：所述的促进剂为4-4'-二硫化二吗啉。
CN 201210213560 2012-06-26 2012-06-26 耐160度的高温橡胶 Active CN102731871B (zh)