CN102730972A - Glaze for plastic surfaces - Google Patents
Glaze for plastic surfaces Download PDFInfo
- Publication number
- CN102730972A CN102730972A CN2012101952328A CN201210195232A CN102730972A CN 102730972 A CN102730972 A CN 102730972A CN 2012101952328 A CN2012101952328 A CN 2012101952328A CN 201210195232 A CN201210195232 A CN 201210195232A CN 102730972 A CN102730972 A CN 102730972A
- Authority
- CN
- China
- Prior art keywords
- parts
- glaze
- weight parts
- frosting
- weight
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a glaze capable of being applied on plastic surfaces for ceramic, comprising 30-60 weight parts of SiO2, 15-25 weight parts of Al(OH)3, 1-5 weight parts of CrO3, 1-5 weight parts of MgS, 10-20 weight parts of KPO3, 10-20 weight parts of quartz powder, 10-20 weight parts of PbO, 5-10 weight parts of ZnCl2, and 15-30 weight parts of sodium borate. The glaze provided by the invention can be applied on plastic surfaces, can form a compact glaze layer on the plastic surfaces, has the advantages of strong adhesive force, difficulty in fading, smoothness and gloss of ceramic glaze, light weight, and difficult in cracking, can satisfy the high life quality standards of people, and has a wide scope of application.
Description
?
Technical field
The present invention relates to a kind of glaze, be specifically related to a kind of glaze that can be used for frosting.
Background technology
Pottery has become the daily life articles for use, and easy cracked but pottery exists, resistance to shock is poor; Cost is higher, and there are shortcomings such as weight is big in ceramic, but people ask the decorative effect and the smooth feeling of Ceramic glaze again most; Therefore; Necessary on the basis of prior art, the research and development design is a kind of to be bed material with plastics, can be at the glaze of frosting close attachment.
Summary of the invention
Goal of the invention: technical problem to be solved by this invention is the deficiency that overcomes prior art, provides a kind of and can be applicable to frosting, can show that densification adheres to the good glaze of good, the anti-cut of one deck slickness at plastics.
Technical scheme: for solving above technical problem, the present invention takes following technical scheme:
A kind of glaze that can be used for frosting, it is processed by the raw material of following parts by weight:
SiO
230 ~ 60 parts, Al (OH)
315 ~ 25 parts, CrO
31 ~ 5 part, 1 ~ 5 part of MgS, KPO
310 ~ 20 parts, 10 ~ 20 parts of silica powders, PbO10 ~ 20 part, ZnCl
215 ~ 30 parts of 5 ~ 10 parts, Sodium Tetraborate.
As preferred version, the above-described glaze that can be used for frosting, it is processed by the raw material of following parts by weight:
SiO
230 ~ 40 parts, Al (OH)
315 ~ 20 parts, CrO
33 ~ 5 parts, 3 ~ 5 parts of MgS, KPO
310 ~ 15 parts, 10 ~ 15 parts of silica powders, PbO10 ~ 15 part, ZnCl
215 ~ 25 parts of 5 ~ 8 parts, Sodium Tetraborate.
As more preferably scheme, the above-described glaze that can be used for frosting, it is processed by the raw material of following parts by weight:
SiO
240 parts, Al (OH)
320 parts, CrO
33 parts, 3 parts of MgS, KPO
315 parts, 15 parts of silica powders, PbO15 part, ZnCl
220 parts of 8 parts, Sodium Tetraborate.
The present invention is according to the deficiency of prior art; Physico-chemical property according to frosting; Confirm to be used for the overglaze composition of frosting and the ratio of each component through a large amount of experiments, test experience result shows that the each component proportioning is scientific and reasonable, the glaze that can be used for frosting provided by the invention; Various physico-chemical properties meet the requirements, and this glaze specific product parameter that can be used for frosting is:
(degree 620, sintering point (degree) 660, softening temperature (degree) 750, ball point (degree) 1000, hemisphere point (degree) 1100, each item character meets the requirements, Functionality, quality and appealing design for thermal expansivity 56, change point (degree) 542 expansion softening temperatures.
Beneficial effect: the glaze that can be used for frosting provided by the invention is compared with prior art has following advantage:
The glaze that can be used for frosting of the ceramic usefulness of preparation provided by the invention, it is fine and close to form one deck at frosting
Glaze, plurality of advantages such as strong adhesion is difficult for fading, and has the slickness and the Guan Ze of Ceramic glaze, and has light weight, and is not easily broken can satisfy the high quality of life standard of people, and the scope of application is extensive.
Embodiment
Below in conjunction with specific embodiment; Further illustrate the present invention; Should understand these embodiment only be used to the present invention is described and be not used in the restriction scope of the present invention; After having read the present invention, those skilled in the art all fall within the application's accompanying claims institute restricted portion to the modification of the various equivalent form of values of the present invention.
Embodiment 1
A kind of glaze that can be used for frosting, it is processed by the raw material of following parts by weight:
SiO
260 parts, Al (OH)
325 parts, CrO
35 parts, 5 parts of MgS, KPO
320 parts, 20 parts of silica powders, 20 parts of PbO, ZnCl
230 parts of 10 parts, Sodium Tetraborate.
Embodiment 2
A kind of glaze that can be used for frosting, it is processed by the raw material of following parts by weight:
SiO
230 parts, Al (OH)
315 parts, CrO
31 part, 1 part of MgS, KPO
310 parts, 10 parts of silica powders, PbO10 part, ZnCl
215 parts of 5 parts, Sodium Tetraborate.
Embodiment 3
A kind of glaze that can be used for frosting, it is processed by the raw material of following parts by weight:
SiO
240 parts, Al (OH)
320 parts, CrO
33 parts, 3 parts of MgS, KPO
315 parts, 15 parts of silica powders, 15 parts of PbO, ZnCl
225 parts of 8 parts, Sodium Tetraborate.
Embodiment 4
A kind of glaze that can be used for frosting, it is processed by the raw material of following parts by weight:
SiO
240 parts, Al (OH)
320 parts, CrO
33 parts, 3 parts of MgS, KPO
315 parts, 15 parts of silica powders, PbO15 part, ZnCl
220 parts of 8 parts, Sodium Tetraborate.
The above only is a preferred implementation of the present invention; Should be pointed out that for those skilled in the art, under the prerequisite that does not break away from the principle of the invention; Can also make some improvement and retouching, these improvement and retouching also should be regarded as protection scope of the present invention.
Claims (3)
1. the glaze that can be used for frosting is characterized in that, it is processed by the raw material of following parts by weight:
SiO
230 ~ 60 parts, Al (OH)
315 ~ 25 parts, CrO
31 ~ 5 part, 1 ~ 5 part of MgS, KPO
310 ~ 20 parts, 10 ~ 20 parts of silica powders, PbO10 ~ 20 part, ZnCl
215 ~ 30 parts of 5 ~ 10 parts, Sodium Tetraborate.
2. the glaze that can be used for frosting according to claim 1 is characterized in that, it is processed by the raw material of following parts by weight:
SiO
230 ~ 40 parts, Al (OH)
315 ~ 20 parts, CrO
33 ~ 5 parts, 3 ~ 5 parts of MgS, KPO
310 ~ 15 parts, 10 ~ 15 parts of silica powders, PbO10 ~ 15 part, ZnCl
215 ~ 25 parts of 5 ~ 8 parts, Sodium Tetraborate.
3. the glaze that can be used for frosting according to claim 1 is characterized in that, it is processed by the raw material of following parts by weight:
SiO
240 parts, Al (OH)
320 parts, CrO
33 parts, 3 parts of MgS, KPO
315 parts, 15 parts of silica powders, PbO15 part, ZnCl
220 parts of 8 parts, Sodium Tetraborate.