CN102719149A - 氯化橡胶防腐涂料 - Google Patents

氯化橡胶防腐涂料 Download PDF

Info

Publication number
CN102719149A
CN102719149A CN2012102304676A CN201210230467A CN102719149A CN 102719149 A CN102719149 A CN 102719149A CN 2012102304676 A CN2012102304676 A CN 2012102304676A CN 201210230467 A CN201210230467 A CN 201210230467A CN 102719149 A CN102719149 A CN 102719149A
Authority
CN
China
Prior art keywords
parts
chlorinated rubber
protective system
rubber protective
paraffin
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN2012102304676A
Other languages
English (en)
Inventor
张跃
钱强
扈占才
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
CHANGSHU FANGTA COATING CHEMICAL Co Ltd
Original Assignee
CHANGSHU FANGTA COATING CHEMICAL Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by CHANGSHU FANGTA COATING CHEMICAL Co Ltd filed Critical CHANGSHU FANGTA COATING CHEMICAL Co Ltd
Priority to CN2012102304676A priority Critical patent/CN102719149A/zh
Publication of CN102719149A publication Critical patent/CN102719149A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种氯化橡胶防腐涂料，包括按质量份数组成的下列成分：氯化橡胶粉末10-12份；石蜡8-10份；热塑性丙烯酸树脂5-10份；二甲苯20-25份；颜填料15-20份；膨润土0.5-1.5份；填料20-25份；改质剂7-10份。通过上述方式，本发明能够提高产品的附着力，使产品粒度均匀，耐腐蚀、抗老化，光泽持久，同时降低生产成本。

Description

氯化橡胶防腐涂料
技术领域
本发明涉及涂料领域，特别是涉及一种氯化橡胶防腐涂料。
背景技术
氯化橡胶防腐涂料主要用于各种车辆、桥梁、厂房及其他钢结构的防腐涂装，使其免受大气、海水、化工气体等介质的侵蚀，延长物件使用寿命和起装饰作用。
现有的氯化橡胶防腐涂料主要是以氯化橡胶为成膜物质，加入颜料、各种填料制成。在常温下干燥快，耐久性好，且不受气温限制。但是其附着力不够理想，需涂刷三道甚至三道以上，且产品粒度不够均匀，生产成本较高。
发明内容
本发明主要解决的技术问题是提供一种氯化橡胶防腐涂料，能够提高产品的附着力，使产品粒度均匀，耐腐蚀、抗老化，光泽持久，同时降低生产成本。
为解决上述技术问题，本发明采用的一个技术方案是：提供一种氯化橡胶防腐涂料，包括按质量份数组成的下列成分：
氯化橡胶粉末        10-12份；
石蜡                8-10份；
热塑性丙烯酸树脂    5-10份；
二甲苯   20-25份；
颜填料              15-20份；
膨润土   0.5-1.5份；
填料                20-25份；
改质剂              7-10份。
在本发明一个较佳实施例中，包括按质量份数组成的下列成分：
氯化橡胶粉末        11份；
石蜡                9份；
热塑性丙烯酸树脂    8份；
二甲苯   22.3份；
颜填料              17份；
膨润土   1份；
填料                23份；
改质剂              8.7份。
在本发明一个较佳实施例中，所述石蜡为52#石蜡。
在本发明一个较佳实施例中，所述颜填料为钛白粉。
在本发明一个较佳实施例中，所述填料为硫酸钡。
在本发明一个较佳实施例中，所述改质剂为滑石粉。
本发明的有益效果是：本发明揭示了一种氯化橡胶防腐涂料，通过在配方中加入了热塑性丙烯酸树脂，大大提高了产品的附着力；钛白粉的加入降低了产品成本；硫酸钡和滑石粉的加入更加提高了产品的性能，使产品粒度均匀，耐腐蚀、抗老化，光泽持久。
具体实施方式
下面对本发明的较佳实施例进行详细阐述，以使本发明的优点和特征能更易于被本领域技术人员理解，从而对本发明的保护范围做出更为清楚明确的界定。
实施例一
一种氯化橡胶防腐涂料，包括按质量份数组成的下列成分：
氯化橡胶粉末        11份；
52#石蜡             9份；
热塑性丙烯酸树脂    8份；
二甲苯   22.3份；
钛白粉              17份；
膨润土   1份；
硫酸钡              23份；
滑石粉              8.7份。
按上述组分生产出来的氯化橡胶防腐涂料，其细度为35μm，弯曲性为10mm，附着力（拉开法）为3.3MPa。
实施例二
一种氯化橡胶防腐涂料，包括按质量份数组成的下列成分：
氯化橡胶粉末        10份；
52#石蜡             10份；
热塑性丙烯酸树脂    5份；
二甲苯   25份；
钛白粉              15份；
膨润土   1份；
硫酸钡              24份；
滑石粉              10份。
按上述组分生产出来的氯化橡胶防腐涂料，其细度为35μm，弯曲性为10mm，附着力（拉开法）为3.3MPa。
实施例三
一种氯化橡胶防腐涂料，包括按质量份数组成的下列成分：
氯化橡胶粉末        12份；
52#石蜡             8份；
热塑性丙烯酸树脂    10份；
二甲苯   20份；
钛白粉              20份；
膨润土   1份；
硫酸钡              22份；
滑石粉              7份。
按上述组分生产出来的氯化橡胶防腐涂料，其细度为35μm，弯曲性为10mm，附着力（拉开法）为3.3MPa。
各成分的主要作用如下：
钛白粉：作为颜填料，可吸收屏蔽紫外线，其具备最佳的化学稳定性和良好的耐老化、抗粉化和抗变色性能，应用于涂料中，可改善涂料的性能。
硫酸钡：应用于涂料中，可以提高漆膜的遮盖、致密性等性能。在一定程度上改善机械性能，且可大大降低成本。
滑石粉：具有润滑性、抗黏、助流、耐火性、抗酸性、绝缘性、熔点高、化学性不活泼、遮盖力良好、柔软、光泽好、吸附力强等优良的物理、化学特性。应用于涂料中，可增加产品形状的稳定，增加张力强度、剪切强度、绕曲强度及压力强度，降低变形、伸张率及热膨胀系数，提高白度高及粒度均匀分散性。
本发明揭示了一种氯化橡胶防腐涂料，通过在配方中加入了热塑性丙烯酸树脂，大大提高了产品的附着力；钛白粉的加入降低了产品成本；硫酸钡和滑石粉的加入更加提高了产品的性能，使产品粒度均匀，耐腐蚀、抗老化，光泽持久。
以上所述仅为本发明的实施例，并非因此限制本发明的专利范围，凡是利用本发明说明书内容所作的等效结构或等效流程变换，或直接或间接运用在其他相关的技术领域，均同理包括在本发明的专利保护范围内。

Claims (6)

1.一种氯化橡胶防腐涂料，其特征在于，包括按质量份数组成的下列成分：
氯化橡胶粉末        10-12份；
石蜡                8-10份；
热塑性丙烯酸树脂    5-10份；
二甲苯 20-25份；
颜填料              15-20份；
膨润土 0.5-1.5份；
填料                20-25份；
改质剂              7-10份。
2.根据权利要求1所述的氯化橡胶防腐涂料，其特征在于，包括按质量份数组成的下列成分：
氯化橡胶粉末        11份；
石蜡                9份；
热塑性丙烯酸树脂    8份；
二甲苯 22.3份；
颜填料              17份；
膨润土 1份；
填料                23份；
改质剂              8.7份。
3.根据权利要求1-2所述的氯化橡胶防腐涂料，其特征在于，所述石蜡为52#石蜡。
4.根据权利要求1-2所述的氯化橡胶防腐涂料，其特征在于，所述颜填料为钛白粉。
5.根据权利要求1-2所述的氯化橡胶防腐涂料，其特征在于，所述填料为硫酸钡。
6.根据权利要求1-2所述的氯化橡胶防腐涂料，其特征在于，所述改质剂为滑石粉。
CN2012102304676A 2012-07-05 2012-07-05 氯化橡胶防腐涂料 Pending CN102719149A (zh)