CN102718453A - 住宅楼板节能减振混凝土 - Google Patents

住宅楼板节能减振混凝土 Download PDF

Info

Publication number
CN102718453A
CN102718453A CN2012102217767A CN201210221776A CN102718453A CN 102718453 A CN102718453 A CN 102718453A CN 2012102217767 A CN2012102217767 A CN 2012102217767A CN 201210221776 A CN201210221776 A CN 201210221776A CN 102718453 A CN102718453 A CN 102718453A
Authority
CN
China
Prior art keywords
concrete
energy
cement
water
admixture
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN2012102217767A
Other languages
English (en)
Other versions
CN102718453B (zh
Inventor
王军强
姜艳霞
孙克纬
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Jiangsu Guangxing Group Co. Ltd.
Jiangsu Guangxing Group Construction Assembly Technology Co., Ltd.
Original Assignee
Jiangsu Institute of Architectural Technology
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Jiangsu Institute of Architectural Technology filed Critical Jiangsu Institute of Architectural Technology
Priority to CN 201210221776 priority Critical patent/CN102718453B/zh
Publication of CN102718453A publication Critical patent/CN102718453A/zh
Application granted granted Critical
Publication of CN102718453B publication Critical patent/CN102718453B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种住宅楼板节能减振混凝土，属混凝土领域。适用于高要求住宅楼板的减振隔音和节能保温。其组成成分及质量配比为：水泥1份，复合矿物掺合料0.10-0.20份，砂子1.3-1.5份，陶粒1.5-2.0份，橡胶颗粒0.1-0.15份；外加剂占水泥质量的1%-2%，纤维掺量为0.2-1kg/m3。提前将陶粒浸水湿润，然后将胶凝材料水泥、复合矿物掺合料、砂子、陶粒投入搅拌机搅拌1min，接着加50%搅拌用水和外加剂，搅拌1min，最后将纤维和剩余的一半水加入搅拌机继续搅拌1-2min，即可形成工作性良好的节能减振混凝土。该混凝土材料耐久可靠，无污染，低碳环保，寿命可以与楼板中的结构混凝土匹配。

Description

住宅楼板节能减振混凝土
技术领域
本发明涉及一种住宅楼板节能减振混凝土，属建筑混凝土领域。主要应用于住宅楼板中的构造层，位于结构层和装修层之间，满足高要求住宅楼板保温节能和减振隔音的综合功能需要。
背景技术
随着人们生活水平的提高，对居住空间、环境、品质等方面有了新的想法和要求，从过去的追求居住空间过渡到追求住宅品质。《健康住宅建设技术规程》(CECS179：2005)、《住宅性能评定技术标准》（GB50362-2005）、《绿色建筑评价标准》（GB 50378-2006）等标准和规程，对住宅环境和品质提出了明确的指标要求。高要求住宅中，楼板需要满足安全性、耐久性、经济性、适用性、环境性等要求，如隔声性能满足要求，是“3A”住宅性能认定中，必须满足的要求之一，其中规定楼板计权标准化撞击声压级≤65dB和楼板空气声计权隔声量≥50dB。《夏热冬冷地区居住建筑节能设计标准》(JGJ134-2010)中规定楼板的传热系数K≤2.0(W/m2·K)。施工实践中，楼板如果不做减振和隔音处理，楼上的活动，如走路、小孩跑动、敲打、搬移、振动等都会给楼下造成影响。为了降低或改善楼板撞击声对楼下住户的影响，采用在楼板结构层上设置减振垫板或弹性材料，上面再浇筑一定厚度的细石混凝土，其上再做装饰面层的方法，基本可以达到楼板撞击声压≤65dB的要求，但存在施工成本高，楼板厚度增大较多，楼板净空小的一些问题。而对于有地采暖要求的楼板，还需要考虑保温节能的综合功能要求。
发明内容
本发明提供一种住宅楼板节能减振混凝土，适用于高要求住宅楼板的减振隔音和节能保温。
本发明是以如下技术方案实现的：一种住宅楼板节能减振混凝土，其组成成分及质量配比为： 
水泥1份 ， 复合矿物掺合料0.10-0.20份，   砂子1.3-1.5份，
    陶粒1.5-2.0份，橡胶颗粒0.1-0.15份；
外加剂占水泥质量的1%-2%，纤维掺量为0.2-1kg/m3。
所述水泥为硅酸盐水泥或普通硅酸盐水泥；
所述复合矿物掺合料是7d和28d的活性指数分别不低于70%和90%，其他性能指标符合规范要求的复合矿物掺合料；
所述陶粒为圆球形，粒径5-10mm，筒压强度≥4.0MPa，堆积密度500-800kg/m3，吸水率≤10%；
所述橡胶颗粒经过改性处理，最大粒径2mm，表观密度980kg/m3，吸水率≤8%。
所述外加剂为聚羧酸高效减水剂。
所述纤维采用聚丙烯纤维。
上述住宅楼板节能减振混凝土，通过在混凝土中配置弹性材料橡胶颗粒和陶粒，降低了混凝土的弹性模量，改善了混凝土的固体传声效果，提高了楼板的保温节能效果。
上述住宅楼板节能减振混凝土，其配置方法为：提前将陶粒浸水湿润，然后将胶凝材料水泥、复合矿物掺合料、砂子、陶粒投入搅拌机搅拌1min，接着加50%搅拌用水和外加剂，搅拌1min，最后将纤维和剩余的一半水加入搅拌机继续搅拌1-2min，即可形成工作性良好的节能减振混凝土。
上述住宅楼板节能减振混凝土，适用于夏热冬冷地区高要求住宅楼板的构造施工，该混凝土铺设于楼板结构层之上，楼板装饰层之下，对于改善楼板撞击声压，提高楼本节能保温效果良好。
上述住宅楼板节能减振混凝土，应用于夏热冬冷地区，可以代替浮筑楼板中的找平层、减振垫、细石混凝土、钢筋网片或钢丝网以及节能需要设置的EPS保温板等楼板做法。
本发明的有益效果是：能同时满足楼板减振隔音、保温节能的综合功能需求，代替楼板中保温层、找平层、浮筑层、减振层、防裂层，有效降低楼板构造层厚度，具有施工简单快捷、综合功能好、安全耐久等优点。该混凝土材料耐久可靠，无污染，低碳环保，寿命可以与楼板中的结构混凝土匹配。
附图说明
图1为本发明的一种住宅楼板节能减振混凝土在高要求住宅楼板中的做法示意图。
图中：1、结构层；2、节能减振混凝土；3、装饰层；4、楼板周边墙体；5、踢脚；6、减振垫。
具体实施方式
实施例1：
各原料组成和质量配比为：
水泥：复合矿物掺合料：砂子：陶粒：橡胶颗粒=364：50：510：680：48, 聚羧酸高效减水剂掺量占水泥质量的1.2%，纤维掺量为0.48kg/m3。
水泥采用普通硅酸盐水泥，强度等级42.5MPa。
砂子采用河砂，细度模数2.7，含泥量≤1%，泥块含量≤0.5%，其它性能指标符合要求。
陶粒采用圆球形，粒径5-10mm，筒压强度4.7MPa，堆积密度570kg/m3，吸水率7%，含泥量1.2%，表观密度1140 kg/m3，空隙率46%。
橡胶颗粒经过NaOH改性处理，最大粒径2mm，表观密度980kg/m3，吸水率≤8%.
纤维采用聚丙烯纤维，耐酸耐碱，掺量为0.2-1.0kg/m3。
其配置方法为：提前5天将陶粒浸水湿润，然后将胶凝材料水泥和复合矿物掺合料与砂子、陶粒依次投入搅拌机，搅拌1min，接着加50%搅拌用水和外加剂，搅拌1min，最后将纤维和剩余的一半水加入搅拌机继续搅拌1-2min，即可形成工作性良好的节能减振混凝土。
结合附图1，对住宅楼板节能减振混凝土在高要求住宅楼板中的应用做具体说明。1、结构层；2、节能减振混凝土；3、装饰层；4、楼板周边墙体；5、踢脚；6、减振垫。
结构为框架剪力墙结构，楼板为现浇钢筋混凝土楼板，板厚140mm，楼板浇筑完毕，进行基层的清理和验收，洒水湿润，涂刷界面结合剂或水泥浆一道，然后用配置好的节能减振混凝土浇筑楼板构造层。当楼板室内面积超过30m2时，需要在节能减振混凝土构造层设置钢筋网或钢丝网片，节能减振混凝土浇筑层厚度一般去50-80mm，浇筑到位后，采用二次抹压工艺进行收面，所形成的表面，即可作为楼板的装饰承载面层。现场测试的楼板撞击声压为63dB，满足了《健康住宅建设技术规程》(CECS179：2005)、《住宅性能评定技术标准》（GB50362-2005）、《绿色建筑评价标准》（GB 50378-2006）等标准、规程的楼板隔声要求。实验室测试的节能减振混凝土，其导热系数为0.347(W/m·K)，楼板传热系数0.93(W/m2·K)，满足住宅楼板保温节能的需要。 
采用节能减振混凝土浇筑结构层1，厚度为50-80mm，可以代替对比构造方案中浮筑保温楼板做法中的找平层，即10-20mm砂浆， 20-40mmEPS保温板，50mm细石混凝土层，而综合的现场测试效果，表明采用60mm节能减振混凝土构造层的楼板，隔声性能和保温性能得到改善，但施工程序少了，楼层净空大了，节能减振混凝土耐火安全，耐久可靠，与结构楼板寿命能保持同步，发明的节能减振混凝土适用于高要求住宅楼板的构造层施工，具有很好的推广应用意义。

Claims (3)

1.一种住宅楼板节能减振混凝土，其特征在于，其组成成分及质量配比为： 
水泥1份 ， 复合矿物掺合料0.10-0.20份，   砂子1.3-1.5份，
    陶粒1.5-2.0份，橡胶颗粒0.1-0.15份；
外加剂占水泥质量的1%-2%，纤维掺量为0.2-1kg/m3；
所述水泥为硅酸盐水泥或普通硅酸盐水泥；
所述复合矿物掺合料是7d和28d的活性指数分别不低于70%和90%，其他性能指标符合规范要求的复合矿物掺合料；
所述陶粒为圆球形，粒径5-10mm，筒压强度≥4.0MPa，堆积密度500-800kg/m3，吸水率≤10%；
所述橡胶颗粒经过改性处理，最大粒径2mm，表观密度980kg/m3，吸水率≤8%；
所述外加剂为聚羧酸高效减水剂。
2. 根据权利要求1所述的住宅楼板节能减振混凝土，其特征在于，所述纤维采用聚丙烯纤维。
3.一种权利要求1或2所述的住宅楼板节能减振混凝土的配置方法，其特征在于，提前将陶粒浸水湿润，然后将胶凝材料水泥、复合矿物掺合料、砂子、陶粒投入搅拌机搅拌1min，接着加50%搅拌用水和外加剂，搅拌1min，最后将纤维和剩余的一半水加入搅拌机继续搅拌1-2min，即可形成工作性良好的节能减振混凝土。
CN 201210221776 2012-07-01 2012-07-01 住宅楼板节能减振混凝土 Active CN102718453B (zh)