CN102701659A - 一种b02级轻质砂加气混凝土防火保温板 - Google Patents

一种b02级轻质砂加气混凝土防火保温板 Download PDF

Info

Publication number
CN102701659A
CN102701659A CN2012102194835A CN201210219483A CN102701659A CN 102701659 A CN102701659 A CN 102701659A CN 2012102194835 A CN2012102194835 A CN 2012102194835A CN 201210219483 A CN201210219483 A CN 201210219483A CN 102701659 A CN102701659 A CN 102701659A
Authority
CN
China
Prior art keywords
aerated concrete
insulation board
heated board
fireproof heated
fireproof insulation
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN2012102194835A
Other languages
English (en)
Other versions
CN102701659B (zh
Inventor
李世香
和平
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
TIANJIN HAIBIN TIANZHU YONGLI BUILDING MATERIAL CO Ltd
Original Assignee
TIANJIN HAIBIN TIANZHU YONGLI BUILDING MATERIAL CO Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by TIANJIN HAIBIN TIANZHU YONGLI BUILDING MATERIAL CO Ltd filed Critical TIANJIN HAIBIN TIANZHU YONGLI BUILDING MATERIAL CO Ltd
Priority to CN 201210219483 priority Critical patent/CN102701659B/zh
Publication of CN102701659A publication Critical patent/CN102701659A/zh
Application granted granted Critical
Publication of CN102701659B publication Critical patent/CN102701659B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种B02级轻质砂加气混凝土防火保温板，其原料组分及其重量百分比含量为：石英砂：45～55％；石灰：12～16％；水泥：24～37％；石膏：5％；铝粉：0.25～0.35％；复合型外加剂：0.2～0.6％。所述的复合型外加剂为复合稳定、增韧及防水作用的外加剂，其原料组分及其重量百分比含量为：松脂酸钠：25～30％；氯化石蜡：22～26％；石油醚：24～28％；有机硅氧烷：20～25％。本发明的优点是：弥补了现有技术的不足与缺陷，克服了其生产难点，在降低砂加气混凝土制品干密度的同时提高了其浇注稳定性，从而方便其制品的运输与施工，满足建筑市场巨大的需求量和人们对城市建筑材料节能、环保的要求。

Description

一种B02级轻质砂加气混凝土防火保温板
技术领域
本发明涉及一种轻质无机非金属防火保温材料，更具体的说，本发明涉及一种干密度低于国家标准GB 11968—2006中最低等级且抗压强度大于等于0.5MPa的B02级砂加气混凝土防火保温板。 
背景技术
目前，国内建筑市场的外保温材料多为有机高分子材料，而这些有机高分子材料均具有易燃、可燃性，遇到明火燃烧时还会释放有毒气体，所以，不符合现代人们崇尚绿色、环保、无毒、低VOC的要求。 
基于此，业内人员开展了有关研究，希望开发一种新型的无机非金属环保材料替代前述的有机高分子产品，以克服现有技术的诸多缺点，应运而生的无机硅酸盐制品砂加气混凝土砌块当属此类。 
所述的无机硅酸盐制品属于A1级不燃材料，其具有质轻、高强、保温、抗渗、隔热、隔声、防火、便于加工、施工便捷、绿色环保等特点，如果以其作为外保温材料，将完全满足人们对环保产品的推崇并符合行业内65%节能的规定。 
但是，本领域的技术人员均知，生产砂加气混凝土产品有如下难点： 
一是，砂加气混凝土制品的浇注稳定性会随着产品干密度的降低而变差，因此，目前几乎没有企业能生产干密度低于255kg/m3的砂加气混凝土砌块。 
二是，砂加气混凝土砌块（板材）属于无机非金属材料，其制品脆性大，因此限制了其使用效果，而且不便于制品的运输。 
发明内容
本发明所要解决的问题，就是弥补前述现有技术的不足与缺陷，并克服其生产难点，从而提供一种通过稳定增韧抗渗工艺而确保其质轻、高强、保温、抗渗、隔热、隔声、防火、便于加工制作、方便施工运输的B02级轻质砂加气混凝土防火保温板，该保温板的干密度将低于国家标准GB11968—2006中的最低等级，但却可以保持其浇注稳定性以及0.5MPa及以上的抗压强度。 
本发明的B02级轻质砂加气混凝土防火保温板，其原料组分及其重量百分比含量为： 
石英砂：45～55％； 
石灰：12～16％； 
水泥：24～37％； 
石膏：5％； 
铝粉：0.25～0.35％； 
复合型外加剂：0.2～0.6％。 
所述的复合型外加剂为复合稳定、增韧及防水作用的外加剂，其原料组分及其重量百分比含量为： 
松脂酸钠：25～30％； 
氯化石蜡：22～26％； 
石油醚：24～28％； 
有机硅氧烷：20～25％。 
所述石英砂的细度为200目以上，其中的硅含量为94%以上。 
所述石灰的有效钙含量在80%以上。 
所述石膏为脱硫石膏。 
所述的铝粉为发气剂。 
本发明的B02级轻质砂加气混凝土防火保温板，与现有技术的有机高分子材料的防火保温板相比，其有益效果在于： 
（1）通过合理的组分配比，在降低砂加气混凝土制品干密度的同时，提高了其浇注稳定性，使B02级轻质保温板材料得以批量生产，从而解决了目前国内外建筑用新型外保温绝热材料品种匮乏的难题。 
（2）通过合理的组分配比以及在组分中添加稳定、增韧、防水作用外加剂的加工工艺，解决了行业中一直以来难以解决的混凝土制品脆性大的问题，从而方便了其制品的运输与施工。 
（3）本发明防火保温板的A1级不燃材料属性及其无毒、无害、质轻、保温、抗渗、隔热、防火、绿色环保等特点，满足了建筑市场巨大的需求量和人们对城市建筑材料节能、环保的要求。 
（4）本发明弥补了现有技术的诸多不足，克服了一直以来砂加气混凝土制品的生产难点，产品的干密度仅为180-255kg/m3，小于国家标准GB11968—2006“蒸压加气混凝土砌块”干密度分级中最小的B03级（225-325kg/m3）级别，导热系数小于0.06W/（M·K），抗压强度达0.5MPa及以上，具有很好的实用性。 
具体实施方式
为了使本发明更容易被清楚理解，以下结合实施例对本发明的技术方案作以详细描述。 
实施例1： 
一种B02级轻质砂加气混凝土防火保温板，按照下列原料的重量百分比进行配料： 
石英砂：48％； 
石灰：13％； 
水泥：33.3％； 
石膏：5％； 
铝粉：0.3％； 
复合型外加剂：0.4％。 
所述的复合型外加剂为复合稳定、增韧及防水作用的外加剂，其原料重量百分比含量为： 
松脂酸钠：25％； 
氯化石蜡：22％； 
石油醚：28％； 
有机硅氧烷：25％。 
该实施例产品的性能是：干密度198.4kg/m3，强度0.51MPa,导热系数0.054W/(M·K)。 
实施例2： 
一种B02级轻质砂加气混凝土防火保温板，按照下列原料的重量百分比进行配料： 
石英砂：50％： 
石灰：15％； 
水泥：29.29％： 
石膏：5％： 
铝粉：0.26％； 
复合型外加剂：0.45％。 
所述的复合型外加剂为复合稳定、增韧及防水作用的外加剂，其原料重量百分比含量为： 
松脂酸钠：25％； 
氯化石蜡：26％； 
石油醚：24％； 
有机硅氧烷：25％。 
该实施例产品的性能是：干密度237kg/m3，强度0.59MPa,导热系数0.057W/(M·K)。 
本发明的主要优点如下： 
（1）通过大量实验，优化了基础配方和生产工艺，从而提高了低密度砂加气混凝土的浇注稳定性，提高了制品的韧性，从而增强了制品的应用效果，并使其摆脱了不便于施工与运输的诸多限制。 
（3）使高效、稳定地生产B02级砂加气混凝土砌块成为可能，并在保证制品干密度小于国家标准中最小级别的同时，保证其大于等于0.5MPa的抗压强度和小于0.06W/（M·K）的导热系数。 
（4）价位适中，绿色环保，使用效果良好，是建筑行业可以广泛使用且不可多得的轻质、低密度、无机环保的非金属防火保温材料。 
以上通过实施例对本发明的B02级轻质砂加气混凝土防火保温板的原料配方和产品特点进行了描述，该描述没有限制性，而实际的应用也不仅仅限于以上的实施例。本领域人员应能理解，在实际应用中，为了适合于某种需要，前述实施例中各组分的含量均可能在其范围内获得其它选择，而其他人员在本发明的启示下也可能作出相同或相似的技术方案。特别需要指出的是，只要不脱离本发明的宗旨，所有显而易见的改变均包含在本发明的保护范围之内。 

Claims (7)

1.一种B02级轻质砂加气混凝土防火保温板，其特征是，原料组分及其重量百分比含量为：石英砂：45～55％；石灰：12～16％；水泥：24～37％；石膏：5％；铝粉：0.25～0.35％；复合型外加剂：0.2～0.6％。
2.根据权利要求1所述的B02级轻质砂加气混凝土防火保温板，其特征是，所述的复合型外加剂为复合稳定、增韧及防水作用的外加剂，其原料组分及其重量百分比含量为：松脂酸钠：25～30％；氯化石蜡：22～26％；石油醚：24～28％；有机硅氧烷：20～25％。
3.根据权利要求1所述的B02级轻质砂加气混凝土防火保温板，其特征是，所述石英砂的细度为200目以上。
4.根据权利要求1所述的B02级轻质砂加气混凝土防火保温板，其特征是，所述石英砂中的硅含量为94%以上。
5.根据权利要求1所述的B02级轻质砂加气混凝土防火保温板，其特征是，所述石灰的有效钙含量在80%以上。
6.根据权利要求1所述的B02级轻质砂加气混凝土防火保温板，其特征是，所述石膏为脱硫石膏。
7.根据权利要求1所述的B02级轻质砂加气混凝土防火保温板，其特征是，所述的铝粉为发气剂。
CN 201210219483 2012-06-28 2012-06-28 一种b02级轻质砂加气混凝土防火保温板 Expired - Fee Related CN102701659B (zh)