CN102701649A - 无机水泥发泡保温板及其制备方法 - Google Patents
无机水泥发泡保温板及其制备方法 Download PDFInfo
- Publication number
- CN102701649A CN102701649A CN2012101482233A CN201210148223A CN102701649A CN 102701649 A CN102701649 A CN 102701649A CN 2012101482233 A CN2012101482233 A CN 2012101482233A CN 201210148223 A CN201210148223 A CN 201210148223A CN 102701649 A CN102701649 A CN 102701649A
- Authority
- CN
- China
- Prior art keywords
- insulation board
- inorganic cement
- foaming insulation
- stablizer
- cement foaming
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及一种无机水泥发泡保温板,其按重量百分比包含如下物质:水泥56-63%,煤灰35-42%,发泡剂0.6-1.0%,稳定剂0.4-0.6%,聚丙稀纤维0.6-1.2%。本发明还提供一种上述无机水泥发泡保温板的制备方法。本发明的无机水泥发泡保温板的导热性能好、质量轻、强度高、施工简单,特别是放火不会燃烧,增强了建筑的安全性。而且,本发明的无机水泥发泡保温板主要采用水泥和煤灰制成,成本低廉,非常有利于市场推广。
Description
技术领域
本发明涉及建筑材料领域,尤其是涉及一种无机水泥发泡保温板及其制备方法。
背景技术
现有的外墙内保温材料主要包括无机保温材料和有机保温材料。用有机保温材料作外墙内保温,一旦发生火灾,其释放的有毒气体内可使人窒息甚至死亡。目前,国外一些国家要求20米以上的建筑物不允许使用有机保温材料,特别是外墙内保温更不可使用有机保温材料,而我国一些地方,则仍然使用有机保温板作外墙内保温,后患无穷。因此,无机保温材料逐渐成为市场的主流产品。目前,水泥是最常见的无机建筑材料,而煤灰作为常见的城市垃圾,也是一种重要的无机材料,如何利用水泥和煤灰生产出无机保温材料,成为本领域技术人员亟待解决的技术问题。
发明内容
本发明的目的是针对上述问题,提供一种防燃、成本低的无机水泥发泡保温板。
为达到上述目的,本发明采用了下列技术方案:一种无机水泥发泡保温板,其按重量百分比包含如下物质:
水泥 56-63%,
煤灰 35-42%,
发泡剂 0.6-1.0%,
稳定剂 0.4-0.6%,
聚丙稀纤维 0.6-1.2%。
优选地,上述的无机水泥发泡保温板按重量百分比包含如下物质:水泥60%,煤灰38%,发泡剂0.7%,稳定剂0.5%,聚丙稀纤维0.8%。
优选地,上述的无机水泥发泡保温板按重量百分比包含如下物质:水泥58%,煤灰40%,发泡剂0.6%,稳定剂0.4%,聚丙稀纤维1.0%。
优选地,上述的无机水泥发泡保温板按重量百分比包含如下物质:水泥56%,煤灰42%,发泡剂1.0%,稳定剂0.4%,聚丙稀纤维0.6%。
优选地,上述的无机水泥发泡保温板中,所述发泡剂为过氧化氢和/或松香钠皂。
优选地,上述的无机水泥发泡保温板中,所述稳定剂为硬脂酸钙。
本发明还提供一种上述无机水泥发泡保温板的制备方法,其包括以下步骤:
将水泥、煤灰、发泡剂、稳定剂和聚丙稀纤维按所述无机水泥发泡保温板的组分比例配置好;
将配置好的混合物投入搅拌机中,加水搅拌;
将搅拌后的浆料注入保温板箱内,静置固化成型;
脱模,得到成型板料;
根据所需尺寸对成型板料进行切割,得到所述无机水泥发泡保温板。
优选地,上述的无机水泥发泡保温板的制备方法中,脱模得到成型板料后,对成型板料养护10-15天。
本发明的无机水泥发泡保温板的导热性能好、质量轻、强度高、施工简单,特别是放火不会燃烧,增强了建筑的安全性。而且,本发明的无机水泥发泡保温板主要采用水泥和煤灰制成,成本低廉,非常有利于市场推广。
具体实施方式
本发明提供一种无机水泥发泡保温板,其按重量百分比包含如下物质:
水泥 56-63%,
煤灰 35-42%,
发泡剂 0.6-1.0%,
稳定剂 0.4-0.6%,
聚丙稀纤维 0.6-1.2%。
下面提供上述无机水泥发泡保温板的三个实施例:
实施例1:
一种无机水泥发泡保温板,按重量百分比包含如下物质:水泥60%,煤灰38%,发泡剂0.7%,稳定剂0.5%,聚丙稀纤维0.8%。
实施例2:
一种无机水泥发泡保温板,按重量百分比包含如下物质:水泥58%,煤灰40%,发泡剂0.6%,稳定剂0.4%,聚丙稀纤维1.0%。
实施例3:
一种无机水泥发泡保温板,按重量比包含如下物质:水泥56%,煤灰42%,发泡剂1.0%,稳定剂0.4%,聚丙稀纤维0.6%。
在上述实施例中,发泡剂可以为过氧化氢、松香钠皂,稳定剂可以为硬脂酸钙。
经按国家标准进行检测,其物理力学性能如下表所示。
本发明的无机水泥发泡保温板的导热性能好、质量轻、强度高、施工简单,特别是放火不会燃烧,增强了建筑的安全性。而且,本发明的无机水泥发泡保温板主要采用水泥和煤灰制成,成本低廉,非常有利于市场推广。
本发明还提供一种上述无机水泥发泡保温板的制备方法,其包括以下步骤:
将水泥、煤灰、发泡剂、稳定剂和聚丙稀纤维按上述组分比例配置好;
将配置好的混合物投入搅拌机中,加水搅拌10分钟;
将搅拌后的浆料注入保温板箱内,静置两天,固化成型;
脱模,得到成型板料,脱模后可以对成型板料养护10-15天;
根据所需尺寸对成型板料进行切割,得到所述无机水泥发泡保温板。
本文中所描述的具体实施例仅仅是对本发明精神作举例说明。本发明所属技术领域的技术人员可以对所描述的具体实施例做各种各样的修改或补充或采用类似的方式替代,但并不会偏离本发明的精神或者超越所附权利要求书所定义的范围。
尽管本文较多地使用了水泥、煤灰、发泡剂、稳定剂等术语,但并不排除使用其它术语的可能性。使用这些术语仅仅是为了更方便地描述和解释本发明的本质;把它们解释成任何一种附加的限制都是与本发明精神相违背的。
Claims (8)
1.一种无机水泥发泡保温板,其特征在于,按重量百分比包含如下物质:
水泥 56-63%,
煤灰 35-42%,
发泡剂 0.6-1.0%,
稳定剂 0.4-0.6%,
聚丙稀纤维 0.6-1.2%。
2.根据权利要求1所述的无机水泥发泡保温板,其特征在于,按重量百分比包含如下物质:水泥60%,煤灰38%,发泡剂0.7%,稳定剂0.5%,聚丙稀纤维0.8%。
3.根据权利要求1所述的无机水泥发泡保温板,其特征在于,按重量百分比包含如下物质:水泥58%,煤灰40%,发泡剂0.6%,稳定剂0.4%,聚丙稀纤维1.0%。
4.根据权利要求1所述的无机水泥发泡保温板,其特征在于,按重量百分比包含如下物质:水泥56%,煤灰42%,发泡剂1.0%,稳定剂0.4%,聚丙稀纤维0.6%。
5.根据权利要求1-4任一项所述的无机水泥发泡保温板,所述发泡剂为过氧化氢和/或松香钠皂。
6.根据权利要求1-4任一项所述的无机水泥发泡保温板,所述稳定剂为硬脂酸钙。
7.一种如权利要求1-6任一项所述的无机水泥发泡保温板的制备方法,其特征在于,包括以下步骤:
将水泥、煤灰、发泡剂、稳定剂和聚丙稀纤维按所述无机水泥发泡保温板的组分比例配置好;
将配置好的混合物投入搅拌机中,加水搅拌;
将搅拌后的浆料注入保温板箱内,静置固化成型;
脱模,得到成型板料;
根据所需尺寸对成型板料进行切割,得到所述无机水泥发泡保温板。
8.如权利要求7所述的无机水泥发泡保温板的制备方法,脱模得到成型板料后,对成型板料养护10-15天。