CN102683844A - 一种美化天线罩及其制备方法 - Google Patents
一种美化天线罩及其制备方法 Download PDFInfo
- Publication number
- CN102683844A CN102683844A CN2012101277559A CN201210127755A CN102683844A CN 102683844 A CN102683844 A CN 102683844A CN 2012101277559 A CN2012101277559 A CN 2012101277559A CN 201210127755 A CN201210127755 A CN 201210127755A CN 102683844 A CN102683844 A CN 102683844A
- Authority
- CN
- China
- Prior art keywords
- preparation
- slurry
- cloth
- antenna cover
- reinforcement fibers
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明公开一种美化天线罩及其制备方法,其包括步骤:将热固性合成树脂溶液和经过改性处理的填料搅拌混合后形成所需浆料,其中所述填料质量为浆料质量的2.5%至9.7%;制备玻璃纤维复合层,所述玻璃纤维复合层包括内层和外层,所述内层由纯玻璃纤维毡制成,所述外层为附着有根据应用环境设计的使得天线罩隐蔽或伪装的图案花纹的表面毡;将多片增强纤维布依次涂覆所述浆料;将所述玻璃纤维复合层的内层贴附于最外层的涂覆有浆料的增强纤维布上并将多个增强纤维布与玻璃纤维复合层固化一体。本发明通过将美化天线罩的图案层和天线罩本体通过手糊工艺一体成型,减少了后期重复进行喷漆美化的工艺,节省资源也克服了现有的喷涂工艺的缺陷。
Description
技术领域
本发明涉及天线罩技术领域,尤其涉及一种美化天线罩及其制备方法。
背景技术
近年来,随着国内移动通信的迅猛发展,为了提供更高质量的服务,移动、电信和联通三大运营商提出了全面覆盖、无缝覆盖的概念,为了达到该目标,需要大量增设基站天线,并且还很多基站天线需要设置在居民小区、办公区域内。
杂乱无章的基站天线不符合城市对环境景观的要求,同时也给居民带来不安全感;为了克服上述问题同时保护基站天线,一般在基站天线外面设置美化天线罩,该天线罩在不增大传输损耗的前提下,通过各种手段对天线罩的外表进行伪装和修饰以达到隐蔽和美化的效果。
现有的美化天线罩以玻璃钢为原料制成,现有玻璃钢材料是以玻璃纤维及其制品作为增强材料,以合成树脂作为基体材料的一种复合材料。采用该类玻璃钢制备美化天线罩时存在如下问题:(1)天线罩厚度较厚,电气性能,例如透波率、驻波比等不佳;如减薄厚度则会造成机械性能较差,不能满足安全性能要求;(2)玻璃钢表面沙眼气孔较多,当采用喷涂工艺在玻璃钢表面喷涂伪装图案时会给喷涂过程造成很大不便,造成资源的浪费。
发明内容
本发明所要解决的技术问题在于,针对现有技术的上述不足,提出一种电气性能和机械性能均良好且图案与天线罩本体一体成型的美化天线罩及其制备方法。
本发明解决其技术问题采用的技术方案是,提出一种美化天线罩的制备方法,其包括步骤:
S1:将热固性合成树脂溶液和经过改性处理的填料搅拌混合后形成所需浆料,其中所述填料质量为浆料质量的2.5%至9.7%;
S2:制备玻璃纤维复合层,所述玻璃纤维复合层包括内层和外层,所述内层由纯玻璃纤维毡制成,所述外层为附着有根据应用环境设计的使得天线罩隐蔽或伪装的图案花纹的表面毡;
S3:将增强纤维以平纹、斜纹或缎纹的编织方式编织成多片增强纤维布,将第一增强纤维布放置于备好的天线罩模具上,并在第一增强纤维布上均匀涂覆所述浆料,然后在已涂覆好浆料的第一增强纤维布上对齐放置第二增强纤维布,并在第二增强纤维布上均匀涂覆所述浆料,重复上述操作直至涂覆好浆料的多个增强纤维布的厚度满足预设厚度;
S4:将所述玻璃纤维复合层的内层贴附于步骤S3中最外层的涂覆有浆料的增强纤维布上并将多个增强纤维布与玻璃纤维复合层固化一体。
进一步地,所述填料改性处理方式为酸碱蚀刻处理、偶联剂处理或涂层处理。
进一步地,所述热固性合成树脂溶液由不饱和聚酯树脂、环氧树脂、酚醛树脂、呋喃树脂、乙烯基酯树脂中的一种或多种构成。
进一步地,所述填料包括玻璃微珠、聚苯乙烯微球、磁性微球、气相二氧化硅微粉、气凝胶粉、聚乙烯微粉、陶瓷微粉、PTFE微粉中的一种或多种。
进一步地,所述玻璃微珠的粒径范围为10-180微米,堆积密度为0.1-0.28克每立方厘米。
进一步地,所述填料还包括色母粉。
进一步地,所述增强纤维为玻璃纤维、碳纤维、超高分子量聚乙烯纤维、芳纶纤维或者石英纤维。
进一步地,所述增强纤维在浸渍前还包括表面改性处理步骤。
进一步地,所述图案为瓷砖条纹图案、岩石图案、树纹图案或者镜面图案。
本发明还提供一种美化天线罩,其由上述制备方法制得。
本发明通过将美化天线罩的图案层和天线罩本体通过手糊工艺一体成型,减少了后期重复进行喷漆美化的工艺,节省资源也克服了现有的喷涂工艺的缺陷。另外,采用特定配方的填料和增强纤维使得本发明天线罩本体的机械强度和电气强度均良好。进一步地,本发明采用手糊工艺制备天线罩而非挤拉一体成型工艺,其工艺简单,无需设置和调试复杂的机器参数且节约成本。
附图说明
图1为本发明美化天线罩的制备方法工艺流程图。
具体实施方式
图1为本发明美化天线罩的制备方法的工艺流程图。本发明美化天线罩通过如下方法制备:
步骤S1:将热固性合成树脂溶液和经过改性处理的填料搅拌混合后形成所需浆料,其中填料质量为浆料质量的2.5%至9.7%;
热固性合成树脂溶液可包括不饱和聚酯树脂、环氧树脂、酚醛树脂、呋喃树脂、乙烯基酯树脂中的任意一种或多种。热固性合成树脂溶液视具体情况可添加引发剂、促进剂、阻燃剂、溶剂等其他辅助材料。
不同的树脂类型和用量,可选用不同的固化体系。在本实施例中,所述热固性合成树脂溶液是以不饱和聚酯树脂为原料配制,可采用咪唑类固化体系或胺类固化体系。
搅拌混合所述热固性合成树脂和填料的方法可为机械搅拌的方式,例如利用不产生漩涡的混合机,也可采用人工搅拌的方式,只要使得填料和热固性合成树脂混合均匀即可。
填料可包括玻璃微珠、聚苯乙烯微球、磁性微球、气相二氧化硅微粉、气凝胶粉、聚乙烯微粉、陶瓷微粉、PTFE(聚四氟乙烯,Poly tetra fluoro ethylene)微粉中的一种或多种。玻璃微珠是一种尺寸微小(典型的粒径范围为10-180微米)且轻质(堆积密度为0.1-0.28克每立方厘米)的空心玻璃球体,主要由二氧化硅和三氧化二铝等组成,具有低导热、隔音、高分散、电绝缘性和热稳定性好等优异性能。玻璃微珠加入所述热固性合成树脂溶液后呈蜂窝状,从而提高了所述热固性合成树脂溶液的孔隙率,使其介电常数和损耗角正切降低并同时使得最终制备得到的玻璃钢的刚度和硬度提高。
当然,除了上述填料外,可依据需要增加着色剂,例如色母粉等。
为了改善填料和树脂间的界面结合力以及填料的分散性,增强树脂与填料之间的结合力,需要对填料进行改性处理,处理方式可以是酸碱蚀刻处理、偶联剂处理或涂层处理。
步骤S2:制备玻璃纤维复合层,所述玻璃纤维复合层包括内层和外层,所述内层由纯玻璃纤维毡制成,所述外层为附着有根据应用环境设计的使得天线罩隐蔽或伪装的图案花纹的表面毡。
表面毡能很好的与玻璃纤维结合,提高天线罩整体的表面光洁度和防渗透性、提高天线罩的耐腐蚀性和耐候性。
同时本发明还在表面毡上附着图案花纹,该些图案花纹可以为瓷砖条纹图案、岩石图案、树纹图案、镜面图案等,图案可以根据天线罩使用的环境具体设计,只要能达到美化和隐蔽的效果即可。因此利用表面毡
步骤S3:将增强纤维以平纹、斜纹或缎纹的编织方式编织成多片增强纤维布,将第一增强纤维布放置于备好的天线罩模具上,并在第一增强纤维布上均匀涂覆所述浆料,然后在已涂覆好浆料的第一增强纤维布上对齐放置第二增强纤维布,并在第二增强纤维布上均匀涂覆所述浆料,重复上述操作直至涂覆好浆料的多个增强纤维布的厚度满足预设厚度。
放置增强纤维布之前可以在天线罩模具上涂覆脱模剂,以便固化后天线罩制品较便捷地从模具上脱离。
优选地,为了增强增强纤维与浆料的结合力,也可事先将增强纤维进行表面改性处理,处理方式可以是酸碱蚀刻处理、偶联剂处理或者涂层处理。
增强纤维可采用玻璃纤维、碳纤维、超高分子量聚乙烯纤维、芳纶纤维或者石英纤维等。
美化天线罩的预设厚度可根据应用环境的不同而不同,如其应用环境对机械强度要求较高,则厚度需求就较高,不同的厚度对应不同层数的增强纤维布。例如3mm厚度的美化天线罩则需要使用4-8层增强纤维布。
步骤S4:将所述玻璃纤维复合层的内层贴附于步骤S3中最外层的涂覆有浆料的增强纤维布上并将多个增强纤维布与玻璃纤维复合层固化一体。
由于本发明采用手糊工艺将增强纤维以及玻璃纤维复合层制备成型,无需设置繁琐和复杂的机器参数,节约成本且工艺简单。
本发明通过将美化天线罩的图案层和天线罩本体一体成型,减少了后期重复进行喷漆美化的工艺,节省资源也克服了现有的喷涂工艺的缺陷。
测试本发明采用不同质量比的填料时制得的美化天线罩的电气性能和机械性能,其结果如下表:
从以上结果可以看出,当填料质量占浆料质量百分比为2.5%-9.7%时,其机械性能和电气性能都较好。其中填料质量占浆料质量百分比为7.5%-8.5%时为本发明优选方案。
上面结合附图对本发明的实施例进行了描述,但是本发明并不局限于上述的具体实施方式,上述的具体实施方式仅仅是示意性的,而不是限制性的,本领域的普通技术人员在本发明的启示下,在不脱离本发明宗旨和权利要求所保护的范围情况下,还可做出很多形式,这些均属于本发明的保护之内。
Claims (10)
1.一种美化天线罩的制备方法,其特征在于:包括步骤:
S1:将热固性合成树脂溶液和经过改性处理的填料搅拌混合后形成所需浆料,其中所述填料质量为浆料质量的2.5%至9.7%;
S2:制备玻璃纤维复合层,所述玻璃纤维复合层包括内层和外层,所述内层由纯玻璃纤维毡制成,所述外层为附着有根据应用环境设计的使得天线罩隐蔽或伪装的图案花纹的表面毡;
S3:将增强纤维以平纹、斜纹或缎纹的编织方式编织成多片增强纤维布,将第一增强纤维布放置于备好的天线罩模具上,并在第一增强纤维布上均匀涂覆所述浆料,然后在已涂覆好浆料的第一增强纤维布上对齐放置第二增强纤维布,并在第二增强纤维布上均匀涂覆所述浆料,重复上述操作直至涂覆好浆料的多个增强纤维布的厚度满足预设厚度;
S4:将所述玻璃纤维复合层的内层贴附于步骤S3中最外层的涂覆有浆料的增强纤维布上并将多个增强纤维布与玻璃纤维复合层固化一体。
2.如权利要求1所述的美化天线罩的制备方法,其特征在于:所述填料改性处理方式为酸碱蚀刻处理、偶联剂处理或涂层处理。
3.如权利要求1所述的美化天线罩的制备方法,其特征在于:所述热固性合成树脂溶液由不饱和聚酯树脂、环氧树脂、酚醛树脂、呋喃树脂、乙烯基酯树脂中的一种或多种构成。
4.如权利要求3所述的美化天线罩的制备方法,其特征在于:所述填料包括玻璃微珠、聚苯乙烯微球、磁性微球、气相二氧化硅微粉、气凝胶粉、聚乙烯微粉、陶瓷微粉、PTFE微粉中的一种或多种。
5.如权利要求4所述的美化天线罩的制备方法,其特征在于:所述玻璃微珠的粒径范围为10-180微米,堆积密度为0.1-0.28克每立方厘米。
6.如权利要求1所述的美化天线罩的制备方法,其特征在于:所述填料还包括色母粉。
7.如权利要求1所述的美化天线罩的制备方法,其特征在于:所述增强纤维为玻璃纤维、碳纤维、超高分子量聚乙烯纤维、芳纶纤维或者石英纤维。
8.如权利要求7所述的美化天线罩的制备方法,其特征在于:所述增强纤维在浸渍前还包括表面改性处理步骤。
9.如权利要求1所述的美化天线罩的制备方法,其特征在于:所述图案为瓷砖条纹图案、岩石图案、树纹图案或者镜面图案。
10.一种美化天线罩,其特征在于:由权利要求1至权利要求9任一项所述制备方法制得。