CN102670419A - Stellerite anti-staining toothpaste friction agent and preparation method thereof - Google Patents
Stellerite anti-staining toothpaste friction agent and preparation method thereof Download PDFInfo
- Publication number
- CN102670419A CN102670419A CN2012101782100A CN201210178210A CN102670419A CN 102670419 A CN102670419 A CN 102670419A CN 2012101782100 A CN2012101782100 A CN 2012101782100A CN 201210178210 A CN201210178210 A CN 201210178210A CN 102670419 A CN102670419 A CN 102670419A
- Authority
- CN
- China
- Prior art keywords
- epidesmine
- toothpaste
- stellerite
- staining
- dry
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides a stellerite anti-staining toothpaste friction agent and a preparation method thereof. The preparation method is that the stellerite raw ore is dressed, washed, ground in a dry state, modified with hydrochloric acid sodium chloride, and then is washed and dried to obtain the stellerite anti-staining toothpaste friction agent, and the stellerite anti-staining toothpaste friction agent is added into toothpaste production as per a certain proportion, so that the practical anti-staining toothpaste is made. The stellerite anti-staining toothpaste friction agent can prolong the retention time of effective components of the toothpaste, enables moisture not to volatilize easily and to be stable, removes stain quickly, improves the toothpaste quality, and reduces the production cost of the toothpaste.
Description
Technical field
The present invention relates to the application of epidesmine, specifically is that epidesmine goes stain type toothpaste abrasives and preparation method thereof.
Background technology
Natural parastilbite is a natural zeolite, is the aluminium silicate mineral of a kind of aqueous alkali metal or alkaline-earth metal, the tectosilicate of being made up of silicon-oxy tetrahedron and aluminum-oxygen tetrahedron.The epidesmine purposes is a lot, can mend solvent additive as rubber, can be used as water purification agent, also have as toothpaste abrasives, but this toothpaste abrasives does not have the stain effect.The existing stain type toothpaste abrasives of going is to remove to steep composition with the sodium phytate conduct, 6,000 yuan per ton of sodium phytate, and cost is too high.
As going stain type toothpaste abrasives not see as yet report is arranged with epidesmine.
Summary of the invention
The objective of the invention is to provide a kind of epidesmine to go stain type toothpaste abrasives and preparation method thereof.
Epidesmine of the present invention goes stain type toothpaste abrasives; Be to be primary raw material with the epidesmine raw ore; Through ore dressing, elutriation, dry grinding, with hydrochloric acid, sodium chloride remodeling, washing is dry and the powdery article processed add in the toothpaste with certain proportion, can produce stain type effect toothpaste.
Epidesmine goes the method for preparing of stain type toothpaste abrasives, comprises the steps:
1, the epidesmine raw ore is carried out ore dressing, purity reaches more than 90%;
2, eluriate, dry, adsorbed water content is less than 5%;
3, the Raymond mill dry grinding is extremely greater than 400 orders;
4, epidesmine is retrofited: press 50-100g epidesmine powder, pour in the distilled water of 250-500ml, the materials ratio that adds the pure hydrochloric acid of 0.75-1.5mol then mixes; At room temperature soaked 2-3 hour; Filter then, filtrate is cleaned to neutral with clear water, filters;
5, set by step in 4 gained filtrate 70-80g join in the water of 250-500ml, the materials ratio that adds 10-20g sodium chloride mixes, and at room temperature soaks 3-4 hour, filters then, dry packing.
Behind the epidesmine remodeling; Can effectively improve its pore passage structure; Absorbability obviously improves, and the effective ingredient of toothpaste is kept and slowly release like washing foam, binding agent, heat preserving agent, sweeting agent, aromatic and moisture lastingly, and toothpaste can be dry.Through clinical verification, with epidesmine as primary raw material go steep toothpaste abrasive and go to steep effect and remove to steep toothpaste and improve about 20% than common.
Advantage of the present invention is:
1, epidesmine goes stain type toothpaste abrasives can prolong the effective ingredient retention time of toothpaste;
2, epidesmine has good caking property, adsorptivity, can improve toothpaste quality, and can be not dry;
3, to remove to steep the most of on the market now cost of material of ratio of the prices of raw and semifnished materials low for this patent, goes to steep effective;
4, epidesmine itself is nontoxic, goes to steep the interpolation material non-toxic side effect of using in the process of toothpaste abrasive in production more;
5, the physical characteristic of epidesmine (duct and hole account for cumulative volume 45%) has determined it to have very strong adsorptivity, caking property, can remove the tooth stain fast.
The specific embodiment
Embodiment:
Epidesmine goes the method for preparing of stain type toothpaste abrasives, and its primary raw material is natural parastilbite mineral, hydrochloric acid solution and Sal, and concrete method for preparing comprises the steps:
(1) the epidesmine raw ore is eluriated;
(1) the epidesmine raw ore is carried out ore dressing, purity reaches more than 90%;
(2) eluriate, dry, adsorbed water content is less than 5%;
(3) the Raymond mill dry grinding is extremely greater than 400 orders;
(4) to epidesmine remodeling, get 100g epidesmine powder, pour in the distilled water of 500ml, add the pure hydrochloric acid of 1.5mol then, at room temperature soaked 2 hours, filter then, filtrate is cleaned to neutral with clear water, filters;
(5) gained filtrate in the step (4) is joined in the water of 500ml, add 20g sodium chloride, at room temperature soaked 2 hours, then filtration, dry packing.
Claims (3)
1. epidesmine goes stain type toothpaste abrasives, it is characterized in that: it is to be primary raw material with the stellerite ore, and through ore dressing, elutriation, dry grinding, hydrochloric acid, sodium chloride retrofit, wash dry and powdery product that make.
2. epidesmine goes the method for preparing of stain type toothpaste abrasives, comprises the steps:
(1) the epidesmine raw ore is carried out ore dressing, purity reaches more than 90%;
(2) eluriate, dry, adsorbed water content is less than 5%;
(3) the Raymond mill dry grinding is extremely greater than 400 orders;
(4) epidesmine is retrofited: press 50-100g epidesmine powder, pour in the distilled water of 250-500ml, the materials ratio that adds the pure hydrochloric acid of 0.75-1.5mol then mixes; At room temperature soaked 2-3 hour; Filter then, filtrate is cleaned to neutral with clear water, filters;
(5) set by step gained filtrate 70-80g joins in the water of 250-500ml in (4), and the materials ratio that adds 10-20g sodium chloride mixes, and at room temperature soaks 3-4 hour, then filtration, dry packing.
3. the epidesmine with the described method for preparing preparation of claim 2 goes stain type toothpaste abrasives.