CN102661438A - 一种耐磨损不结垢暖气阀芯 - Google Patents
一种耐磨损不结垢暖气阀芯 Download PDFInfo
- Publication number
- CN102661438A CN102661438A CN2012101528186A CN201210152818A CN102661438A CN 102661438 A CN102661438 A CN 102661438A CN 2012101528186 A CN2012101528186 A CN 2012101528186A CN 201210152818 A CN201210152818 A CN 201210152818A CN 102661438 A CN102661438 A CN 102661438A
- Authority
- CN
- China
- Prior art keywords
- graphite
- wear
- incubated
- heating installation
- parts
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明属于材料领域,涉及一种耐磨损不结垢暖气阀芯及其制备方法。按照重量份计,该暖气阀芯的主要成分为:聚四氟乙烯50-80份,石墨10-30份,碳纤维5-15份。本发明所述的不结垢暖气阀芯以聚四氟乙烯、石墨、碳纤维为原料,避免了使用过程中水垢的附着沉积,机械强度高,耐磨,制备方法简单,可以广泛应用于暖气阀门上。
Description
技术领域
本发明涉及一种耐磨损不结垢暖气阀芯及其制备方法,属于材料领域。
背景技术
随着社会的发展,暖气已经成为人们冬季取暖的主要方式之一,因此,暖气的质量也成为人们逐渐关注的问题。目前,人们暖气上采用的暖气阀芯,通常是由铜、铁等普通金属制成,容易磨损,使用时间长了,容易导致水垢附着沉积,从而造成密封效果不好而且缩短使用寿命。
发明内容
针对上述问题,本发明提出了一种耐磨损不结垢暖气阀芯及其制备方法。
本发明所述的耐磨损不结垢暖气阀芯,按照重量份计,主要成分为:聚四氟乙烯50-80份,石墨10-30份,碳纤维5-15份。
经过发明人多次试验发现,当聚四氟乙烯70份,石墨20份,碳纤维10份时,其使用效果最好。
本发明所述的耐磨损不结垢暖气阀芯的制备方法,其具体步骤为:
(1)将聚四氟乙烯、石墨、碳纤维按照配比混合均匀,加入球形模具中;
(2)将上述原料加热至300-450℃,保温5-10分钟;
(3)保温完毕后,降温至50-150℃,保温5-10分钟;
(4)将上述原料再次升温至350-450℃,保温0.5-2小时,冷却、磨圆得产品。
经过发明人长期摸索试验,发现其最佳的制备工艺为:
(1)将聚四氟乙烯、石墨、碳纤维按照配比混合均匀,加入球形模具中;
(2)将上述原料加热至390℃,保温5分钟;
(3)保温完毕后,降温至100℃,保温5分钟;
(4)将上述原料再次升温至390℃,保温1小时,冷却、磨圆得产品。
综上所述,本发明所述的耐磨损不结垢暖气阀芯以聚四氟乙烯、石墨、碳纤维为原料,避免了使用过程中水垢的附着沉积,机械强度高,耐磨,制备方法简单,可以广泛应用于暖气阀门上。
具体实施方式
下面通过实施例对本发明涉及的技术方案进行进一步描述,但不作为对本发明保护范围的限制。
实施例1
一种耐磨损不结垢暖气阀芯,按照重量份计,该暖气阀芯的主要成分为:聚四氟乙烯70份,石墨20份,碳纤维10份。
其具体步骤为:
(1)将聚四氟乙烯、石墨、碳纤维按照配比混合均匀,加入球形模具中;
(2)将上述原料加热至390℃,保温5分钟;
(3)保温完毕后,降温至100℃,保温5分钟;
(4)将上述原料再次升温至390℃,保温1小时,冷却、磨圆得产品。
实施例2
一种耐磨损不结垢暖气阀芯,按照重量份计,该暖气阀芯的主要成分为:聚四氟乙烯50份,石墨10份,碳纤维5份。
其具体步骤为:
(1)将聚四氟乙烯、石墨、碳纤维按照配比混合均匀,加入球形模具中;
(2)将上述原料加热至300℃,保温5分钟;
(3)保温完毕后,降温至50℃,保温5分钟;
(4)将上述原料再次升温至350℃,保温0.5小时,冷却、磨圆得产品。
实施例3
一种耐磨损不结垢暖气阀芯,按照重量份计,该暖气阀芯的主要成分为:聚四氟乙烯80份,石墨30份,碳纤维15份。
其具体步骤为:
(1)将聚四氟乙烯、石墨、碳纤维按照配比混合均匀,加入球形模具中;
(2)将上述原料加热至450℃,保温10分钟;
(3)保温完毕后,降温至150℃,保温10分钟;
(4)将上述原料再次升温至450℃,保温2小时,冷却、磨圆得产品。
Claims (4)
1.一种耐磨损不结垢暖气阀芯,其特征在于:按照重量份计,该暖气阀芯的主要成分为:聚四氟乙烯50-80份,石墨10-30份,碳纤维5-15份。
2.根据权利要求1所述的一种耐磨损不结垢暖气阀芯,其特征在于:按照重量份计,该暖气阀芯的主要成分为:聚四氟乙烯70份,石墨20份,碳纤维10份。
3.制备权利要求1或2所述的耐磨损不结垢暖气阀芯的方法,其特征在于:其具体步骤为:
(1)将聚四氟乙烯、石墨、碳纤维按照配比混合均匀,加入球形模具中;
(2)将上述原料加热至300-450℃,保温5-10分钟;
(3)保温完毕后,降温至50-150℃,保温5-10分钟;
(4)将上述原料再次升温至350-450℃,保温0.5-2小时,冷却、磨圆得产品。
4.根据权利要求3所述的耐磨损不结垢暖气阀芯的制备方法,其特征在于:其具体步骤为:
(1)将聚四氟乙烯、石墨、碳纤维按照配比混合均匀,加入球形模具中;
(2)将上述原料加热至390℃,保温5分钟;
(3)保温完毕后,降温至100℃,保温5分钟;
(4)将上述原料再次升温至390℃,保温1小时,冷却、磨圆得产品。