CN102660757B - 铝电解用惰性阳极材料或惰性阴极涂层材料的制备工艺 - Google Patents

铝电解用惰性阳极材料或惰性阴极涂层材料的制备工艺 Download PDF

Info

Publication number
CN102660757B
CN102660757B CN201210161985.7A CN201210161985A CN102660757B CN 102660757 B CN102660757 B CN 102660757B CN 201210161985 A CN201210161985 A CN 201210161985A CN 102660757 B CN102660757 B CN 102660757B
Authority
CN
China
Prior art keywords
inert
anode material
titanium boride
inert anode
preparation technology
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN201210161985.7A
Other languages
English (en)
Other versions
CN102660757A (zh
Inventor
陈学敏
杨军
李志红
伍卫平
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Shenzhen Sunxing Light Alloy Materials Co Ltd
Original Assignee
Shenzhen Sunxing Light Alloy Materials Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Shenzhen Sunxing Light Alloy Materials Co Ltd filed Critical Shenzhen Sunxing Light Alloy Materials Co Ltd
Priority to CN201210161985.7A priority Critical patent/CN102660757B/zh
Priority to PCT/CN2012/078380 priority patent/WO2013174067A1/zh
Publication of CN102660757A publication Critical patent/CN102660757A/zh
Priority to EP12195421.8A priority patent/EP2666887B1/en
Priority to ES12195421.8T priority patent/ES2534969T3/es
Priority to US13/709,029 priority patent/US20130115370A1/en
Application granted granted Critical
Publication of CN102660757B publication Critical patent/CN102660757B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明提供一种铝电解用惰性阳极材料或惰性阴极涂层材料的制备工艺，包括如下步骤：A）将铝放入反应器中，抽真空后通入惰性气体，往反应器中加入干燥的氟硼酸盐和氟钛酸盐混合物，反应生成硼化钛和冰晶石，分离得到硼化钛；B）将得到的硼化钛与碳素材料熔融，捣固到碳素阴极表面，经烧结后形成铝电解用惰性阴极涂层材料；或将得到的硼化钛与碳素材料混合均匀后，高压成型，经高温烧结后形成铝电解用惰性阳极材料。本发明具有制备工艺简单，无需苛刻反应条件，且反应产物得率高，用于铝电解用惰性阳极材料或惰性阴极涂层材料的制备，具有良好的抗腐蚀性能、优良的导电性能以及抗热冲击性能，其牢固度也能满足工业使用要求。

Description

铝电解用惰性阳极材料或惰性阴极涂层材料的制备工艺
技术领域
本发明涉及铝电解用惰性阳极材料或惰性阴极涂层材料的制备工艺。
背景技术
目前铝电解工业仍采用传统的Hall-Heroult法，电解质一直以冰晶石-氧化铝为基本体系，现行的预焙阳极电解槽主要采用碳素阳极和碳素阴极，碳素阳极在电解过程中被析出的氧不断消耗，转变成一氧化碳及二氧化碳排入大气中，碳素阴极对铝液不润湿，且会受到冰晶石的长期腐蚀。为延长电解槽的使用寿命，降低对大气的碳排放量，并且降低电解温度，提高电解效率，往往需要制备廉价并可以大规模工业化生产的惰性阳极材料或者制备可用于碳素阴极表面涂覆的惰性阴极材料。
现有的硼化钛工业生产方法主要包括以下三种：
（1）金属钛和单质硼在高温下直接反应：Ti+2B=TiB2；
（2）碳化硼法：二氧化钛和碳化硼在C存在下，在碳管内直接反应：
  2TiO2+B4C+3C=2TiB2 +4CO ，如果碳管内为H2气氛，反应温度为1800~1900℃；如果碳管为真空，则反应温度可以降至1650~1750℃；
 （3）气相沉积法：以TiCl4和 BCl3为原料，在H2参与下，进行如下反应：
   TiCl4+BCl3+5H2=TiB2+10HCl ；沉积温度为8000-1000℃，可以制得磨料级和电子级产品。
硼化钛对铝液具有良好的润湿性，且耐冰晶石的腐蚀，但现有的硼化钛工业生产方法存在反应条件苛刻，反应的得率不高（低于90%），综合制备成本高的缺点。由于硼化钛价格昂贵，目前难以实现硼化钛在惰性阳极材料和惰性阴极材料制备过程中的广泛应用。
发明内容
为解决现有技术中存在的技术问题，发明人在硼化钛的制备及其应用方面进行了大量的探索，预料不到地发现，以氟硼酸盐和氟钛酸盐的混合物为原料，无需苛刻反应条件即可制备硼化钛，且反应产物得率高，反应产物用于铝电解用惰性阳极材料或惰性阴极涂层材料的制备，具有很好的牢固度。
本发明提供一种铝电解用惰性阳极材料或惰性阴极涂层材料的制备工艺，包括如下步骤：
A） 将铝放入反应器中，抽真空后通入惰性气体，升温至700~800℃，往反应器中加入干燥的氟硼酸盐和氟钛酸盐混合物，快速搅拌，反应4~6h，生成硼化钛和冰晶石，分离得到硼化钛； 
B） 将得到的硼化钛与碳素材料熔融，捣固到碳素阴极表面，经烧结后形成铝电解用惰性阴极涂层材料；或将得到的硼化钛与碳素材料混合均匀后，高压成型，经高温烧结后形成铝电解用惰性阳极材料。
采用上述技术方案，本发明提供的铝电解用惰性阳极材料或惰性阴极涂层材料的制备工艺简单，无需苛刻反应条件，中间产物硼化钛的制备周期短且具有得率高、比表面积大、接触角多和铝含量可控等优点，用于铝电解用惰性阳极材料的制备或惰性阴极涂层材料的制备，具有很好的牢固度，对铝液具有良好的润湿性，抗冰晶石的腐蚀能力强，可延长电解槽的使用寿命，铝电解过程的综合生产成本更低。
作为本发明的进一步改进，所述氟硼酸盐采用氟硼酸钾；所述氟钛酸盐采用氟钛酸钾。涉及的化学反应式为：                                                。
作为本发明的进一步改进，所述氟硼酸盐采用氟硼酸钠；所述氟钛酸盐采用氟钛酸钠。涉及的化学反应式为：。
作为本发明的进一步改进，所述惰性气体采用氩气。
作为本发明的进一步改进，所述碳素材料选自碳、石墨和沥青、树脂中的一种或多种。
与现有技术相比，本发明的有益效果是：本发明提供的铝电解用惰性阳极材料或惰性阴极涂层材料的制备工艺简单，无需苛刻反应条件，中间产物硼化钛的制备周期短且具有得率高、比表面积大、接触角多和铝含量可控等优点，用于铝电解用惰性阳极材料的制备或惰性阴极涂层材料的制备，具有很好的牢固度，对铝液具有良好的润湿性，抗冰晶石的腐蚀能力强，可延长电解槽的使用寿命，铝电解过程的综合生产成本更低。
具体实施方式
下面通过具体实施例对本发明做进一步详细说明。
实施例一
称取2吨铝置于反应器中，抽真空后通入氩气保护，升温至750℃，按反应比例往反应器中加入干燥的氟硼酸钾和氟钛酸钾的混合物，快速搅拌，反应5h，生成硼化钛和冰晶石，经现有的常规分离方法分离后得到硼化钛，干燥后称重为1.52吨，反应产物得率达到97%以上。 
将得到的硼化钛与树脂以90：（1~10）的重量比混后，经高压烧结，可制成惰性阳极材料；将得到的硼化钛与树脂以90：（1~10）的重量比混后，经熔融后捣固到碳素阴极表面，经烧结后形成惰性阴极涂层材料。
实施例二
称取2吨铝置于反应器中，抽真空后通入氩气保护，升温至750℃，按反应比例往反应器中加入干燥的氟硼酸钠和氟钛酸钠的混合物，快速搅拌，反应5h，生成硼化钛和冰晶石，经现有的常规分离方法分离后得到硼化钛，干燥后称重为1.53吨，反应产物得率达到97%以上。 
将得到的硼化钛与树脂按99：1的重量比混后，经高压烧结，可制成惰性阳极材料；将得到的硼化钛与树脂按99：1的重量比混后，经熔融后捣固到碳素阴极表面，经烧结后形成惰性阴极涂层材料。
以上内容是结合具体的优选实施方式对本发明所作的进一步详细说明，不能认定本发明的具体实施只局限于这些说明。对于本发明所属技术领域的普通技术人员来说，在不脱离本发明构思的前提下，还可以做出若干简单推演或替换，都应当视为属于本发明的保护范围。 

Claims (5)

1.一种铝电解用惰性阳极材料或惰性阴极涂层材料的制备工艺，其特征在于：包括如下步骤：
将铝放入反应器中，抽真空后通入惰性气体，升温至700~800℃，往反应器中加入干燥的氟硼酸盐和氟钛酸盐混合物，快速搅拌，反应4~6h，生成硼化钛和冰晶石，分离得到硼化钛； 
将得到的硼化钛与碳素材料或沥青或树脂熔融，捣固到碳素阴极表面，经烧结后形成铝电解用惰性阴极涂层材料；或将得到的硼化钛与碳素材料或沥青或树脂混合均匀后，高压成型，经高温烧结后形成铝电解用惰性阳极材料。
2.根据权利要求1所述的铝电解用惰性阳极材料或惰性阴极涂层材料的制备工艺，其特征在于：所述氟硼酸盐采用氟硼酸钾；所述氟钛酸盐采用氟钛酸钾。
3.根据权利要求1所述的铝电解用惰性阳极材料或惰性阴极涂层材料的制备工艺，其特征在于：所述氟硼酸盐采用氟硼酸钠；所述氟钛酸盐采用氟钛酸钠。
4.根据权利要求1所述的铝电解用惰性阳极材料或惰性阴极涂层材料的制备工艺，其特征在于：所述惰性气体采用氩气。
5.根据权利要求1至4中任一项所述的铝电解用惰性阳极材料或惰性阴极涂层材料的制备工艺，其特征在于：所述碳素材料选自碳、石墨中的一种或两种。
CN201210161985.7A 2012-05-23 2012-05-23 铝电解用惰性阳极材料或惰性阴极涂层材料的制备工艺 Active CN102660757B (zh)