CN102660177A - 一种聚苯乙烯改性耐高温防腐涂料 - Google Patents
一种聚苯乙烯改性耐高温防腐涂料 Download PDFInfo
- Publication number
- CN102660177A CN102660177A CN2012101571398A CN201210157139A CN102660177A CN 102660177 A CN102660177 A CN 102660177A CN 2012101571398 A CN2012101571398 A CN 2012101571398A CN 201210157139 A CN201210157139 A CN 201210157139A CN 102660177 A CN102660177 A CN 102660177A
- Authority
- CN
- China
- Prior art keywords
- parts
- modified
- high temperature
- mixed solvent
- calcium carbonate
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种聚苯乙烯改性耐高温防腐涂料,原料及其质量分数为:PS泡沫塑料,11.5份;混合溶剂,37.4份,混合溶剂为二甲苯质量∶丁酯质量=7∶3的混合溶剂;改性醇酸树脂,3份;有机硅共聚物,8份;邻苯二甲酸二丁酯,0.75份;铝银浆,2.75份;氧化铁红,25份;硫酸钡,3.8份;轻钙,4.8份;膨润土,3份;本发明产品以改性醇酸树脂和有机硅共聚物加以改性,使该产品具有优良的柔韧性和附着力,耐高温性加之原有耐防腐性,使该产品能广泛适应于电厂、化工的各类设备、管道等金属结构的防腐。
Description
技术领域
本发明涉及化工技术领域,尤其涉及的是一种聚苯乙烯改性耐高温防腐涂料。
背景技术
聚苯乙烯作为化工行业产品,具有价廉、容易着色,透明吸湿性低,耐化学介质腐蚀,广泛应用于电子器工业、化学工业以及日用产品,但聚苯乙烯质硬、性脆作为涂料用基料聚苯乙烯存在着柔韧性和附着力差等缺陷,虽有以聚苯乙烯为基料的一般改性涂料,但不能作为防腐涂料。
因此,现有技术存在缺陷,需要改进。
发明内容
本发明所要解决的技术问题是针对现有技术的不足提供一种聚苯乙烯改性耐高温防腐涂料。
本发明的技术方案如下:
一种聚苯乙烯改性耐高温防腐涂料,原料及其质量分数为:PS泡沫塑料,11.5份;混合溶剂,37.4份,混合溶剂为二甲苯质量∶丁酯质量=7∶3的混合溶剂;改性醇酸树脂,3份;有机硅共聚物,8份;邻苯二甲酸二丁酯,0.75份;铝银浆,2.75份;氧化铁红,25份;硫酸钡,3.8份;轻钙,4.8份;膨润土,3份;将PS泡沫塑料经机械除尘、除杂物和水洗干净,待干燥后,破碎溶于含混合溶剂的反应釜中溶解,再加入有机硅共聚物,升温至75~90℃反应1~1.5h,即得改性PS清漆,即基料,基料中加入改性醇酸树脂,升温至100℃搅拌30分钟,然后将该基料通过泵送入另一配料罐中中,加入邻苯二甲酸二丁酯,再加入填料:轻钙、氧化铁红、膨润土、硫酸钡,充分搅匀,经砂磨机研磨后再加入铝银浆,高速搅拌30分钟,过筛,即为成品。
所述的聚苯乙烯改性耐高温防腐涂料,所述氧化铁红、所述硫酸钡、轻钙、膨润土均为320目。
本发明产品以改性醇酸树脂和有机硅共聚物加以改性,使该产品具有优良的柔韧性和附着力,耐高温性加之原有耐防腐性,使该产品能广泛适应于电厂、化工的各类设备、管道等金属结构的防腐。
附图说明
图1为本发明工艺流程图。
具体实施方式
以下结合具体实施例,对本发明进行详细说明。
1、原材料与配方
PS泡沫塑料(回收品),11.5kg;混合溶剂,37.4kg,混合溶剂为二甲苯质量∶丁酯质量=7∶3的混合溶剂;改性醇酸树脂,3kg;有机硅共聚物,8kg;邻苯二甲酸二丁酯,0.75kg;铝银浆,2.75kg;氧化铁红(320目),25kg;硫酸钡(320目),3.8kg;轻钙(320目),4.8kg;膨润土(320目),3kg。
2、工艺流程
按照上述重量比,将回收的废旧PS(聚苯乙烯)泡沫塑料经机械除尘、除杂物和水洗干净,待干燥后,破碎溶于含混合溶剂的反应釜中溶解,再加入有机硅共聚物,升温至75~90℃反应1~1.5h,即得改性PS清漆,即基料,基料中加入改性醇酸树脂,升温至100℃搅拌30分钟,然后将该基料通过泵送入另一配料罐中中,加入邻苯二甲酸二丁酯,再加入填料:轻钙、氧化铁红、膨润土、硫酸钡,充分搅匀,经砂磨机研磨后再加入铝银浆,高速搅拌30分钟,过80目筛,即为成品。
本产品保护性能良好,可适用于300℃左右的金属耐热保护,在此工作温度下,漆膜具有一定的抵抗酸、碱、盐及其它化学介质侵蚀的能力。干燥快、硬度强、附着力强、机械性能好。与底材配套性能好,三防性能超群。用于各种工件的防腐涂装、电厂、污水厂、交通、市政、油田、化工厂、油罐、网架、化工设备等钢铁金属表面及混凝土表面防腐蚀打底。输油管道、热力管线、锅炉、热风机、火电厂钢结构、冶金机械等表面耐热防腐保护。
表1本发明产品理化指标:
本发明产品施工及注意事项:
1、理论用量:150~200g/m2
2、建议涂装道数:涂装二道,干膜厚度65±5mm
3、复涂间隔:温度25℃,最短1h,最长24h
4、配套用漆:
BZ04-70聚氨酯中间漆
S06-16金属底漆H06-2环氧酯底漆J06-2聚苯乙烯防腐底漆
5、表面处理:
工件除油、除锈、刮腻子、打磨干净,避免基面有灰尘及酸、碱或水分凝结。
6、涂装方法:
空气喷涂:稀释剂:XLZ聚苯乙烯稀释剂
喷嘴口径:1.5~2.5mm空气压力:0.3~0.5MPa
滚涂/刷涂:稀释剂:XLZ聚苯乙烯稀释剂
应当理解的是,对本领域普通技术人员来说,可以根据上述说明加以改进或变换,而所有这些改进和变换都应属于本发明所附权利要求的保护范围。
Claims (2)
1.一种聚苯乙烯改性耐高温防腐涂料,其特征在于,原料及其质量分数为:PS泡沫塑料,11.5份;混合溶剂,37.4份,混合溶剂为二甲苯质量∶丁酯质量=7∶3的混合溶剂;改性醇酸树脂,3份;有机硅共聚物,8份;邻苯二甲酸二丁酯,0.75份;铝银浆,2.75份;氧化铁红,25份;硫酸钡,3.8份;轻钙,4.8份;膨润土,3份;将PS泡沫塑料经机械除尘、除杂物和水洗干净,待干燥后,破碎溶于含混合溶剂的反应釜中溶解,再加入有机硅共聚物,升温至75~90℃反应1~1.5h,即得改性PS清漆,即基料,基料中加入改性醇酸树脂,升温至100℃搅拌30分钟,然后将该基料通过泵送入另一配料罐中中,加入邻苯二甲酸二丁酯,再加入填料:轻钙、氧化铁红、膨润土、硫酸钡,充分搅匀,经砂磨机研磨后再加入铝银浆,高速搅拌30分钟,过筛,即为成品。
2.根据权利要求1所述的聚苯乙烯改性耐高温防腐涂料,其特征在于,所述氧化铁红、所述硫酸钡、轻钙、膨润土均为320目。