CN102644079B - 镁合金上镍磷合金镀层退除溶液 - Google Patents
镁合金上镍磷合金镀层退除溶液 Download PDFInfo
- Publication number
- CN102644079B CN102644079B CN 201210135803 CN201210135803A CN102644079B CN 102644079 B CN102644079 B CN 102644079B CN 201210135803 CN201210135803 CN 201210135803 CN 201210135803 A CN201210135803 A CN 201210135803A CN 102644079 B CN102644079 B CN 102644079B
- Authority
- CN
- China
- Prior art keywords
- content
- magnesium alloy
- nickel
- solution
- stripping
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
本发明涉及一种镁合金上镍磷合金镀层退除溶液,其是由硝酸、氢氟酸、溴代十六烷基吡啶、烯丙基硫脲、植酸盐组成的水溶液,其中,68%硝酸的含量为200-400ml/L,40%氢氟酸的含量为200-420ml/L,溴代十六烷基吡啶含量为5-20mg/L,烯丙基硫脲含量为5-15mg/L、植酸盐含量为5-15mg/L。室温下,将镁合金零件放入所述退除溶液中,退除时间10秒至3分钟。可有效退除镁合金零部件上化学镀镍磷层。退除后的基体均匀,不腐蚀损伤基体。本发明组成简单、配方合理,可用于镁合金上化学镀中不合格镍磷合金镀层的多次退除、返修。
Description
技术领域
本发明涉及一种化学退镀溶液,具体地说是一种镁合金上镍磷合金镀层退除溶液。
背景技术
镁合金的密度是铝合金的三分之二,铁的四分之一,是最轻的结构金属材料之一。镁合金还具有切削性好、比强度高、比刚度高、阻尼性好、导热性好等优点,可以替代钢、铝合金、塑料等制件,在汽车、电子、航空航天等领域有广泛的应用前景。
镁是极活泼的金属,标准电势为-2.36V,其耐蚀性极差,因此,镁合金材料使用前必须进行适当的表面处理,以提高其耐蚀性。在诸多的表面处理方法中,在要求表面层具有导电性、导热性、钎焊性的场合,合金表面化学镀镍磷层是一种不可替代的表面处理的方法。目前有许多关于镁合金表面化学镀镍工艺的探讨。然而,对不合格镁合金表面镍磷合金镀层的安全退除,是生产过程中无法回避的环节,目前这方面的研究报道很少。
“电镀与环保” 2001,120(4):6-9 公开的《镁合金基体上镍磷镀层的阳极退除》,采用阳极退镀法退除镍磷镀层,溶液主要成分为氟化氢和氟化钾,其对于平面镀层有效,但很难将凹槽、孔等特殊部位退除干净。“电镀与涂饰” 2005,24(7):33-34公开的《镁合金基体上镍磷镀层的退除》,采用HF + HNO3退除化学镍磷镀层,退镀时间要求严格,退镀时间在几秒,否则有可能造成镁基体的过腐蚀。中国专利申请CN102230177公开了一种镁合金退镀溶液及其退镀方法,该镁合金退镀溶液包含硝酸、氢氟酸和柠檬酸铵。退镀方法采用4步处理。但是,上述退镀溶液及其退镀方法不同程度上存在退除不净、操作步骤复杂、过腐蚀等问题,多次退镀效果差,难以满足实际需求。
发明内容
本发明所要解决的技术问题是克服上述现有技术的不足,提供一种配方合理,工艺过程简单,容易控制,可有效退除复杂形状的镁合金零部件上的镍磷合金镀层,退除后的基体均匀,不会腐蚀损伤基体的镁合金上镍磷合金镀层退除溶液。
本发明解决上述技术问题采用的技术方案是:一种镁合金上镍磷合金镀层退除溶液,其特征是:其是由硝酸、氢氟酸、溴代十六烷基吡啶、烯丙基硫脲、植酸盐组成的水溶液,其中,68%硝酸的含量为200-400ml/L,40%氢氟酸的含量为200-420ml/L, 溴代十六烷基吡啶含量为5-20mg/L,烯丙基硫脲含量为5-15mg/L 、植酸盐含量为5-15mg/L 。
本发明优选的溶液配方是:68%硝酸的含量为300ml/L,40%氢氟酸的含量为400ml /L, 溴代十六烷基吡啶含量为20mg/L,烯丙基硫脲含量为10mg/L 、植酸盐含量为10mg/L。
本发明退除溶液采用硝酸、氢氟酸、溴代十六烷基吡啶、烯丙基硫脲、植酸盐组成的水溶液,使用时,在室温下,可将化学镀有镍磷合金镀层的镁合金零件直接放入本发明所述溶液中,退除时间10秒至3分钟。可有效退除镁合金零部件上化学镀镍磷合金镀层,特别是对复杂形状的镁合金零部件上镍磷合金镀层有很好的退除效果。退除后的基体均匀,溶液不腐蚀损伤基体。对照现有技术,本发明组成简单、配方合理,可有效退除化学镀镍磷层。本发明退除溶液具有操作简单、容易控制、成本低等优点,退除溶液可以循环使用。可用于镁合金上化学镀中不合格镍磷合金镀层的多次退除、返修。本发明也适用于镁合金上电镀中不合格镍镀层的退除和返修。
具体实施方式
下面结合实施例对本发明做进一步说明。
本发明一种镁合金上镍磷合金镀层退除溶液,其特征是:其是由硝酸、氢氟酸、溴代十六烷基吡啶、烯丙基硫脲、植酸盐组成的水溶液,其中,68%硝酸的含量为200-400ml/L,40%氢氟酸的含量为200-420ml/L, 溴代十六烷基吡啶含量为5-20mg/L,烯丙基硫脲含量为5-15mg/L 、植酸盐含量为5-15mg/L 。
本发明所述硝酸、氢氟酸是退除溶液的主要成分。溶液中硝酸的作用是退除镍磷合金镀层,氢氟酸的作用是辅助硝酸退除镍磷合金镀层,并与镁基体生成氟化镁钝化膜。本发明经过大量的实验优化筛选出溴代十六烷基吡啶、烯丙基硫脲和植酸盐作为缓蚀剂,它们有效地形成复配协同作用,在镁合金基体表面活性点处,形成薄而均匀的吸附层,从而避免了活性点过腐蚀的发生。对镁合金基体具有很好的缓蚀作用,可以有效地延长镁合金在退镀液中的搁置时间,退镀后基体平整,能够保证镁合金零件多次退镀和施镀的质量。特别是加入添加剂烯丙基硫脲后,基本上无黄烟析出,消除了黄烟对人体的伤害,其有效含量为5-15mg/L。
本发明优选的溶液配方是:68%硝酸的含量为300ml/L,40%氢氟酸的含量为400ml /L, 溴代十六烷基吡啶含量为20mg/L,烯丙基硫脲含量为10mg/L、植酸盐含量为10mg/L。
本发明使用时,按比例配置溶液,将镀有镍磷合金镀层的镁合金零件放入所述镁合金退除溶液中,温度为室温,退除时间10秒至3分钟。本发明退除时间最长可达3分钟,镁合金不会发生腐蚀,这样非常有利于退镀操作。本发明可有效退除镁合金零部件上化学镀镍磷合金镀层,特别是对复杂形状的镁合金零部件上镍磷合金镀层有很好的退除效果。退除后的基体均匀,溶液不腐蚀损伤基体,退除溶液可以循环使用。退镀后的镁合金基体水洗后,再进行除膜处理,继续下一次化学镀。
实施例1:一种镁合金上镍磷合金镀层退除溶液,其是由硝酸、氢氟酸、溴代十六烷基吡啶、烯丙基硫脲、植酸盐组成的水溶液,其中,68%硝酸的含量为300ml/L,40%氢氟酸的含量为400ml/L, 溴代十六烷基吡啶含量为20mg/L,烯丙基硫脲含量为10mg/L 、植酸钾含量为10 mg/L。使用时,在室温下,将镀有镍磷合金镀层的镁合金零件放入上述退除溶液中,退除时间可达1-3分钟;其可有效退除镁合金零部件上镀镍层及化学镀镍磷层,特别是对复杂形状的镁合金零部件上镀镍层及化学镀镍磷层有很好的退除效果。退除后的基体均匀,退除溶液不腐蚀损伤基体。
实施例2:一种镁合金上镍磷合金镀层退除溶液,其是由硝酸、氢氟酸、溴代十六烷基吡啶、烯丙基硫脲、植酸盐组成的水溶液,其中,68%硝酸的含量为200ml/L,40%氢氟酸的含量为420ml/L, 溴代十六烷基吡啶含量为5mg/L,烯丙基硫脲含量为15mg/L、植酸钠含量为10mg/L 。使用时,在室温下,将镀有镍磷合金镀层的镁合金零件放入上述退除溶液中,退除时间30秒;其可有效退除镁合金零部件上镀镍层及化学镀镍磷层。退除后的基体均匀,不腐蚀损伤基体。
实施例3:一种镁合金上镍磷合金镀层退除溶液,其特征是:其是由硝酸、氢氟酸、溴代十六烷基吡啶、烯丙基硫脲、植酸盐组成的水溶液,其中,68%硝酸的含量为400ml/L,40%氢氟酸的含量为200ml/L, 溴代十六烷基吡啶含量为15mg/L,烯丙基硫脲含量为5 mg/L 、植酸钾含量为5mg/L 。使用时,在室温下,将镀有镍磷合金镀层的镁合金零件放入上述退除溶液中,退除时间10秒至1分钟,其可有效退除镁合金零部件上镀镍层及化学镀镍磷层,特别是对复杂形状的镁合金零部件上镀镍层及化学镀镍磷层有很好的退除效果。
实施例4:一种镁合金上镍磷合金镀层退除溶液,其特征是:其是由硝酸、氢氟酸、溴代十六烷基吡啶、烯丙基硫脲、植酸盐组成的水溶液,其中,68%硝酸的含量为280ml/L,40%氢氟酸的含量为320ml/L, 溴代十六烷基吡啶含量为18mg/L,烯丙基硫脲含量为12 mg/L 、植酸钠含量为15mg/L 。使用时,在室温下,将镀有镍磷合金镀层的镁合金零件放入上述退除溶液中,退除时间10秒至3分钟,其可有效退除镁合金零部件上镀镍层及化学镀镍磷层。
Claims (1)
1.一种镁合金上镍磷合金镀层退除溶液,其特征是:其是由硝酸、氢氟酸、溴代十六烷基吡啶、烯丙基硫脲、植酸钾组成的水溶液,其中,68%硝酸的含量为400ml/L,40%氢氟酸的含量为200ml/L,溴代十六烷基吡啶含量为15mg/L,烯丙基硫脲含量为5 mg/L,植酸钾含量为5mg/L。