CN102634204A - 一种耐寒的尼龙复合材料 - Google Patents

一种耐寒的尼龙复合材料 Download PDF

Info

Publication number
CN102634204A
CN102634204A CN2012101283348A CN201210128334A CN102634204A CN 102634204 A CN102634204 A CN 102634204A CN 2012101283348 A CN2012101283348 A CN 2012101283348A CN 201210128334 A CN201210128334 A CN 201210128334A CN 102634204 A CN102634204 A CN 102634204A
Authority
CN
China
Prior art keywords
cold
parts
nylon composite
resistant
composite materials
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN2012101283348A
Other languages
English (en)
Inventor
叶法冬
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
CHANGSHU CITY FADONG PLASTIC INDUSTRY Co Ltd
Original Assignee
CHANGSHU CITY FADONG PLASTIC INDUSTRY Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by CHANGSHU CITY FADONG PLASTIC INDUSTRY Co Ltd filed Critical CHANGSHU CITY FADONG PLASTIC INDUSTRY Co Ltd
Priority to CN2012101283348A priority Critical patent/CN102634204A/zh
Publication of CN102634204A publication Critical patent/CN102634204A/zh
Pending legal-status Critical Current

Abstract

一种耐寒的尼龙复合材料，属于高分子材料技术领域。其是由以下重量份数的原料组成：尼龙 610 树脂 20 ～ 25 份；尼龙 6 树脂 7.5 ～ 13 份；耐寒剂 8 ～ 12 份；偶联剂 0.2 ～ 0.6 份；填料 8 ～ 15 份；抗氧剂 0.2 ～ 0.6 份；短切玻璃纤维 13 ～ 17 份；表面改性剂 0.1 ～ 0.4 份。优点：拉伸强度大于 150MPa ，弯曲强度大于 182MPa, 悬臂梁缺口冲击强度大于 34kj/m 2 , 熔融指数大于 22g/10min, 耐零下 40 ℃低温。

Description

一种耐寒的尼龙复合材料
技术领域
本发明属于高分子材料技术领域，具体涉及一种耐寒的尼龙复合材料。
背景技术
作为一种材料和/或制品，需要适应环境变化，但是大多数尼龙材料存在脆性，即遇到低温后发脆，容易损坏。这主要由于尼龙树脂的结晶倾向高，玻璃花转变温度高所致。因此，开发得以避免在低温下发脆的尼龙材料具有积极意义。
发明内容
本发明的任务在于提供一种有助于保障优异的机械物理性能、有益于提高耐低温效果而藉以避免发脆的耐寒的尼龙复合材料。
本发明的任务是这样来完成的，一种耐寒的尼龙复合材料，其是由以下重量份数的原料组成：
尼龙610树脂20～25份；
尼龙6树脂7.5～13份；
耐寒剂8～12份；
偶联剂0.2～0.6份；
填料8～15份；
抗氧剂0.2～0.6份；
短切玻璃纤维13～17份；
表面改性剂0.1～0.4份。
在本发明的一个具体的实施例中，所述的尼龙610树脂是指熔点在230℃的树脂。
在本发明的另一个具体的实施例中，所述的尼龙6树脂是指熔点为220℃的树脂。
在本发明的又一个具体的实施例中，所述的耐寒剂是指丙烯酸甲酯-丁二烯-苯乙烯共聚物。
在本发明的再一个具体的实施例中，所述的偶联剂是指乙烯基三(β甲氧乙氧基)硅烷。
在本发明的还有一个具体的实施例中，所述的填料是指经过活化处理的陶土。
在本发明的更而一个具体的实施例中，所述的抗氧剂是指四[甲基-β-(3，5-二叔丁基-4-羟基苯基)丙酸酯]季戊四醇酯。
在本发明的进而一个具体的实施例中，所述的短切玻璃纤维是指长度为2mm mm的无碱短切玻璃纤维。
在本发明的又更而一个具体的实施例中，所述的表面改性剂是指芥酸酰胺。
本发明提供的耐寒的尼龙复合材料经测试具有如下优异的性能：拉伸强度大于150MPa，弯曲强度大于182MPa，悬臂梁缺口冲击强度大于34kj/m2，熔融指数大于22g/10min，耐零下40℃低温。
具体实施方式
实施例1：
按重量份数取：尼龙610树脂(熔点在230℃)20.2份、尼龙6树脂(熔点在220℃)7.5份、耐寒剂即丙烯酸甲酯-丁二烯-苯乙烯共聚物8.3份、偶联剂即乙烯基三(β甲氧乙氧基)硅烷0.2份、填料即经过活化处理的陶土8.1份、抗氧剂即四[甲基-β-(3，5-二叔丁基-4-羟基苯基)丙酸酯]季戊四醇酯0.2份、长度为2mmmm的无碱短切玻璃纤维13.3份和表面改性剂即芥酸酰胺0.1份。
实施例2：
按重量份数取：尼龙610树脂(熔点在230℃)22.5份、尼龙6树脂(熔点在220℃)9.6份、耐寒剂即丙烯酸甲酯-丁二烯-苯乙烯共聚物10.8份、偶联剂即乙烯基三(β甲氧乙氧基)硅烷0.4份、填料即经过活化处理的陶土10.6份、抗氧剂即四[甲基-β-(3，5-二叔丁基-4-羟基苯基)丙酸酯]季戊四醇酯0.3份、长度为2mmmm的无碱短切玻璃纤维15.4份和表面改性剂即芥酸酰胺0.2份。
实施例3：
按重量份数取：尼龙610树脂(熔点在230℃)24.1份、尼龙6树脂(熔点在220℃)11.7份、耐寒剂即丙烯酸甲酯-丁二烯-苯乙烯共聚物10.1份、偶联剂即乙烯基三(β甲氧乙氧基)硅烷0.5份、填料即经过活化处理的陶土13.8份、抗氧剂即四[甲基-β-(3，5-二叔丁基-4-羟基苯基)丙酸酯]季戊四醇酯0.5份、长度为2mmmm的无碱短切玻璃纤维16.2份和表面改性剂即芥酸酰胺0.4份。
实施例4：
按重量份数取：尼龙610树脂(熔点在230℃)24.8份、尼龙6树脂(熔点在220℃)12.9份、耐寒剂即丙烯酸甲酯-丁二烯-苯乙烯共聚物12份、偶联剂即乙烯基三(β甲氧乙氧基)硅烷0.6份、填料即经过活化处理的陶土14.7份、抗氧剂即四[甲基-β-(3，5-二叔丁基-4-羟基苯基)丙酸酯]季戊四醇酯0.6份、长度为2mmmm的无碱短切玻璃纤维17份和表面改性剂即芥酸酰胺0.3份。
由上述实施例1至4得到的耐寒的尼龙复合材料具有下表所示的技术效果。
Figure BDA0000158148310000031

Claims (9)

1.一种耐寒的尼龙复合材料，其特征在于其是由以下重量份数的原料组成：
尼龙610树脂  20～25份；
尼龙6树脂      7.5～13份；
耐寒剂              8～12份；
偶联剂              0.2～0.6份；
填料            8～15份；
抗氧剂              0.2～0.6份；
短切玻璃纤维  13～17份；
表面改性剂      0.1～0.4份。
2.根据权利要求1所述的一种耐寒的尼龙复合材料，其特征在于所述的尼龙610树脂是指熔点在230℃的树脂。
3.根据权利要求1所述的一种耐寒的尼龙复合材料，其特征在于所述的尼龙6树脂是指熔点为220℃的树脂。
4.根据权利要求1所述的一种耐寒的尼龙复合材料，其特征在于所述的耐寒剂是指丙烯酸甲酯-丁二烯-苯乙烯共聚物。
5.根据权利要求1所述的一种耐寒的尼龙复合材料，其特征在于所述的偶联剂是指乙烯基三（β甲氧乙氧基）硅烷。
6.根据权利要求1所述的一种耐寒的尼龙复合材料，其特征在于所述的填料是指经过活化处理的陶土。
7.根据权利要求1所述的一种耐寒的尼龙复合材料，其特征在于所述的抗氧剂是指四[甲基-β-（3，5-二叔丁基-4-羟基苯基）丙酸酯]季戊四醇酯。
8.根据权利要求1所述的一种耐寒的尼龙复合材料，其特征在于所述的短切玻璃纤维是指长度为2㎜㎜的无碱短切玻璃纤维。
9.根据权利要求1所述的一种耐寒的尼龙复合材料，其特征在于所述的表面改性剂是指芥酸酰胺。
CN2012101283348A 2012-04-27 2012-04-27 一种耐寒的尼龙复合材料 Pending CN102634204A (zh)