CN102618134A - Water-based glass heat insulation paint - Google Patents
Water-based glass heat insulation paint Download PDFInfo
- Publication number
- CN102618134A CN102618134A CN201210102463XA CN201210102463A CN102618134A CN 102618134 A CN102618134 A CN 102618134A CN 201210102463X A CN201210102463X A CN 201210102463XA CN 201210102463 A CN201210102463 A CN 201210102463A CN 102618134 A CN102618134 A CN 102618134A
- Authority
- CN
- China
- Prior art keywords
- heat insulation
- insulation paint
- water
- glass heat
- based glass
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a water-based glass heat insulation paint which contains water-borne acrylic resin so as to have good weather fastness; an adhesion promoter can be used for enhancing the adhesive force of the water-based glass heat insulation paint; and a hardening agent and a scratch-resistant agent can be used for enhancing the scratch resistance of the water-based glass heat insulation paint; therefore, the water-based glass heat insulation paint has good weather fastness as well as stronger adsorptive power and scratch resistance, thus not easily falling off and effectively guaranteeing the heat insulation performance of the heat insulation glass.
Description
Technical field
The present invention relates to a kind of coating, particularly a kind of aqueous glass heat insulation paint.
Background technology
Its staple of transparent heat-insulated thermal insulation coatings is a tin indium oxide; Transparent heat-insulated thermal insulation coatings is divided into two types of water-based is arranged (inorganic type) and solvent borne (waterproof type) according to different environments for use; Wherein not only light transmission is good for aqueous glass heat insulation paint; And can effectively completely cut off sun heat radiation heat, the general thickness that only needs several microns of brushings just can make indoor/outdoor temperature-difference reach 6 deg.c; Can not reach the effect of " cool in summer and warm in winter " even do not turn on the aircondition yet, can be widely used on automobile, equipment and all kinds of buildings.Though existing aqueous glass heat insulation paint can play good effect of heat insulation, its weathering resistance, tack are relatively poor, are coated in and on glassly are easy to scratch, come off, and then can cause detrimentally affect to the heat-proof quality of heat-protecting glass.
Summary of the invention
To the deficiency of above-mentioned prior art, the technical problem that the present invention will solve provides a kind of good weatherability, strong adhesion, is difficult for the aqueous glass heat insulation paint that scratch breaks away from.
For solving the problems of the technologies described above, the present invention adopts following technical scheme:
A kind of aqueous glass heat insulation paint, it comprises by weight percentage:
Preferably, said water-borne acrylic resin comprises acrylic acid dispersion, modified acroleic acid interpolymer and ACRYLIC EMULSION.
Technique scheme has following beneficial effect: the water-borne acrylic resin in this aqueous glass heat insulation paint can make aqueous glass heat insulation paint have good weathering resistance; Adhesion promoter can strengthen the sticking power of aqueous glass heat insulation paint; Increase the scratch resistance ability that hard agent, scratching resistant can strengthen aqueous glass heat insulation paint; Therefore this aqueous glass heat insulation paint has good weathering resistance, stronger adsorptive power and scratch resistance ability; Difficult drop-off can effectively guarantee the heat-proof quality of heat-protecting glass.
Embodiment
With specific embodiment implementation step of the present invention is described in detail below, in following embodiment, if no special instructions, be mass parts.
Embodiment one
This aqueous glass heat insulation paint comprises by weight percentage:
Above-mentioned water-borne acrylic resin comprises acrylic acid dispersion, modified acroleic acid interpolymer and ACRYLIC EMULSION.
Embodiment two
This aqueous glass heat insulation paint comprises by weight percentage:
Embodiment three
This aqueous glass heat insulation paint, it comprises by weight percentage:
Respectively the glass that scribbles embodiment 3 aqueous glass heat insulation paints and the physicals of common white glass are detected, it is following to detect data:
| Sequence number | Test item | Scribble the glass data of thermal insulating coating | Common white glass |
| 1 | The far infrared rejection rate | 67 | 12 |
| 2 | The ultraviolet isolating rate | 100 | 33 |
| 3 | Transmittance | 70 | 89 |
| 4 | Sticking power | 0 grade | |
| 5 | Ageing-resistant | 750 hours | |
| 6 | Scratch resistance | 1000 grams | |
| 7 | Hardness | 5H | |
| 8 | Water tolerance | 480 hours | No change |
| 9 | 100 ℃ of anti-boiling water | 12 hours | No change |
| 10 | Acid and alkali-resistance | 12 hours | No change |
| 11 | Salt fog resistance | 12 hours | No change |
| 12 | High temperature resistant 120 ℃ | 12 hours | No change |
| 13 | Low temperature resistant-40 ℃ | 48 hours | No change |
| 14 | Anti-solvent | 12 hours | No change |
| 15 | The glass free cutting | Can (glass coating play the limit) |
Describe through last table and can know that the glass of this aqueous glass heat insulation paint has barriering effect preferably to far infrared rays and ultraviolet ray, and the sticking power of aqueous glass heat insulation paint, scratch resistance ability are stronger, difficult drop-off.
Water-borne acrylic resin in this aqueous glass heat insulation paint can make aqueous glass heat insulation paint have good weathering resistance; Adhesion promoter can strengthen the sticking power of aqueous glass heat insulation paint, increases the scratch resistance ability that hard agent, scratching resistant can strengthen aqueous glass heat insulation paint, so this aqueous glass heat insulation paint has good weathering resistance, stronger adsorptive power and scratch resistance ability; Difficult drop-off; Can effectively guarantee to guarantee product of the present invention simultaneously outside the heat insulating function of heat-protecting glass, have practicality more; In permanent work-ing life, product all can not influence the quality of product in secondary processing and transportation.
More than a kind of aqueous glass heat insulation paint that the embodiment of the invention provided has been carried out detailed introduction; For one of ordinary skill in the art, according to the thought of the embodiment of the invention, part all can change on embodiment and range of application; In sum; This description should not be construed as limitation of the present invention, is allly made any change with design philosophy of the present invention, all within protection scope of the present invention.
Claims (2)
1. aqueous glass heat insulation paint is characterized in that it comprises by weight percentage:
。
2. aqueous glass heat insulation paint according to claim 1 is characterized in that: said water-borne acrylic resin comprises acrylic acid dispersion, modified acroleic acid interpolymer and ACRYLIC EMULSION.