CN102604612A - 油气田采封作业浆料及其使用方法 - Google Patents
油气田采封作业浆料及其使用方法 Download PDFInfo
- Publication number
- CN102604612A CN102604612A CN2012100561384A CN201210056138A CN102604612A CN 102604612 A CN102604612 A CN 102604612A CN 2012100561384 A CN2012100561384 A CN 2012100561384A CN 201210056138 A CN201210056138 A CN 201210056138A CN 102604612 A CN102604612 A CN 102604612A
- Authority
- CN
- China
- Prior art keywords
- slurry
- superfine
- gypsum
- silica powder
- fld
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及一种油气田采封作业浆料及其使用方法,原料由超细水泥、超细矿渣、超细硅粉、石膏和粉煤灰构成,将超细水泥、超细矿渣、超细硅粉、石膏和粉煤灰混合均匀,然后在混合后的原料内加水并搅拌均匀即可使用。本发明是一种设计合理、成本低、使用寿命长的油气田采封作业浆料及其使用方法,本浆料具有对孔洞支撑强度大、能填补孔洞内壁缝隙、安全无污染、制作及使用简单方便等诸多优点。
Description
技术领域
本发明涉及油气田领域中的浆料,尤其是一种油气田采封作业浆料及其使用方法。
背景技术
在油气田采封作业中需要使用钻孔机进行打孔,为了避免孔洞塌陷,需要在孔洞内灌注浆料来支撑孔壁。目前比较常用的浆料是采用超细水泥、超细矿渣以及超细硅粉三种原料混合搅拌制成的,该超细水泥、超细矿渣的比表面积为650,超细硅粉的粒径为0.2μm,由于该浆料比较细,在水中为悬浮状态,容易分层,因此现有的这种浆料支撑孔洞的效果不好,使用寿命短。此外,油气会对孔洞内壁产生较大压力,内壁会产生裂缝,现有的这种浆料不能起到填补缝隙的作用。目前已经出现一种有机添加剂,其具有良好的支撑及填补缝隙的作用,但是该有机添加剂具有毒性,其残留在土壤中后会对周围的土壤及水质产生不良影响,破坏生态环境。
发明内容
本发明的目的在于克服现有技术的不足,提供了一种设计合理、制作方便、支撑孔洞效果好、使用安全无毒害的油气田采封作业浆料及其使用方法。
本发明解决其技术问题是通过以下技术方案实现的:
一种油气田采封作业浆料,其特征在于:原料由超细水泥、超细矿渣、超细硅粉、石膏和粉煤灰构成。
而且,所述原料各组分的重量份数为:超细水泥30;超细矿渣30;超细硅粉15;石膏15;粉煤灰10。
而且,所述的石膏和粉煤灰的粒度为25μm。
一种油气田采封作业浆料的使用方法,其特征在于:将超细水泥、超细矿渣、超细硅粉、石膏和粉煤灰混合均匀,然后在混合后的原料内加水并搅拌均匀即可。
而且,所述原料和水的份数比为4∶5。
本发明的优点和有益效果为:
1、本浆料在原有浆料内添加了石膏和粉煤灰,该石膏和粉煤灰起到了缓凝剂和悬浮剂的作用,可以减少浆料的悬浮情况、避免分层现象、提高浆料对孔洞的支撑强度、延长浆料的使用寿命,并起到修补孔壁裂缝的作用。
2、本浆料使用安全无毒,不会对周围的土壤和水质造成污染,符合环保要求,并且本浆料能够达到有机添加剂90%的效果。
3、本浆料的加工流程简单、易于实现,制备过程快捷省力,且使用方法同样简单方便。
4、本发明是一种设计合理、成本低、使用寿命长的油气田采封作业浆料及其使用方法,本浆料具有对孔洞支撑强度大、能填补孔洞内壁缝隙、安全无污染、制作及使用简单方便等诸多优点。
具体实施方式
下面通过具体实施例对本发明作进一步详述,以下实施例只是描述性的,不是限定性的,不能以此限定本发明的保护范围。
一种油气田采封作业浆料,其原料由超细水泥、超细矿渣、超细硅粉、石膏和粉煤灰构成,其各组分的重量份数为:
超细水泥 30;
超细矿渣 30;
超细硅粉 15;
石膏 15;
粉煤灰 10。
其中石膏和粉煤灰的粒度为25μm。
上述油气田采封作业浆料的使用方法是:将超细水泥、超细矿渣、超细硅粉、石膏和粉煤灰混合均匀,然后在混合后的原料内加水并搅拌均匀即可,上述原料和水的份数比为4∶5。
Claims (5)
1.一种油气田采封作业浆料,其特征在于:原料由超细水泥、超细矿渣、超细硅粉、石膏和粉煤灰构成。
2.根据权利要求1所述的油气田采封作业浆料,其特征在于:所述原料各组分的重量份数为:
超细水泥 30;
超细矿渣 30;
超细硅粉 15;
石膏 15;
粉煤灰 10。
3.根据权利要求1所述的油气田采封作业浆料,其特征在于:所述的石膏和粉煤灰的粒度为25μm。
4.一种如权利要求1所述的油气田采封作业浆料的使用方法,其特征在于:将超细水泥、超细矿渣、超细硅粉、石膏和粉煤灰混合均匀,然后在混合后的原料内加水并搅拌均匀即可。
5.根据权利要求4所述的油气田采封作业浆料的使用方法,其特征在于:所述原料和水的份数比为4:5。