CN102603265A - 利用固体废弃物再生制成的砖和方法 - Google Patents
利用固体废弃物再生制成的砖和方法 Download PDFInfo
- Publication number
- CN102603265A CN102603265A CN2012100848929A CN201210084892A CN102603265A CN 102603265 A CN102603265 A CN 102603265A CN 2012100848929 A CN2012100848929 A CN 2012100848929A CN 201210084892 A CN201210084892 A CN 201210084892A CN 102603265 A CN102603265 A CN 102603265A
- Authority
- CN
- China
- Prior art keywords
- brick
- solid waste
- waste regeneration
- machine
- sulfamic acid
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明涉及工业废弃物的再利用方法,主要是利用固体废弃物再生制成砖的方法,其特征在于该砖的配方为用量的重量百分比配制:轻烧镁粉10%~20%,氯化镁4%~8%,有机硅0.1%~0.3%,磷酸三钠0.1%~0.3%,复合改性剂0.1%~0.3%,氨基磺酸高效减水剂0.1%~0.3%,固体废渣75%~85%。本发明以固体废渣为原料,将其经过一系列加工制成砖,可达到一定的硬度,且可通过压砖机制成形状各异的砖形,生产效率高,节能环保,且制造成本低,制造出的砖可广泛用于各个领域,尤其是建筑领域,具有卓越的经济效益和环保价值。
Description
[技术领域]
本发明涉及工业废弃物的再利用方法,主要是利用固体废弃物再生制成砖的方法。
[背景技术]
众所周知,随着科技产业的发达,工业的蓬勃发展,在建造的过程中随之产生的工业垃圾也越来越多。在环保的大课题下,如何化废为宝,将工业垃圾二次利用与工业生产无疑是环保节能的主要手段。固体废弃物包括建筑垃圾、工业矿渣、化学废渣、城市垃圾废弃物等,这些废弃物排入河流或经过焚烧排入大气后均会对环境造成严重的污染破坏,并且在这些废料堆放过程中,也占用了大量的面积。如果能将这些建筑、工业垃圾合理地利用起来,不仅可以有效消纳大量建筑垃圾等多种固体废弃物,有效解决建筑垃圾侵占土地、污染环境等问题,还可以有效解决目前我国生产粘土砖大量毁坏良田土地、大量燃烧造成空气污染等问题,并由此推进建筑墙体材料生产产业结构优化升级,实现该行业生产技术大跨越。因此,如何将这些废料经过加工处理使其成为有用的二次能源,长久以来一直是人们研究探讨的技术难题。
[发明内容]
本发明的目的是解决现有技术中能源浪费,资源利用不足的缺陷,提供节能环保,利用率高的利用固体废弃物再生制成砖的方法。
为实现上述目的,提供利用固体废弃物再生制成的砖,其特征在于该砖的配方为用量的重量百分比配制:
轻烧镁粉10%~20%,
氯化镁(化水)4%~8%,
有机硅(增水剂)0.1%~0.3%,
磷酸三钠0.1%~0.3%,
复合改性剂0.1%~0.3%,
氨基磺酸高效减水剂0.1%~0.3%,
固体废渣75%~85%。
先将上述含量的氯化镁化水后温度至27~29℃,在强力搅拌机或布料机搅拌下加上上述含量的轻烧镁粉、有机硅、磷酸三钠、复合改性剂、氨基磺酸高效减水剂,搅拌十分钟,使其均匀分解后,将配料送入全自动砖机,料斗自动压制成型,成型砖的硬度达到25.2MPa。
该砖应用于建设承重墙或防汛墙或地砖或井盖式车行道路面或港区路面块领域。
本发明以固体废渣为原料,将其经过一系列加工制成砖,可达到一定的硬度,且可通过压砖机制成形状各异的砖形,生产效率高,节能环保,且制造成本低,制造出的砖可广泛用于各个领域,尤其是建筑领域,具有卓越的经济效益和环保价值。
[具体实施方式]
以下结合实施例对本发明作进一步说明。本发明的生产技术对本专业的人来说是容易实施的。
本发明所述该砖的配方为用量的重量百分比配制如下:
轻烧镁粉10%~20%,
氯化镁(化水)4%~8%,
有机硅(增水剂)0.1%~0.3%,
磷酸三钠0.1%~0.3%,
复合改性剂0.1%~0.3%,
氨基磺酸高效减水剂0.1%~0.3%,
固体废渣75%~85%。
本发明所述砖的制造方法包括以下步骤:先将上述含量的氯化镁化水后温度至27~29℃,在强力搅拌机或布料机搅拌下加上上述含量的轻烧镁粉、有机硅、磷酸三钠、复合改性剂、氨基磺酸高效减水剂,搅拌十分钟,使其均匀分解后,将配料送入全自动砖机,料斗自动压制成型,成型砖的硬度达到25.2MPa。本实施例中的压砖机采用的是QTY8-15全自动免烧砖机,可生产出390×190×190mm的砌砖,240×115×90mm的多孔砖,240×115×53mm的标准砖等,在压制过程中只需要换相应的模具即可生产不同规格形状的制品,如各种砌块、铺路砖、草坪砖、装饰砖等。本发明中所述的砖应用于建设承重墙或防汛墙或地砖或井盖式车行道路面或港区路面块领域。固体废弃物,包括建筑垃圾,工业矿渣,金,铜,铁,磷,矿渣,铸造厂废渣,或城市垃圾废弃物,石墨矿渣,大理石粉末,海化企业的碱渣,尾矿渣,粉煤灰,江河泥沙,污水厂污泥等均可作为本发明的填充原料,尤其是粉煤灰,炉渣,钢渣,石墨,矿渣等含有硅酸盐成分,具有良好的改性作用。
Claims (3)
1.利用固体废弃物再生制成的砖,其特征在于该砖的配方为用量的重量百分比配制:
轻烧镁粉10%~20%,
氯化镁4%~8%,
有机硅0.1%~0.3%,
磷酸三钠0.1%~0.3%,
复合改性剂0.1%~0.3%,
氨基磺酸高效减水剂0.1%~0.3%,
固体废渣75%~85%。
2.权1所述的利用固体废弃物再生制成砖的制造方法,其特征在于先将所述含量的氯化镁化水后温度至27~29℃,在强力搅拌机或布料机搅拌下加上所述含量的轻烧镁粉、有机硅、磷酸三钠、复合改性剂、氨基磺酸高效减水剂,搅拌十分钟,使其均匀分解后,将配料送入全自动砖机,料斗自动压制成型,成型砖的硬度达到25.2MPa。
3.如权1所述的利用固体废弃物再生制成砖的方法,其特征在于该砖应用于建设承重墙或防汛墙或地砖或井盖式车行道路面或港区路面块领域。