CN102603213B - 低成本电子级玻璃纤维纱用浸润剂及其生产方法 - Google Patents

低成本电子级玻璃纤维纱用浸润剂及其生产方法 Download PDF

Info

Publication number
CN102603213B
CN102603213B CN201110400105.2A CN201110400105A CN102603213B CN 102603213 B CN102603213 B CN 102603213B CN 201110400105 A CN201110400105 A CN 201110400105A CN 102603213 B CN102603213 B CN 102603213B
Authority
CN
China
Prior art keywords
grade glass
parts
starch slurry
production method
add
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN201110400105.2A
Other languages
English (en)
Other versions
CN102603213A (zh
Inventor
胡元虎
阮翠英
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Jushi Group Co Ltd
Original Assignee
JUSHI PANDENG ELECTRONIC PARENT METAL CO Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by JUSHI PANDENG ELECTRONIC PARENT METAL CO Ltd filed Critical JUSHI PANDENG ELECTRONIC PARENT METAL CO Ltd
Priority to CN201110400105.2A priority Critical patent/CN102603213B/zh
Publication of CN102603213A publication Critical patent/CN102603213A/zh
Application granted granted Critical
Publication of CN102603213B publication Critical patent/CN102603213B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明所设计的一种低成本电子级玻璃纤维纱用浸润剂生产方法，它主要包含93-95份软化水、1.8-2.4份未改性高直链玉米淀粉、1.8-2.4份改性马铃薯淀粉、1.3-1.7份植物油乳液、0.1-0.3份塑化剂和0.2-0.4份阳离子软化剂组成，通过一定制造方法完成。用这种浸润剂所生产的电子级玻璃纤维纱性能优良，管纱毛羽率低，纱线硬挺度均匀，完全满足后续工序使用性能，而且吨纱浸润剂成本低，节约了吨纱生产成本。

Description

低成本电子级玻璃纤维纱用浸润剂及其生产方法
技术领域
本发明涉及一种电子级玻璃纤维纱浸润剂领域，尤其是一种减少电子级玻璃纤维纱浸润剂浪费，降低环境污染而开发的低成本电子级玻璃纤维纱用浸润剂生产方法。
背景技术
现有的浸润剂中，使用常规进口高直链改性玉米淀粉和氢化玉米油。由于一方面，高直链改性玉米淀粉不易于配制过程的蒸煮和糊化，造成浸润剂配制能源浪费；另一方面，使用进口淀粉和氢化玉米油的浸润剂成本较高。不利于企业在竞争激烈的市场中成本优势。
发明内容
本发明的目的是为了解决上述技术的不足而提供一种低成本电子级玻璃纤维纱用浸润剂及其生产方法。
为了达到上述目的，本发明所设计的一种低成本电子级玻璃纤维纱用浸润剂，它主要包含93-95份软化水、1.8-2.4份未改性高直链玉米淀粉、1.8-2.4份改性马铃薯淀粉、1.3-1.7份植物油乳液、0.1-0.3份塑化剂和0.2-0.4份阳离子软化剂组成，上述份数为质量份数。
低成本电子级玻璃纤维纱用浸润剂的生产方法：第一步，先将未改性高直链玉米淀粉与改性马铃薯淀粉混合于软化水中形成淀粉浆，搅拌均匀，将淀粉浆通过蒸煮器，将淀粉浆的糊化程度控制在80%-84%;第二步，分别溶解塑化剂和阳离子软化剂；第三步，将糊化后的淀粉浆移至混合罐内，随后加入溶解好的增塑剂，充分搅拌与淀粉浆充分混合，再加入溶解好的阳离子软化剂，最后加入植物油乳液，加入60℃软化水，控制混合液固含量在6.4%±0.2%，粘度在3-7mPas即可。
低成本电子级玻璃纤维纱用浸润剂中植物油乳液的制作方法：称取油脂，加入乳化剂和热水，使混合液的温度控制于64℃-78℃，搅拌均匀，混合液缓慢通过挤压式乳化剂，乳化成乳白色油脂乳液，控制乳液粒径在一粒径范围内即可。
本发明所得到的低成本电子级玻璃纤维纱用浸润剂及其生产方法，经过2年多的测试使用，所生产的电子级玻璃纤维纱性能优良，管纱毛羽率低，纱线硬挺度均匀，完全满足后续工序使用性能，而且吨纱浸润剂成本低，节约了吨纱生产成本。
具体实施方式
下面通过实施例对本发明作进一步的描述。
实施例1：
本实施例描述的低成本电子级玻璃纤维纱用浸润剂生产方法：第一步，先将1.8份未改性高直链玉米淀粉与1.8份改性马铃薯淀粉混合于软化水中形成淀粉浆，搅拌均匀，将淀粉浆通过蒸煮器，将淀粉浆的糊化程度控制在80%;第二步，分别溶解0.1份塑化剂和0.2阳离子软化剂；第三步，将糊化后的淀粉浆移至混合罐内，随后加入溶解好的增塑剂，充分搅拌与淀粉浆充分混合，再加入溶解好的阳离子软化剂，最后加入1.3份植物油乳液，加入60℃软化水，控制混合液固含量在6.6%，粘度在3mPas即可。
实施例2：
本实施例描述的低成本电子级玻璃纤维纱用浸润剂生产方法：第一步，先将2.4份份未改性高直链玉米淀粉与2.4份改性马铃薯淀粉混合于软化水中形成淀粉浆，搅拌均匀，将淀粉浆通过蒸煮器，将淀粉浆的糊化程度控制在84%;第二步，分别溶解0.3份塑化剂和0.4阳离子软化剂；第三步，将糊化后的淀粉浆移至混合罐内，随后加入溶解好的增塑剂，充分搅拌与淀粉浆充分混合，再加入溶解好的阳离子软化剂，最后加入1.7份植物油乳液，加入60℃软化水，控制混合液固含量在6.2%，粘度在7mPas即可。
实施例3：
本实施例描述的低成本电子级玻璃纤维纱用浸润剂生产方法：第一步，先将2.1份份未改性高直链玉米淀粉与2.1份改性马铃薯淀粉混合于软化水中形成淀粉浆，搅拌均匀，将淀粉浆通过蒸煮器，将淀粉浆的糊化程度控制在82%;第二步，分别溶解0.2份塑化剂和0.3阳离子软化剂；第三步，将糊化后的淀粉浆移至混合罐内，随后加入溶解好的增塑剂，充分搅拌与淀粉浆充分混合，再加入溶解好的阳离子软化剂，最后加入1.5份植物油乳液，加入60℃软化水，控制混合液固含量在6.4%，粘度在5mPas即可。
浸润剂的使用工艺要求：第一，浸润剂在涂油带上呈均匀分布，丝束在涂油带接触宽在18cm～25cm,原丝含油控制在1.0%～1.15%;第二,原丝找头后进行调理以使淀粉成膜，调理工艺为：温度65%±10，温度26±5℃，调理时间6～10小时；第三，捻线机内温度为28℃±2℃，湿度为46%±3%。

Claims (2)

1.一种低成本电子级玻璃纤维纱用浸润剂的生产方法，其所述的低成本电子级玻璃纤维纱用浸润剂，主要包含93-95份软化水、1.8-2.4份未改性高直链玉米淀粉、1.8-2.4份改性马铃薯淀粉、1.3-1.7份植物油乳液、0.1-0.3份塑化剂和0.2-0.4份阳离子软化剂组成，上述份数为质量份数；其特征是第一步，先将未改性高直链玉米淀粉与改性马铃薯淀粉混合于软化水中形成淀粉浆，搅拌均匀，将淀粉浆通过蒸煮器，将淀粉浆的糊化程度控制在80%-84%;第二步，分别溶解塑化剂和阳离子软化剂；第三步，将糊化后的淀粉浆移至混合罐内，随后加入溶解好的增塑剂，充分搅拌与淀粉浆充分混合，再加入溶解好的阳离子软化剂，最后加入植物油乳液，加入60℃软化水，控制混合液固含量在6.4%±0.2%，粘度在3-7mpas。 
2.根据权利要求1所述的低成本电子级玻璃纤维纱用浸润剂生产方法，其特征是植物油乳液的制作方法为，称取油脂，加入乳化剂和热水，使混合液的温度控制于64℃-78℃，搅拌均匀，混合液缓慢通过挤压式乳化剂，乳化成乳白色油脂乳液，控制乳液粒径在一粒径范围内即可。 
CN201110400105.2A 2011-12-06 2011-12-06 低成本电子级玻璃纤维纱用浸润剂及其生产方法 Active CN102603213B (zh)