CN102587619A - Soft wood printing floor and production method soft wood printing floor - Google Patents
Soft wood printing floor and production method soft wood printing floor Download PDFInfo
- Publication number
- CN102587619A CN102587619A CN2012100760227A CN201210076022A CN102587619A CN 102587619 A CN102587619 A CN 102587619A CN 2012100760227 A CN2012100760227 A CN 2012100760227A CN 201210076022 A CN201210076022 A CN 201210076022A CN 102587619 A CN102587619 A CN 102587619A
- Authority
- CN
- China
- Prior art keywords
- printing
- cork
- soft wood
- layer
- plastic film
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a soft wood printing floor and a production method of the soft wood printing floor. The soft wood printing floor comprises a soft wood layer, wherein a printing plastic film layer with tensile performances is adhered to the soft wood layer. During production, the soft wood layer is dried until the moisture content is 3-7%; the adhesion surface of the soft wood layer is polished smoothly; glue is applied to the adhesion surface of the soft wood layer; the printing plastic film layer with the tensile performances is placed on the adhesion surface of the soft wood layer so that the soft wood layer and the printing plastic film layer with the tensile performances are pressed into a whole by using a hot press. The soft wood printing floor and the production method of the soft wood printing floor have the advantages of reasonable structure, convenience for manufacturing, low production cost, low equipment investment, attractive product and excellent performances.
Description
Technical field
The present invention relates to a kind of production method of printing cork flooring.
Background technology
Cork: the crust of cork robur or quercus suber tree, can adopt stripping once, reproducible natural resource in per 9 years.
Cork flooring: apply the floor that bonding adhesive is processed through the cork robur of processing or the crust of quercus suber tree.Cork flooring has the characteristic that environmental protection, sound insulation, protection against the tide, wear-resisting, resistance to compression, insulation, free from insect pests, other flexible etc. ground materials do not possess.Can be applicable to the ground surface finishing in various places, particularly have specific (special) requirements the kindergarten, perform in a radio or TV programme places such as the Room, cinema.
Although cork flooring has numerous advantages, its surperficial pattern is single, can not adapt to people to the multifarious needs of pattern.
The printing cork flooring; It is the floor of directly printing various textures on the surface of cork slab; Decorative effect abundant and the enhancing cork flooring keeps the characteristic of cork flooring, but its special equipment limitation is big, the plate-making cost is high, cork surface printing poor adhesive force is prone to come off, and can only print pure flat.
Summary of the invention
The object of the present invention is to provide a kind of rational in infrastructurely, performance is good, printing cork flooring and production method thereof attractive in appearance.
Technical solution of the present invention is:
A kind of printing cork flooring is characterized in that: comprise the cork layer, on the cork layer, be bonded with the printing plastic film layers of tool tensile property.
Said printing plastic film layers is the chamfering form and extends the side that covers the cork layer.
A kind of production method of printing cork flooring is characterized in that: comprise the following steps:
(1) the cork layer is dry, to moisture content be 3 ~ 7%;
(2) cork layer binding face polished flat;
(3) at the binding face gluing of cork layer;
(4) the printing plastic film layers with the tool tensile property is positioned on the binding face of cork layer, makes the printing plastic film laminate integrator of cork layer and tool tensile property with hot press.
Temperature is 90 ~ 130 ℃ during hot pressing, and pressing time is 1 ~ 10 minute, and pressure is>=5-25kg/cm
2, the bonding strength that the printing plastic sheeting combines with the cork layer is>=1.6MPa.
During step (4) pressing, the impression template is set on the pressing plate of hot press, the impression frame that cooperates with finished product ground board size is arranged on the impression template, will print plastic film layers through pressing down of additional impression frame and be the side that the extension of chamfering form covers the cork layer.Leave the allowance size between the adjacent indentations frame.
The present invention is rational in infrastructure, and is easy to make, and cost of production is low, and equipment investment is little, and product is attractive in appearance, excellent performance.
Description of drawings
Below in conjunction with accompanying drawing and embodiment the present invention is described further.
Fig. 1 is the structural representation of one embodiment of the invention.
Fig. 2 is the processing sketch map of impression template.
Fig. 3 is the product sketch map after the compacting.
The specific embodiment
(1) the cork layer is dry, to moisture content be 3 ~ 7%;
(2) cork layer binding face polished flat;
(3) at the binding face gluing of cork layer;
(4) the printing plastic film layers with the tool tensile property is positioned on the binding face of cork layer, makes the printing plastic film laminate integrator of cork layer and tool tensile property with hot press.
Temperature is 90 ~ 130 ℃ during hot pressing, and pressing time is 1 ~ 10 minute, and pressure is 5kg/cm
2~ 25g/cm
2, the bonding strength that the printing plastic sheeting combines with the cork layer is>=1.6MPa.
The printing cork flooring that obtains comprises cork layer 1, on the cork layer, is bonded with the printing plastic film layers 2 of tool tensile property.
Embodiment 2:
During step (4) pressing, impression template 3 is set on the pressing plate of hot press, the impression frame 4 that cooperates with finished product ground board size is arranged on the impression template, will print plastic film layers through pressing down of additional impression frame and be the side that the extension of chamfering form covers the cork layer.Leave the allowance size between the adjacent indentations frame; Product after the pressing, after allowance 5 excisions, the cork flooring tangent plane is chamfering shape 6.
All the other are with embodiment 1.The printing cork flooring that obtains comprises the cork layer, on the cork layer, is bonded with the printing plastic film layers of tool tensile property, and said printing plastic film layers is the chamfering form and extends the side that covers the cork layer.
Claims (6)
1. a printing cork flooring is characterized in that: comprise the cork layer, on the cork layer, be bonded with the printing plastic film layers of tool tensile property.
2. printing cork flooring according to claim 1 is characterized in that: said printing plastic film layers is the chamfering form and extends the side that covers the cork layer.
3. the production method of the described printing cork flooring of claim 1 is characterized in that: comprise the following steps:
(1) the cork layer is dry, to moisture content be 3 ~ 7%;
(2) cork layer binding face polished flat;
(3) at the binding face gluing of cork layer;
(4) the printing plastic film layers with the tool tensile property is positioned on the binding face of cork layer, makes the printing plastic film laminate integrator of cork layer and tool tensile property with hot press.
4. the production method of printing cork flooring according to claim 3 is characterized in that: temperature is 90 ~ 130 ℃ during hot pressing, and pressing time is 1 ~ 10 minute, and pressure is 5-25kg/cm
2, the bonding strength that the printing plastic sheeting combines with the cork layer is>=1.6MPa.
5. according to the production method of claim 3 or 4 described printing cork floorings; It is characterized in that: during step (4) pressing; The impression template is set on the pressing plate of hot press; The impression frame that cooperates with finished product ground board size is arranged on the impression template, will print plastic film layers through pressing down of additional impression frame and be the side that the extension of chamfering form covers the cork layer.
6. the production method of printing cork flooring according to claim 5 is characterized in that: leave the allowance size between the adjacent indentations frame.