CN102584121A - 一种无机非金属轻质防火保温板 - Google Patents
一种无机非金属轻质防火保温板 Download PDFInfo
- Publication number
- CN102584121A CN102584121A CN2012100188721A CN201210018872A CN102584121A CN 102584121 A CN102584121 A CN 102584121A CN 2012100188721 A CN2012100188721 A CN 2012100188721A CN 201210018872 A CN201210018872 A CN 201210018872A CN 102584121 A CN102584121 A CN 102584121A
- Authority
- CN
- China
- Prior art keywords
- thermal insulation
- percent
- insulation board
- building
- inorganic nonmetallic
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明公开了一种无机非金属轻质防火保温板,其原料组分及其重量百分比含量为:石英砂:45~55%;石灰:12~16%;水泥:24~37%;石膏:5%;铝粉:0.15~0.16%;稳定增强型外加剂:0.1~0.3%。本发明以优化的基础配方配以稳定增强型外加剂,可使产品获得稳定生产,并令其产品砌块的强度达到高于国家标准中B03级产品标准的1.8MPa以上。本发明的优点是:符合防火要求,性能稳定,造价适中,可以从根本上改变目前建筑的外保温形式,使之从粘贴外保温层变成单一材料保温,可与建筑物同寿命,防止开裂等现象出现。
Description
技术领域
本发明涉及一种无机防火保温材料,更具体的说,本发明涉及一种符合国家标准GB/T11968-2006且强度高于该标准中B03级的砂加气轻质防火混凝土保温板。
背景技术
近年来,建筑用易燃可燃外保温材料已成为一类新的火灾隐患,由此引发的火灾已呈多发势头,因此,公安部对民用建筑外保温材料提出了更高的要求。而随着科技发展和人们环保意识的增强,科技含量高、性能高且稳定、绿色环保型的复合型保温绝热材料也已成为国内外建筑行业所关注的重点及热点。但是,目前国内外建筑用外保温绝热材料的品种匮乏,特别是高性能保温绝热材料的生产难以适应市场上巨大的需求量,个别能够起到防火作用的保温材料,也因为造价太高不能普及使用。
砂加气混凝土砌块(板材)为无机硅酸盐制品,属于A1级不燃材料,具有质轻、高强、保温、隔热、防火、隔声、便于加工、施工便捷、绿色环保等特点,作为外墙自保温技术体系,完全满足65%节能要求,并可与建筑同寿命。然而,针对城市及城市周边地区中、高层建筑通常采用的结构形式,作为外墙保温材料的砂加气混凝土制品,尚需解决梁柱、短肢剪力墙或剪力墙等热桥部位的节能和制作等问题,方可满足城市建筑的节能要求。
本领域的技术人员均知,生产砂加气混凝土产品有两个主要难点:
一是随着密度的降低,其强度会随之下降,常规生产根本无法达到国家标准GB/T11968-2006中B03级砂加气砌块强度大于1.0Mp的标准;
二是随着密度的降低,其浇注稳定性会随之变差,故目前市场只有少数企业能够生产符合B03级标准的砂加气产品。
发明内容
本发明的目的,就是针对目前建筑市场上外保温材料不能达到防火性能和要求,或者能起到防火要求而造价太高的问题,提供一种自身就可达到防火要求且造价适中的无机非金属轻质防火保温板。
根据国家标准要求,“GB/T11968-2006蒸压加气混凝土砌块”是按混凝土砌块的干密度分级,其中的B03级砂加气轻质防火混凝土材料是指干密度为225-325KG/m3的加气混凝土砌块。本发明人经过有关研究与试验,提出以自身性能即可达到防火要求且造价适中的低密度B03级砂加气混凝土制作保温材料薄板制品的主张,该主张的实施,不仅可以作为前述高性能保温绝热防火材料的替代产品,而且将其应用于中、高层建筑有关部位的外贴还可实现建筑节能与围护结构一体化的目的,从而有力推动建筑节能和绿色建筑的发展方向,并解决当前建筑市场上高性能保温绝热材料巨大需求量的问题。
本发明通过如下技术方案予以实现。
一种无机非金属轻质防火保温板,其原料组分及其重量百分比含量为:
石英砂:45~55%;
石灰:12~16%;
水泥:24~37%;
石膏:5%;
铝粉:0.15~0.16%;
稳定增强型外加剂:0.1~0.3%。
所述稳定增强型外加剂的原料组分及其重量百分比含量为:
松脂酸钠:20~25%;
油酸:12%;
三乙醇胺:38%;
硅粉:25~30%。
所述石英砂的细度为200目以上,其中的硅含量为90%以上。
所述石灰的有效钙含量在75%以上。
所述的铝粉为发气剂。
本发明无机非金属轻质防火保温板的有益效果是:
(1)可以自身达到防火要求,从而以单一材料代替外保温层的粘贴,改变目前建筑的外保温形式和外保温材料的防火性能。
(2)可以直接作为外墙建筑材料使用,无需另外粘贴外保温层,从而避免外贴工艺中开裂等现象的出现。
(3)性能可靠,造价适中,可与建筑物同寿命,利于发展绿色建筑,实现建筑节能与围护结构的一体化。
具体实施方式
为了使本发明更容易被清楚理解,以下结合实施例对本发明的技术方案作以详细描述。
一种无机非金属轻质防火保温板,按照下列原料的重量百分比进行配料:
石英砂:45~55%;
石灰:12~16%;
水泥:24~37%;
石膏:5%;
铝粉:0.15~0.16%;
稳定增强型外加剂:0.1~0.3%。
所述稳定增强型外加剂的原料重量百分比含量为:
松脂酸钠:20~25%;
油酸:12%;
三乙醇胺:38%;
硅粉:25~30%。
本发明对石英砂的要求是:硅含量在90%以上,细度在200目以上;对石灰的要求是:有效钙含量在75%以上;所用的水泥为早强325普通硅酸盐水泥。
将上述混合料加入水搅拌、浇注、并经预养后切割成半成品,再通过湿掰工艺提高合格率,然后蒸压养护,制成本发明的无机非金属轻质防火保温板。
本发明的具体实施例如下:
实施例1:
一种无机非金属轻质防火保温板,按照下列原料的重量百分比进行配料:
石英砂:53%;
石灰:12%;
水泥:29.69%;
石膏:5%;
铝粉:0.15%;
稳定增强型外加剂:0.16%。
所述稳定增强型外加剂的原料重量百分比含量为:
松脂酸钠:25%;
油酸:12%;
三乙醇胺:38%;
硅粉:25%。
该实施例产品的性能是:干密度320KG/m3,强度2.1Mpa,导热系数0.0812W/(m·K)
实施例2:
一种无机非金属轻质防火保温板,按照下列原料的重量百分比进行配料:
石英砂:55%:
石灰:12%;
水泥:27.68%:
石膏:5%:
铝粉:0.16%;
稳定增强型外加剂:0.16%。
所述稳定增强型外加剂的原料重量百分比含量为:
松脂酸钠:20%;
油酸:12%;
三乙醇胺:38%;
硅粉:30%。
该实施例产品的性能是:干密度305KG/m3,强度2.0Mpa,导热系数0.08W/(m·K)
本发明采用优化的基础配方并配以超细无机粉复合材料的稳定增强型外加剂,不仅克服了前述的两个生产难点,在一定程度上提高了无机非金属轻质防火保温板的强度和浇注稳定性,而且使其产品得以稳定生产,且令其产品砌块的强度高于国家标准中B03级产品标准,达到1.8MPa以上。
本发明的优点是在于:能够从根本上改变目前建筑的外保温形式,使之从粘贴外保温层变成单一材料保温。其显著特点是:符合公安部规定的防火要求,性能稳定,造价适中,与建筑物同寿命,并防止开裂等现象的出现。
以上通过实施例对本发明无机非金属轻质防火保温板的原料配方进行了描述,该描述没有限制性。本领域人员应能理解,在实际应用中,为了适合于某种需要,上述实施例中各组分的含量均可在其范围内获得选择,而其他人员在本发明的启示下也可能作出相同或相似的方案。特别需要指出的是,只要不脱离本发明的宗旨,所有显而易见的改变,均包含在本发明的保护范围之内。
Claims (4)
1.一种无机非金属轻质防火保温板,其原料组分及其重量百分比含量为:石英砂:45~55%;石灰:12~16%;水泥:24~37%;石膏:5%;铝粉:0.15~0.16%;稳定增强型外加剂:0.1~0.3%;所述稳定增强型外加剂的原料组分及其重量百分比含量为:松脂酸钠:20~25%;油酸:12%;三乙醇胺:38%;硅粉:25~30%。
2.根据权利要求1所述的无机非金属轻质防火保温板,其特征是,所述石英砂的细度为200目以上,其中的硅含量为90%以上。
3.根据权利要求1所述的无机非金属轻质防火保温板,其特征是,所述石灰的有效钙含量在75%以上。
4.根据权利要求1所述的无机非金属轻质防火保温板,其特征是,所述的铝粉为发气剂。