CN102560044A - Copper strip surface treatment method and device - Google Patents
Copper strip surface treatment method and device Download PDFInfo
- Publication number
- CN102560044A CN102560044A CN2012100380020A CN201210038002A CN102560044A CN 102560044 A CN102560044 A CN 102560044A CN 2012100380020 A CN2012100380020 A CN 2012100380020A CN 201210038002 A CN201210038002 A CN 201210038002A CN 102560044 A CN102560044 A CN 102560044A
- Authority
- CN
- China
- Prior art keywords
- release agent
- strip surface
- copper strip
- surface treatment
- copper
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a copper strip surface treatment method and a copper strip surface treatment device. The copper strip surface treatment method comprises a rolling procedure, an anti-sticking agent spraying procedure and an annealing procedure, wherein the anti-sticking agent spraying procedure is that an anti-sticking agent is sprayed onto the surface of a rolled copper strip, so that a uniform layer of film is formed on the surface of the copper strip; and the film serves as a heat insulating film in the annealing procedure to prevent adhesion between copper strips. The invention solves the problem that the copper strips are adhered in the annealing procedure.
Description
Technical field
The present invention relates to a kind of copper strip surface treatment process and device, belong to technical field of nonferrous metal processing.
Background technology
, low consumption energy-conservation in order to satisfy, environmental protection and economy developing direction, copper processing enterprise all carries out technological innovation constantly both at home and abroad, in the hope of improving the quality of products, enhances productivity, and reduces product cost.Copper strips is widely used in electronics industry, building and traffic and transport field, machinery and instrument field etc., is used to make radiator tank band, concentric cable band, micromotor commutator, transformer winding, blaster fuse frame material, elasticity connector assembly, photovoltaic welding belt or the like.At present; The production technique of copper strips comprises the steps: the copper strips base---roughing---in roll that------------cleaning by degreasing---is cut---packing to finished products in finish rolling in process annealing; During finish rolling; Because tension force before and after existing is easy to generate the adhesive tape phenomenon between the copper strips behind the finished products, influence quality product.The existing method that solves this technical problem mainly contains two kinds, and the one, the copper strips after the finish rolling is carried out loose winding, reduce its tension force, the 2nd, adopt air cushion furnace annealing.But all there is deficiency in these two kinds of methods, and first method has increased production process one, have reduced production efficiency and have improved production cost, and second method exists production unit to involve great expense, several ten million yuan of cover air cushion furnace equipment manufacturing cost, and production cost is higher.
Summary of the invention
The object of the present invention is to provide a kind of copper strip surface treatment process and device, the problem of adhesive tape takes place when the invention solves copper strips annealing.
In order to achieve the above object, technical scheme of the present invention is:
A kind of copper strip surface treatment process; Comprise rolling, spray release agent, annealing operation; Described spray release agent operation sprays release agent at copper strip surface after being meant rolling process; Make it form a uniform skim at copper strip surface, and when annealing operation as one deck thermal insulation film, prevent the bonding between the copper strips.
Described rolling process adopts the cold rolling unit of reversible hydraulic AGC that copper strips is rolled; Copper strips supplied materials thickness is 1.5 mm~0.1mm; F strain is controlled at 1.0~8.0KN, and B strain is controlled at 2.5~10.0KN, and roll speed is 250~360m/min; The rolling pass working modulus is: 20~40%, and the thickness after copper strips is rolling is 1.2 mm~0.06mm.
Described spray release agent operation adopts release agent to be stored in the release agent liquor box, adopts water pump that release agent solution is arrived atomizing nozzle through flexible pipe, and under compressed-air actuated effect, release agent solution is sprayed at copper strip surface equably with atomization style.
Described release agent adopts SiO 2 powder or alumina powder, is scattered in the alcohol equably and processes, and alcohol is industrial alcohol, and the weight ratio of SiO 2 powder or alumina powder and alcohol is 1:100~1:150.
Described annealing operation adopts bell-jar layering annealed mode, 150 ℃~250 ℃ of annealing temperatures, annealing time 2~6h; The copper strips branch is placed on the heat-resistance stainless steel shelf, covers the bell-jar furnace shell,, take out most air to 10 with vacuum pump through the gaseous state sealing
-3Pa charges into any one gas of the gas mixture of hydrogen, nitrogen or hydrogen and nitrogen, accomplishes annealing operation through heating, insulation, cooling three phases.
A kind of copper strip surface treatment unit comprises release agent liquor box, water pump, ball valve, flexible pipe, support, atomizing nozzle, tracheae, source of the gas; Described release agent liquor box links to each other with water pump through pipeline, and water pump passes through pipeline and links to each other with flexible pipe, and pipeline and hose connection place are equipped with ball valve; Be connected with atomizing nozzle on the described flexible pipe, and atomizing nozzle is rack-mount; Also be connected with tracheae on the described atomizing nozzle, tracheae links to each other with source of the gas.
The invention has the beneficial effects as follows: 1. adopt the method for online spray release agent, solved the phenomenon that adhesive tape takes place copper strips when finished products, improved quality product, reduced production process one, reduced production cost, improved production efficiency than prior art.Adopt the cost of 10 yuan of per ton need of method of online spray release agent.
2. spray release agent equipment is easy to operate, can satisfy the online spray of different in width copper strips, and release agent is sprayed at copper strip surface uniformly, makes copper strip surface form a uniform skim, in annealing, forms one deck thermal insulation film, prevents the bonding between the copper strips.
3. employing pressurized air sprays release agent at copper strip surface with atomizing state through atomizing nozzle uniformly, direct finished products, and the copper strip surface color and luster is even, does not have aberration, and copper strip surface quality is high.
Description of drawings
Fig. 1 is a structural representation of the present invention.
Embodiment
Below in conjunction with accompanying drawing a nearly step being done in enforcement of the present invention describes in detail.
A kind of copper strip surface treatment process of present embodiment comprises rolling, spray release agent, annealing operation, and at first be rolled operation: rolling process adopts the cold rolling unit of reversible hydraulic AGC that copper strips is rolled; Copper strips supplied materials thickness is 1.5 mm~0.1mm; F strain is controlled at 1.0~8.0KN, and B strain is controlled at 2.5~10.0KN, and roll speed is 250~360m/min; The rolling pass working modulus is: 20~40%, and the thickness after copper strips is rolling is 1.2 mm~0.06mm.
Spray the release agent operation then: adopt described copper strip surface treatment unit, as shown in Figure 1, comprise release agent liquor box 1, water pump 2, ball valve 3, flexible pipe 4, support 5, atomizing nozzle 6, tracheae 7, source of the gas 8; Described release agent liquor box 1 links to each other with water pump 2 through pipeline, and water pump 2 passes through pipeline and links to each other with flexible pipe 4, and pipeline and flexible pipe 4 junctions are equipped with ball valve 3; Be connected with atomizing nozzle 6 on the described flexible pipe 4, and atomizing nozzle 6 is installed on the support 5; Also be connected with tracheae 7 on the described atomizing nozzle 6, tracheae 7 links to each other with source of the gas 8.After being meant rolling process, spray release agent operation sprays release agent at copper strip surface; Release agent is stored in the release agent liquor box 1, adopts water pump 2 that release agent solution is arrived atomizing nozzle 6 through flexible pipe 4, under the compressed-air actuated effect in source of the gas 8; Release agent solution is sprayed at copper strip surface equably with atomization style; Make it form a uniform skim at copper strip surface, and when annealing operation as one deck thermal insulation film, prevent the bonding between the copper strips.Described release agent adopts SiO 2 powder or alumina powder, is scattered in the alcohol equably and processes, and the weight ratio of SiO 2 powder or alumina powder and alcohol is 1:100~1:150.Carry out annealing operation at last, annealing operation adopts bell-jar layering annealed mode, 150 ℃~250 ℃ of annealing temperatures, annealing time 2~6h; The copper strips branch is placed on the heat-resistance stainless steel shelf, covers the bell-jar furnace shell,, take out most air to 10 with vacuum pump through the gaseous state sealing
-3Pa charges into any one gas of the gas mixture of hydrogen, nitrogen or hydrogen and nitrogen, accomplishes annealing operation through heating, insulation, cooling three phases.
The copper strip surface treatment process and the device of present embodiment have following characteristics: 1. the method that adopts online spray release agent; Solved the phenomenon that adhesive tape takes place copper strips when finished products; Improved quality product; Reduce production process one than prior art, reduced production cost, improved production efficiency.Adopt the cost of 10 yuan of per ton need of method of online spray release agent.2. the copper strip surface treatment unit is easy to operate, can satisfy the online spray of different in width copper strips; Release agent is sprayed at copper strip surface uniformly; Make copper strip surface form a uniform skim, in annealing, form one deck thermal insulation film, prevent the bonding between the copper strips.3. employing pressurized air sprays release agent at copper strip surface with atomizing state through atomizing nozzle uniformly, direct finished products, and the copper strip surface color and luster is even, does not have aberration, and copper strip surface quality is high.
Claims (6)
1. copper strip surface treatment process; Comprise rolling, spray release agent, annealing operation; It is characterized in that: spray release agent at copper strip surface behind the described rolling process; Make it form a uniform skim at copper strip surface, and when annealing operation as one deck thermal insulation film, prevent the bonding between the copper strips.
2. a kind of copper strip surface treatment process as claimed in claim 1; It is characterized in that: described rolling process adopts the cold rolling unit of reversible hydraulic AGC that copper strips is rolled, and copper strips supplied materials thickness is 1.5 mm~0.1mm, and rolling F strain is controlled at 1.0~8.0KN; Rolling B strain is controlled at 2.5~10.0KN; Roll speed is 250~360m/min, and the rolling pass working modulus is: 20~40%, and the thickness after copper strips is rolling is 1.2 mm~0.06mm.
3. a kind of copper strip surface treatment process as claimed in claim 1; It is characterized in that: described spray release agent operation adopts release agent to be stored in the release agent liquor box; Adopt water pump that release agent solution is arrived atomizing nozzle through flexible pipe; Under compressed-air actuated effect, release agent solution is sprayed at copper strip surface equably with atomization style.
4. like claim 1 or 3 described a kind of copper strip surface treatment processs; It is characterized in that: described release agent adopts SiO 2 powder or alumina powder; Be scattered in the alcohol equably and process, the weight ratio of SiO 2 powder or alumina powder and alcohol is 1:100~1:150.
5. a kind of copper strip surface treatment process as claimed in claim 1 is characterized in that: described annealing operation adopts bell-jar layering annealed mode, 150 ℃~250 ℃ of annealing temperatures, annealing time 2~6h; The copper strips branch is placed on the heat-resistance stainless steel shelf, covers the bell-jar furnace shell,, take out most air to 10 with vacuum pump through the gaseous state sealing
-3Pa charges into any one gas of the gas mixture of hydrogen, nitrogen or hydrogen and nitrogen, accomplishes annealing operation through heating, insulation, cooling three phases.
6. a copper strip surface treatment unit as claimed in claim 1 is characterized in that: comprise release agent liquor box (1), water pump (2), ball valve (3), flexible pipe (4), support (5), atomizing nozzle (6), tracheae (7), source of the gas (8); Described release agent liquor box (1) links to each other with water pump (2) through pipeline, and water pump (2) passes through pipeline and links to each other with flexible pipe (4), and pipeline and flexible pipe (4) junction are equipped with ball valve (3); Be connected with atomizing nozzle (6) on the described flexible pipe (4), and atomizing nozzle (6) is installed on the support (5); Also be connected with tracheae (7) on the described atomizing nozzle (6), tracheae (7) links to each other with source of the gas (8).