CN102558978A - Antifogging agent composition and preparation method and application thereof - Google Patents
Antifogging agent composition and preparation method and application thereof Download PDFInfo
- Publication number
- CN102558978A CN102558978A CN2011103982766A CN201110398276A CN102558978A CN 102558978 A CN102558978 A CN 102558978A CN 2011103982766 A CN2011103982766 A CN 2011103982766A CN 201110398276 A CN201110398276 A CN 201110398276A CN 102558978 A CN102558978 A CN 102558978A
- Authority
- CN
- China
- Prior art keywords
- antifogging agent
- resin film
- agent constituent
- agent composition
- antifogging
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to the technical field of the transparent resin film antifogging agent, and in particular relates to an antifogging agent composition and a preparation method and application thereof. The antifogging agent composition comprises a resin film. The antifogging agent composition is characterized in that the antifogging agent composition consists of hydroxyl-containing fatty acid ester, polyvinyl alcohol and a solvent, wherein the weight ratio of hydroxyl-containing fatty acid ester to polyvinyl alcohol is 0.1-10; the alcoholysis degree of polyvinyl alcohol is 80-100%, and the viscosity is 5-10; and the solvent and water are mutually soluble. The preparation method of the antifogging resin film comprises the following steps: mixing polyvinyl alcohol and water, heating the mixture to 80-90 DEG C, stirring for 1 hour for complete dissolving, then adding hydroxyl-containing fatty acid ester to stir evenly, and spraying the evenly stirred solution on a resin film. The antifogging agent composition can be used to produce the transparent resin film with good antifogging property; and oil stains can not be generated and the roller can not be polluted after long-time production.
Description
[technical field]
The present invention relates to transparent resin film antifogging agent technical field, a kind of specifically antifogging agent constituent and methods and applications thereof.
[background technology]
Polyester resin sheet is the hydrophobic resin sheet; Its surface tension is low, when it is used for the refrigerated food packing, because the surface tension of water is higher; Its steam can the form with little water droplet form water smoke on the resin sheet surface; This just makes the transparent variation of wrapping material, and the content visibility reduces, thereby has reduced the magnetism to client.
Mainly be through using antifogging agent to address the above problem at present; With antifogging agent be coated on resin sheet surface or with its blend; To improve the surface tension and the wetting ability of resin sheet, reduce contact angle between resin sheet surface and the water, thereby make it can form a uniform thin layer; It is transparent that resin sheet still keeps, the optics obstacle that the discrete water droplet of having gone out causes.
It mainly is the hydrophilic surfactant active that tradition is used more antifogging agent; Like polysaccharide fatty acid tensio-active agent, though above-mentioned tensio-active agent has certain anti-fog effect, because the polysaccharide fatty ester has certain oiliness; Its coating back resin sheet oil stain is heavier, causes following problem
Film with the lines of the hand appear after hand contacts, outward appearance is defective;
After producing for some time, the roller of surface in contact promoting agent can be contaminated.
In order to address the above problem, can in above-mentioned tensio-active agent, add hydrophilic Z 150PH, it can reduce the oiliness of polysaccharide fatty ester, solves the oil stain problem that occurs.But the specification of Z 150PH is very big to the production influence of antifog resin sheet, and inappropriate specification can cause following problem:
Inhomogeneous, the antifog deleterious of spraying during production.
With poor, the antifog resin sheet of antifogging agent consistency become opaque.
[summary of the invention]
The objective of the invention is to solve the deficiency of prior art, a kind of antifogging agent constituent and methods and applications thereof are provided.
For realizing that above-mentioned purpose designs a kind of antifogging agent constituent, it is characterized in that said antifogging agent constituent by hydroxyl fatty ester, Z 150PH and solvent composition, wherein the weight ratio of hydroxyl fatty ester and Z 150PH is 0.1~10; The Z 150PH alcoholysis degree is 80~90%, viscosity is 5-10; Described solvent and water dissolve each other, and described hydroxyl fatty ester is Surfhope SE Cosme C 1216 or sucrose stearate, and described Z 150PH alcoholysis degree is preferred 88%, and Z 150PH viscosity is preferably 5.7, and described solvent is water or ethanol.
The present invention also comprises a kind of transparent antifog resin film that is coated with the antifogging agent constituent, comprises the resin film, it is characterized in that being coated with the antifogging agent constituent on the described transparent antifog resin film said antifog resin film mist degree≤4%.
The present invention also comprises a kind of method of antifogging agent constituent production resin film, it is characterized in that this method comprises the steps:
Be heated to 80~90 ℃ with alcoholysis degree is 80~90%, viscosity is 5-10 Z 150PH with solvent that water dissolves each other, stir 1 hour to dissolving fully;
Then, said hydroxyl fatty ester also stirs, and the weight ratio of hydroxyl fatty ester weight and Z 150PH is 0.1~10;
At last, with preparing transparent antifog resin film on the solution spraying that stirs to the said resin film.
The present invention also comprises a kind of application of antifogging agent constituent, it is characterized in that described antifogging agent constituent can be used for food product pack.
The present invention compares with prior art, can produce the good transparent resin sheet of anti-fog performance through the Z 150PH specification that this method adopts, and can not produce the oil stain problem, and through the production of long period, roller can be not contaminated yet.
[description of drawings]
[embodiment]
In conjunction with specific embodiment, the present invention is done further explanation:
Embodiment 1:
Experimental raw:
Surfhope SE Cosme C 1216 125g
The PET film
Deionized water 4.875kg
Preparation technology:
Take by weighing the 125g Surfhope SE Cosme C 1216, join in the 4.875g water, be configured to antifog solution after stirring.With above-mentioned antifog solution spraying to PET film surface, prepare antifog PET film.
Embodiment 2:
Test raw material:
Preparation technology:
Take by weighing the 50g Z 150PH; Join in the 4.875kg water, be heated to 80~90 ℃, stir after 1 hour to dissolving fully; In this aqueous solution, add the 125g Surfhope SE Cosme C 1216; Be configured to antifog solution after stirring, above-mentioned anti-fogging liquid is sprayed into PET film surface, promptly prepare antifog PET film.
Embodiment 3:
Change the Surfhope SE Cosme C 1216 among the embodiment 2 into sucrose stearate, its wetting ability is less than Surfhope SE Cosme C 1216, and preparation technology is constant.
Embodiment 4:
Z 150PH specification among the embodiment 2 is changed into: alcoholysis degree 88%, viscosity 22.4, preparation technology is constant.Excessive because of its viscosity, cause spraying inhomogeneous, antifog deleterious.
Embodiment 5:
Z 150PH specification among the embodiment 2 is changed into: alcoholysis degree 99%, viscosity 5.7, preparation technology is constant.Coating back film transparency reduces, should be its incompatible with Surfhope SE Cosme C 1216 due to.
Embodiment 6:
Z 150PH specification among the embodiment 2 is changed into: alcoholysis degree 99%, viscosity 26.6, preparation technology is constant.Excessive because of its viscosity, cause spraying inhomogeneous, antifog deleterious.
The film performance that the foregoing description is processed is following:
Title | Contact angle (degree) | Antifog grade | Mist degree (%) | Outward appearance |
Blank PET film | 63 | Unacceptable product | - | - |
Embodiment 1 | 11 | The top grade article | 1.2 | After oil stain, the touch lines of the hand are arranged |
Embodiment 2 | 9 | The top grade article | 1.5 | No oil stain, the no lines of the hand in touch back |
Embodiment 3 | 15 | Good level article | 1.43 | No oil stain, the no lines of the hand in touch back |
Embodiment 4 | 19 | Good level article | 0.33 | No oil stain, the no lines of the hand in touch back |
Embodiment 5 | 10.5 | The top grade article | 5.0 | No oil stain, the no lines of the hand in touch back |
Embodiment 6 | 12.5 | The top grade article | 0.64 | No oil stain, the no lines of the hand in touch back |
Learn that from the practice of embodiments of the invention antifogging agent constituent of the present invention can be prepared the good resin sheet of anti-fog performance, can be widely used in the packing of foodstuffs material.
Wherein, the top grade article are that transparent a little water droplet, salable product are that transparent water droplet is more for transparent anhydrous, good level article, and unacceptable product is opaque and contain a large amount of water droplets.
Alcoholysis degree: Z 150PH obtains through the PVA alcoholysis; Be exactly total the functional group of its alcoholysis degree alcoholysis accounts for the percentage ratio of functional group; Alcoholysis degree is big more, Z 150PH water-soluble good more, its anti-fog effect and to improve the effect of oil stain also good more.
Viscosity: after the sign Z 150PH is dissolved in water, the index of aqueous solution viscosity size, viscosity is more little, and anti-fogging liquid sprays evenly more easily, and outward appearance, the anti-fog effect of its coating back film are also good more.
Contact angle: contact angle is meant that the tangent line of the liquid-gas interface of doing in gas-liquid-solid three-phase intersection point place passes the angle between the liquid solid-liquid boundary line, is the index that characterizes anti-fog effect, and contact angle is more little, and anti-fog effect is good more.
Mist degree: the inside of transparent or semitransparent material or surface are because cloud that light diffusion causes or muddy outward appearance; Optical throughput with diffusion is represented with the percentage of the ratio of the optical throughput of permeable material; Mist degree is big more, and film is opaque more, transparent antifog film mist degree index request≤4%.
Claims (10)
1. an antifogging agent constituent is characterized in that said antifogging agent constituent by hydroxyl fatty ester, Z 150PH and solvent composition, and wherein the weight ratio of hydroxyl fatty ester and Z 150PH is 0.1~10; The Z 150PH alcoholysis degree is 80~90%, viscosity is 5-10; Described solvent and water dissolve each other.
2. a kind of antifogging agent constituent as claimed in claim 1 is characterized in that described hydroxyl fatty ester is a Surfhope SE Cosme C 1216.
3. a kind of antifogging agent constituent as claimed in claim 1 is characterized in that described hydroxyl fatty ester is a sucrose stearate.
4. a kind of antifogging agent constituent as claimed in claim 1 is characterized in that described Z 150PH alcoholysis degree is 88%.
5. a kind of antifogging agent constituent as claimed in claim 1 is characterized in that described Z 150PH viscosity is 5.7.
6. a kind of antifogging agent constituent as claimed in claim 1 is characterized in that described solvent is a water.
7. a kind of antifogging agent constituent as claimed in claim 1 is characterized in that described solvent is an ethanol.
8. a transparent antifog resin film that is coated with the antifogging agent constituent comprises the resin film, it is characterized in that being coated with the antifogging agent constituent on the described transparent antifog resin film said antifog resin film mist degree≤4%.
9. the method that the antifogging agent constituent is produced the resin film is characterized in that this method comprises the steps:
Be heated to 80~90 ℃ with alcoholysis degree is 80~90%, viscosity is 5-10 Z 150PH with solvent that water dissolves each other, stir 1 hour to dissolving fully;
Then, said hydroxyl fatty ester also stirs, and the weight ratio of hydroxyl fatty ester weight and Z 150PH is 0.1~10;
At last, with preparing transparent antifog resin film on the solution spraying that stirs to the said resin film.
10. the application of an antifogging agent constituent is characterized in that described antifogging agent constituent can be used for food product pack.