CN102558693A - 一种氯磺化聚乙烯护套及其制备方法 - Google Patents

一种氯磺化聚乙烯护套及其制备方法 Download PDF

Info

Publication number
CN102558693A
CN102558693A CN2011104195397A CN201110419539A CN102558693A CN 102558693 A CN102558693 A CN 102558693A CN 2011104195397 A CN2011104195397 A CN 2011104195397A CN 201110419539 A CN201110419539 A CN 201110419539A CN 102558693 A CN102558693 A CN 102558693A
Authority
CN
China
Prior art keywords
polyethylene sheath
preparation
cpe
mills
chlorosuphonated
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN2011104195397A
Other languages
English (en)
Inventor
姜睿
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Anhui Jinqiao Cable Co Ltd
Original Assignee
Anhui Jinqiao Cable Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Anhui Jinqiao Cable Co Ltd filed Critical Anhui Jinqiao Cable Co Ltd
Priority to CN2011104195397A priority Critical patent/CN102558693A/zh
Publication of CN102558693A publication Critical patent/CN102558693A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种氯磺化聚乙烯护套及其制备方法，其按组成原料的重量份将氯化聚乙烯CPE-135B切胶，然后与活性氧化镁、复合稳定剂、低分子PE蜡、防老剂264、白碳黑、超细滑石粉、二辛酯、环氧大豆油、氯化石蜡、偶联剂1206、三氧化二锑和陶土混合均匀，进行一次捏炼、400开炼机、300开炼机开练；向其中加入活化剂和硫化剂DCP，进行二次捏炼、400开炼机、300开炼机开练，最后叠片出胶得到成品。本发明采用多种化学材料制成氯磺化聚乙烯护套，具有良好的耐高温、耐热性能，压缩性能和韧性强，阻燃性能好，制备成本低，工艺简单。

Description

一种氯磺化聚乙烯护套及其制备方法
技术领域
本发明涉及一种氯磺化聚乙烯护套及其制备方法，属于电缆材料领域。
背景技术
大量火灾报告证实致人死亡的罪魁祸首是塑料燃烧时生成的烟和有毒气体，特别是对于高层建筑，情况更明显，据统计火灾中发生的死亡事故，有80是由于烟和有毒气体的窒息造成的。由于聚氯乙烯与聚乙烯、聚丙烯、聚苯乙烯和ABS统称为五大通用树脂，是我国第一、世界第二大通用型合成树脂材料，广泛地应用在各类建材、各类生活用品等方面。因此成为近年来阻燃塑料领域中重点研究课题之一就是降低塑料燃烧时生成的烟量和有毒气体量。
氯化聚乙烯在国内外的主要用途是制造电缆，现有的氯化聚乙烯护套电线电缆存在相当严重的污染，都会产生大量的二恶英、氯氢酸、铅等有害物质，燃烧时会发生很大的浓烟，并产生有害的HCL气体，会对人体健康造成一定的危害；焚烧或掩埋后，会造成对土壤和水源的污染
发明内容
为了缓解现有技术的不足和缺陷，本发明的目的在于提供一种氯磺化聚乙烯护套及其制备方法。本发明采用多种化学材料制成氯磺化聚乙烯护套，具有良好的耐高温、耐热性能，压缩性能和韧性强，阻燃性能好，制备成本低，工艺简单。
为了实现上述目的本发明采用如下技术方案：
氯磺化聚乙烯护套，其特征在于其组成原料的重量比为：氯化聚乙烯CPE-135B36.15-36.20、活性氧化镁6.00-6.10、复合稳定剂1.60-1.70、低分子PE蜡2.10-2.20、防老剂264 0.25-0.30、白碳黑12.30-12.35、超细滑石粉7.35-7.45、二辛酯1.60-1.70、环氧大豆油1.60-1.70、氯化石蜡9.80-10.00、偶联剂1206 0.45-0.55、活化剂1.10-1.30、硫化剂DCP 1.15-1.20、三氧化二锑5.90-5.95和陶土11.90-12.10。
所述的氯磺化聚乙烯护套，其特征在于其组成原料的重量比为：氯化聚乙烯CPE-135B36.18、活性氧化镁6.08、复合稳定剂1.64、低分子PE蜡2.14、防老剂264 0.28、白碳黑12.33、超细滑石粉7.40、二辛酯1.64、环氧大豆油1.64、氯化石蜡9.87、偶联剂1206 0.49、活化剂1.20、硫化剂DCP 1.17、三氧化二锑5.92和陶土12.00。
所述的氯磺化聚乙烯护套的制备方法，其特征在于包括以下步骤：
(1)按组成原料的重量份称取各原料，将氯化聚乙烯CPE-135B切胶，然后与活性氧化镁、复合稳定剂、低分子PE蜡、防老剂264、白碳黑、超细滑石粉、二辛酯、环氧大豆油、氯化石蜡、偶联剂1206、三氧化二锑和陶土混合均匀，进行一次捏炼8-12分钟，控制温度在73-78℃；
(2)将步骤(1)的料依次通过400开炼机、300开炼机开练，然后向其中加入活化剂和硫化剂DCP，进行二次捏炼1分钟，控制温度在48-52℃；
(3)将步骤(2)的料依次通过400开炼机、300开炼机开练，最后叠片出胶得到成品。
本发明的有益效果：
本发明采用多种化学材料制成氯磺化聚乙烯护套，具有良好的耐高温、耐热性能，压缩性能和韧性强，阻燃性能好，制备成本低，工艺简单。
具体实施方式
实施例1：氯磺化聚乙烯护套，其组成原料的重量比为：氯化聚乙烯CPE-135B36.18、活性氧化镁6.08、复合稳定剂1.64、低分子PE蜡2.14、防老剂264 0.28、白碳黑12.33、超细滑石粉7.40、二辛酯1.64、环氧大豆油1.64、氯化石蜡9.87、偶联剂1206 0.49、活化剂1.20、硫化剂DCP 1.17、三氧化二锑5.92和陶土12.00。
氯磺化聚乙烯护套的制备方法，包括以下步骤：
(1)按组成原料的重量份称取各原料，将氯化聚乙烯CPE-135B切胶，然后与活性氧化镁、复合稳定剂、低分子PE蜡、防老剂264、白碳黑、超细滑石粉、二辛酯、环氧大豆油、氯化石蜡、偶联剂1206、三氧化二锑和陶土混合均匀，进行一次捏炼8-12分钟，控制温度在73-78℃；
(2)将步骤(1)的料依次通过400开炼机、300开炼机开练，然后向其中加入活化剂和硫化剂DCP，进行二次捏炼1分钟，控制温度在48-52℃；
(3)将步骤(2)的料依次通过400开炼机、300开炼机开练，最后叠片出胶得到成品。
实施例2：本发明制得的氯磺化聚乙烯护套的性能数据：

Claims (3)

1.一种氯磺化聚乙烯护套，其特征在于其组成原料的重量比为：氯化聚乙烯CPE-135B 36.15-36.20、活性氧化镁6.00-6.10、复合稳定剂1.60-1.70、低分子PE蜡2.10-2.20、防老剂264 0.25-0.30、白碳黑12.30-12.35、超细滑石粉7.35-7.45、二辛酯1.60-1.70、环氧大豆油1.60-1.70、氯化石蜡9.80-10.00、偶联剂1206 0.45-0.55、活化剂 1.10-1.30、硫化剂DCP 1.15-1.20、三氧化二锑5.90-5.95和陶土11.90-12.10。
2.根据权利要求1所述的氯磺化聚乙烯护套，其特征在于其组成原料的重量比为：氯化聚乙烯CPE-135B 36.18、活性氧化镁6.08、复合稳定剂1.64、低分子PE蜡2.14、防老剂264 0.28、白碳黑12.33、超细滑石粉7.40、二辛酯1.64、环氧大豆油1.64、氯化石蜡9.87、偶联剂1206 0.49、活化剂 1.20、硫化剂DCP 1.17、三氧化二锑5.92和陶土12.00。
3.一种如权利要求1所述的氯磺化聚乙烯护套的制备方法，其特征在于包括以下步骤：
（1）按组成原料的重量份称取各原料，将氯化聚乙烯CPE-135B切胶，然后与活性氧化镁、复合稳定剂、低分子PE蜡、防老剂264、白碳黑、超细滑石粉、二辛酯、环氧大豆油、氯化石蜡、偶联剂1206 、三氧化二锑和陶土混合均匀，进行一次捏炼8-12分钟，控制温度在73-78℃；
（2）将步骤（1）的料依次通过400开炼机、300开炼机开练，然后向其中加入活化剂和硫化剂DCP，进行二次捏炼1分钟，控制温度在48-52℃；
（3）将步骤（2）的料依次通过400开炼机、300开炼机开练，最后叠片出胶得到成品。
CN2011104195397A 2011-12-15 2011-12-15 一种氯磺化聚乙烯护套及其制备方法 Pending CN102558693A (zh)