CN102557750A - Formula of matt glaze - Google Patents
Formula of matt glaze Download PDFInfo
- Publication number
- CN102557750A CN102557750A CN2011104177736A CN201110417773A CN102557750A CN 102557750 A CN102557750 A CN 102557750A CN 2011104177736 A CN2011104177736 A CN 2011104177736A CN 201110417773 A CN201110417773 A CN 201110417773A CN 102557750 A CN102557750 A CN 102557750A
- Authority
- CN
- China
- Prior art keywords
- parts
- glaze
- formula
- matting
- calcite
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a formula of matt glaze. According to the formula, the matt glaze comprises the following components in part by weight: 20 to 30 parts of potash feldspar, 3 to 8 parts of kaolin, 3 to 8 parts of raw talc, 15 to 25 parts of dolomite, 1 to 5 parts of calcite, 30 to 50 parts of quartz, 5 to 10 parts of barium carbonate, and 3 to 8 parts of boric acid. The matt glaze is simple in formula and reasonable in proportioning; and the matt glaze which is prepared according to the formula is fine and smooth in glaze surface, good in handfeel, and high in whiteness; and production is easy to control.
Description
Technical field
The present invention relates to the prescription of a kind of pottery with the prescription, particularly a kind of matting glaze of glaze.
Background technology
Matting glaze is between a kind of special glaze that has between light glaze and the matt glaze.Matting glaze is different with transparent bright glaze, in groups small crystallization is embedded in the glass basis. and after being the complete fusion of glaze, the part of its composition is separated out the crystalline glaze in process of cooling. and knot article are very small and be well-regulated dispersion.The plain elegance of high-grade matting glaze, level and smooth mercerising, finger touch be like suet, seems satin, like thin,tough silk, and be white like VELVET, the dirt that bears dirty, and under same case, thermostability and ultimate compression strength are all good than common glaze.After the big area paving, aberration is little, whole structure good, under light-illuminating, sends the light of flicker, occupies body wherein. the sandy beach under the imitative lunar light, make the quiet serenity of people, and body and mind loosens, and is happy.
High-grade matting glaze product, the psychology of having catered to the human consumer with its distinctive decorative effect.Along with the continuous quickening of rhythm of life, people's body and mind of anxiety tired out of releiving of always wanting to have living space.Yet most matting glaze product on the market all belongs to hyaloplasmic alkaline matting glaze and high alumina matter matting glaze.Though the debugging of alkalescence matting glaze easily, color is white inadequately, does not reach velvety whiteness, and glaze texture is also bad, is prone to reveal the color of base substrate, seems high-grade inadequately.And high alumina matter matting glaze product glaze is fine and smooth inadequately, does not reach the feel as the suet, and produces bad control, and the firing temperature model is made pottery, and burns till matt glaze or bright glaze easily.
Summary of the invention
The object of the invention is the deficiency to prior art, and a kind of prescription of matting glaze is provided.
For addressing the above problem; The technical scheme that the present invention adopted is: a kind of prescription of matting glaze, it comprises the component of following parts by weight: 20 ~ 30 parts of potassium felspar sands, 3 ~ 8 parts of kaolin, 3 ~ 8 parts in living talcum, 15 ~ 25 parts of rhombspars, 1 ~ 5 part in calcite, 30 ~ 50 parts in quartz, 5 ~ 10 parts of barium carbonates, 3 ~ 8 parts of boric acid.
The prescription of said a kind of matting glaze comprises the component of following parts by weight: 10 ~ 20 parts of potassium felspar sands, 3 ~ 7 parts of kaolin, give birth to 3 ~ 6 parts in talcum, 15 ~ 20 parts of rhombspars, 1 ~ 4 part in calcite, quartzy 30-40 part, 3 ~ 8 parts of barium carbonates, 3 ~ 6 parts of boric acid.
The present invention with respect to the beneficial effect of prior art is: the prescription of matting glaze according to the invention is simple, and reasonable ratio adopts the present invention's prepared matting glaze that goes out of filling a prescription, and the product glaze is fine and smooth, good hand touch, and whiteness is high, produces easy to control.
Embodiment
Through embodiment the present invention is explained further details below, these embodiment only are used for explaining the present invention, do not limit the scope of the invention.
Embodiment 1Adopt following formulation matting glaze according to the invention: in the raw material of parts by weight: 20 parts of potassium felspar sands, 8 parts of kaolin, give birth to 4 parts in talcum, 15 parts of rhombspars, 1 part in calcite, quartzy 30 parts, 10 parts of barium carbonates, 8 parts of boric acid.
Embodiment 2Adopt following formulation matting glaze according to the invention: in the raw material of parts by weight: 10 parts of potassium felspar sands, 7 parts of kaolin, give birth to 56 parts in talcum, 17 parts of rhombspars, 4 parts in calcite, quartzy 40 parts, 8 parts of barium carbonates, 6 parts of boric acid.
Embodiment 3Adopt following formulation matting glaze according to the invention: in the raw material of parts by weight: 15 parts of potassium felspar sands, 5 parts of kaolin, give birth to 6 parts in talcum, 20 parts of rhombspars, 3 parts in calcite, quartzy 50 parts, 3 parts of barium carbonates, 5 parts of boric acid.
Embodiment 4Adopt following formulation matting glaze according to the invention: in the raw material of parts by weight: 30 parts of potassium felspar sands, 3 parts of kaolin, give birth to 8 parts in talcum, 25 parts of rhombspars, 5 parts in calcite, quartzy 35 parts, 5 parts of barium carbonates, 8 parts of boric acid.
Claims (2)
1. the prescription of a matting glaze is characterized in that: the component that comprises following parts by weight: 20 ~ 30 parts of potassium felspar sands, 3 ~ 8 parts of kaolin, 3 ~ 8 parts in living talcum, 15 ~ 25 parts of rhombspars, 1 ~ 5 part in calcite, 30 ~ 50 parts in quartz, 5 ~ 10 parts of barium carbonates, 3 ~ 8 parts of boric acid.
2. a kind of prescription of matting glaze according to claim 1 is characterized in that: the component that comprises following parts by weight: 10 ~ 20 parts of potassium felspar sands, 3 ~ 7 parts of kaolin, give birth to 3 ~ 6 parts in talcum, 15 ~ 20 parts of rhombspars, 1 ~ 4 part in calcite, quartzy 30-40 part, 3 ~ 8 parts of barium carbonates, 3 ~ 6 parts of boric acid.