CN109336390A - White is unglazed crystal glaze and its preparation process - Google Patents
White is unglazed crystal glaze and its preparation process Download PDFInfo
- Publication number
- CN109336390A CN109336390A CN201811536839.1A CN201811536839A CN109336390A CN 109336390 A CN109336390 A CN 109336390A CN 201811536839 A CN201811536839 A CN 201811536839A CN 109336390 A CN109336390 A CN 109336390A
- Authority
- CN
- China
- Prior art keywords
- parts
- glaze
- white
- unglazed
- component
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of unglazed crystal glaze of white and its preparation process, the component and each component mass parts in glaze used in crystal glaze that white is unglazed are as follows: 30~35 parts of potassium feldspar；14 parts~23 parts of dolomite；12 parts~16 parts of talcum；3 parts~6 parts of zinc oxide；6 parts~9 parts of barium carbonate；7 parts~11 parts of kaolin；13 parts~16 parts of zirconium silicate；10~15 parts of titanium oxide.Matt state is presented in glaze paint of the invention, and has good mobile performance.
Description
Technical field
The present invention relates to a kind of unglazed crystal glaze of white and its preparation processes.
Background technique
Currently, all kinds of furniture of life, day eats as enthusiasm of the people to the collection of different crystal glaze constantly increases
Tool all gradually level off to crystallite furnace transmutation glaze, need to develop a kind of glaze paint and matt state be presented, and there is good flowing
The crystal glaze of performance.
Summary of the invention
The technical problem to be solved by the present invention is to overcome the deficiencies of existing technologies, a kind of unglazed crystal glaze of white is provided,
Matt state is presented in its glaze paint, and has good mobile performance.
In order to solve the above technical problems, the technical scheme is that a kind of unglazed crystal glaze of white, used in it
Component and each component mass parts in glaze is as follows:
30~35 parts of potassium feldspar；14 parts~23 parts of dolomite；12 parts~16 parts of talcum；3 parts~6 parts of zinc oxide；Barium carbonate 6
Part~9 parts；7 parts~11 parts of kaolin；13 parts~16 parts of zirconium silicate；10~15 parts of titanium oxide.
The present invention also provides a kind of preparation process of unglazed crystal glaze of white, the step of technique in contain:
A) it stocks up according to each component and each component mass parts:
B) according to mass ratio=1 ︰ 1.6 ︰ 0.7 of Liao ︰ Qiu ︰ water, wet ball grinding 15~17 hours, the glaze mistake after ball milling
After 200 meshes, it is stand-by to be modulated into 51~53 Baume concentration, obtains glaze slip；
C) clean green body is taken, using glaze slip glazing.
D) base of first-class glaze is burnt into 1270 DEG C of drawer kiln.
After above-mentioned technical proposal, crystal glaze that the white is unglazed is fired by 1270 DEG C of high temperature, passes through crystallization
Reaction makes glaze paint that matt state be presented, and because the glaze has good mobile performance, makes 1/5th position of part in glaze paint
Present light state, lower part is piled into no light condition by white micro-crystals and forms a sharp contrast effect, deep by the majority of consumers
Favor.
Specific embodiment
In order that the present invention can be more clearly and readily understood, below according to specific embodiment, to the present invention make into
One step detailed description.
Comparative example one
A kind of unglazed crystal glaze of white, the component and each component mass parts in glaze used in it are as follows:
30 parts of potassium feldspar；14 parts of dolomite；12 parts of talcum；3 parts of zinc oxide；6 parts of barium carbonate；7 parts of kaolin；Zirconium silicate 13
Part；10 parts of titanium oxide；5 parts of rutile；
Contain in the step of preparation process for crystal glaze that the white is unglazed, technique:
A) it stocks up according to each component and each component mass parts:
B) according to 1.6 ︰ 0.7 of mass ratio=1 ︰ of Liao ︰ Qiu ︰ water, wet ball grinding 15 hours, the glaze after ball milling crossed 200 mesh
After sieve, it is stand-by to be modulated into 51~53 Baume concentration, obtains glaze slip；
C) clean green body is taken, using glaze slip glazing.
D) base of first-class glaze is burnt into 1270 DEG C of drawer kiln.
Comparative example two
A kind of unglazed crystal glaze of white, the component and each component mass parts in glaze used in it are as follows:
35 parts of potassium feldspar；23 parts of dolomite；16 parts of talcum；6 parts of zinc oxide；9 parts of barium carbonate；11 parts of kaolin；Zirconium silicate
16 parts；5 parts of titanium oxide.
Contain in the step of preparation process for crystal glaze that the white is unglazed, technique:
A) it stocks up according to each component and each component mass parts:
B) according to 1.6 ︰ 0.7 of mass ratio=1 ︰ of Liao ︰ Qiu ︰ water, wet ball grinding 17 hours, the glaze after ball milling crossed 200 mesh
After sieve, it is stand-by to be modulated into 51~53 Baume concentration, obtains glaze slip；
C) clean green body is taken, using glaze slip glazing.
D) base of first-class glaze is burnt into 1270 DEG C of drawer kiln.
Embodiment one
A kind of unglazed crystal glaze of white, the component and each component mass parts in glaze used in it are as follows:
30 parts of potassium feldspar；14 parts of dolomite；12 parts of talcum；3 parts of zinc oxide；6 parts of barium carbonate；7 parts of kaolin；Zirconium silicate 13
Part；10 parts of titanium oxide.
Contain in the step of preparation process for crystal glaze that the white is unglazed, technique:
A) it stocks up according to each component and each component mass parts:
B) according to 1.6 ︰ 0.7 of mass ratio=1 ︰ of Liao ︰ Qiu ︰ water, wet ball grinding 15 hours, the glaze after ball milling crossed 200 mesh
After sieve, it is stand-by to be modulated into 51~53 Baume concentration, obtains glaze slip；
C) clean green body is taken, using glaze slip glazing.
D) base of first-class glaze is burnt into 1270 DEG C of drawer kiln.
Embodiment two
A kind of unglazed crystal glaze of white, the component and each component mass parts in glaze used in it are as follows:
35 parts of potassium feldspar；23 parts of dolomite；16 parts of talcum；6 parts of zinc oxide；9 parts of barium carbonate；7 parts of kaolin；Zirconium silicate 16
Part；15 parts of titanium oxide.
Contain in the step of preparation process for crystal glaze that the white is unglazed, technique:
A) it stocks up according to each component and each component mass parts:
B) according to 1.6 ︰ 0.7 of mass ratio=1 ︰ of Liao ︰ Qiu ︰ water, wet ball grinding 17 hours, the glaze after ball milling crossed 200 mesh
After sieve, it is stand-by to be modulated into 51~53 Baume concentration, obtains glaze slip；
C) clean green body is taken, using glaze slip glazing.
D) base of first-class glaze is burnt into 1270 DEG C of drawer kiln.
Embodiment three
A kind of unglazed crystal glaze of white, the component and each component mass parts in glaze used in it are as follows:
32 parts of potassium feldspar；20 parts of dolomite；14 parts of talcum；5 parts of zinc oxide；8 parts of barium carbonate；9 parts of kaolin；Zirconium silicate 15
Part；13 parts of titanium oxide.
Contain in the step of preparation process for crystal glaze that the white is unglazed, technique:
A) it stocks up according to each component and each component mass parts:
B) according to 1.6 ︰ 0.7 of mass ratio=1 ︰ of Liao ︰ Qiu ︰ water, wet ball grinding 17 hours, the glaze after ball milling crossed 200 mesh
After sieve, it is stand-by to be modulated into 51~53 Baume concentration, obtains glaze slip；
C) clean green body is taken, using glaze slip glazing.
D) base of first-class glaze is burnt into 1270 DEG C of drawer kiln.
Comparative example one: crystal glaze that the white is unglazed, crystal effect force glaze paint that no light condition is presented comprehensively very much.
Comparative example two: crystal glaze that white is unglazed, crystal effect is weaker, has light and unglazed Contrast on effect not strong enough.
Embodiment one, embodiment two and embodiment three: matt state is presented in the glaze paint for crystal glaze that white is unglazed, and has
Good mobile performance, mobile performance make 1/5th position of part in glaze paint present light state, and lower part is by white micro-crystals heap
Product forms a sharp contrast effect at no light condition, meets design requirement.
Particular embodiments described above has carried out further in detail the purpose of the present invention, technical scheme and beneficial effects
It describes in detail bright, it should be understood that the above is only a specific embodiment of the present invention, is not intended to restrict the invention, it is all
Within the spirit and principles in the present invention, any modification, equivalent substitution, improvement and etc. done should be included in guarantor of the invention
Within the scope of shield.
Claims (2)
1. a kind of unglazed crystal glaze of white, it is characterised in that the component and each component mass parts in glaze used in it are as follows:
30~35 parts of potassium feldspar；14 parts~23 parts of dolomite；12 parts~16 parts of talcum；3 parts~6 parts of zinc oxide；6 parts of barium carbonate~
9 parts；7 parts~11 parts of kaolin；13 parts~16 parts of zirconium silicate；10~15 parts of titanium oxide.
2. a kind of preparation process of the unglazed crystal glaze of white as described in claim 1, it is characterised in that contain in the step of technique
Have:
A) it stocks up according to each component and each component mass parts:
B) according to 1.6 ︰ 0.7 of mass ratio=1 ︰ of Liao ︰ Qiu ︰ water, wet ball grinding 15~17 hours, the glaze after ball milling crossed 200 mesh
After sieve, it is stand-by to be modulated into 51~53 Baume concentration, obtains glaze slip；
C) clean green body is taken, using glaze slip glazing.
D) base of first-class glaze is burnt into 1270 DEG C of drawer kiln.