CN102555309A - Method for utilizing yellow paperboard to manufacture bent wood - Google Patents
Method for utilizing yellow paperboard to manufacture bent wood Download PDFInfo
- Publication number
- CN102555309A CN102555309A CN2010106192308A CN201010619230A CN102555309A CN 102555309 A CN102555309 A CN 102555309A CN 2010106192308 A CN2010106192308 A CN 2010106192308A CN 201010619230 A CN201010619230 A CN 201010619230A CN 102555309 A CN102555309 A CN 102555309A
- Authority
- CN
- China
- Prior art keywords
- utilizing
- paper
- yellow plate
- yellow paperboard
- make
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a method for utilizing a yellow paperboard to manufacture bent wood. The method comprises the following steps: placing the yellow paperboard between two polar plates of a working capacitor of a high-frequency oscillating circuit; applying a high-frequency voltage; softening the yellow paperboard by electrically heating; utilizing a mold or steel belt to press and bend the softened yellow paperboard into the required shape; and drying the yellow paperboard and fixing the shape. Compared with the prior art, the method provided by the invention has the advantages that the manufacturing of a high-curvature part is realized by utilizing the advantages of excellent toughness and high mechanical strength of the yellow paperboard and matching the bent wood forming technology, the processing of the high-curvature part is realized, parts are compactly arranged and are seamless, and the waterproof property of a cabinet is increased by utilizing a subsequent painting process.
Description
Technical field
The present invention relates to the method for a kind of Qu Mu of making, especially relate to a kind of method of utilizing yellow plate paper to make Qu Mu.
Background technology
In the manufacture craft of multilayer composite sheet, main raw material(s) is 2mm MDF, poplar plate etc.Usually, these raw materials can be supported the making of common product.But for some special products, for example the bigger parts of curvature in forming process, can cause fracture.Moreover, in the last handling process of paint, also can bring a lot of defectives, cause the water proofing property variation of product.
Summary of the invention
The object of the invention is exactly to provide a kind of processing of deep camber parts, yellow plate paper that utilizes of raising water proofing property can realized to make the method for Qu Mu for the defective that overcomes above-mentioned prior art existence.
The object of the invention can be realized through following technical scheme:
A kind of method of utilizing yellow plate paper to make Qu Mu; It is characterized in that; This method may further comprise the steps: Calusena lansium paper is placed between two pole plates of high-frequency oscillating circuits working capacitor, add high frequency voltage, through the softening Calusena lansium paper of electrical heating; Utilize mould or steel band will soften the shape that good Calusena lansium paper pressurization bends to requirement then, fixed in shape is got final product the yellow plate paper drying then.
The frequency of described high frequency voltage is 27～28MHZ.
The preferred 27.12MHZ of the frequency of described high frequency voltage.
The described electrically heated time is 5min, and pressurize 10min.
Its moisture content is 8～10wt% after the described yellow plate paper drying.
Compared with prior art, the present invention utilizes Calusena lansium paper good toughness, the mechanical strength advantages of higher, and cooperate bent wooden moulding process, and realize the making of deep camber parts, have the following advantages:
(1) can realize the processing of deep camber parts;
(2) tight, seamless between the parts, follow-up paint process, the water proofing property of raising cabinet.
The specific embodiment
Below in conjunction with specific embodiment the present invention is elaborated.
Embodiment
A kind of method of utilizing yellow plate paper to make Qu Mu, this method may further comprise the steps:
For the big parts of curvature, need use a kind of good toughness, the mechanical strength height and can be in hot press with high frequency material processed; Calusena lansium paper is placed between two pole plates of high-frequency oscillating circuits working capacitor, add high frequency voltage, the frequency of control high frequency voltage is 27～28MHZ; The frequency of the high frequency voltage that uses in the present embodiment is 27.12MHZ, and controlling the electrically heated time is 5min, and pressurize 10min; Thereby between the two poles of the earth, produce alternating electric field, under its effect, cause the polarization repeatedly of Calusena lansium paper interior molecules; Intermolecular generation strong friction so just becomes the electric energy that absorbs in the electromagnetic field into heat energy, thereby makes the thermoplastic of Calusena lansium paper.After thermoplastic is accomplished, the method for utilizing mould, steel band etc. to reach machinery by hand will be softened the shape that good Calusena lansium paper pressurization bends to requirement.Is 10wt% with the drying of wood under the case of bending to moisture content, and its flexural deformation is fixed up, and promptly accomplishes the making of Qu Mu.
Claims (5)
1. method of utilizing yellow plate paper to make Qu Mu; It is characterized in that; This method may further comprise the steps: Calusena lansium paper is placed between two pole plates of high-frequency oscillating circuits working capacitor, add high frequency voltage, through the softening Calusena lansium paper of electrical heating; Utilize mould or steel band will soften the shape that good Calusena lansium paper pressurization bends to requirement then, fixed in shape is got final product the yellow plate paper drying then.
2. a kind of method of utilizing yellow plate paper to make Qu Mu according to claim 1 is characterized in that the frequency of described high frequency voltage is 27～28MHZ.
3. a kind of method of utilizing yellow plate paper to make Qu Mu according to claim 2 is characterized in that the preferred 27.12MHZ of the frequency of described high frequency voltage.
4. a kind of method of utilizing yellow plate paper to make Qu Mu according to claim 1 is characterized in that the described electrically heated time is 5min, and pressurize 10min.
5. a kind of method of utilizing yellow plate paper to make Qu Mu according to claim 1 is characterized in that its moisture content is 8～10wt% after the described yellow plate paper drying.