CN102534136A - 高抗磨双金属复合热处理工艺 - Google Patents

高抗磨双金属复合热处理工艺 Download PDF

Info

Publication number
CN102534136A
CN102534136A CN2010105970114A CN201010597011A CN102534136A CN 102534136 A CN102534136 A CN 102534136A CN 2010105970114 A CN2010105970114 A CN 2010105970114A CN 201010597011 A CN201010597011 A CN 201010597011A CN 102534136 A CN102534136 A CN 102534136A
Authority
CN
China
Prior art keywords
hours
warming
incubated
furnace
uniform velocity
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN2010105970114A
Other languages
English (en)
Inventor
顾伟
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN2010105970114A priority Critical patent/CN102534136A/zh
Publication of CN102534136A publication Critical patent/CN102534136A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种高抗磨双金属复合热处理工艺，分三步来完成，1)消除应力：将工件匀称装炉，匀速升温至590℃±20℃，保温5小时，炉冷至200℃，出炉空冷；2)正火、淬火：将工件匀称装炉，匀速以30℃-60℃/h升温至630℃±20℃，保温2-4小时，再匀速以30℃/h升温至980℃±20℃，保温6小时，出炉强风淬火；3)回火：将工件匀称装炉，匀速升温至590℃±20℃，保温3小时，随炉冷却。本发明采用的上述工艺，使得双金属复合材料表面高铬铸铁的硬度可以达到HRC65-75，从而提高耐磨性能，延长使用寿命。

Description

高抗磨双金属复合热处理工艺
技术领域
本发明涉及一种热处理工艺领域，具体地说是一种高抗磨双金属复合热处理工艺。
背景技术
众所周知，为使金属工件具有所需要的力学性能、物理性能和化学性能，除合理选用材料和各种成形工艺外，热处理工艺往往是必不可少的。双金属复合材料一般在磨损严重或者腐蚀性的条件下工作，在一些承受高周疲劳的齿轮和轴类的零件中使用。因此，为了保证双金属复合材料具有良好的工作状态，理想的复合材料表面应具备高的耐磨损、耐腐蚀性能。而基体材料必须具有良好的韧性和塑性。目前，对于同样的双金属高铬铸铁复合材料，用标准的热处理工艺处理后，高铬铸铁的硬度为HRC55-62，还达不到理想要求参数。
发明内容
本发明的目的是提供一种高抗磨双金属复合热处理工艺，能够解决硬度不够以及耐磨性能不理想的技术问题。
本发明所需要解决的问题是通过如下的技术方案实现的：它分三步来完成，(1)消除应力：将工件匀称装炉，匀速升温至590℃±20℃，保温5小时，炉冷至200℃，出炉空冷；(2)正火、淬火：将工件匀称装炉，匀速以30℃-60℃/h升温至630℃±20℃，保温2-4小时，再匀速以30℃/h升温至980℃±20℃，保温6小时，出炉强风淬火；(3)回火：将工件匀称装炉，匀速升温至590℃±20℃，保温3小时，随炉冷却。
本发明采用的上述工艺，使得双金属复合材料表面高铬铸铁的硬度可以达到HRC65-75，从而提高耐磨性能，延长使用寿命。
具体实施方式
实施例一
1、消除应力：将工件匀称装炉，匀速升温至610℃，保温5小时，炉冷至200℃，出炉空冷；
2、正火、淬火：将工件匀称装炉，匀速以30℃/h升温至650℃，保温2小时，再匀速以30℃/h升温至1000℃，保温6小时，出炉强风淬火；
3、回火：将工件匀称装炉，匀速升温至610℃，保温3小时，随炉冷却。
实施例二
1、消除应力：将工件匀称装炉，匀速升温至590℃，保温5小时，炉冷至200℃，出炉空冷；
2、正火、淬火：将工件匀称装炉，匀速以50℃/h升温至630℃，保温3小时，再匀速以30℃/h升温至980℃，保温6小时，出炉强风淬火；
3、回火：将工件匀称装炉，匀速升温至590℃，保温3小时，随炉冷却。
实施例三
1、消除应力：将工件匀称装炉，匀速升温至570℃，保温5小时，炉冷至200℃，出炉空冷；
2、正火、淬火：将工件匀称装炉，匀速以60℃/h升温至610℃，保温4小时，再匀速以30℃/h升温至960℃，保温6小时，出炉强风淬火；
3、回火：将工件匀称装炉，匀速升温至570℃，保温3小时，随炉冷却。
本发明工艺可以得到韧性、抗磨性很高的产品，适合批量生产。
本发明的上述实施例仅仅是为清楚地说明本发明所作的举例，而并非是对本发明的实施方式的限定。对于所属领域的普通技术人员来说，在上述说明的基础上还可以做出其他不同形式的变化或变动。这里无需也无法对所有的实施方式予以穷举，而这些属于本发明的精神所引出的显而易见的变化或变动仍处于本发明的保护范围之中。

Claims (1)

1.一种高抗磨双金属复合热处理工艺，分三步来完成，其特征在于(1)消除应力：将工件匀称装炉，匀速升温至590℃±20℃，保温5小时，炉冷至200℃，出炉空冷；(2)正火、淬火：将工件匀称装炉，匀速以30℃-60℃/h升温至630℃±20℃，保温2-4小时，再匀速以30℃/h升温至980℃±20℃，保温6小时，出炉强风淬火；(3)回火：将工件匀称装炉，匀速升温至590℃±20℃，保温3小时，随炉冷却。
CN2010105970114A 2010-12-20 2010-12-20 高抗磨双金属复合热处理工艺 Pending CN102534136A (zh)