A kind of composite dissolving clean-out system and manufacture method thereof of calcic indissoluble solid
Technical field
The present invention relates to the solid waste clean-out system, particularly a kind of composite dissolving clean-out system and manufacture method thereof of calcic indissoluble solid.
Background technology
Because the solid of calcic is a kind of solid waste that very easily produces, the calcium sulfate class then is representative wherein, mainly be created in boiler use in, make in the foundry pattern, the medium all respects of Hospital medical, removing these materials then is to be difficult for very much.
Use mechanical means to damage easily main body, use hydrochloric acid then can produce potential hazard and very severe corrosive is arranged the user.Tradition solvating agent prescription is single and have dissolution rate slow, and the dissolving total amount is little, and the defective such as dissolution process easy to identify does not make it be subject in the use various restrictions, and function singleness.
Summary of the invention
The object of the present invention is to provide a kind of composite dissolving clean-out system and manufacture method thereof of calcic indissoluble solid, mainly solve above-mentioned the deficiencies in the prior art part, during use, not only can quicker more dissolving calcic indissoluble solid, and produce bubble solute is pushed away body surfaces, increase solute effect, more have the function that changes color; And the number of the color that changes and bubble can cooperate a kind of information that prompting user is in time changed the dissolving clean-out system that becomes.In dissolving main body is had cleanup action, and its environment-protecting asepsis, pH value are neutral, the body skin of not hurting sb.'s feelings uses safer.
For achieving the above object, the present invention realizes like this.
A kind of composite dissolving clean-out system of calcic indissoluble solid is characterized in that: it is comprised of the deionized water of 65 ~ 70wt%, the disodium ethylene diamine tetraacetate of 13 ~ 15wt%, the Trisodium Citrate of 10 ~ 11wt%, the sodium hydroxide of 1 ~ 1.5wt%, the whipping agent of 3 ~ 5wt%, the tensio-active agent of 1.5wt% and the color indicator of 1 ~ 1.5wt%.
The composite dissolving clean-out system of described calcic indissoluble solid is characterized in that: described whipping agent is one or both in yellow soda ash and the sodium bicarbonate.
The composite dissolving clean-out system of described calcic indissoluble solid is characterized in that: described tensio-active agent is one or more in sodium laurylsulfonate, Sodium dodecylbenzene sulfonate and the sodium lauryl sulphate.
The composite dissolving clean-out system of described calcic indissoluble solid is characterized in that: described color indicator is one or more the spirituous solution in toluylene red, phenol, reindeer moss, the methyl red.
A kind of preparation method of composite dissolving clean-out system of aforesaid calcic indissoluble solid, it is characterized in that: its step comprises: (A) base-material dissolving: by weight percentage disodium ethylene diamine tetraacetate, sodium hydroxide, whipping agent are mixed with deionized water, be stirred to that to become base-material after solution is clarified for subsequent use; (B) add Trisodium Citrate: in the base-material that has mixed, add by weight percentage Trisodium Citrate, be stirred to solution clarification and for subsequent use without bubble collapse; (C) add tensio-active agent: will be added into by weight percentage tensio-active agent by the solution that step B obtains, and slowly stir and avoid Bubble formation, extremely for subsequent use after the clarification; (D) adjust color: will be added into by weight percentage the color indicator by the solution that step C obtains, and slowly stir and avoid Bubble formation, to clarification.
The present invention has following apparent outstanding substance and remarkable advantage compared with prior art.
1, because the present invention uses disodium ethylene diamine tetraacetate and Trisodium Citrate compounded formula, therefore dissolves the gypsum total amount greater than the conventional gypsum solvating agent.
2, the dissolving clean-out system because of made of the present invention contains tensio-active agent and foaming ingredient, therefore can produce larger bubble, pushes solute open, and reduces surface tension and improve penetration degree, and dissolution rate is greatly improved than the conventional gypsum solvating agent
3, contain the colored indicator and can produce bubble because of the dissolving clean-out system of made of the present invention, so the user can decide when change clean-out system according to these two features, easy to use than the conventional gypsum solvating agent
4, therefore the prescription non-corrosiveness that adopts because of the present invention does not produce reaction, non-corrosiveness to plastics, metal.
5, because of the dissolving clean-out system pH value of made of the present invention 7 ~ 8 and do not contain toxic substance, so the user is in use safer and can not cause environmental pollution.
6, the dissolving clean-out system because of made of the present invention contains tensio-active agent, therefore can clean attaching surface in the process of dissolving, saves user's time and money.
7, because of the scrap build expense of the present invention without large-scale equipment or costliness, it is convenient to make simple production, therefore applicable to scale operation.
Embodiment
Embodiment 1: a kind of tooth section's calcic solid cleaner and preparation thereof.
A kind of tooth section calcic solid cleaner, it is by the deionized water of 70wt%, the disodium ethylene diamine tetraacetate of 13wt%, the Trisodium Citrate of 10wt%, the sodium hydroxide of 1wt%, the whipping agent of 3wt%, the color indicator of the tensio-active agent of 1.5wt% and 1.5wt% forms, and described whipping agent is that yellow soda ash and sodium bicarbonate respectively account for the 50wt% composition.Described tensio-active agent is that the 33.33wt% that respectively accounts in sodium laurylsulfonate, Sodium dodecylbenzene sulfonate and the sodium lauryl sulphate forms, and described color indicator is the spirituous solution composition that toluylene red, reindeer moss respectively account for 50wt%.
Preparation method's step of the said products is.
(A) base-material dissolving: by aforesaid weight percent disodium ethylene diamine tetraacetate, sodium hydroxide, whipping agent are mixed with deionized water, be stirred to that to become base-material after solution is clarified for subsequent use.
(B) add Trisodium Citrate: in the base-material that has mixed, add Trisodium Citrate by aforesaid weight percent, be stirred to solution clarification and for subsequent use without bubble collapse.
(C) add tensio-active agent: will be added into tensio-active agent by aforesaid weight percent by the solution that step B obtains, and slowly stir and avoid Bubble formation, extremely for subsequent use after the clarification.
(D) adjust color: will be added into the color indicator by aforesaid weight percent by the solution that step C obtains, and slowly stir and avoid Bubble formation, to clarification.
Other variation pattern as this example: described whipping agent can be in yellow soda ash and the sodium bicarbonate one or both.Described tensio-active agent is one or more compositions in sodium laurylsulfonate, Sodium dodecylbenzene sulfonate and the sodium lauryl sulphate.Described color indicator is one or more the spirituous solution in toluylene red, phenol, reindeer moss, the methyl red.
Embodiment 2, boiler calcic dirt solvating agent.
A kind of boiler calcic dirt solvating agent, it is by the deionized water of 65wt%, the disodium ethylene diamine tetraacetate of 15wt%, the Trisodium Citrate of 11wt%, the sodium hydroxide of 1.5wt%, the whipping agent of 5wt%, the color indicator of the tensio-active agent of 1.5wt% and 1wt% forms, and described whipping agent is that sodium bicarbonate forms.Described tensio-active agent is that the 50wt% that respectively accounts in Sodium dodecylbenzene sulfonate and the sodium lauryl sulphate forms, and the spirituous solution that described color indicator is phenol forms.
The variation pattern that this is routine and preparation process and embodiment 1 are basically identical, so repeat no more.
Being preferred embodiment of the present invention only in sum, is not to limit practical range of the present invention.Be that all equivalences of doing according to the content of the present patent application claim change and modification, all should be technology category of the present invention.