CN103614266B - Bubbling dissolving washing agent for alginate material and preparation method of bubbling dissolving washing agent - Google Patents
Bubbling dissolving washing agent for alginate material and preparation method of bubbling dissolving washing agent Download PDFInfo
- Publication number
- CN103614266B CN103614266B CN201310699193.XA CN201310699193A CN103614266B CN 103614266 B CN103614266 B CN 103614266B CN 201310699193 A CN201310699193 A CN 201310699193A CN 103614266 B CN103614266 B CN 103614266B
- Authority
- CN
- China
- Prior art keywords
- bubbling
- subsequent use
- washing agent
- dissolving
- gained
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention relates to a solid waste washing agent and in particular relates to a bubbling dissolving washing agent for an alginate material and a preparation method of the bubbling dissolving washing agent. The bubbling dissolving washing agent comprises the following components: 40.00wt% of potassium carbonate, 21.20wt% of polyethylene glycol 200, 20.00wt% of dipotassium tetraethylammonium oxalate, 10.00wt% of potassium bicarbonate, 4.87wt% of anhydrous ethanol, 2.00wt% of oxalic acid, 1wt% of sodium dodecyl sulfate, 0.8wt% of polyethylene glycol 6000 and 0.13% of water-soluble pigment. When in use, the bubbling dissolving washing agent is convenient and efficient and is capable of dissolving the alginate material quickly; bubbles are generated to push a solute to be away from the surface of a main body so as to increase dissolution effects. While dissolving, the bubbling dissolving washing agent has the effect of washing the main body, is nontoxic and environment-friendly, does not hurt human skins due to the neutral pH value, and is safe to use.
Description
Technical field
The present invention relates to solid waste clean-out system, particularly a kind of bubbling of alginate material dissolves clean-out system and manufacture method thereof.
Background technology
Because the various materials based on alginate are more and more wider in modern society's use range, traditional alginate material solvating agent, particularly liquor have inconvenience in transport and use procedure, easily leak.And it is all non-bubbling formula, and alveolately do not seethe and push away effect, clean rate is lower.
Summary of the invention
A kind of bubbling of alginate material is the object of the present invention is to provide to dissolve clean-out system and manufacture method thereof, mainly solve above-mentioned the deficiencies in the prior art part, during use, not only convenient and swift, alginate material can be dissolved rapidly, and produce bubble and solute is pushed away body surfaces, increase solute effect.While dissolving, have cleanup action to main body, and its environment-protecting asepsis, pH value are neutral, do not hinder human body skin, use safer.
For achieving the above object, the present invention realizes like this.
The bubbling of alginate material dissolves a clean-out system, it is characterized in that: it is made up of the salt of wormwood of 40.00wt%, the Macrogol 200 of 21.20wt%, the oxalic acid triethylammonium tetrakis dipotassium of 20.00wt%, 10.00wt% saleratus, 4.87wt% dehydrated alcohol, the oxalic acid of 2.00wt%, the sodium laurylsulfonate of 1wt%, the polyethylene glycol 6000 of 0.8wt%, the water colo(u)r of 0.13%.
The bubbling of alginate material as above dissolves a manufacture method for clean-out system, it is characterized in that: its step comprises:
(A) acid base-material is coated: by weight percentage by EDTA-2K, that oxalic acid puts into steeliness blender is for subsequent use, by weight percentage polyethylene glycol 6000 put into dehydrated alcohol and airtightly heat to 70 ~ 80 DEG C, after polyethylene glycol 6000 dissolves completely, the sealing of half solution is for subsequent use, second half solution is poured in stainless steel cask, turn on agitator stirs 30 minutes, and the acid base-material moisture sealed of gained is for subsequent use;
(B) alkaline base-material is coated: by weight percentage by salt of wormwood, that saleratus puts into steeliness blender is for subsequent use, to pour in stainless steel cask from second half polyoxyethylene glycol-ethanol solution of steps A gained, turn on agitator stirs 30 minutes, and gained alkalescence base-material moisture sealed is for subsequent use;
(C) auxiliary material mixing: by weight percentage sodium laurylsulfonate, water colo(u)r are put into polyoxyethylene glycol, for subsequent use after stirring;
(D) batch mixing: the base-material obtained by steps A, B is put into steeliness blender, after turn on agitator stirs 15 minutes, is evenly sprinkling upon step C gained auxiliary material on powder, and turn on agitator continues stirring 30 minutes, and gained compound is for subsequent use;
(E) stamping: step D gained compound is poured in sheet-punching machine, strike out sheet by the specification of the every sheet of 50g and both obtain finished product.
The present invention compared with prior art, has following apparent outstanding substance and remarkable advantage.
1, because the dissolving clean-out system made by the present invention contains tensio-active agent and foaming ingredient, therefore larger bubble can be produced, push solute open, and reduce surface tension raising penetration degree, the clean-out system of the more traditional alginate material of dissolution rate is greatly improved.
2, because the present invention uses EDTA-2K and oxalic acid compounded formula, the clean-out system of total amount much larger than traditional alginate material is therefore dissolved.
3, because the dissolving clean-out system made by the present invention is tablet, therefore produce, store in a warehouse, transport, use all comparatively convenient.
4, because of the formula non-corrosiveness that the present invention adopts, therefore reaction is not produced, non-corrosiveness to plastics, metal.
5, because the dissolving clean-out system pH value made by the present invention is 7 ~ 8 and not containing phosphorus, therefore user is in use safer and can not cause environmental pollution.
6, because the clean-out system made by the present invention contains tensio-active agent, therefore can carry out routine cleaning to attaching surface in the process of dissolving, save the time and money of user.
7, because the present invention is without the scrap build expense of large-scale equipment or costliness, make simple production convenient, be therefore applicable to scale operation.
Embodiment
Embodiment 1: a kind of bubbling of tooth family alginate material dissolves clean-out system and manufacture method thereof.
The bubbling of tooth family alginate material dissolves a clean-out system, it is characterized in that: it is made up of the salt of wormwood of 40.00wt%, the Macrogol 200 of 21.20wt%, the oxalic acid triethylammonium tetrakis dipotassium of 20.00wt%, 10.00wt% saleratus, 4.87wt% dehydrated alcohol, the oxalic acid of 2.00wt%, the sodium laurylsulfonate of 1wt%, the polyethylene glycol 6000 of 0.8wt%, the water colo(u)r of 0.13%.
Preparation method's step of the said products is.
(A) acid base-material is coated: by weight percentage by EDTA-2K, that oxalic acid puts into steeliness blender is for subsequent use, by weight percentage polyethylene glycol 6000 put into dehydrated alcohol and airtightly to heat to 70 ~ 80 DEG C.After polyethylene glycol 6000 dissolves completely, the sealing of half solution is for subsequent use, and second half solution is poured in stainless steel cask, and turn on agitator stirs 30 minutes, and the acid base-material moisture sealed of gained is for subsequent use.
(B) alkaline base-material is coated: by weight percentage by salt of wormwood, that saleratus puts into steeliness blender is for subsequent use, to pour in stainless steel cask from second half polyoxyethylene glycol-ethanol solution of steps A gained, turn on agitator stirs 30 minutes, and gained alkalescence base-material moisture sealed is for subsequent use.
(C) auxiliary material mixing: by weight percentage sodium laurylsulfonate, water colo(u)r are put into polyoxyethylene glycol, for subsequent use after stirring.
(D) batch mixing: the base-material obtained by steps A, B is put into steeliness blender, after turn on agitator stirs 15 minutes, is evenly sprinkling upon step C gained auxiliary material on powder, and turn on agitator continues stirring 30 minutes, and gained compound is for subsequent use.
(E) stamping: step D gained compound is poured in sheet-punching machine, strike out sheet by the specification of the every sheet of 50g and both obtain finished product.
Described water colo(u)r is applied as light green herein.
Be only preferred embodiment of the present invention in sum, be not used for limiting practical range of the present invention.Namely all equivalences done according to the content of the present patent application the scope of the claims change and modify, and all should be technology category of the present invention.
Claims (2)
1. the bubbling of alginate material dissolves a clean-out system, it is characterized in that: it is made up of the salt of wormwood of 40.00wt%, the Macrogol 200 of 21.20wt%, the EDTA-2K of 20.00wt%, 10.00wt% saleratus, 4.87wt% dehydrated alcohol, the oxalic acid of 2.00wt%, the sodium laurylsulfonate of 1wt%, the polyethylene glycol 6000 of 0.8wt%, the water colo(u)r of 0.13%.
2. the bubbling of alginate material as claimed in claim 1 dissolves a manufacture method for clean-out system, it is characterized in that: its step comprises:
(A) acid base-material is coated: by weight percentage by EDTA-2K, that oxalic acid puts into steeliness blender is for subsequent use, by weight percentage polyethylene glycol 6000 put into dehydrated alcohol and airtightly heat to 70 ~ 80 DEG C, after polyethylene glycol 6000 dissolves completely, the sealing of half solution is for subsequent use, second half solution is poured in stainless steel cask, turn on agitator stirs 30 minutes, and the acid base-material moisture sealed of gained is for subsequent use;
(B) alkaline base-material is coated: by weight percentage by salt of wormwood, that saleratus puts into steeliness blender is for subsequent use, to pour in stainless steel cask from second half polyoxyethylene glycol-ethanol solution of steps A gained, turn on agitator stirs 30 minutes, and gained alkalescence base-material moisture sealed is for subsequent use;
(C) auxiliary material mixing: by weight percentage sodium laurylsulfonate, water colo(u)r are put into polyoxyethylene glycol, for subsequent use after stirring;
(D) batch mixing: the base-material obtained by steps A, B is put into steeliness blender, after turn on agitator stirs 15 minutes, is evenly sprinkling upon step C gained auxiliary material on powder, and turn on agitator continues stirring 30 minutes, and gained compound is for subsequent use;
(E) stamping: step D gained compound is poured in sheet-punching machine, strike out sheet by the specification of the every sheet of 50g and both obtain finished product.