CN102532784A - 一种阻燃abs/pvc合金专用料 - Google Patents

一种阻燃abs/pvc合金专用料 Download PDF

Info

Publication number
CN102532784A
CN102532784A CN2010105990974A CN201010599097A CN102532784A CN 102532784 A CN102532784 A CN 102532784A CN 2010105990974 A CN2010105990974 A CN 2010105990974A CN 201010599097 A CN201010599097 A CN 201010599097A CN 102532784 A CN102532784 A CN 102532784A
Authority
CN
China
Prior art keywords
abs
flame
pvc
retardant
polyvinyl chloride
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN2010105990974A
Other languages
English (en)
Inventor
揣成智
刘宇
任秀龙
王月朗
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
DEHAO SUPERMICRO NEW MATERIALS Co Ltd TIANJIN
Original Assignee
DEHAO SUPERMICRO NEW MATERIALS Co Ltd TIANJIN
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by DEHAO SUPERMICRO NEW MATERIALS Co Ltd TIANJIN filed Critical DEHAO SUPERMICRO NEW MATERIALS Co Ltd TIANJIN
Priority to CN2010105990974A priority Critical patent/CN102532784A/zh
Publication of CN102532784A publication Critical patent/CN102532784A/zh
Pending legal-status Critical Current

Abstract

本发明是一种阻燃ABS/PVC合金专用料。其特征在于：采用先进的生产技术，将ABS、聚氯乙烯、稳定剂、阻燃剂、润滑剂、抗氧剂等组合在一起，制备出一种阻燃ABS/PVC合金材料。本发明所提供的阻燃ABS/PVC合金材料，具有优异的综合性能；其制品保持了ABS的机械强度，而且还显著提高了它的冲击韧性，并且赋予了较好的阻燃性。广泛适用于汽车仪表盘、计算机外壳、电视机、电话机及吸尘器壳体、电动工具壳体、办公用品及各种板、管型材等。

Description

一种阻燃ABS/PVC合金专用料
技术领域 本发明涉及高分子材料改性技术，尤其是制造阻燃ABS/PVC合金专用料的新技术。
背景技术 ABS树脂是橡胶质聚合物，具有良好的抗冲击性、耐热性以及良好的加工性，综合性能良好，是应用广泛的热塑性工程塑料之一。但是ABS树脂易燃，没有阻燃性，常常导致火灾事故，给人们带来生命财产损失，从而限制了其在一些领域的应用。
PVC树脂的突出优点是难燃性、耐磨性、抗化学腐蚀性、气体水汽低渗漏性好，综合机械性能好，其缺陷是热稳定性和抗冲击性较差。ABS树脂含有侧苯基、氰基和不饱和双键，与PVC有比较好的相容性。采用具有阻燃性的PVC与ABS进行共混，可提高ABS的冲击强度、耐化学腐蚀性，赋予阻燃性和抗静电性，降低成本。生成的ABS/PVC合金可同时具有优良的力学机械性能和阻燃性。ABS树脂与PVC的共混改性已成为ABS研究领域的一个活跃分支。
发明内容 本发明提供一种阻燃ABS/PVC合金专用料，它是由ABS；聚氯乙烯，即PVC；稳定剂；润滑剂；抗氧剂等组成。首先将计量好的PVC及其稳定剂搅拌混合，然后将混合料与计量好的ABS和其他助剂加入高速混合机中高速混合，直至均匀，再经双螺杆挤出造粒，制备出阻燃ABS/PVC合金。
具体实施方式
以下通过实施例进一步说明本发明：
实施例1：
阻燃ABS/PVC合金配方：(质量份)
  ABS   60
  PVC   40
  稳定剂Sb2O3   2.4
  阻燃剂CPE   10
  润滑剂(CaSt2)   1.5
  抗氧剂1010   0.5
将计量好的PVC及Sb2O3搅拌混合，然后将混合料与计量好的ABS、CPE、CaSt2、抗氧剂1010加入高速混合机中高速混合，直至均匀，再经双螺杆挤出造粒，挤出温度控制在170-180℃，制备出阻燃ABS/PVC合金。
其挤出成型工艺(温度℃)参数：
  1段   2段   3段   4段   5段   6段   模头
  温度，℃   165   170   170   175   175   180   175
实施例2：
阻燃ABS/PVC合金配方：(质量份)
  ABS   60
  PVC   40
  稳定剂(Ca/Zn羧酸盐)   4
  阻燃剂CPE   8
  润滑剂(石蜡)   2.5
  抗氧剂1010   0.5
将计量好的PVC及Ca/Zn羧酸盐搅拌混合，然后将混合料与计量好的ABS、CPE、石蜡、抗氧剂1010加入高速混合机中高速混合，直至均匀，再经双螺杆挤出造粒，挤出温度控制在170-180℃，制备出阻燃ABS/PVC合金。
其挤出成型工艺(温度℃)参数：
  1段   2段   3段   4段   5段   6段   模头
温度，℃ 165 170 170 175 175 180 175
本发明方法制成的阻燃ABS/PVC合金材料具有优异的性能，其性能指标如下：(1)缺口冲击强度/KJ/m2≥10；(2)断裂伸长率/％≥100；(3)氧指数/％≥30；(4)吸水率/％≤0.5；(5)拉伸强度/MPa≥50。
以上所述，仅是本发明的较佳实施例而已，并非对本发明作任何形式上的限制，凡是依据本发明的技术实质对以上实施例所作的任何简单修改、等同变化与修饰，均仍属于本发明技术方案的范围内。

Claims (2)

1.一种阻燃ABS/PVC合金，包括ABS；聚氯乙烯，即PVC；稳定剂；阻燃剂；润滑剂；抗氧剂等。其特征在于，ABS的重量分数为60；PVC的重量分数为30-40；稳定剂的重量分数为2-5；阻燃剂的重量分数为7-10；润滑剂的重量分数为1.5-2.5；抗氧剂的重量分数为0.5-1.0。
2.根据权利要求1所述的一种阻燃ABS/PVC合金的制备方法，其特征在于，双螺杆挤出机在生产制品时温度要控制在170℃-180℃之间。
CN2010105990974A 2010-12-21 2010-12-21 一种阻燃abs/pvc合金专用料 Pending CN102532784A (zh)