CN102531546A - Blank containing light calcium carbonate for vitrified tile - Google Patents
Blank containing light calcium carbonate for vitrified tile Download PDFInfo
- Publication number
- CN102531546A CN102531546A CN2011104178349A CN201110417834A CN102531546A CN 102531546 A CN102531546 A CN 102531546A CN 2011104178349 A CN2011104178349 A CN 2011104178349A CN 201110417834 A CN201110417834 A CN 201110417834A CN 102531546 A CN102531546 A CN 102531546A
- Authority
- CN
- China
- Prior art keywords
- parts
- calcium carbonate
- light calcium
- blank
- brick
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a blank containing light calcium carbonate for vitrified tiles, which comprises the following ingredients in parts by weight: 20-35 parts of albite, 1-3 parts of feldspar, 1-3 parts of light calcium carbonate, 2-8 parts of talc, 1-3 parts of potassium nitrate, 25-40 parts of kaolin, 30-45 parts of quartz, 5-10 parts of borax, 8-15 parts of iron trioxide, 2-5 parts of cobalt oxide, and 3-6 parts of manganese oxide. The formulation of the invention is obtained based on the improvement of the traditional formulation, the advantages of regular particle shape and small particle size of light calcium carbonate are combined, so that the vitrified tile made with the blank as raw material has less micropores and has the characteristics of high luminosity, high hardness, high wear-resistance and low water absorptivity.
Description
Technical field
The present invention relates to a kind of pottery and use blank, the vitreous brick that particularly contains light calcium carbonate is used blank, belongs to ceramic processing technique field.
Background technology
The vitreous brick is the brick of the surface of entire body adobe body through a kind of light of forming of polishing, belongs to a kind of of entire body brick, and in general, water-intake rate is lower than 0.5% pottery and is also referred to as the vitreous brick.The vitreous brick is to be fired according to a certain percentage by silica sand, mud to form; Economy-combat is polished bright but is not needed polishing then; The surface is smooth bright as glass-mirror; Be the hardest a kind of in all ceramic tiles, it all is superior to common ornamental brick, polished tile and general marble at aspects such as water-intake rate, straightness of sides, flexural strength, resistance to acids and basess.
Growing along with ceramic technology, in recent years, the vitreous brick of big specification has developed into the main flow of indoor decoration.This ceramic tile has the texture of lithotome, and it is low to have more high luminosity, high firmness, high abrasion, water-intake rate, advantages such as the few and multi-sizeization of aberration and rich color.The building of decorating with the ceramic tile paving has graceful more taste, can be with classic and modern fully inclusive and equitable.This HS, highdensity large-sized ceramic plate glass except that diversified variation is arranged in appearance, decorate and can play sound insulation, heat insulation effect on the wall outside the building, and it are lighter than marble; Quality even compact, high, the stable chemical performance of intensity, its good physical and chemical performance derives from its microtexture.
But because the vitreous brick all is to be burnt till through HTHP time property by native embryo earth material, some very small pore of the surface of brick, spot is infiltrated the brick body easily.General spread the vitreous brick after, be to the processing of waxing of brick face, polish after waxing for 3 times; Per 3 months later on or play wax half a year one time, if do not wax, water can infiltrate the brick body from brick face micropore so; If coloured water; Like soy sauce, ink, vegetable soup, tea etc., these color relations are stayed in the brick body after can infiltrating the brick face so, form ornamental slab for paving the floor.If do not wax, the gloss of brick face can become crow gradually, influences attractive in appearance.Therefore, the distinctive microvoid structure of vitreous brick is its critical defect.
Summary of the invention
The object of the invention is the deficiency to prior art; Provide a kind of vitreous brick that contains light calcium carbonate to use blank; Add light calcium carbonate in this blank formulation; Utilize the particle shape rule of light calcium carbonate powder, the advantage that particle diameter is little, make with this blank to be that the vitreous brick brick face micropore that comes out of raw material production is few, and have high luminosity, high firmness, high abrasion, characteristics that water-intake rate is low.
For addressing the above problem, the technical scheme that the present invention adopted is: the vitreous brick that contains light calcium carbonate is used blank, counts proportioning by following components by weight parts and processes: 20 ~ 35 parts of albites, 1 ~ 3 part of feldspar; Light calcium carbonate 1-3 part, 2 ~ 8 parts in talcum, 1 ~ 3 part in saltpetre; 25 ~ 40 parts of kaolin, quartzy 30 ~ 45 parts, 5 ~ 10 parts of boraxs; 8 ~ 15 parts of red oxide of iron, 2 ~ 5 parts of powder blues, 3 ~ 6 parts of manganese oxide.
The present invention with respect to the beneficial effect of prior art is: the vitreous brick that contains light calcium carbonate of the present invention is used blank; Its prescription is on the conventional formulation basis, to improve to obtain; In conjunction with the particle shape rule of light calcium carbonate powder, the advantage that particle diameter is little; Make with this blank to be that the vitreous brick brick face micropore that comes out of raw material production is few, and have high luminosity, high firmness, high abrasion, characteristics that water-intake rate is low.
Embodiment
Through embodiment the present invention is explained further details below, these embodiment only are used for explaining the present invention, do not limit the scope of the invention.
Embodiment 1The vitreous brick that contains light calcium carbonate is counted proportioning with blank by following components by weight parts and is processed: 20 parts of albites, 3 parts of feldspars, 1 part of light calcium carbonate, 2 parts in talcum; 2 parts in saltpetre, 40 parts of kaolin, quartzy 45 parts, 5 parts of boraxs; 11 parts of red oxide of iron, 5 parts of powder blues, 4 parts of manganese oxide.
Embodiment 2The vitreous brick that contains light calcium carbonate is counted proportioning with blank by following components by weight parts and is processed: 28 parts of albites, 1 part of feldspar, 3 parts of light calcium carbonates, 5 parts in talcum; 3 parts in saltpetre, 25 parts of kaolin, quartzy 35 parts, 9 parts of boraxs; 8 parts of red oxide of iron, 4 parts of powder blues, 3 parts of manganese oxide.
Embodiment 3The vitreous brick that contains light calcium carbonate is counted proportioning with blank by following components by weight parts and is processed: 35 parts of albites, 2 parts of feldspars, 2 parts of light calcium carbonates, 8 parts in talcum; 1 part in saltpetre, 35 parts of kaolin, quartzy 30 parts, 8 parts of boraxs; 15 parts of red oxide of iron, 2 parts of powder blues, 6 parts of manganese oxide.
Claims (1)
1. the vitreous brick that contains light calcium carbonate is used blank, it is characterized in that: count proportioning by following components by weight parts and process: 20 ~ 35 parts of albites, 1 ~ 3 part of feldspar; Light calcium carbonate 1-3 part, 2 ~ 8 parts in talcum, 1 ~ 3 part in saltpetre; 25 ~ 40 parts of kaolin, quartzy 30 ~ 45 parts, 5 ~ 10 parts of boraxs; 8 ~ 15 parts of red oxide of iron, 2 ~ 5 parts of powder blues, 3 ~ 6 parts of manganese oxide.