CN102515489A - 一种低辐射镀膜玻璃的钢化方法 - Google Patents
一种低辐射镀膜玻璃的钢化方法 Download PDFInfo
- Publication number
- CN102515489A CN102515489A CN2011103607489A CN201110360748A CN102515489A CN 102515489 A CN102515489 A CN 102515489A CN 2011103607489 A CN2011103607489 A CN 2011103607489A CN 201110360748 A CN201110360748 A CN 201110360748A CN 102515489 A CN102515489 A CN 102515489A
- Authority
- CN
- China
- Prior art keywords
- low
- coated glass
- tempering
- heat
- radiation coated
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开一种低辐射镀膜玻璃的钢化方法，其将低辐射镀膜玻璃的膜面朝向导热传动辊进行钢化，所述的导热传动辊的表面包设有软性导热材料以保护低辐射镀膜玻璃的膜面。本发明的钢化方法利用传动辊的传导传热补偿低辐射膜面从辐射传热中获得热量少的不足，使得玻璃两个表面达到受热均匀，从而很好地解决了低辐射镀膜玻璃在钢化加工过程中刚性变形的问题。
Description
技术领域
本发明涉及玻璃的钢化方法，特别是，涉及一种低辐射镀膜玻璃的钢化方法。
背景技术
传统技术中，在对低辐射镀膜玻璃进行钢化加工时，为了避免损坏膜面，采取膜面朝上（如附图1所示），即背向导热传动辊的方式进行钢化，这样，由于玻璃两表面对热辐射的吸收程度不一致、受热不均匀，导低辐射镀膜玻璃的刚性变形难以控制，造成不合格率较高。
发明内容
本发明的目的是提供一种对低辐射镀膜玻璃进行钢化加工的方法。
为解决上述技术问题，本发明采用如下技术方案：
一种低辐射镀膜玻璃的钢化方法，其将低辐射镀膜玻璃的低辐射膜面朝向导热传动辊进行钢化。
其中，所述的导热传动辊的表面包设有软性导热材料以保护低辐射镀膜玻璃的低辐射膜面。
本发明的有益效果是：利用传动辊的传导传热补偿低辐射膜面从辐射传热中获得热量少的不足，使得玻璃两个表面达到受热均匀，从而很好地解决了低辐射镀膜玻璃在钢化加工过程中刚性变形的问题。
附图说明
附图1为传统技术中对低辐射镀膜玻璃钢化加工的示意图；
附图2为本发明技术中对低辐射镀膜玻璃钢化加工的示意图。
附图中：1、玻璃本体；2、低辐射膜面；3、传动辊。
具体实施方式
下面结合附图所示的实施例对本发明的技术方案作以下详细描述：
如附图2所示，本发明的低辐射镀膜玻璃的钢化方法，其将低辐射镀膜玻璃的低辐射膜面2朝向导热传动辊3、玻璃本体1背向导热传动辊3而进行钢化，导热传动辊3的表面包设有软性导热材料以保护低辐射镀膜玻璃的低辐射膜面2。
本发明的钢化方法利用传动辊的传导传热补偿低辐射膜面从辐射传热中获得热量少的不足，使得玻璃两个表面达到受热均匀，从而很好地解决了低辐射镀膜玻璃在钢化加工过程中刚性变形的问题。
上述实施例只为说明本发明的技术构思及特点，其目的在于让熟悉此项技术的人士能够了解本发明的内容并据以实施，并不能以此限制本发明的保护范围。凡根据本发明精神所作的等效变化或修饰，都应涵盖在本发明的保护范围之内。
Claims (2)
1.一种低辐射镀膜玻璃的钢化方法，其特征在于：将低辐射镀膜玻璃的低辐射膜面朝向导热传动辊进行钢化。
2.根据权利要求1所述的一种低辐射镀膜玻璃的钢化方法，其特征在于：所述的导热传动辊的表面包设有软性导热材料以保护低辐射镀膜玻璃的低辐射膜面。