CN102504033A - 造纸用改性阳离子淀粉的制备方法 - Google Patents
造纸用改性阳离子淀粉的制备方法 Download PDFInfo
- Publication number
- CN102504033A CN102504033A CN2011103450567A CN201110345056A CN102504033A CN 102504033 A CN102504033 A CN 102504033A CN 2011103450567 A CN2011103450567 A CN 2011103450567A CN 201110345056 A CN201110345056 A CN 201110345056A CN 102504033 A CN102504033 A CN 102504033A
- Authority
- CN
- China
- Prior art keywords
- starch
- preparation
- water
- papermaking
- microwave
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及造纸设备,尤其涉及造纸设备中的成型网的结构。本发明的造纸成型网是以复数根棉质经线和棉质纬线平织法织造形成片状网带,且经线和纬线与在造纸机上使用时的运行方向是不相垂直或平行的;再利用接头工序,将片状网带变成无端环形网带;将形成的无端环形棉质网带浸入聚氨酯溶液,并烘干形成覆盖有聚氨酯包覆层的造纸成型网。本发明的造纸成型网用于造纸机上使用。
Description
技术领域
本发明涉及阳离子淀粉的制备工艺,尤其是应用于造纸行业的改性阳离子淀粉的制备工艺。
背景技术
阳离子淀粉是由淀粉与阳离子试剂反应制得的,它是一类很重要的淀粉衍生物,其实用性的关键正是在于它对带负电荷物质的亲和性,可应用于造纸,纺织,油田,粘合剂,采矿和化妆品等领域。
阳离子淀粉在造纸行业的最大的用途是利用其阳离子性和强粘结性在造纸时作内添加剂,能改善纸的耐破度,抗张力,耐折度,抗掉毛性等诸多物理性质,提高松香,矾士的施胶效果。纸浆中阳离子淀粉比率凝集固定了填料和细纤维,使纸的滤水性能良好,提高了纸的抄写速度,也大大有利于减少水质的污染。另外,阳离子淀粉对能制造出理想纸质的中性胶料中使用的烷基烯酮二聚物的乳化和固定也有效果,其在纸的表面施胶,涂布方面具有应用。
目前广泛采用的造纸用阳离子淀粉一般是带有叔铵盐或季铵盐基团的一类淀粉。这类阳离子淀粉的制备方法一般有:(1)水溶剂法:将糊化的淀粉溶液与阳离子化试剂反应制得阳离子淀粉糊的方法,淀粉水悬浮液与阳离子化试剂反应,经过过滤、洗涤、干燥制得粉状阳离子淀粉;(2)有机溶剂法:是淀粉用大量的水溶性有机溶剂(如乙醇、甲醇等)作为介质来合成阳离子淀粉的方法,需要使用大量有机溶剂,成本较高、安全性较差、需要大型反应容器;(3)干法:顾名思义就是无需大量水的条件下进行制备,阳离子化试剂不必精制,多余的醚化剂和副产物的沸点较低;以及(4)半干法:就是介于湿法(浆法)于干法直接的制备方法。
目前国内采用上述几种方法制备的同类产品普遍存在取代度低、增强效果不佳等缺点,不适合造纸工业应用。
发明内容
我公司经过优化生产工艺,提出一种造纸用改性阳离子淀粉的制备方法,其反应效率提高,降低了生产成本。
本发明的技术方案是:
造纸用改性阳离子淀粉的制备方法,包括步骤:
A,筛选:将淀粉原料经过过滤筛进行杂质晒除;
B,喷水:将经过筛除后的淀粉原料平铺,通过雾化喷头进行喷水,并定期用湿度计检测,直到淀粉原料的含水量介于在20%至30%为止;
C,搅拌调浆:将喷水处理后的淀粉原料加入调浆池内,加入定量的氯化钠后,通过调浆池上的搅拌机构进行搅拌成淀粉浆;
D,碱化:向淀粉浆内加入定量的氢氧化钠溶液进行碱化处理;
E,醚化:向碱化后的淀粉浆加入定量的季铵盐;
F,微波:将上述的淀粉浆置于微波装置内进行微波处理5-10分钟;
G,洗涤:置于洗涤器内进行洗涤;
H,干燥:置于烘干机内进行干燥。
进一步的,所述的步骤B中的喷水处理后的淀粉原料的含水量是23%。
进一步的,所述的步骤F中的微波处理的时间是8分钟。
本发明采用上述的制备方法,可以获得一种适合造纸用改性阳离子淀粉,该改性阳离子淀粉的粘度、溶解性、润胀性降低;并且其反应效率提高,降低了生产成本。
具体实施方式
现结合具体实施方式对本发明进一步说明。
实施例1:
该实施例的制备方法,包括步骤:
A,筛选:将淀粉原料经过过滤筛进行杂质晒除;
B,喷水:将经过筛除后的淀粉原料平铺,通过雾化喷头进行喷水,并定期用湿度计检测,直到淀粉原料的含水量介于在20%为止;
C,搅拌调浆:将喷水处理后的淀粉原料加入调浆池内,加入定量的氯化钠后,通过调浆池上的搅拌机构进行搅拌成淀粉浆;
D,碱化:向淀粉浆内加入定量的氢氧化钠溶液进行碱化处理;
E,醚化:向碱化后的淀粉浆加入定量的季铵盐;
F,微波:将上述的淀粉浆置于微波装置内进行微波处理10分钟;
G,洗涤:置于洗涤器内进行洗涤;
H,干燥:置于烘干机内进行干燥。
实施例2(优选实施例):
该实施例的制备方法,包括步骤:
A,筛选:将淀粉原料经过过滤筛进行杂质晒除;
B,喷水:将经过筛除后的淀粉原料平铺,通过雾化喷头进行喷水,并定期用湿度计检测,直到淀粉原料的含水量介于在23%为止;
C,搅拌调浆:将喷水处理后的淀粉原料加入调浆池内,加入定量的氯化钠后,通过调浆池上的搅拌机构进行搅拌成淀粉浆;
D,碱化:向淀粉浆内加入定量的氢氧化钠溶液进行碱化处理;
E,醚化:向碱化后的淀粉浆加入定量的季铵盐;
F,微波:将上述的淀粉浆置于微波装置内进行微波处理8分钟;
G,洗涤:置于洗涤器内进行洗涤;
H,干燥:置于烘干机内进行干燥。
实施例3:
该实施例的制备方法,包括步骤:
A,筛选:将淀粉原料经过过滤筛进行杂质晒除;
B,喷水:将经过筛除后的淀粉原料平铺,通过雾化喷头进行喷水,并定期用湿度计检测,直到淀粉原料的含水量介于在30%为止;
C,搅拌调浆:将喷水处理后的淀粉原料加入调浆池内,加入定量的氯化钠后,通过调浆池上的搅拌机构进行搅拌成淀粉浆;
D,碱化:向淀粉浆内加入定量的氢氧化钠溶液进行碱化处理;
E,醚化:向碱化后的淀粉浆加入定量的季铵盐;
F,微波:将上述的淀粉浆置于微波装置内进行微波处理5分钟;
G,洗涤:置于洗涤器内进行洗涤;
H,干燥:置于烘干机内进行干燥。
本发明的造纸用改性阳离子淀粉的制备方法中,步骤B的中淀粉原料的喷水控制的含水量和步骤F中微波处理时长是关键,对于改性阳离子淀粉的制备起到了关键性的作用。
尽管结合优选实施方案具体展示和介绍了本发明,但所属领域的技术人员应该明白,在不脱离所附权利要求书所限定的本发明的精神和范围内,在形式上和细节上可以对本发明做出各种变化,均为本发明的保护范围。
Claims (3)
1.造纸用改性阳离子淀粉的制备方法,其特征在于,包括步骤:
A,筛选:将淀粉原料经过过滤筛进行杂质晒除;
B,喷水:将经过筛除后的淀粉原料平铺,通过雾化喷头进行喷水,并定期用湿度计检测,直到淀粉原料的含水量介于在20%至30%为止;
C,搅拌调浆:将喷水处理后的淀粉原料加入调浆池内,加入定量的氯化钠后,通过调浆池上的搅拌机构进行搅拌成淀粉浆;
D,碱化:向淀粉浆内加入定量的氢氧化钠溶液进行碱化处理;
E,醚化:向碱化后的淀粉浆加入定量的季铵盐;
F,微波:将上述的淀粉浆置于微波装置内进行微波处理5-10分钟;
G,洗涤:置于洗涤器内进行洗涤;
H,干燥:置于烘干机内进行干燥。
2.根据权利要求1所述的造纸用改性阳离子淀粉的制备方法,其特征在于:所述的步骤B中的喷水处理后的淀粉原料的含水量是23%。
3.根据权利要求1所述的造纸用改性阳离子淀粉的制备方法,其特征在于:所述的步骤F中的微波处理的时间是8分钟。