CN102503206A - 废弃纤维再生混凝土制备方法 - Google Patents

废弃纤维再生混凝土制备方法 Download PDF

Info

Publication number
CN102503206A
CN102503206A CN2011103240573A CN201110324057A CN102503206A CN 102503206 A CN102503206 A CN 102503206A CN 2011103240573 A CN2011103240573 A CN 2011103240573A CN 201110324057 A CN201110324057 A CN 201110324057A CN 102503206 A CN102503206 A CN 102503206A
Authority
CN
China
Prior art keywords
concrete
discarded
fibre
reclaimed
waste fiber
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN2011103240573A
Other languages
English (en)
Inventor
周静海
孟宪宏
李婷婷
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Shenyang Jianzhu University
Original Assignee
Shenyang Jianzhu University
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Shenyang Jianzhu University filed Critical Shenyang Jianzhu University
Priority to CN2011103240573A priority Critical patent/CN102503206A/zh
Publication of CN102503206A publication Critical patent/CN102503206A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种废弃纤维再生混凝土制备方法，此项技术提供一种新型混凝土，在混凝土中添加再生混凝土骨料以及废弃纤维。在不改变混凝土强度及其他性能的情况下，对废弃纤维以及建筑废料进行重新利用。在混凝土中添加再生混凝土骨料和废弃纤维形成废弃纤维再生混凝土，其中再生混凝土骨料与混凝土的质量比为40%—60%，废弃纤维与再生混凝土的体积比为1%-3%。混凝土骨料为废弃的混凝土或废弃的砖石，废弃纤维为废地毯或废化纤。混凝土骨料为小于20毫米的块料，废弃废弃纤维为15-30毫米。可有效改善我国资源短缺的现状，节约资源，提高资源利用率。是我国新型建筑材料得到更好的发展。

Description

废弃纤维再生混凝土制备方法
技术领域
   本发明涉及建筑材料，具体的说是利用废弃纤维以及废弃混凝土作为骨料所
形成的一种新型混凝土材料废弃纤维再生混凝土制备方法。
背景技术
随着我国经济建设的发展，建筑垃圾的量逐步增多，建筑垃圾资源化不仅可以减少垃圾堆放带来的环境问题，也可以节约资源，因而建筑垃圾的有效处理显得尤为重要。建筑垃圾成分复杂，多数的建筑垃圾中都含有大量的废弃混凝土，国内外研究认为，用废弃混凝土做再生骨料是可行的。
众所周知混凝土拉伸强力低的内在原因是由于其内部存在疵点，韧性低，因此降低内部疵点的尺寸和数量可改善混凝土的韧性和抗拉伸性能。可通过在混凝土中掺入少量的短纤维以弥补内部疵点。这种纤维通常称为增强纤维。而每年在世界各地作为垃圾处理的大量纺织废料以及用弃的地毯、服装等纺织品中，有大多数为不可降解的丙纶、涤纶等，通常采用的填埋方法占用了大量土地资源，造成环境污染。而国内外研究表明，在混凝土中掺入再生纤维可以提高混凝土的抗拉性能及韧性。
由于再生骨料与天然骨料在性能上存在一定的差异，再生聚丙烯纤维也有一定疵点，但是若能找到再生骨料以及再生纤维的最佳掺入量则可以在改善混凝土力学性能的同时，达到节约资源、保护环境的目的。
发明内容
     本发明的目的是提供一种废弃纤维再生混凝土。它对废弃纤维以及建筑废料进行了充分的再利用。技术方案如下，在混凝土中添加再生混凝土骨料和废
弃纤维形成废弃纤维再生混凝土，其中再生混凝土骨料与混凝土的质量比为40%—60%，废弃纤维与再生混凝土的体积比为1%-3%。混凝土骨料为废弃的混凝土或废弃的砖石，废弃纤维为废地毯或废化纤。混凝土骨料为小于20毫米的块料，废弃废弃纤维为15——30毫米。
本发明的优点是，解决我国随经济发展而产生的建筑废料及大量的纺织废料这些垃圾所造成的问题，提供一种新的建筑材料，所形成的再生纤维再生混凝土在不降低混凝土强度以及其他性能的情况下，对废弃纤维以及建筑废料进行了充分的再利用。
具体实施方式
在混凝土中添加再生混凝土骨料，废弃纤维形成废弃纤维再生混凝土，其中再生混凝土骨料与混凝土的质量比为40%—60%，废弃纤维与再生混凝土的体积比为1%-3%。混凝土骨料为废弃的混凝土或废弃的砖石，废弃纤维为废地毯或废化纤。混凝土骨料为小于20毫米的块料，废弃废弃纤维为15——30毫米。
   本发明可在现场配置实施，也可配制好在到现场搅拌。

Claims (3)

1.废弃纤维再生混凝土制备方法，其特征在于：在混凝土中添加再生混凝土骨料和废弃纤维形成废弃纤维再生混凝土，其中再生混凝土骨料与混凝土的质量比为40%—60%，废弃纤维与再生混凝土的体积比为1%-3%。
2.根据权利要求1所述的废弃纤维再生混凝土制备方法，其特征在于：混凝土骨料为废弃的混凝土或废弃的砖石，废弃纤维为废地毯或废化纤。
3.根据权利要求1所述的废弃纤维再生混凝土制备方法，其特征在于：混凝土骨料为小于20毫米的块料，废弃废弃纤维为15——30毫米。
CN2011103240573A 2011-10-24 2011-10-24 废弃纤维再生混凝土制备方法 Pending CN102503206A (zh)