CN102492358A - Thermo-setting transfer mould release agent and method for preparing and using same - Google Patents
Thermo-setting transfer mould release agent and method for preparing and using same Download PDFInfo
- Publication number
- CN102492358A CN102492358A CN2011103592958A CN201110359295A CN102492358A CN 102492358 A CN102492358 A CN 102492358A CN 2011103592958 A CN2011103592958 A CN 2011103592958A CN 201110359295 A CN201110359295 A CN 201110359295A CN 102492358 A CN102492358 A CN 102492358A
- Authority
- CN
- China
- Prior art keywords
- transfer printing
- agent
- parting agent
- fluorocarbon resin
- thermosetting transfer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention provides a thermo-setting transfer mould release agent. The thermo-setting transfer mould release agent comprises polyisocyanates and an ingredient, wherein the ingredient comprises the following components in part by weight: 15 to 45 parts of fluorocarbon resin, 2 to10 parts of polytetrafluoroethylene micro powder, 40 to 62 parts of C4-C8 alkane, 0.2 to 0.5 part of antifoaming agent, 1 to 3 parts of flatting agent, 1 to 5 parts of release auxiliaries, and 1 to 4 parts of flatting silica, wherein the weight ratio of the polyisocyanates to the fluorocarbon resin is 1 to 8. and the method for preparing and using the mould release agent is as follows: adding the fluorocarbon resin while agitating the C4-C8 alkane and the polytetrafluoroethylene; adding the antifoaming agent, the flatting agent, the release auxiliaries and the flatting silica, and then agitating the mixture; and, regulating the weight ratio of the fluorocarbon resin to the polyisocyanates in the product to be 8 to 1. The acquired mould release agent is coated on a PET (Polymer) film by a mesh plate and then dried for the use. The mould release agent is not transferred after being transfer-printed, so that the performances of the printing oil are not affected; the bottom film has no change after transfer-printing, and the friction resistant and solvent resistant performances are very good.
Description
Technical field
The present invention relates to a kind of transfer printing parting agent, be specifically related to a kind of thermosetting transfer printing parting agent and preparation and method of use.
Background technology
Hot transfer printing parting agent in the market mainly is resinous type and wax type.Hot transfer printing parting agent grammar in use is: heat transfer film disengaging carrier thin film under heat and pressure, more securely transfer printing on stock.
The wax parting agent is the most a kind of parting agent of purposes.But the part wax in the wax parting agent can move with pattern, and fused wax can be penetrated in the printing ink, thereby influences color.Therefore not good in the tack of pet sheet face, and also not anti-solvent.In transfer process, temperature is too high or mistake is low all can be to the pattern generating influence of transfer printing.It is poor that many resin type parting agents are laid property, and release layer takes place crisply firmly after the film forming, only is suitable for the transfer of hard surface.And the not anti-solvent of resin type parting agent, not good in the tack of pet sheet face yet.In the silk-screen process, because the influence of scraper plate and solvent, if chromatography too much will seriously have influence on the transfer printing effect.
In view of this, the inventor develops a kind of thermosetting transfer printing parting agent and preparation and method of use on the basis through a series of research and test, and this case produces thus.
Summary of the invention
To the deficiency of prior art, the invention provides a kind of thermosetting transfer printing parting agent.This parting agent is no any migration after transfer printing, can not influence the performance of printing ink.Counterdie no change after the transfer printing, and rub resistance and solvent resistance are all splendid.
For achieving the above object, the present invention realizes through following technical scheme:
A kind of thermosetting transfer printing parting agent, it comprises:
POLYMETHYLENE POLYPHENYLISOCYANATE; And a composition, it is composed of the following components by weight:
Fluorocarbon resin 15-35, ptfe micropowder 2-10, C
4-C
8Alkane 40-62,
Skimmer 0.2-0.5, flow agent 1-3, peel off auxiliary agent 1-5, flatting silica 1-4;
POLYMETHYLENE POLYPHENYLISOCYANATE is 1:8 with the ratio of the weight of fluorocarbon resin.
The wherein above-mentioned auxiliary agent of peeling off is a modified silicon oil.
Wherein the solid content of above-mentioned fluorocarbon resin is 15%-35% by weight percentage.
Wherein above-mentioned skimmer is silicone based skimmer.
Wherein above-mentioned flatting silica is a silicon-dioxide.
Wherein above-mentioned flow agent is a polysiloxane-polyether copolymer.
The wherein above-mentioned auxiliary agent of peeling off is the wax powder.
The present invention also provides a kind of method for preparing thermosetting transfer printing parting agent, and this method may further comprise the steps:
(a) with C
4-C
8Alkane and ptfe micropowder stirring and evenly mixing, stirring velocity are 300-400 rev/min;
(b) under condition of stirring, add fluorocarbon resin, stirring velocity is 300-400 rev/min, mixes;
(c) add respectively again skimmer, flow agent, peel off auxiliary agent and flatting silica, control stirring velocity be 500-600 rev/min, stirred 15 minutes;
(d) step (b) component that obtains and the component that step (c) obtains are allocated in proportion, allotment is 8:1 with the ratio of controlling the fluorocarbon resin that contains in the product and the weight of POLYMETHYLENE POLYPHENYLISOCYANATE, mixes then and obtains thermosetting transfer printing parting agent; Thermosetting transfer printing parting agent used within 20 hours.
The present invention further provides a kind of method of using thermosetting transfer printing parting agent, and this method may further comprise the steps:
(a) with C
4-C
8Alkane and ptfe micropowder stirring and evenly mixing, stirring velocity are 300-400 rev/min;
(b) under condition of stirring, add fluorocarbon resin, stirring velocity is 300-400 rev/min, mixes;
(c) add respectively again skimmer, flow agent, peel off auxiliary agent and flatting silica, control stirring velocity be 500-600 rev/min, stirred 15 minutes;
(d) step (b) component that obtains and the component that step (c) obtains are allocated in proportion, allotment is 8:1 with the ratio of controlling the fluorocarbon resin that contains in the product and the weight of POLYMETHYLENE POLYPHENYLISOCYANATE, mixes then and obtains thermosetting transfer printing parting agent; Thermosetting transfer printing parting agent used within 20 hours;
(e) the thermosetting transfer printing type parting agent that step (b) is prepared uses 300-350 order web plate to be coated on the PET film, 100-130 ℃ of control oven for drying temperature, and drying rate 30-40 rice/minute.
Beneficial effect of the present invention is mainly reflected in following two aspects:
(1) dicing film that solidify to form of the thermosetting transfer printing parting agent of the present invention preparation has excellent solvent resistance and crocking resistance, and can reuse;
(2) in the use of thermosetting transfer printing parting agent, no matter be to adopt heat to tear or cold tearing, the pattern of its transfer all there is not disadvantageous effect, can protect pattern muchly.
Embodiment
A kind of thermosetting transfer printing parting agent, it comprises:
POLYMETHYLENE POLYPHENYLISOCYANATE; And a composition, it is composed of the following components by weight:
Fluorocarbon resin 15-35, ptfe micropowder 2-10, C
4-C
8Alkane 40-62,
Skimmer 0.2-0.5, flow agent 1-3, peel off auxiliary agent 1-5, flatting silica 1-4;
POLYMETHYLENE POLYPHENYLISOCYANATE is 1:8 with the ratio of the weight of fluorocarbon resin.
Embodiment 1:
Count by weight: get 22 parts of fluorocarbon resins, 60.7 parts of C
4-C
8Alkane, 10 parts of ptfe micropowders, 0.3 part of skimmer, 2 parts of flow agents are peeled off auxiliary agent for 3 parts, 2 parts of flatting silicas.Above mixture of ingredients is labeled as the A component;
POLYMETHYLENE POLYPHENYLISOCYANATE (MDI) is labeled as the B component.POLYMETHYLENE POLYPHENYLISOCYANATE is 1:8 with the ratio of the weight of fluorocarbon resin, and promptly POLYMETHYLENE POLYPHENYLISOCYANATE is 2.75 parts;
Prepare thermosetting transfer printing parting agent according to following steps:
A) with C
4-C
8Alkane, ptfe micropowder are poured in the bucket, low speed 300-400 rev/min, stir;
B) under condition of stirring, add fluorocarbon resin in the agitation vat, rotating speed 300-400 rev/min, stir;
C) in bucket, add skimmer, flow agent respectively, peel off auxiliary agent and flatting silica, rotating speed 500-600 rev/min, stirred 15 minutes, can obtain the A component;
D) parting agent AB component is stirred earlier before using, by weight fluorocarbon resin: POLYMETHYLENE POLYPHENYLISOCYANATE=8:1 mixed re-uses after evenly, and the product that allotment is good must use up within 20 hours;
E) use the coating of 300-350 order web plate, the bake out temperature of drying tunnel is 100-130 ℃, and speed is 30-40m/min;
In the present embodiment, peeling off auxiliary agent is modified silicon oil, and skimmer is silicone based skimmer, and flatting silica is a silicon-dioxide, and flow agent is a polysiloxane-polyether copolymer, and peeling off auxiliary agent is the wax powder;
Thermosetting transfer printing parting agent property in the present embodiment is the preferable embodiment of performance.In use, no matter be to adopt heat to tear or cold tearing, the pattern that shifts all there is not disadvantageous effect, can protect pattern muchly.
Embodiment 2:
Count by weight: get 30 parts of fluorocarbon resins, 53.7 parts of C
4-C
8Alkane, 10 parts of ptfe micropowders, 0.3 part of skimmer, 2 parts of flow agents are peeled off auxiliary agent for 3 parts, 1 part of flatting silica.Above mixture of ingredients is labeled as the A component;
POLYMETHYLENE POLYPHENYLISOCYANATE (MDI) is labeled as the B component.POLYMETHYLENE POLYPHENYLISOCYANATE is 1:8 with the ratio of the weight of fluorocarbon resin, and promptly POLYMETHYLENE POLYPHENYLISOCYANATE is 3.75 parts;
Prepare thermosetting transfer printing parting agent according to the step among the embodiment 1;
In the present embodiment, peeling off auxiliary agent is modified silicon oil, and skimmer is silicone based skimmer, and flatting silica is a silicon-dioxide, and flow agent is a polysiloxane-polyether copolymer, and peeling off auxiliary agent is the wax powder;
The dicing film that the thermosetting transfer printing parting agent of present embodiment preparation solidify to form has excellent solvent resistance and crocking resistance, and can reuse.
Embodiment 3:
Count by weight: get 35 parts of fluorocarbon resins, 51.5 parts of C
4-C
8Alkane, 6 parts of ptfe micropowders, 0.5 part of skimmer, 2 parts of flow agents are peeled off auxiliary agent for 3.5 parts, 1.5 parts of flatting silicas.Above mixture of ingredients is labeled as the A component;
B component: 4.375 parts of POLYMETHYLENE POLYPHENYLISOCYANATE (MDI);
Prepare thermosetting transfer printing parting agent according to the step among the embodiment 1;
In the present embodiment, peeling off auxiliary agent is modified silicon oil, and skimmer is silicone based skimmer, and flatting silica is a silicon-dioxide, and flow agent is a polysiloxane-polyether copolymer, and peeling off auxiliary agent is the wax powder;
The dicing film that the thermosetting transfer printing parting agent of present embodiment preparation solidify to form has excellent solvent resistance and crocking resistance, and can reuse.
Embodiment 4:
Count by weight: get 25.8 parts of fluorocarbon resins, 62 parts of C
4-C
8Alkane, 5 parts of ptfe micropowders, 0.2 part of skimmer, 2 parts of flow agents are peeled off auxiliary agent for 3 parts, 2 parts of flatting silicas.Above mixture of ingredients is labeled as the A component;
B component: 3.225 parts of POLYMETHYLENE POLYPHENYLISOCYANATE (MDI).
Prepare thermosetting transfer printing parting agent according to the step among the embodiment 1.
In the present embodiment, peeling off auxiliary agent is modified silicon oil, and skimmer is silicone based skimmer, and flatting silica is a silicon-dioxide, and flow agent is a polysiloxane-polyether copolymer, and peeling off auxiliary agent is the wax powder.
No matter the thermosetting transfer printing parting agent of present embodiment preparation is to adopt heat to tear or cold tearing in the use of thermosetting transfer printing parting agent, and the pattern of its transfer is not all had disadvantageous effect, can protect pattern muchly.
The variation that is appreciated that a lot of details is possible, but therefore this do not run counter to scope of the present invention and spirit, and the those of ordinary skill of any affiliated technical field all should be regarded as not breaking away from the category of patent of the present invention to its suitable variation of doing.
Claims (9)
1. thermosetting transfer printing parting agent, it comprises:
POLYMETHYLENE POLYPHENYLISOCYANATE; And a composition, it is composed of the following components by weight:
Fluorocarbon resin 15-35, ptfe micropowder 2-10, C
4-C
8Alkane 40-62,
Skimmer 0.2-0.5, flow agent 1-3, peel off auxiliary agent 1-5, flatting silica 1-4;
POLYMETHYLENE POLYPHENYLISOCYANATE is 1:8 with the ratio of the weight of fluorocarbon resin.
2. thermosetting transfer printing parting agent according to claim 1, the wherein said auxiliary agent of peeling off is a modified silicon oil.
3. thermosetting transfer printing parting agent according to claim 1, wherein the solid content of institute's fluorocarbon resin is 15%-35% by weight percentage.
4. thermosetting transfer printing parting agent according to claim 1, wherein said skimmer is silicone based skimmer.
5. thermosetting transfer printing parting agent according to claim 1, wherein said flatting silica is a silicon-dioxide.
6. thermosetting transfer printing parting agent according to claim 1, wherein said flow agent is a polysiloxane-polyether copolymer.
7. thermosetting transfer printing parting agent according to claim 1, the wherein said auxiliary agent of peeling off is the wax powder.
8. the method for preparing the said thermosetting transfer printing of claim 1 parting agent is characterized in that this method may further comprise the steps:
(a) with C
4-C
8Alkane and ptfe micropowder stirring and evenly mixing, stirring velocity are 300-400 rev/min;
(b) under condition of stirring, add fluorocarbon resin, stirring velocity is 300-400 rev/min, mixes;
(c) add respectively again skimmer, flow agent, peel off auxiliary agent and flatting silica, control stirring velocity be 500-600 rev/min, stirred 15 minutes;
(d) step (b) component that obtains and the component that step (c) obtains are allocated in proportion, allotment is 8:1 with the ratio of controlling the fluorocarbon resin that contains in the product and the weight of POLYMETHYLENE POLYPHENYLISOCYANATE, mixes then and obtains thermosetting transfer printing parting agent; Thermosetting transfer printing parting agent used within 20 hours.
9. use the method for the said thermosetting transfer printing of claim 1 parting agent, it is characterized in that this method may further comprise the steps:
(a) with C
4-C
8Alkane and ptfe micropowder stirring and evenly mixing, stirring velocity are 300-400 rev/min;
(b) under condition of stirring, add fluorocarbon resin, stirring velocity is 300-400 rev/min, mixes;
(c) add respectively again skimmer, flow agent, peel off auxiliary agent and flatting silica, control stirring velocity be 500-600 rev/min, stirred 15 minutes;
(d) step (b) component that obtains and the component that step (c) obtains are allocated in proportion, allotment is 8:1 with the ratio of controlling the fluorocarbon resin that contains in the product and the weight of POLYMETHYLENE POLYPHENYLISOCYANATE, mixes then and obtains thermosetting transfer printing parting agent; Thermosetting transfer printing parting agent used within 20 hours;
(e) the thermosetting transfer printing type parting agent that step (b) is prepared uses 300-350 order web plate to be coated on the PET film, 100-130 ℃ of control oven for drying temperature, and drying rate 30-40 rice/minute.