CN102491650A - Mineral oil composite emulsifier and preparation method thereof - Google Patents
Mineral oil composite emulsifier and preparation method thereof Download PDFInfo
- Publication number
- CN102491650A CN102491650A CN2011104228899A CN201110422889A CN102491650A CN 102491650 A CN102491650 A CN 102491650A CN 2011104228899 A CN2011104228899 A CN 2011104228899A CN 201110422889 A CN201110422889 A CN 201110422889A CN 102491650 A CN102491650 A CN 102491650A
- Authority
- CN
- China
- Prior art keywords
- parts
- tensio
- add
- mineral oil
- emulsification still
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to the technical field of glass cotton production, in particular a mineral oil composite emulsifier and a preparation method thereof. The mineral oil composite emulsifier comprises the following components in part by weight: 50 to 80 parts of bright oil, 10 to 20 parts of oleic acid, 20 to 40 parts of triethanolamine, 20 to 50 parts of sodium dodecyl benzene sulfonate, 10 to 40 parts of surfactant and 60 to 80 parts of distilled water. The mineral oil composite emulsifier mainly solves the technical problem that much silicon dioxide dust is easily generated in the production process of the glass and the glass cotton product, and can soften glass fibre and greatly reduce the silicon dioxide dust in the air.
Description
Technical field
The present invention relates to the glass wool production technical field, particularly a kind of MO compound emulsifying agent and method of manufacture thereof.
Background technology
Be easy to generate a large amount of silica dusts in glass, glass wool production of articles process; The dust of silicon-dioxide is superfine; Specific surface area reaches 100 ㎡/g above (available Brunauer-En-met-Teller is that the low temperature conditioning adsorption method is measured); The long-term dust that contains silicon-dioxide that sucks of people can be suspended in the air, if will be suffered from silicosis.Silicosis is a kind of occupational illness, its generation and severity, the content of silicon-dioxide and the time that contacts with the people etc. in the content that depends on dust in the air and the dust.The amount that contains free silica in the dust is big more, causes that then pathology is serious more, and pathological development speed is fast more.Even patient breaks away from the dust work place, pathology also can continue development.
Summary of the invention
The object of the present invention is to provide a kind of MO compound emulsifying agent and method of manufacture thereof; Mainly the existing glass of solution, glass wool production of articles process are easy to generate the technical problem of a large amount of silica dusts; Its ability ability soften glass fiber significantly reduces airborne silica dust.
For realizing above-mentioned purpose, the present invention realizes like this.
A kind of MO compound emulsifying agent is characterized in that: it according to the composition of parts by weight is: 50~80 parts of bright stocks, 10~20 parts of oleic acid; 20~40 parts of trolamines; 20~50 parts of X 2073es, 10~40 parts in tensio-active agent, 60~80 parts of zero(ppm) water.
Described MO compound emulsifying agent is characterized in that: described tensio-active agent is OP seven tensio-active agents, OP nine tensio-active agents, OP 12 tensio-active agents, or wherein one or both or be above mixture.
A kind of method of manufacture of aforesaid MO compound emulsifying agent is characterized in that: its process step is, A, oleic acid, tensio-active agent added in the emulsification still, and mixing stirs; B, in the emulsification still, add trolamine, stir, C, in the emulsification still, add X 2073, add bright stock again, stirred 1 hour; D, in the emulsification still, add zero(ppm) water and stirred 1 hour, get product after mixing.
The advantage that prescription of the present invention and method can embody is:
MO compound emulsifying agent of the present invention is oleic acid, trolamine, X 2073 three's a synthetic oil-in-water emulsion; Easily and the aqueous adhesive of the use in the glass wool production process miscible; Oil pole in the MO compound emulsifying agent is prone to be adsorbed onto fiberglass surfacing; And ability soften glass fiber, significantly reduce airborne silica dust.
Embodiment
Embodiment 1:A, 10 parts of oleic acid, tensio-active agent are added in the emulsification still for 10 parts, mixing stirs; B, in the emulsification still, add 20 parts of trolamines, stir, C, in the emulsification still, add 20 parts of X 2073es, add 50 parts of bright stocks again, stirred 1 hour; D, in the emulsification still, add 60 parts of zero(ppm) water, stirred 1 hour, get product after mixing.
Embodiment 2:A, 15 parts of oleic acid, tensio-active agent are added in the emulsification still for 25 parts, mixing stirs; B, in the emulsification still, add 30 parts of trolamines, stir, C, in the emulsification still, add 35 parts of X 2073es, add 65 parts of bright stocks again, stirred 1 hour; D, in the emulsification still, add 70 parts of zero(ppm) water, stirred 1 hour, get product after mixing.
Embodiment 3:A, 20 parts of oleic acid, tensio-active agent are added in the emulsification still for 40 parts, mixing stirs; B, in the emulsification still, add 40 parts of trolamines, stir, C, in the emulsification still, add 50 parts of X 2073es, add 80 parts of bright stocks again, stirred 1 hour; D, in the emulsification still, add 80 parts of zero(ppm) water, stirred 1 hour, get product after mixing.
Through detecting; The MO compound emulsifying agent that above-mentioned each embodiment disposed, miscible tackiness agent sprays in the glass surface fiber in glass wool goods manufacturing processed, and it can the soften glass fiber; Reduce airborne silica dust greatly; Improve work situation, improve glass wool production scene workers health degree, reduce silicosis to a greater degree and take place.
Being merely preferred embodiment of the present invention in sum, is not to be used for limiting practical range of the present invention.Be that all equivalences of doing according to the content of claim of the present invention change and modification, all should be technological category of the present invention.
Claims (3)
1. MO compound emulsifying agent, it is characterized in that: it according to the composition of parts by weight is: 50~80 parts of bright stocks, 10~20 parts of oleic acid; 20~40 parts of trolamines; 20~50 parts of X 2073es, 10~40 parts in tensio-active agent, 60~80 parts of zero(ppm) water.
2. MO compound emulsifying agent according to claim 1 is characterized in that: described tensio-active agent is OP seven tensio-active agents, OP nine tensio-active agents, OP 12 tensio-active agents, or wherein one or both or be above mixture.
3. the method for manufacture of a MO compound emulsifying agent according to claim 1 or claim 2 is characterized in that: its process step is, A, oleic acid, tensio-active agent added in the emulsification still, and mixing stirs; B, in the emulsification still, add trolamine, stir, C, in the emulsification still, add X 2073, add bright stock again, stirred 1 hour; D, in the emulsification still, add zero(ppm) water and stirred 1 hour, get product after mixing.