CN102490227A - Preparation process for mould-proof bamboo floor boards - Google Patents
Preparation process for mould-proof bamboo floor boards Download PDFInfo
- Publication number
- CN102490227A CN102490227A CN2011103952050A CN201110395205A CN102490227A CN 102490227 A CN102490227 A CN 102490227A CN 2011103952050 A CN2011103952050 A CN 2011103952050A CN 201110395205 A CN201110395205 A CN 201110395205A CN 102490227 A CN102490227 A CN 102490227A
- Authority
- CN
- China
- Prior art keywords
- mildew
- resistant
- bamboo
- mould
- hot
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a preparation process for mould-proof bamboo floor boards, which belongs to the field of bamboo floor board preparation and comprises steps of bamboo chip forming, mould prevention, dry sizing, hot forming and post treatment. The preparation process is characterized in that boards are treated by mould prevention and dried after the step of hot forming is finished, and specifically boards after hot pressed are soaked in mould-proof soup at the temperature of 20 DEG C to 35 DEG C for 20 minutes to 50 minutes and dried in kilns. The preparation process has the advantages of being excellent in mould prevention effect, durable in mould prevention action, simple in manufacture process and the like.
Description
Skill
Technical field
The present invention relates to a kind of bamboo floor preparation method, be specifically related to the preparation technology on a kind of mildew-resistant bamboo floor.
Background technology
The bamboo floor is a kind of new decorative material for building, and it is a raw material with natural high-quality bamboo, through twenties procedures, sloughs the former juice of bamboo, pieces together through HTHP and presses, and again through 3 layers of paint, last infrared baking forms.
China's bamboo resource is very abundant, and annual production accounts for about 1/ 3 of the world.Because bamboo wood internal starch, carbohydrate, protein content are all high than timber; And fiber is vertically arranged, thereby in the use of storage, processing and the bamboo product of bamboo wood, more be prone to produce than timber go mouldy, brown stain and being damaged by worms; Influenced the attractive in appearance and service life of bamboo product; Institutional framework is changed, and related characteristics also will change, and reduce greatly even will lose like hardness, intensity and workability.For improving the quality of bamboo product, bamboo wood is handled extremely important.Thereby research bamboo wood anti-corrosion characteristic and aseptic technic thereof are alleviated the timber imbalance between supply and demand and are all had crucial meaning to rationally, utilize bamboo timber resource efficiently.
Domestic research and the report of aspect the bamboo wood mildew-resistant, having, the means of defence of bamboo product mainly is divided into two big types: one is the physics method, like Infrared Heating method, steam method, baking, microwave method, supercritical ultrasonics technology etc.; Two is chemical method, be with chemical agent killing insect that has had in the bamboo wood and the domestomycetes that has infected effectively, but also can protect bamboo wood no longer to be corroded by the bacterium worm.The major advantage of physics method is that toxicity is low, and environmental pollution is little, but sterilization worm weak effect; The chemical method protection effect is good, and the term of validity is long, does not damage the physicochemical characteristics of bamboo wood, is prone to toxigenicity and to the pollution problem of environment but shortcoming is a chemical agent.Different with mould inhibitor, treatment process etc. because of the bamboo wood handling property in practice, each is variant for anti-mold effect, and the problem that the bamboo wood mildew-resistant is handled in the production still remains to be furtherd investigate.
The bamboo floor is ground and the dado ornament materials of graceful building, but in production, warehousing and use generation going mouldy and damage by worms in various degree, influence outward appearance, cause damage.Therefore, be necessary that the bamboo flooring board is carried out mildew-resistant to be handled to improve the performance and the value on bamboo floor.
Summary of the invention
The purpose of this invention is to provide and a kind ofly can play mildew-proof function, the simple mildew-resistant bamboo of manufacturing process flooring method better.
Above-mentioned technical purpose of the present invention is achieved through following technical scheme: the preparation technology on a kind of mildew-resistant bamboo floor; Comprise bamboo chip shaping, mildew-resistant and preservative treatment, dry applying glue, hot-forming and post-processing step; It is characterized in that: after the said hot-forming step plate is carried out mildew-resistant and dried, be specially with through hot-forming plate with the mildew-resistant soup 20
oC ~ 35
oKiln drying got final product after C soaked 20min ~ 50min down.
The component of said mildew-resistant soup is sodium chloride 3 ~ 5% by weight percentage, borax 1 ~ 3%, card pine 0.5% ~ 1%, excess water.
In sum, the present invention utilizes the method for pressurization to force anti-enzyme medicament to get into the bamboo wood histocyte, and it is good to have an anti-mold effect, and mildew-proof function is lasting, 5 all intact values 99%, and manufacturing process is simple, can improve advantages such as bamboo floor added value.
The specific embodiment
Below in conjunction with embodiment the present invention is done further explain.
Embodiment 1
The preparation technology on a kind of mildew-resistant bamboo floor; Comprise bamboo chip shaping, mildew-resistant and preservative treatment, dry applying glue, hot-forming and post-processing step; It is characterized in that: after the said hot-forming step plate is carried out mildew-resistant and dried, be specially with through hot-forming plate with the mildew-resistant soup 20
oKiln drying got final product after C soaked 20min down, and the component of used mildew-resistant soup is sodium chloride 3% by weight percentage, borax 5%, card pine 1%, excess water.
Embodiment 2
The preparation technology on a kind of mildew-resistant bamboo floor; Comprise bamboo chip shaping, mildew-resistant and preservative treatment, dry applying glue, hot-forming and post-processing step; It is characterized in that: after the said hot-forming step plate is carried out mildew-resistant and dried, be specially with through hot-forming plate with the mildew-resistant soup 35
oKiln drying got final product after C soaked 50min down, and the component of used mildew-resistant soup is sodium chloride 5% by weight percentage, borax 1%, card pine 0.5%, excess water.
Embodiment 3
The preparation technology on a kind of mildew-resistant bamboo floor; Comprise bamboo chip shaping, mildew-resistant and preservative treatment, dry applying glue, hot-forming and post-processing step; It is characterized in that: after the said hot-forming step plate is carried out mildew-resistant and dried, be specially with through hot-forming plate with the mildew-resistant soup 25
oKiln drying got final product after C soaked 35min down, and the component of used mildew-resistant soup is sodium chloride 5% by weight percentage, borax 3%, card pine 0.5%, excess water.
This specific embodiment only is to explanation of the present invention; It is not the restriction to invention; Those skilled in the art can make any modification to present embodiment as required after reading this specification, but as long as in claim scope of the present invention, all receive the protection of Patent Law.
Claims (2)
1. the preparation technology on a mildew-resistant bamboo floor; Comprise bamboo chip shaping, mildew-resistant and preservative treatment, dry applying glue, hot-forming and post-processing step; It is characterized in that: after the said hot-forming step plate is carried out mildew-resistant and dried; Being specially and will using the mildew-resistant soup through hot-forming plate is 0.2 ~ 0.4MPa at pressure, 20
oC ~ 35
oKiln drying got final product after C soaked 20 ~ 50min down.
2. according to the preparation method on the said a kind of mildew-resistant bamboo of claim 1 floor, it is characterized in that: the component of said mildew-resistant soup is sodium chloride 3 ~ 5% by weight percentage, borax 1 ~ 3%, card pine 0.5% ~ 1%, excess water.