CN102464967A - Adhesive for repairing stone surface and in the use of stone material repair method - Google Patents
Adhesive for repairing stone surface and in the use of stone material repair method Download PDFInfo
- Publication number
- CN102464967A CN102464967A CN201010543416XA CN201010543416A CN102464967A CN 102464967 A CN102464967 A CN 102464967A CN 201010543416X A CN201010543416X A CN 201010543416XA CN 201010543416 A CN201010543416 A CN 201010543416A CN 102464967 A CN102464967 A CN 102464967A
- Authority
- CN
- China
- Prior art keywords
- stone
- repairing
- tackiness agent
- adhesive
- repaired
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses an adhesive for repairing a stone surface and in the use of stone material repair method. The adhesive is prepared from the following raw materials in parts by weight: 30-50 parts of bees wax, 20-40 parts of rosin and 20-40 parts of aggregate. The method for repairing the stone surface by using the adhesive comprises the following steps of: (1) cleaning positions required to be repaired on the stone, drying and heating to 20-40 DEG C; (2) selecting a stone surface repairing adhesive of the same color and repairing the color of the stone to be repaired, and melting; (3) filling the stone required to be repaired with the molten adhesive; and (4) ironing and repairing. Due to the adoption of the technical scheme, the invention has the advantage that: stone surface repairing adhesives of different colors can be prepared by using stone powder of different colors to adapt to stone of different colors. The adhesive is made of natural components, and is free from toxic and side effects. Moreover, the adhesive is made of readily-available materials, and is low in cost. Places repaired with the adhesive are as hard as stone and are free from repairing marks.
Description
Technical field
The present invention relates to the tackiness agent that a kind of stone material is repaired, also relate to the method for use of this tackiness agent in stone material is repaired.
Background technology
At present, the unsaturated polyester tackiness agent is mainly used in the repairing on stone surface microfracture, ant road, and it is fast that this tackiness agent has curing speed, and the brushing performance is good, and characteristics such as low price are occupied suitable share on market; But its weak point is to solidify polishing back low in glossiness, and anti-yellowing property is poor, and cure shrinkage is big.Solvent benzol ethene toxicity is bigger, has limited its application.
Summary of the invention
The object of the invention just is to overcome above-mentioned deficiency a kind of tackiness agent of stone skin patching and method of use of repairing at stone material thereof of being used for is provided.
The object of the invention can be realized through following measure:
A kind of tackiness agent that is used for stone skin patching is processed by the raw material of following weight part: beeswax 30-50, rosin 20-40, aggregate 20-40.
The above-mentioned tackiness agent that is used for stone skin patching is made up of the raw material of following weight part: beeswax 35-45, rosin 25-35, aggregate 25-35.
The above-mentioned tackiness agent that is used for stone skin patching is processed by the raw material of following weight part: beeswax 40, rosin 30, aggregate 30.
On be set forth in the tackiness agent of stone skin patching, said aggregate is a stone flour.
The method of use of the tackiness agent of above-mentioned stone skin patching; (1). the position that stone material need be repaired is cleaned out oven dry, the 20-40 degree of heating; (2). select the stone skin patching tackiness agent identical for use according to the color of required repairing stone material with the stone material color; With its fusing, (3). the tackiness agent after will melting fills up the stone material that needs repairing, (4). and plate and repair.
The method of use of the tackiness agent of above-mentioned stone skin patching, step (1). the position that stone material need be repaired is cleaned out oven dry, 30 degree of heating.
Adopt technique scheme, the present invention has following advantage: be used for the tackiness agent of stone skin patching, can select the stone flour of different colours for use, make the tackiness agent of different colours, to adapt to the stone material of different colours.Because what this tackiness agent adopted all is natural component, has no side effect.And adhesive material of the present invention is easy to get, and is with low cost.Repair the local as hard as flint that repair good back with this tackiness agent, do not see the vestige of repairing.
Embodiment
Embodiment 1: a kind of tackiness agent that is used for stone skin patching, process by the raw material of following weight part: and beeswax 30kg, rosin 20kg, red stone flour 20kg evenly makes tackiness agent with these raw materials mix.
Embodiment 2: a kind of tackiness agent that is used for stone skin patching, process by the raw material of following weight part: and beeswax 35kg, rosin 25kg, red stone flour 25kg evenly makes tackiness agent with these raw materials mix.
Embodiment 3: a kind of tackiness agent that is used for stone skin patching, process by the raw material of following weight part: and beeswax 50kg, rosin 40kg, red stone flour 40kg evenly makes tackiness agent with these raw materials mix.
Embodiment 4: a kind of tackiness agent that is used for stone skin patching, process by the raw material of following weight part: and beeswax 30kg, rosin 20kg, white stone flour 20kg evenly makes tackiness agent with these raw materials mix.
Embodiment 5: a kind of tackiness agent that is used for stone skin patching, process by the raw material of following weight part: and beeswax 35kg, rosin 25kg, white stone flour 25kg evenly makes tackiness agent with these raw materials mix.
Embodiment 6: a kind of tackiness agent that is used for stone skin patching, process by the raw material of following weight part: and beeswax 50kg, rosin 40kg, white stone flour 40kg evenly makes tackiness agent with these raw materials mix.
Embodiment 7: a kind of tackiness agent that is used for stone skin patching, process by the raw material of following weight part: and beeswax 40kg, rosin 30kg, black stone flour 30kg evenly makes tackiness agent with these raw materials mix.
In the foregoing invention stone flour can also select green stone flour for use, unbutton or divest one's upper garment the colored stone powder, versicolor stone flour such as orange stone flour, yellow stone flour, cyan stone flour, blue colored stone powder, purple stone flour, to adapt to the stone material of different colours.
The method of use of the tackiness agent of above-mentioned stone skin patching; (1). the position that stone material need be repaired is cleaned out oven dry, the 20-40 degree of heating; (2). select the stone skin patching tackiness agent identical for use according to the color of required repairing stone material with the stone material color; With its fusing, (3). the tackiness agent after will melting fills up the stone material that needs repairing, (4). and plate and repair.
If the present invention selects for use beeswax to strengthen some tackiness agent in winter, if summer rosin and aggregate add more.
Claims (6)
1. tackiness agent that is used for stone skin patching, it is characterized in that: the raw material by following weight part is processed: beeswax 30-50, rosin 20-40, aggregate 20-40.
2. the tackiness agent that is used for the stone material repairing according to claim 1, it is characterized in that: the raw material by following weight part is formed: beeswax 35-45, rosin 25-35, aggregate 25-35.
3. the tackiness agent that is used for stone skin patching according to claim 2 is characterized in that: the raw material by following weight part is processed: beeswax 40, rosin 30, aggregate 30.
4. like each described tackiness agent that is used for stone skin patching among the claim 1-4, it is characterized in that: said aggregate is a stone flour.
5. like the method for use of the tackiness agent of each described stone skin patching among the claim 1-4; It is characterized in that: (1). the position that stone material need be repaired is cleaned out oven dry, the 20-40 degree of heating; (2). select the stone skin patching tackiness agent identical for use according to the color of required repairing stone material with the stone material color; With its fusing, (3). the tackiness agent after will melting fills up the stone material that needs repairing, (4). and plate and repair.
6. like the method for use of the tackiness agent of each described stone skin patching among the claim 1-4, it is characterized in that: (1). the position that stone material need be repaired is cleaned out oven dry, 30 degree of heating.