CN102464920A - 防霉抗菌涂料及制作方法 - Google Patents
防霉抗菌涂料及制作方法 Download PDFInfo
- Publication number
- CN102464920A CN102464920A CN2010105323947A CN201010532394A CN102464920A CN 102464920 A CN102464920 A CN 102464920A CN 2010105323947 A CN2010105323947 A CN 2010105323947A CN 201010532394 A CN201010532394 A CN 201010532394A CN 102464920 A CN102464920 A CN 102464920A
- Authority
- CN
- China
- Prior art keywords
- parts
- oxide
- chlorinated rubber
- mould proof
- tributyl
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种防霉抗菌涂料及制作方法,由氯化橡胶、磷酸三丁酯、200号溶剂油、氧化锌、三丁基氟化锡、双氧化锡、氧化亚铜、偏三甲苯、古马隆树脂经混合、研磨、过滤等步骤制成,所述涂料各组分的重量分数比为:氯化橡胶6-9份、磷酸三丁酯4-5份、200号溶剂油5-9份、氧化锌21-25份、三丁基氟化锡3-5份、双氧化锡1-2份、氧化亚铜25-28份、偏三甲苯20-25份、古马隆树脂3-6份。本发明提供的防霉抗菌涂料主要用作建筑涂料,具有防止藻类、霉菌及有机污物生成的作用,同时本发明还可用作船底的防污涂料。
Description
技术邻域
本发明涉及一种化工涂料,具体涉及一种一种防霉抗菌涂料及制作方法。
背景技术
在自然界中,细菌、霉菌、病毒等微生物分布很广,空气、水、土壤等自然环境中都大量存在,这些微生物通常会引起工业设备、建筑物发生腐蚀及霉化。
发明内容
发明目的:本发明的目的是为解决现有技术的不足,提供一种具有防止藻类、霉菌及有机污物生成的防霉抗菌涂料及制作方法。
本发明采用的技术方案:一种防霉抗菌涂料,由氯化橡胶、磷酸三丁酯、200号溶剂油、氧化锌、三丁基氟化锡、双氧化锡、氧化亚铜、偏三甲苯、古马隆树脂配制而成,所述涂料各组分的重量分数比为:
氯化橡胶6-9份
磷酸三丁酯4-5份
200号溶剂油5-9份
氧化锌21-25份
三丁基氟化锡3-5份
双氧化锡1-2份
氧化亚铜25-28份
偏三甲苯20-25份
古马隆树脂3-6份
一种防霉抗菌涂料的制作方法,其特征在于:所述的防霉抗菌涂料的的制作方法包括如下步骤:
1)在搅拌釜中先加入200号溶剂油5-9份、偏三甲苯20-25份、磷酸三丁酯4-5份,搅拌均匀后再加入氯化橡胶6-9份、古马隆树脂3-6份待氯化橡胶和古马隆树脂充分混匀后加入氧化锌21-25份、三丁基氟化锡3-5份、双氧化锡1-2份、氧化亚铜25-28份;
2)将搅拌釜内的混合原料送入研磨机研磨,再经过滤后即制得防霉抗菌涂料。
有益效果:本发明与现有技术相比,其显著优点是:本发明提供的防霉抗菌涂料主要用作建筑涂料,具有防止藻类、霉菌及有机污物生成的作用,同时本发明还可用作船底的防污涂料。
具体实施方式:
下面对本发明的实施例做详细说明。
实施例1
在搅拌釜中先加入200号溶剂油5千克、偏三甲苯20千克、磷酸三丁酯4千克,搅拌均匀后再加入氯化橡胶6千克、古马隆树脂3千克,待氯化橡胶和古马隆树脂充分混匀后加入氧化锌21千克、三丁基氟化锡3千克、双氧化锡1千克、氧化亚铜25千克;将搅拌釜内的混合原料送入研磨机研磨,再经过滤后即制得防霉抗菌涂料。
实施例2
在搅拌釜中先加入200号溶剂油7千克、偏三甲苯22千克、磷酸三丁酯4.5千克,搅拌均匀后再加入氯化橡胶6千克、古马隆树脂5千克,待氯化橡胶和古马隆树脂充分混匀后加入氧化锌23千克、三丁基氟化锡4千克、双氧化锡1.5千克、氧化亚铜27千克;将搅拌釜内的混合原料送入研磨机研磨,再经过滤后即制得防霉抗菌涂料。
实施例3
在搅拌釜中先加入200号溶剂油9千克、偏三甲苯25千克、磷酸三丁酯5千克,搅拌均匀后再加入氯化橡胶9千克、古马隆树脂6千克,待氯化橡胶和古马隆树脂充分混匀后加入氧化锌25千克、三丁基氟化锡5千克、双氧化锡2千克、氧化亚铜28千克;将搅拌釜内的混合原料送入研磨机研磨,再经过滤后即制得防霉抗菌涂料。
Claims (2)
1.一种防霉抗菌涂料,由氯化橡胶、磷酸三丁酯、200号溶剂油、氧化锌、三丁基氟化锡、双氧化锡、氧化亚铜、偏三甲苯、古马隆树脂配制而成,其特征在于:所述涂料各组分的重量分数比为:
氯化橡胶6-9份
磷酸三丁酯4-5份
200号溶剂油5-9份
氧化锌21-25份
三丁基氟化锡3-5份
双氧化锡1-2份
氧化亚铜25-28份
偏三甲苯20-25份
古马隆树脂3-6份
2.一种防霉抗菌涂料的制作方法,其特征在于:所述的防霉抗菌涂料的的制作方法包括如下步骤:
1)在搅拌釜中先加入200号溶剂油5-9份、偏三甲苯20-25份、磷酸三丁酯4-5份,搅拌均匀后再加入氯化橡胶6-9份、古马隆树脂3-6份,待氯化橡胶和古马隆树脂充分混匀后加入氧化锌21-25份、三丁基氟化锡3-5份、双氧化锡1-2份、氧化亚铜25-28份;
2)将搅拌釜内的混合原料送入研磨机研磨,再经过滤后即制得防霉抗菌涂料。