CN102433803A - 一种轻质玻璃棉毡的制备方法 - Google Patents

一种轻质玻璃棉毡的制备方法 Download PDF

Info

Publication number
CN102433803A
CN102433803A CN2011102901600A CN201110290160A CN102433803A CN 102433803 A CN102433803 A CN 102433803A CN 2011102901600 A CN2011102901600 A CN 2011102901600A CN 201110290160 A CN201110290160 A CN 201110290160A CN 102433803 A CN102433803 A CN 102433803A
Authority
CN
China
Prior art keywords
ultra
glass
preparation
fine
glass wool
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN2011102901600A
Other languages
English (en)
Inventor
陈照峰
徐滕州
李斌斌
王蕾
陈照海
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Nanjing University of Aeronautics and Astronautics
Original Assignee
Nanjing University of Aeronautics and Astronautics
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Nanjing University of Aeronautics and Astronautics filed Critical Nanjing University of Aeronautics and Astronautics
Priority to CN2011102901600A priority Critical patent/CN102433803A/zh
Publication of CN102433803A publication Critical patent/CN102433803A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种超细超轻玻璃棉毡的制备方法，具体步骤为：(1)将超细玻璃纤维送入打浆池内打浆分散，形成超细玻璃纤维浆料；(2)浆料由高压泵抽至热气流烘干炉道顶部，由V型喷料口喷出；(3)玻璃纤维降落过程中经高温除水和气流打散的作用，在热气流炉道内均匀下落；(4)纤维下落过程中，环形喷胶器在纤维表面喷洒粘结剂；(5)表面附有粘结剂的玻璃纤维飘落在成网帘上，在负压泵的作用下，形成玻璃棉预制毡；(6)玻璃棉预制毡经固化、裁切后形成超细超轻玻璃棉毡。该方法制备的玻璃棉毡不仅具有好的撕裂强度、高回弹性，同时玻璃棉毡的保温、隔音性能优异，容重为5kg/m3～10kg/m3。

Description

一种轻质玻璃棉毡的制备方法
技术领域
本发明涉及一种玻璃棉毡的制备方法，特别是涉及一种轻质玻璃棉毡的制备方法。
背景技术
玻璃棉毡是玻璃纤维在空间无序交错穿插，纤维呈无定向三维结构的微孔材料，纤维层内部结构呈曲折路径，孔隙尺寸小，孔隙率高达70％～80％。玻璃棉毡优异的结构，使得其具有良好的保温和隔音性能，被广泛应用于生化、机电、冶金、石油、化工、煤炭、建筑及交通行业，尤其适用于汽车、轮船、火车等箱体的夹层保温及消音系统。
美国专利US20040053031A1(公开日为2004年3月18日)公开了一种玻璃棉毡的制备方法，该方法是离心喷吹法生产的玻璃棉毡，该方法优点是玻璃棉毡撕裂强度大，回弹性较好；缺点是玻璃棉毡密度大，纤维分布不均匀，玻璃棉毡中会出现纤维“絮凝”现象，保温性能、隔音性能不理想。
2003年《玻璃纤维》第3期中“玻璃纤维保温过滤毡的开发与应用”一文提及到“耐高温针刺毡”玻璃棉制品，该玻璃棉制品的制备工艺为将短切玻璃纤维开松、梳理、成网后经针刺工艺处理，最后收卷成为玻璃纤维针刺毡。该工艺生产的玻璃棉毡使用温度较传统玻璃棉毡高，有机物和杂质含量低，但是该玻璃棉毡导热系数过大，为0.078W/m·K，容重过高，不适宜用于精密仪器保温领域。
发明内容
本发明要解决的技术问题是提供一种超细超轻玻璃棉毡的制备方法，该方法制备的玻璃棉毡不仅具有好的撕裂强度、高回弹性，同时玻璃棉毡的保温、隔音性能优异，容重可降至5kg/m3～10kg/m3，纤维分布均匀。本发明按图1表示，其中10是打浆池，20是超细玻璃纤维浆料，30是V型喷料口，40是热气流烘干炉道，50是高温气流喷口，60是环形喷胶器，70是负压泵，80是固化炉，90超细超轻玻璃棉毡。制备超细超轻玻璃棉毡的特征在于下述顺序的步骤：
(1)将一定量超细玻璃纤维送入打浆池10内打浆分散，打浆度为8°SR～10°SR，打浆池内液体料pH为3.0～3.5，分散后的玻璃纤维分布均匀，形成超细玻璃纤维浆料20。
(2)分散后的玻璃纤维浆料20，由高压泵抽至热气流烘干炉道40顶部，浆料由V型喷料口30喷出，浆料的喷射速度为3.5m/s～4.5m/s。
(3)玻璃纤维浆料20喷出后，经热气流烘干炉道40高温除水和气流打撒，热气流烘干炉道40高11.5米，上端口直径0.9米，下端口直径1.8米，高温气流喷口50位于热气流烘干炉道40中部，距离热气流烘干炉道上端口7米～7.5米，环形分布，喷口倾斜向上，热气流温度为200℃～400℃。玻璃纤维经高温除水和气流打撒的作用后，在热气流烘干炉道40内均匀下落。
(4)超细玻璃纤维在下落过程中，喷胶工艺由环形喷胶器60完成，环形喷胶器60位于高温气流喷口50下部，喷嘴压力为0.25MPa～0.3MPa，雾化风压力为0.08MPa～0.1MPa，流量为30kg/h～50kg/h。
(5)超细玻璃纤维飘落在成网帘上，负压泵位于成网帘下部，负压泵70、负压泵71、负压泵72的气压分别为0.3kPa～0.4kPa、0.5kPa～0.6kPa、0.6kPa～0.8kPa。超细玻璃纤维在负压泵的作用下，形成具有层状结构的超细超轻玻璃棉预制毡。
(6)预制毡在固化炉80内进行固化，固化温度为180℃～230℃，经裁切后得到尺寸稳定的超细超轻玻璃棉毡。
本发明提供的超细超轻玻璃棉毡制备方法有以下优点：
①超细超轻玻璃棉毡，容重轻，可降至5kg/m3～10kg/m3；②本专利提供方法制备的轻质棉毡，纤维分布均匀，不会发生纤维“絮凝”现象；③尺寸稳定，棉毡平整度优良。
具体实施方式
下面将结合附图对本发明做进一步的详细说明。
实施例一，本实施例是介绍轻质玻璃棉毡制作方法。本实施例按图2表示，其中10是打浆池，20是超细玻璃纤维浆料，30是V型喷料口，40是热气流烘干炉道，50是高温气流喷口，60是环形喷胶器，70是负压泵，80是固化炉，90超细超轻玻璃棉毡。其特征在于下述顺序的步骤：
(1)将一定量超细玻璃纤维送入打浆池10内打浆分散，打浆度为8°SR，打浆池内液体料pH为3.0，分散后的玻璃纤维分布均匀，形成超细玻璃纤维浆料20。
(2)分散后的玻璃纤维浆料20，由高压泵抽至热气流烘干炉道40顶部，浆料由V型喷料口30喷出，两个V型喷料口30向上倾斜，浆料的喷射速度为3.5m/s。
(3)超细玻璃纤维经热气流烘干炉道40高温除水和气流打撒，热气流烘干炉道40高11.5米，上端口直径0.9米，下端口直径1.8米，高温气流喷口50位于热气流烘干炉道40中部，距离热气流烘干炉道上端口7米～7.5米，环形分布，喷口倾斜向上，热气流温度为350℃。玻璃纤维浆料20经高温除水和气流打撒的作用后，飘落至成网帘。
(4)超细玻璃纤维在下落过程中，喷胶工艺由环形喷胶器60完成，环形喷胶器60位于高温气流喷口50下部，喷嘴压力为0.3MPa，雾化风压力为0.08MPa，流量为45kg/h。
(5)超细玻璃纤维飘落在成网帘上，负压泵位于成网帘下部，负压泵70、负压泵71、负压泵72的气压分别为0.3kPa、0.5kPa、0.8kPa。超细玻璃纤维在负压泵的作用下，形成具有层状结构的超细超轻玻璃棉预制毡。
(6)预制毡在固化炉80内进行固化，固化温度为200℃，经裁切后得到尺寸稳定的超细超轻玻璃棉毡。

Claims (7)

1.一种超细超轻玻璃棉毡的制备方法，其特征在于以下述顺序的步骤：
(1)将超细玻璃纤维送入打浆池内分散，形成超细玻璃纤维浆料。
(2)超细玻璃纤维浆料，由高压泵抽至热气流烘干炉道顶部。
(3)玻璃纤维经高温除水和气流打撒的作用，在热气流烘干炉道内飘落。
(4)超细玻璃纤维在下落过程中，环形喷胶器进行喷胶工艺。
(5)超细玻璃纤维飘落在成网帘上，在负压泵的作用下，形成具有层状结构的超细超轻玻璃棉预制毡。
(6)预制毡在固化炉内进行固化，然后进行裁切，得到尺寸稳定的超细超轻玻璃棉毡。
2.根据权利要求1所述的制备方法，其特征在于所述的纤维分散过程中，打浆度为8°SR～10°SR，打浆池内液体料pH为3.0～3.5。
3.根据权利要求1所述的制备方法，其特征在于所述的超细玻璃棉浆料喷射速度为3.5m/s～4.5m/s。
4.根据权利要求1所述的制备方法，其特征在于热气流烘干炉道高11.5米，上端口直径0.9米，下端口直径1.8米，高温气流喷口位于热气流烘干炉道中部，距离热气流烘干炉道上端口7米～7.5米，喷口倾斜向上，热气流温度为200℃～400℃。
5.根据权利要求1所述的制备方法，其特征在于环形喷胶器喷嘴压力0.25MPa～0.3MPa，雾化风压力0.08MPa～0.1MPa，流量30kg/h～50kg/h。
6.根据权利要求1所述的制备方法，其特征在于三个负压泵的气压分别为0.3kPa～0.4kPa、0.5kPa～0.6kPa、0.6kPa～0.8kPa。
7.根据权利要求1所述的制备方法，其特征在于固化温度为180℃～230℃。
CN2011102901600A 2011-09-28 2011-09-28 一种轻质玻璃棉毡的制备方法 Pending CN102433803A (zh)