CN102424559A - 海泡石改性泡沫水泥保温板材料 - Google Patents

海泡石改性泡沫水泥保温板材料 Download PDF

Info

Publication number
CN102424559A
CN102424559A CN201110279042XA CN201110279042A CN102424559A CN 102424559 A CN102424559 A CN 102424559A CN 201110279042X A CN201110279042X A CN 201110279042XA CN 201110279042 A CN201110279042 A CN 201110279042A CN 102424559 A CN102424559 A CN 102424559A
Authority
CN
China
Prior art keywords
sepiolite
foamed cement
warming plate
plate material
material according
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN201110279042XA
Other languages
English (en)
Other versions
CN102424559B (zh
Inventor
章书建
辛春华
李建华
阮丰乐
成时亮
程颐
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
HUNAN YINGSHUO BUILDING ENERGY-SAVING MATERIALS CO., LTD.
Original Assignee
SHANGHAI YINGSHUO POLYMERIC MATERIAL CO Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by SHANGHAI YINGSHUO POLYMERIC MATERIAL CO Ltd filed Critical SHANGHAI YINGSHUO POLYMERIC MATERIAL CO Ltd
Priority to CN 201110279042 priority Critical patent/CN102424559B/zh
Publication of CN102424559A publication Critical patent/CN102424559A/zh
Application granted granted Critical
Publication of CN102424559B publication Critical patent/CN102424559B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开一种海泡石改性泡沫水泥保温板材料，包括如下组分及重量百分比含量：胶凝材料70～80％、粉煤灰10～20％、海泡石5～10％、可再分散乳胶粉0.5～1.5％、减水剂0.2～0.4％、PP纤维0.1～0.2％、憎水剂0.15～0.2％、复合发泡剂<b/>0.45～0.6%。所述的复合发泡剂通过机械设备制得泡沫，所述泡沫体积为300L～450L。与现有技术相比，本发明的海泡石改性泡沫水泥保温板具有良好的抗压强度、耐水性能、保温性能及耐候效果。

Description

海泡石改性泡沫水泥保温板材料
技术领域
本发明涉及建筑保温材料，尤其涉及一种海泡石改性泡沫水泥保温板材料。
背景技术
近年来建筑外保温材料火灾，造成严重人员伤亡和财产损失，建筑易燃可燃外有机保温材料已成为一类新的火灾隐患，且有机保温材料耐候性差，体积稳定性不良，易老化，而无机保温材料有着很多优点，尤其是泡沫水泥保温板，强度高，保温隔热，耐候，施工较无机保温砂浆方便等优点，施工方法同有机保温板材一样，可与粘结砂浆、抹面胶浆及辅助材料一起形成保温隔热、防火抗裂、防水抗渗的保温体系。
但现在市场上的大部分泡沫水泥板存在强度低、不耐水、保温性能不佳等缺点。
发明内容
发明目的在于克服上述现有技术的不足而提供一种海泡石改性泡沫水泥保温板材料。本发明是改进配方的泡沫水泥保温板材，具有良好的抗压强度、耐水性能、保温性能及耐候效果。
本发明的目的是通过以下技术方案来实现的：
本发明涉及的海泡石改性泡沫水泥保温板材料，包括如下组分及重量百分比含量：
胶凝材料：               70～80％                       
粉煤灰：                 10～20％
海泡石：                  5～10％
可再分散乳胶粉：       0.5～1.5％
减水剂：               0.2～0.4％
PP纤维：               0.1～0.2％
憎水剂：              0.15～0.2％
复合发泡剂：           0.45～0.6%。
优选的，所述的复合发泡剂通过机械设备制得泡沫，所述泡沫体积为300L～450L。
优选的，所述的胶凝材料为52.5普通硅酸盐水泥。
优选的，所述的粉煤灰为2级或2级以上等级。
优选的，所述的海泡石为平均粒径为0.6mm～1mm的海泡石。
优选的，所述的可再分散乳胶粉为丙烯酸乳胶粉。
优选的，所述的减水剂为聚羧酸类减水剂。
优选的，所述的PP纤维为6mm规格的聚丙烯纤维。
优选的，所述的憎水剂为有机硅类憎水剂。
与现有技术相比，本发明具有如下有益效果：
1、本发明将海泡石用于泡沫水泥作为改性填充料，海泡石是一种具层链状结构的含水富镁硅酸盐黏土矿物，收缩率低，可塑性好，质轻比表面大,吸附性强；同时还具有脱色、隔热、绝缘、抗腐蚀、抗辐射及热稳定等性能；故将海泡石复合水泥发泡，成型后的板材具有很好的强度、保温隔热及耐候效果。
2、本发明同时利用丙烯酸乳胶粉对泡沫水泥进行改性，由于丙烯酸乳胶粉具有优越的耐水性和耐老化性能，可以保证低泡沫水泥保温板具有良好的耐水和耐候性能。
具体实施方式
下面对本发明的实施例作详细说明：本实施例在以本发明技术方案为前提下进行实施，给出了详细的实施方式和具体的操作过程，但本发明的保护范围不限于下述的实施例。
实施例1
本发明的海泡石改性泡沫水泥保温板材料，其组份及配比为，52.5普通硅酸盐（PO52.5）水泥：80%，粉煤灰（I级）：10%，海泡石（0.6mm）：7.1%，丙烯酸乳胶粉：1.5%，减水剂（聚羧酸类减水剂）：0.4%，PP纤维（6mm规格的聚丙烯纤维）：0.2%，憎水剂（有机硅类憎水剂）：0.2%，复合发泡剂：0.6%，将以上除复合发泡剂外的其他材料按水灰比0.6加入到水中搅拌均匀，再将上述复合发泡剂加入水中利用机械制得的泡沫450L，将泡沫倒入搅拌均匀的浆料中搅拌均匀，将搅拌好的液料倒入模具中成型。制得的保温板性能优良，其性能指标如表1所示。
表1
Figure 204663DEST_PATH_IMAGE001
实施例2
本发明的海泡石改性泡沫水泥保温板材料，其组份及配比为，PO52.5水泥：75%，粉煤灰（I级）：18.5%，海泡石（0.8mm）：5%，丙烯酸乳胶粉：0.5%，减水剂（聚羧酸类减水剂）：0.3%，PP纤维：0.1%，憎水剂：0.15%，复合发泡剂：0.45%，将以上除复合发泡剂外的其他材料按水灰比0.58加入到水中搅拌均匀，再将上述复合发泡剂加入水中利用机械制得的泡沫350L，将泡沫倒入搅拌均匀的浆料中搅拌均匀，将搅拌好的液料倒入模具中成型。制得的保温板性能优良，其性能指标如表2所示。
表2
Figure 201110279042X100002DEST_PATH_IMAGE002
 
实施例3
本发明的海泡石改性泡沫水泥保温板材料，其组份及配比为，PO52.5水泥：70%，粉煤灰（Ⅱ级）：18.0%，海泡石（1.0mm）：10%，丙烯酸乳胶粉：1.0%，减水剂（聚羧酸类减水剂）：0.2%，PP纤维（6mm规格的聚丙烯纤维）：0.15%，憎水剂（有机硅类憎水剂）：0.15%，复合发泡剂：0.5%，将以上除复合发泡剂外的其他材料按水灰比0.55加入到水中搅拌均匀，再将上述复合发泡剂加入水中利用机械制得的泡沫390L，将泡沫倒入搅拌均匀的浆料中搅拌均匀，将搅拌好的液料倒入模具中成型。制得的保温板性能优良，其性能指标如表3所示。
表3
实施例4
本发明的海泡石改性泡沫水泥保温板材料，其组份及配比为，PO52.5水泥：70%，粉煤灰（Ⅰ级）：20%，海泡石（0.9mm）：8%，丙烯酸乳胶粉：1.0%，减水剂（聚羧酸类减水剂）：0.2%，PP纤维（6mm规格的聚丙烯纤维）：0.1%，憎水剂（有机硅类憎水剂）：0.15%，复合发泡剂：0.55%，将以上除复合发泡剂外的其他材料按水灰比0.55加入到水中搅拌均匀，再将上述复合发泡剂加入水中利用机械制得的泡沫430L，将泡沫倒入搅拌均匀的浆料中搅拌均匀，将搅拌好的液料倒入模具中成型。制得的保温板性能优良，其性能指标如表4所示。
                                      表4     
Figure 201110279042X100002DEST_PATH_IMAGE004
由上述实施例1～4可知，海泡石改性泡沫水泥保温板材料可以制备不同导热系数的保温板材料，且具有良好的强度、保温隔热效果、耐水和耐候性能。各项指标满足需求，可以作为高性能保温材料使用。

Claims (9)

1.一种海泡石改性泡沫水泥保温板材料，其特征在于，包括如下组分及重量百分比含量：
胶凝材料：               70～80％                       
粉煤灰：                 10～20％
海泡石：                  5～10％
可再分散乳胶粉：       0.5～1.5％
减水剂：               0.2～0.4％
PP纤维：               0.1～0.2％
憎水剂：              0.15～0.2％
复合发泡剂：           0.45～0.6%。
2.根据权利要求1所述的海泡石改性泡沫水泥保温板材料，其特征在于，所述的复合发泡剂通过机械设备制得泡沫，所述泡沫体积为300L～450L。
3.根据权利要求1所述的海泡石改性泡沫水泥保温板材料，其特征在于，所述的胶凝材料为52.5普通硅酸盐水泥。
4.根据权利要求1所述的海泡石改性泡沫水泥保温板材料，其特征在于，所述的粉煤灰为2级或2级以上等级。
5.根据权利要求1所述的海泡石改性泡沫水泥保温板材料，其特征在于，所述的海泡石为平均粒径为0.6mm～1mm的海泡石。
6.根据权利要求1所述的海泡石改性泡沫水泥保温板材料，其特征在于，所述的可再分散乳胶粉为丙烯酸乳胶粉。
7.根据权利要求1所述的海泡石改性泡沫水泥保温板材料，其特征在于，所述的减水剂为聚羧酸类减水剂。
8.根据权利要求1所述的海泡石改性泡沫水泥保温板材料，其特征在于，所述的PP纤维为6mm规格的聚丙烯纤维。
9.根据权利要求1所述的海泡石改性泡沫水泥保温板材料，其特征在于，所述的憎水剂为有机硅类憎水剂。
CN 201110279042 2011-09-20 2011-09-20 海泡石改性泡沫水泥保温板材料 Expired - Fee Related CN102424559B (zh)