CN102390965A - 环保型墙体饰面砂浆 - Google Patents
环保型墙体饰面砂浆 Download PDFInfo
- Publication number
- CN102390965A CN102390965A CN 201110221255 CN201110221255A CN102390965A CN 102390965 A CN102390965 A CN 102390965A CN 201110221255 CN201110221255 CN 201110221255 CN 201110221255 A CN201110221255 A CN 201110221255A CN 102390965 A CN102390965 A CN 102390965A
- Authority
- CN
- China
- Prior art keywords
- wall facing
- powder
- facing mortar
- mortar
- environment
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明公开了一种环保型墙体饰面砂浆,包括重量百分比合理匹配的400目汉白玉粉、80目汉白玉粉、可再分散胶粉、白水泥、纤维素醚、木质纤维、分散剂、消泡剂和淀粉醚;本发明采用合理粒度的汉白玉粉为主料,配以含量较低的有机胶粉及其它添加剂,使用于外墙面具有现有外墙饰面砂浆的全部优点,能够保证使用强度和稳定性,饰面长时间使用后不会变色,表面光滑,性质致密光亮,具有较强的耐沾污性和自清洁能力,同时,减小胶粉及添加剂含量,不会造成较大的环境污染,利于环保。
Description
技术领域
本发明涉及建筑领域的外墙施工材料,特别涉及一种墙体饰面砂浆。
背景技术
饰面砂浆是一种新型饰面材料,颜色变化范围广,造型丰富。一般由无机胶凝材料、填料、添加剂和骨料所组成的用于建筑墙体表面及顶棚装饰的材料。与现有涂料饰面和瓷砖饰面相比,其材料性能与外保温体系中的抹面砂浆相似,其弹性模量、热膨胀系数等热力学性能与抹面砂浆相近。与涂料等有机材料制备的饰面层相比,饰面砂浆与外保温系统具有更好的匹配性和相容性。与瓷砖饰面相比,饰面砂浆层厚度仅为1~3mm,质量轻,作为高层建筑饰面层时,不会因负风压等问题出现掉砖现象。但是,饰面砂浆存在易泛碱、易出现色差、接茬、耐沾污性和自清洁能力差等一些问题,影响周围环境;并且自身强度较差,使其应用受到阻碍。
现有技术中,为了克服上述问题,出现了一系列饰面砂浆材料,分别针对不同的问题进行不同的配方调配,能达到相应的技术效果,但是针对其他问题则无法进行解决。比如,为增加强度及保持色调,则会添加较大比例的胶粉及添加剂,影响饰面砂浆的环保性能。
因此,需要一种饰面砂浆,使用于外墙面具有现有外墙饰面砂浆的全部优点,具有较好的强度和稳定性,具有较强的耐沾污性和自清洁能力,同时,减小胶粉及添加剂含量,利于环保。
发明内容
有鉴于此,本发明的目的是提供一种环保型墙体饰面砂浆,使用于外墙面具有现有外墙饰面砂浆的全部优点,具有较好的强度和稳定性,具有较强的耐沾污性和自清洁能力,同时,减小胶粉及添加剂含量,利于环保。
本发明的环保型墙体饰面砂浆,按重量百分比包括下列组分:400目汉白玉粉:41-47%,80目汉白玉粉:21-27%,可再分散胶粉:12-16%,白水泥:12-17%,纤维素醚:0.1-0.3%,木质纤维:0.15-0.25%,分散剂:0.18-0.3%,消泡剂:0.1-0.17%,淀粉醚:0.015-0.05%。
进一步,按重量百分比包括下列组分:400目汉白玉粉:44.4%,80目汉白玉粉:25.78%,可再分散胶粉:14%,白水泥:15%,纤维素醚:0.2%,木质纤维:0.2%,分散剂:0.25%,消泡剂:0.15%,淀粉醚:0.02%;
进一步,所述可再分散胶粉为丙烯酸胶粉,所述纤维素醚为甲基纤维素常醚,所述分散剂为甲基纤维素,所述淀粉醚为羟烷基淀粉。
本发明的有益效果是:本发明的环保型墙体饰面砂浆,采用合理粒度的汉白玉粉为主料,80目汉白玉粉和400目汉白玉粉合理配比,保证强度的同时保证表面光洁度,配以含量较低的有机胶粉及其它添加剂,使用于外墙面具有现有外墙饰面砂浆的全部优点,能够保证使用强度和稳定性,饰面长时间使用后不会变色,表面光滑,性质致密光亮,具有较强的耐沾污性和自清洁能力,同时,减小胶粉及添加剂含量,不会造成较大的环境污染,利于环保。
具体实施方式
实施例一
本实施例的环保型墙体饰面砂浆,按重量百分比包括下列组分:按重量百分比包括下列组分:400目汉白玉粉:44.4%,80目汉白玉粉:25.78%,可再分散胶粉:14%,白水泥:15%,纤维素醚:0.2%,木质纤维:0.2%,分散剂:0.25%,消泡剂:0.15%,淀粉醚:0.02%;
其中,可再分散胶粉为丙烯酸胶粉,所述纤维素醚为甲基纤维素常醚,所述分散剂为甲基纤维素,所述淀粉醚为羟烷基淀粉,当然也可使用砂浆专用可再分散胶粉、纤维素醚和淀粉醚,均能实现发明目的;消泡剂为聚醚与脂肪醇反应后经疏水分散配置而成的砂浆专用消泡剂,外购获得。
本实施例的饰面砂浆具有优异的物理性能,外观为粉状,使用成形后抗折强度为3.5/MPa,抗压强度为6MPa,使用时刮涂没有障碍,初期干燥且应用12个月无裂纹,无明显耐候性缺陷,无可见泛碱,并且无变色,表面细致光亮;
由此可见,本发明降低有机胶以及其他添加剂的使用,达到比现有技术饰面砂浆要好的理化性能,并保证了环保性。
实施例二
本实施例的环保型墙体饰面砂浆,按重量百分比包括下列组分:400目汉白玉粉:41%,80目汉白玉粉:27%,可再分散胶粉:14.035%,白水泥:17%,纤维素醚:0.3%,木质纤维:0.25%,分散剂:0.3%,消泡剂:0.1%,淀粉醚:0.015%。
其中,可再分散胶粉为丙烯酸胶粉,所述纤维素醚为甲基纤维素常醚,所述分散剂为甲基纤维素,所述淀粉醚为羟烷基淀粉,当然也可使用砂浆专用可再分散胶粉、纤维素醚和淀粉醚,均能实现发明目的;消泡剂为聚醚与脂肪醇反应后经疏水分散配置而成的砂浆专用消泡剂,外购获得。
本实施例的饰面砂浆具有优异的物理性能,外观为粉状,使用成形后抗折强度为2.9/MPa,抗压强度为5MPa,使用时刮涂没有障碍,初期干燥且应用12个月无裂纹,无明显耐候性缺陷,无可见泛碱,并且无变色,表面细致光亮;
由此可见,本发明降低有机胶以及其他添加剂的使用,达到比现有技术饰面砂浆要好的理化性能,并保证了环保性。
实施例三
本实施例的环保型墙体饰面砂浆,按重量百分比包括下列组分:400目汉白玉粉:47%,80目汉白玉粉:21%,可再分散胶粉:16%,白水泥:15.35%,纤维素醚:0.1%,木质纤维:0.15%,分散剂:0.18%,消泡剂:0.17%,淀粉醚:0.05%。
其中,可再分散胶粉为丙烯酸胶粉,所述纤维素醚为甲基纤维素常醚,所述分散剂为甲基纤维素,所述淀粉醚为羟烷基淀粉,当然也可使用砂浆专用可再分散胶粉、纤维素醚和淀粉醚,均能实现发明目的;消泡剂为聚醚与脂肪醇反应后经疏水分散配置而成的砂浆专用消泡剂,外购获得。
本实施例的饰面砂浆具有优异的物理性能,外观为粉状,使用成形后抗折强度为3.4/MPa,抗压强度为5.3MPa,使用时刮涂没有障碍,初期干燥且应用12个月无裂纹,无明显耐候性缺陷,无可见泛碱,并且无变色,表面细致光亮;
由此可见,本发明降低有机胶以及其他添加剂的使用,达到比现有技术饰面砂浆要好的理化性能,并保证了环保性。
实施例四
本实施例的环保型墙体饰面砂浆,按重量百分比包括下列组分:400目汉白玉粉:44.93%,80目汉白玉粉:27%,可再分散胶粉:15%,白水泥:12%,纤维素醚:0.3%,木质纤维:0.25%,分散剂:0.3%,消泡剂:0.17%,淀粉醚:0.05%。
其中,可再分散胶粉为丙烯酸胶粉,所述纤维素醚为甲基纤维素常醚,所述分散剂为甲基纤维素,所述淀粉醚为羟烷基淀粉,当然也可使用砂浆专用可再分散胶粉、纤维素醚和淀粉醚,均能实现发明目的;消泡剂为聚醚与脂肪醇反应后经疏水分散配置而成的砂浆专用消泡剂,外购获得。
本实施例的饰面砂浆具有优异的物理性能,外观为粉状,使用成形后抗折强度为3.25/MPa,抗压强度为5.41MPa,使用时刮涂没有障碍,初期干燥且应用12个月无裂纹,无明显耐候性缺陷,无可见泛碱,并且无变色,表面细致光亮;
由此可见,本发明降低有机胶以及其他添加剂的使用,达到比现有技术饰面砂浆要好的理化性能,并保证了环保性。
实施例五
400目汉白玉粉:47%,80目汉白玉粉:24.93%,可再分散胶粉:12%,白水泥:15%,纤维素醚:0.3%,木质纤维:0.25%,分散剂:0.3%,消泡剂:0.17%,淀粉醚:0.05%。
其中,可再分散胶粉为丙烯酸胶粉,所述纤维素醚为甲基纤维素常醚,所述分散剂为甲基纤维素,所述淀粉醚为羟烷基淀粉,当然也可使用砂浆专用可再分散胶粉、纤维素醚和淀粉醚,均能实现发明目的;消泡剂为聚醚与脂肪醇反应后经疏水分散配置而成的砂浆专用消泡剂,外购获得。
本实施例的饰面砂浆具有优异的物理性能,外观为粉状,使用成形后抗折强度为3.71/MPa,抗压强度为5.29MPa,使用时刮涂没有障碍,初期干燥且应用12个月无裂纹,无明显耐候性缺陷,无可见泛碱,并且无变色,表面细致光亮;
由此可见,本发明降低有机胶以及其他添加剂的使用,达到比现有技术饰面砂浆要好的理化性能,并保证了环保性。
最后说明的是,以上实施例仅用以说明本发明的技术方案而非限制,尽管参照较佳实施例对本发明进行了详细说明,本领域的普通技术人员应当理解,可以对本发明的技术方案进行修改或者等同替换,而不脱离本发明技术方案的宗旨和范围,其均应涵盖在本发明的权利要求范围当中。
Claims (3)
1.一种环保型墙体饰面砂浆,其特征在于:按重量百分比包括下列组分:400目汉白玉粉:41-47%,80目汉白玉粉:21-27%,可再分散胶粉:12-16%,白水泥:12-17%,纤维素醚:0.1-0.3%,木质纤维:0.15-0.25%,分散剂:0.18-0.3%,消泡剂:0.1-0.17%,淀粉醚:0.015-0.05%。
2.根据权利要求1所述的环保型墙体饰面砂浆,其特征在于:按重量百分比包括下列组分:400目汉白玉粉:44.4%,80目汉白玉粉:25.78%,可再分散胶粉:14%,白水泥:15%,纤维素醚:0.2%,木质纤维:0.2%,分散剂:0.25%,消泡剂:0.15%,淀粉醚:0.02%。
3.根据权利要求1或2所述的环保型墙体饰面砂浆,其特征在于:所述可再分散胶粉为丙烯酸胶粉,所述纤维素醚为甲基纤维素常醚,所述分散剂为甲基纤维素,所述淀粉醚为羟烷基淀粉。