CN102383314A - Rain-proof anti-stain fabric - Google Patents
Rain-proof anti-stain fabric Download PDFInfo
- Publication number
- CN102383314A CN102383314A CN2011102147613A CN201110214761A CN102383314A CN 102383314 A CN102383314 A CN 102383314A CN 2011102147613 A CN2011102147613 A CN 2011102147613A CN 201110214761 A CN201110214761 A CN 201110214761A CN 102383314 A CN102383314 A CN 102383314A
- Authority
- CN
- China
- Prior art keywords
- fabric
- coating
- polyurethane
- acrylonitrile
- butadiene rubber
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a rain-proof anti-stain fabric. The rain-proof anti-stain fabric comprises a fabric body and a coating which is coated on the surface of the fabric body, wherein a high polymer blending method is used for blending polyurethane with nitrile rubbers, thereby forming the coating. The coating is coated on the surface of the fabric body, so that the fabric has the function of resisting rain and stain.
Description
Technical field:
The present invention relates to a kind of fabric that can be rainproof and antifouling.
Background technology:
Fabric is clothes the most frequently used in people's daily life, and it is fit to throughout the year, the dress of different occasion, is loved by the people.Wear because mostly fabric is outer, be easy to make dirty, cleaning dirty also directly influence is attractive in appearance.Meanwhile, existing fabric does not have rainproof function, therefore on fabric, applies to have the coating of waterproofing function; Can improve the function of use of fabric, in the rainy day or prominent meet when raining heavyly people; Particularly dislike people, just need not worry again that fabric is drenched with rain gear.In addition, refuse the water coating, can also improve the look and feel of fabric, increase its added value of product through increase.
The polyurethane coating adhesive occurs on market early; Extensive application in the fabric coating industry at home and abroad; Can be used for sizing, stamp and back arrangement, the textiles with it was put in order has advantages such as well-pressed, attractive in appearance; But also come with some shortcomings, relatively poor etc. such as WATER REPELLENCY and low temperature feel.
Acrylonitrile-butadiene rubber is made through emulsion polymerization by butadiene and acrylonitrile, and it has fabulous oil resistivity, excellent water tolerance, good wear resistance and heat resistance.
Summary of the invention:
The invention provides a kind of have rainproof and fabric anti-pollution function.
Technical scheme of the present invention is: a kind of rainproof antifouling fabric, it comprises the fabric body and is coated in the coating on the fabric body surface.
As optimal technical scheme, said coating is processed by polyurethane and acrylonitrile-butadiene rubber.
As more preferably technical scheme, said coating is that polyurethane and the acrylonitrile-butadiene rubber of 10:90～20:80 processed by weight ratio.
The preparation method of coating is: polyurethane is dissolved in toluene gets solution A, acrylonitrile-butadiene rubber, vulcanizing agent are dissolved in toluene get solution B, under 15～25 ℃ of conditions, A and B two solution are mixed and stir 1～1.5h, mixing speed 1000～2000r/min.
The invention has the advantages that:
1, the present invention adopts the high polymer blend method; Polyurethane and acrylonitrile-butadiene rubber are carried out the mixed coating that gets; Have the advantage of well-pressed, attractive in appearance, oil resistivity and water-tolerant concurrently, overcome defectives such as polyurethane WATER REPELLENCY and low temperature feel be relatively poor simultaneously.
2, be used for rainproof antifouling coating owing on the surface of fabric body, being coated with, make it be difficult for making dirty, and when running into wind and rain, can play the effect of windproof and rain proof.
The specific embodiment
Below in conjunction with embodiment the present invention is described in further detail.
Embodiment 1
A kind of rainproof antifouling fabric comprises the fabric body and is coated in the coating on the fabric body surface that this coating is processed by polyurethane and acrylonitrile-butadiene rubber.
The coating proportioning:
Polyurethane 10 weight portions
Acrylonitrile-butadiene rubber 90 weight portions
The preparation method of coating is:
Polyurethane is dissolved in toluene gets solution A, acrylonitrile-butadiene rubber, vulcanizing agent are dissolved in toluene get solution B, under 15 ℃ of conditions, with A and mixing of B two solution and stirring 1h, mixing speed 1000r/min promptly gets.
Embodiment 2
A kind of rainproof antifouling fabric comprises the fabric body and is coated in the coating on the fabric body surface that this coating is processed by polyurethane and acrylonitrile-butadiene rubber.
The coating proportioning:
Polyurethane 20 weight portions
Acrylonitrile-butadiene rubber 80 weight portions
The preparation method of coating is:
Polyurethane is dissolved in toluene gets solution A, acrylonitrile-butadiene rubber, vulcanizing agent are dissolved in toluene get solution B, under 25 ℃ of conditions, with A and mixing of B two solution and stirring 1.5h, mixing speed 2000r/min promptly gets.
Embodiment 3
A kind of rainproof antifouling fabric comprises the fabric body and is coated in the coating on the fabric body surface that this coating is processed by polyurethane and acrylonitrile-butadiene rubber.
The coating proportioning:
Polyurethane 15 weight portions
Acrylonitrile-butadiene rubber 85 weight portions
The preparation method of coating is:
Polyurethane is dissolved in toluene gets solution A, acrylonitrile-butadiene rubber, vulcanizing agent are dissolved in toluene get solution B, under 20 ℃ of conditions, with A and mixing of B two solution and stirring 1.2h, mixing speed 1500r/min promptly gets.
Embodiment 4
Polyurethane coating and embodiment 1, embodiment 2 and embodiment 3 gained coatings are applied on the identical material fabric test WATER REPELLENCY respectively.Experiment shows, polyurethane and acrylonitrile-butadiene rubber is mixed that the water repellency of coating will obviously be superior to polyurethane, and WATER REPELLENCY improves with the increase of blending ratio.The result sees table 1.
Table 1 blending ratio is to the influence of WATER REPELLENCY
Claims (3)
1. rainproof antifouling fabric is characterized in that: it comprises the fabric body and is coated in the coating on the fabric body surface; Described coating is processed by polyurethane and acrylonitrile-butadiene rubber.
2. rainproof antifouling fabric according to claim 1; The preparation method who it is characterized in that said coating is: polyurethane is dissolved in toluene gets solution A; Acrylonitrile-butadiene rubber, vulcanizing agent are dissolved in toluene get solution B; Under 15～25 ℃ of conditions, A and B two solution are mixed and stir 1～1.5h, mixing speed 1000～2000r/min.
3. according to each described rainproof antifouling fabric of claim 1-2, the weight ratio that it is characterized in that polyurethane and acrylonitrile-butadiene rubber is 10:90～20:80.