CN102352567A - Rainproof antifouling clothing - Google Patents
Rainproof antifouling clothing Download PDFInfo
- Publication number
- CN102352567A CN102352567A CN2011102147670A CN201110214767A CN102352567A CN 102352567 A CN102352567 A CN 102352567A CN 2011102147670 A CN2011102147670 A CN 2011102147670A CN 201110214767 A CN201110214767 A CN 201110214767A CN 102352567 A CN102352567 A CN 102352567A
- Authority
- CN
- China
- Prior art keywords
- clothing
- coating
- rainproof
- acrylonitrile
- butadiene rubber
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a rainproof antifouling clothing comprising a clothing body and a coating coated on the surface of the clothing. According to the invention, poly(1,4-butylene adipate) and nitrile butadiene rubber are mixed through a high polymer blending method, such that the coating is prepared. Because the coating is coated on the surface of the clothing, the clothing is rainproof and antifouling.
Description
Technical field:
The present invention relates to a kind of clothing that can be rainproof and antifouling.
Background technology:
Clothing is clothes the most frequently used in people's daily life, and it is fit to throughout the year, the dress of different occasion, is loved by the people.Wear because mostly clothing is outer, be easy to make dirty, cleaning dirty also directly influence is attractive in appearance.Meanwhile, existing clothing does not have rainproof function, therefore on clothing, applies to have the coating of waterproofing function; Can improve the function of use of clothing, in the rainy day or prominent meet when raining heavyly people; Particularly dislike people, just need not worry again that clothing is drenched with rain gear.In addition, refuse the water coating, can also improve the look and feel of fabric, increase its added value of product through increase.
Gather (1; 4-butylene adipate ester) coating adhesive occurs on market early; Extensive application in the fabric coating industry at home and abroad; Can be used for sizing, stamp and back arrangement; The textiles of putting in order with it; Have advantages such as well-pressed, attractive in appearance, but also come with some shortcomings, relatively poor etc. such as WATER REPELLENCY and low temperature feel.
Acrylonitrile-butadiene rubber is made through emulsion polymerization by butadiene and acrylonitrile, and it has fabulous oil resistivity, excellent water tolerance, good wear resistance and heat resistance.
Summary of the invention:
The invention provides a kind of have rainproof and clothing anti-pollution function.
Technical scheme of the present invention is: a kind of rainproof antifouling clothing, it comprises the clothing body and is coated in the coating on the clothing body surface.
As optimal technical scheme, said coating is processed by gathering (1,4-butylene adipate ester) and acrylonitrile-butadiene rubber.
As more preferably technical scheme, said coating by weight ratio be 10:90～20:80 gather (1,4-butylene adipate ester) and acrylonitrile-butadiene rubber is processed.
The preparation method of coating is: will gather (1; 4-butylene adipate ester) being dissolved in toluene gets solution A, acrylonitrile-butadiene rubber, vulcanizing agent is dissolved in toluene gets solution B, under 15～25 ℃ of conditions; A and B two solution are mixed and stir 1～1.5h, mixing speed 1000～2000r/min.
The invention has the advantages that:
1, the present invention adopts the high polymer blend method; To gather (1,4-butylene adipate ester) and acrylonitrile-butadiene rubber and carry out mixed coating, have the advantage of well-pressed, attractive in appearance, oil resistivity and water-tolerant concurrently; Overcome simultaneously and gathered defectives such as (1,4-butylene adipate ester) WATER REPELLENCY and low temperature feel be relatively poor.
2, be used for rainproof antifouling coating owing on the surface of clothing body, being coated with, make it be difficult for making dirty, and when running into wind and rain, can play the effect of windproof and rain proof.
The specific embodiment
Below in conjunction with embodiment the present invention is described in further detail.
Embodiment 1
A kind of rainproof antifouling clothing comprises the clothing body and is coated in the coating on the clothing body surface that this coating is processed by gathering (1,4-butylene adipate ester) and acrylonitrile-butadiene rubber.
The coating proportioning:
Gather (1,4-butylene adipate ester) 10 weight portions
Acrylonitrile-butadiene rubber 90 weight portions
The preparation method of coating is:
To gather (1,4-butylene adipate ester) and be dissolved in toluene and get solution A, and acrylonitrile-butadiene rubber, vulcanizing agent will be dissolved in toluene get solution B, and under 15 ℃ of conditions, A and B two solution are mixed and stir 1h, mixing speed 1000r/min promptly gets.
Embodiment 2
A kind of rainproof antifouling clothing comprises the clothing body and is coated in the coating on the clothing body surface that this coating is processed by gathering (1,4-butylene adipate ester) and acrylonitrile-butadiene rubber.
The coating proportioning:
Gather (1,4-butylene adipate ester) 20 weight portions
Acrylonitrile-butadiene rubber 80 weight portions
The preparation method of coating is:
To gather (1,4-butylene adipate ester) and be dissolved in toluene and get solution A, and acrylonitrile-butadiene rubber, vulcanizing agent will be dissolved in toluene get solution B, and under 25 ℃ of conditions, A and B two solution are mixed and stir 1.5h, mixing speed 2000r/min promptly gets.
Embodiment 3
A kind of rainproof antifouling clothing comprises the clothing body and is coated in the coating on the clothing body surface that this coating is processed by gathering (1,4-butylene adipate ester) and acrylonitrile-butadiene rubber.
The coating proportioning:
Gather (1,4-butylene adipate ester) 15 weight portions
Acrylonitrile-butadiene rubber 85 weight portions
The preparation method of coating is:
To gather (1,4-butylene adipate ester) and be dissolved in toluene and get solution A, and acrylonitrile-butadiene rubber, vulcanizing agent will be dissolved in toluene get solution B, and under 20 ℃ of conditions, A and B two solution are mixed and stir 1.2h, mixing speed 1500r/min promptly gets.
Embodiment 4
To gather (1,4-butylene adipate ester) coating and embodiment 1, embodiment 2 and embodiment 3 gained coatings and be applied to respectively on the identical material clothing, the test WATER REPELLENCY.Experiment shows, it is mixed that the water repellency of coating will obviously be better than gathering (1,4-butylene adipate ester) to gather (1,4-butylene adipate ester) and acrylonitrile-butadiene rubber, and WATER REPELLENCY improves with the increase of blending ratio.The result sees table 1.
Table 1 blending ratio is to the influence of WATER REPELLENCY
Claims (3)
1. rainproof antifouling clothing is characterized in that: it comprises the clothing body and is coated in the coating on the clothing body surface; Described coating is processed by gathering (1,4-butylene adipate ester) and acrylonitrile-butadiene rubber.
2. rainproof antifouling clothing according to claim 1; The preparation method who it is characterized in that said coating is: will gather (1; 4-butylene adipate ester) being dissolved in toluene gets solution A; Acrylonitrile-butadiene rubber, vulcanizing agent are dissolved in toluene get solution B; Under 15～25 ℃ of conditions; A and B two solution are mixed and stir 1～1.5h, mixing speed 1000～2000r/min.
3. according to each described rainproof antifouling clothing of claim 1-2, it is characterized in that gathering (1,4-butylene adipate ester) and the weight ratio of acrylonitrile-butadiene rubber is 10:90～20:80.